Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+

Detalhes bibliográficos
Autor(a) principal: Alvarenga, Thiago Lemos
Data de Publicação: 2019
Outros Autores: thiagoalvar.fis@gmail.com
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
Texto Completo: http://www.bdtd.uerj.br/handle/1/19468
Resumo: This dissertation aims to synthesize, perform the structural analyze, and study the optical properties of samples composed of a crystal lattice of Zn2SnO4 doped with 0, 01% of divalent cobalt (Co2+). This compound was synthetized by solid state reaction with ultrapure reagents ZnO, SnO2 and CoCO3. The structural properties were obtained by X-ray diffraction. Regarding optical analysis, the spectrum of photoluminescence and excitation were obtained at room temperature and atmospheric pressure. The decay time was measured as well. Based on the Tanabe-Sugano theory the energy transitions were found, therefore the crystalline field parameter (Dq) and the Racah parameters (B and C) were determined. Analyzing the emission spectrum,it were found a broadband in the visible region and one in the infrared region.
id UERJ_b8824e7df8cef725c951f41d804e493c
oai_identifier_str oai:www.bdtd.uerj.br:1/19468
network_acronym_str UERJ
network_name_str Biblioteca Digital de Teses e Dissertações da UERJ
repository_id_str 2903
spelling Sosman, Lilian Pantojahttp://lattes.cnpq.br/9044572545913697López Giménez, Ada Petronilahttp://lattes.cnpq.br/4872736700717227Carvalho, Isabel Cristina dos Santoshttp://lattes.cnpq.br/6140495391360571Reyes López, Daniel Lorenzohttp://lattes.cnpq.br/3217874049382279Pedro, Sandra da Silvahttp://lattes.cnpq.br/1301843346193578Melo, Gabriel Burlandy Mota dehttp://lattes.cnpq.br/5671151404568126http://lattes.cnpq.br/1472520507631748Alvarenga, Thiago Lemosthiagoalvar.fis@gmail.com2023-04-27T22:13:36Z2019-08-02ALVARENGA, Thiago Lemos. Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+. 2019. 60 f. Dissertação (Mestrado em Física) - Instituto de Física Armando Dias Tavares, Universidade do Estado do Rio de Janeiro, Rio de Janeiro, 2019.http://www.bdtd.uerj.br/handle/1/19468This dissertation aims to synthesize, perform the structural analyze, and study the optical properties of samples composed of a crystal lattice of Zn2SnO4 doped with 0, 01% of divalent cobalt (Co2+). This compound was synthetized by solid state reaction with ultrapure reagents ZnO, SnO2 and CoCO3. The structural properties were obtained by X-ray diffraction. Regarding optical analysis, the spectrum of photoluminescence and excitation were obtained at room temperature and atmospheric pressure. The decay time was measured as well. Based on the Tanabe-Sugano theory the energy transitions were found, therefore the crystalline field parameter (Dq) and the Racah parameters (B and C) were determined. Analyzing the emission spectrum,it were found a broadband in the visible region and one in the infrared region.Esta dissertação teve como objetivo sintetizar, realizar a análise estrutural e estudar as propriedades ópticas de amostras compostas por uma rede cristalina de Zn2SnO4 dopadas com 0, 01% de cobalto divalente (Co2+). O composto foi sintetizado pelo método do estado sólido e foram utilizados os seguintes regentes ultrapuros: ZnO, SnO2, e CoCO3. As propriedades estruturais foram obtidas através da difração de raios X. Em relação à análise óptica, foram obtidos espectros, à temperatura ambiente e pressão atmosférica e ao nível do mar, de fotoluminescência e de excitação da amostra, também foram realizadas medidas de tempo de vida radiativo. Com base na teoria de Tanabe-Sugano os transições de energia foram encontradas e, com isso, o parâmetro de campo cristalino (Dq) e os parâmetros de Racah (B e C) foram determinados. Nos espectros de emissão foi encontrada uma banda larga na região de visível com baricentro em 694 nm atribuída à transição permitida por