Análise de citotoxicidade, desmineralização e potencial clareador de géis clareadores experimentais, baseado em peróxido de carbamida 15% adicionados de nano-hidróxiapatita

• Autor(a) principal: Moreira, Rudá França
• Data de Publicação: 2018
• Tipo de documento: Tese
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/14063
• topic: Carbamide peroxide; Tooth whitening; Hydroxyapatite; Dental sensitivity; Peróxido de carbamida; Clareamento dental; Hidroxiapatita; Sensibilidade dental; CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA

Dental whitening is considered a very safe, quick and pleasant procedure, making it one of the most accomplished procedures in dentistry. However, it has some side effects, the main one being sensibility, which can be caused by cytotoxicity, demineralization, oxygen arrival in the dental pulp and the degradation of the interprismatic region facilitating the stimulation in the dentin tubes. Therefore, the present study evaluated the demineralization, cytotoxicity and bleaching potential of 15% carbamide peroxide-based (PC) based bleaching gels added with 5% and 10% nano-hydroxyapatite (n-Hap) particles. For the chromatic evaluation, 36 bovine incisors were divided into 3 groups: Group 1 PC 15%, Group 2 PC 15% added 5% nHap and group 3 PC 15% with 10% n-Hap, measuring the color before and after the the CIELAB coordinates were analyzed to verify the color difference (Δe) obtained between the groups and within the group (L *). After the statistical analysis it was verified that all the gels were able to lighten and there were no differences between the groups. Cytotoxicity was verified by optical density of viable cells after treatment with MTT and 1: 800 of the bleach and gel preparations containing 5% and 10% nHap applied in L929 cells. In this case, the groups were statistically unequal, presenting 15% PC as the most toxic, followed by PC 15% added with 10% n-Hap and the best result was obtained by the 5% n-Hap increased gel. The mineral content analysis was performed by X-ray Fluorescence by energy dispersion, where it was necessary to use 15 bovine teeth, which had their middle sections sectioned, embedded in epoxy resin and planned, and were divided into groups of 5 CPs, each CP was measured at 8 different points before and after, at the same points of the bleaching therapy, then it was verified that the experimental gels presented a lower loss of Ca and P, however there were no statistical differences between groups 2 and 3. On the face of the limitations of the present in vitro study, it is possible to conclude that the experimental gels were effective in reducing the cytotoxicity and demineralization without losing the effectiveness of the bleaching therapy.