spin 4T1(4P) 4 A2(4F) e uma banda na região do infravermelho centrada em 851 nm referente à transição, também permita por spin, [4T1(4P) → 4 A2(4F)]. A partir do espectros de emissão foram encontrados os parâmetros B = 783 cm−1, Dq = 266 cm−1, C = 3524 cm−1 e Dq/B = 0, 34Submitted by Teresa Silva CTC/D (teresadasilvarj@gmail.com) on 2023-04-27T22:13:36Z No. of bitstreams: 1 Dissertação - Thiago Lemos Alvarenga - 2019 - Completa.pdf: 3018610 bytes, checksum: df6bec0f3ab4874ae27be18381601233 (MD5)Made available in DSpace on 2023-04-27T22:13:36Z (GMT). No. of bitstreams: 1 Dissertação - Thiago Lemos Alvarenga - 2019 - Completa.pdf: 3018610 bytes, checksum: df6bec0f3ab4874ae27be18381601233 (MD5) Previous issue date: 2019-08-02Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfporUniversidade do Estado do Rio de JaneiroPrograma de Pós-Graduação em FísicaUERJBrasilCentro de Tecnologia e Ciências::Instituto de Física Armando Dias TavaresPhotoluminescenceX-rays diffractionCobaltZinc stannateSolid stateFotoluminescênciaRaios X - DifraçãoCobaltoEstanato de zincoZn2SnO4Estado sólidoCIENCIAS EXATAS E DA TERRA::FISICA::FISICA DA MATERIA CONDENSADAPreparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+Synthesis, structural properties and photoluminescence of Zn2SnO4 : Co2+info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da UERJinstname:Universidade do Estado do Rio de Janeiro (UERJ)instacron:UERJORIGINALDissertação - Thiago Lemos Alvarenga - 2019 - Completa.pdfDissertação - Thiago Lemos Alvarenga - 2019 - Completa.pdfapplication/pdf3018610http://www.bdtd.uerj.br/bitstream/1/19468/2/Disserta%C3%A7%C3%A3o+-+Thiago+Lemos+Alvarenga+-+2019+-+Completa.pdfdf6bec0f3ab4874ae27be18381601233MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-82123http://www.bdtd.uerj.br/bitstream/1/19468/1/license.txte5502652da718045d7fcd832b79fca29MD511/194682024-02-27 15:40:27.54oai:www.bdtd.uerj.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://www.bdtd.uerj.br/PUBhttps://www.bdtd.uerj.br:8443/oai/requestbdtd.suporte@uerj.bropendoar:29032024-02-27T18:40:27Biblioteca Digital de Teses e Dissertações da UERJ - Universidade do Estado do Rio de Janeiro (UERJ)false
dc.title.por.fl_str_mv Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
dc.title.alternative.eng.fl_str_mv Synthesis, structural properties and photoluminescence of Zn2SnO4 : Co2+
title Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
spellingShingle Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
Alvarenga, Thiago Lemos
Photoluminescence
X-rays diffraction
Cobalt
Zinc stannate
Solid state
Fotoluminescência
Raios X - Difração
Cobalto
Estanato de zinco
Zn2SnO4
Estado sólido
CIENCIAS EXATAS E DA TERRA::FISICA::FISICA DA MATERIA CONDENSADA
title_short Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
title_full Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
title_fullStr Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
title_full_unstemmed Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
title_sort Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+
author Alvarenga, Thiago Lemos
author_facet Alvarenga, Thiago Lemos
thiagoalvar.fis@gmail.com
author_role author
author2 thiagoalvar.fis@gmail.com
author2_role author
dc.contributor.advisor1.fl_str_mv Sosman, Lilian Pantoja
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/9044572545913697
dc.contributor.advisor-co1.fl_str_mv López Giménez, Ada Petronila
dc.contributor.advisor-co1Lattes.fl_str_mv http://lattes.cnpq.br/4872736700717227
dc.contributor.referee1.fl_str_mv Carvalho, Isabel Cristina dos Santos
dc.contributor.referee1Lattes.fl_str_mv http://lattes.cnpq.br/6140495391360571
dc.contributor.referee2.fl_str_mv Reyes López, Daniel Lorenzo
dc.contributor.referee2Lattes.fl_str_mv http://lattes.cnpq.br/3217874049382279
dc.contributor.referee3.fl_str_mv Pedro, Sandra da Silva
dc.contributor.referee3Lattes.fl_str_mv http://lattes.cnpq.br/1301843346193578
dc.contributor.referee4.fl_str_mv Melo, Gabriel Burlandy Mota de
dc.contributor.referee4Lattes.fl_str_mv http://lattes.cnpq.br/5671151404568126
dc.contributor.authorLattes.fl_str_mv http://lattes.cnpq.br/1472520507631748
dc.contributor.author.fl_str_mv Alvarenga, Thiago Lemos
thiagoalvar.fis@gmail.com
contributor_str_mv Sosman, Lilian Pantoja
López Giménez, Ada Petronila
Carvalho, Isabel Cristina dos Santos
Reyes López, Daniel Lorenzo
Pedro, Sandra da Silva
Melo, Gabriel Burlandy Mota de
dc.subject.eng.fl_str_mv Photoluminescence
X-rays diffraction
Cobalt
Zinc stannate
Solid state
topic Photoluminescence
X-rays diffraction
Cobalt
Zinc stannate
Solid state
Fotoluminescência
Raios X - Difração
Cobalto
Estanato de zinco
Zn2SnO4
Estado sólido
CIENCIAS EXATAS E DA TERRA::FISICA::FISICA DA MATERIA CONDENSADA
dc.subject.por.fl_str_mv Fotoluminescência
Raios X - Difração
Cobalto
Estanato de zinco
Zn2SnO4
Estado sólido
dc.subject.cnpq.fl_str_mv CIENCIAS EXATAS E DA TERRA::FISICA::FISICA DA MATERIA CONDENSADA
description This dissertation aims to synthesize, perform the structural analyze, and study the optical properties of samples composed of a crystal lattice of Zn2SnO4 doped with 0, 01% of divalent cobalt (Co2+). This compound was synthetized by solid state reaction with ultrapure reagents ZnO, SnO2 and CoCO3. The structural properties were obtained by X-ray diffraction. Regarding optical analysis, the spectrum of photoluminescence and excitation were obtained at room temperature and atmospheric pressure. The decay time was measured as well. Based on the Tanabe-Sugano theory the energy transitions were found, therefore the crystalline field parameter (Dq) and the Racah parameters (B and C) were determined. Analyzing the emission spectrum,it were found a broadband in the visible region and one in the infrared region.
publishDate 2019
dc.date.issued.fl_str_mv 2019-08-02
dc.date.accessioned.fl_str_mv 2023-04-27T22:13:36Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv ALVARENGA, Thiago Lemos. Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+. 2019. 60 f. Dissertação (Mestrado em Física) - Instituto de Física Armando Dias Tavares, Universidade do Estado do Rio de Janeiro, Rio de Janeiro, 2019.
dc.identifier.uri.fl_str_mv http://www.bdtd.uerj.br/handle/1/19468
identifier_str_mv ALVARENGA, Thiago Lemos. Preparação, propriedades estruturais e fotoluminescência do Zn2SnO4 : Co2+. 2019. 60 f. Dissertação (Mestrado em Física) - Instituto de Física Armando Dias Tavares, Universidade do Estado do Rio de Janeiro, Rio de Janeiro, 2019.
url http://www.bdtd.uerj.br/handle/1/19468
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Universidade do Estado do Rio de Janeiro
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Física
dc.publisher.initials.fl_str_mv UERJ
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Centro de Tecnologia e Ciências::Instituto de Física Armando Dias Tavares
publisher.none.fl_str_mv Universidade do Estado do Rio de Janeiro
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da UERJ
instname:Universidade do Estado do Rio de Janeiro (UERJ)
instacron:UERJ
instname_str Universidade do Estado do Rio de Janeiro (UERJ)
instacron_str UERJ
institution UERJ
reponame_str Biblioteca Digital de Teses e Dissertações da UERJ
collection Biblioteca Digital de Teses e Dissertações da UERJ
bitstream.url.fl_str_mv http://www.bdtd.uerj.br/bitstream/1/19468/2/Disserta%C3%A7%C3%A3o+-+Thiago+Lemos+Alvarenga+-+2019+-+Completa.pdf
http://www.bdtd.uerj.br/bitstream/1/19468/1/license.txt
bitstream.checksum.fl_str_mv df6bec0f3ab4874ae27be18381601233
e5502652da718045d7fcd832b79fca29
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da UERJ - Universidade do Estado do Rio de Janeiro (UERJ)
repository.mail.fl_str_mv bdtd.suporte@uerj.br
_version_ 1811728729185976320

Registros relacionados