Caracterização de folhas de alumínio de uso doméstico por XRF
Autor(a) principal: | |
---|---|
Data de Publicação: | 2020 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da UERJ |
Texto Completo: | http://www.bdtd.uerj.br/handle/1/16462 |
Resumo: | The aluminum metal, due to its property of being infinitely recyclable, can, in each recycling cycle, accumulate undesirable impurities influencing the quality of the final product and, mainly, in aluminum sheets for domestic use that are used indiscriminately by consumers due to lack of knowledge. or incentive from aluminum associations. Over time, that is, with a longer recycling cycle, the amount of impurities the amount of impurities increases and a limit can be reached for secondary aluminum (from scrap) becoming unsuitable for industries. To check these impurities, XRF analysis was used. Five samples were used, four produced in Brazil and one produced in Italy and tripled in a total of fifteen samples. The XRF analysis was performed with the Epsilon 1 equipment from Panalytical. The norm of the Brazilian Association of Technical Standards (ABNT) on aluminum alloy 8011, rich in iron and silicon for the production of aluminum sheets for domestic use, the XRF analysis detected and quantified impurities four to five times greater than the limit tolerable for the alloy. The norm of the National Health Surveillance Agency (Anvisa) on metallic materials in contact with food, all samples were within the tolerable limit, however this norm includes all metals indiscriminately. The European Parliament's 2004 regulation on aluminum in contact with food and beverages from kitchen utensils to machinery for food processing, only the Italian sample exceeded the iron limit. Greater inspection by ANVISA in aluminum foil factories for domestic use is proposed. |
id |
UERJ_df103ceef757bdbdac01922fd7e263e5 |
---|---|
oai_identifier_str |
oai:www.bdtd.uerj.br:1/16462 |
network_acronym_str |
UERJ |
network_name_str |
Biblioteca Digital de Teses e Dissertações da UERJ |
repository_id_str |
2903 |
spelling |
Assis, Joaquim Teixeira dehttp://lattes.cnpq.br/7307238902576135Anjos, Marcelino José doshttp://lattes.cnpq.br/8175635608970623Oliveira, Davi Ferreira dehttp://lattes.cnpq.br/6571271495588914http://lattes.cnpq.br/5205153803194761Bittencourt Junior, Carlos Augusto da Mata2021-08-18T12:56:35Z2020-03-05BITTENCOURT JUNIOR, Carlos Augusto da Mata. Caracterização de folhas de alumínio de uso doméstico por XRF. 2020. 68 f. Dissertação (Mestrado em Ciência e Tecnologia de Materiais) - Universidade do Estado do Rio de Janeiro, Nova Friburgo, 2020.http://www.bdtd.uerj.br/handle/1/16462The aluminum metal, due to its property of being infinitely recyclable, can, in each recycling cycle, accumulate undesirable impurities influencing the quality of the final product and, mainly, in aluminum sheets for domestic use that are used indiscriminately by consumers due to lack of knowledge. or incentive from aluminum associations. Over time, that is, with a longer recycling cycle, the amount of impurities the amount of impurities increases and a limit can be reached for secondary aluminum (from scrap) becoming unsuitable for industries. To check these impurities, XRF analysis was used. Five samples were used, four produced in Brazil and one produced in Italy and tripled in a total of fifteen samples. The XRF analysis was performed with the Epsilon 1 equipment from Panalytical. The norm of the Brazilian Association of Technical Standards (ABNT) on aluminum alloy 8011, rich in iron and silicon for the production of aluminum sheets for domestic use, the XRF analysis detected and quantified impurities four to five times greater than the limit tolerable for the alloy. The norm of the National Health Surveillance Agency (Anvisa) on metallic materials in contact with food, all samples were within the tolerable limit, however this norm includes all metals indiscriminately. The European Parliament's 2004 regulation on aluminum in contact with food and beverages from kitchen utensils to machinery for food processing, only the Italian sample exceeded the iron limit. Greater inspection by ANVISA in aluminum foil factories for domestic use is proposed.O metal alumínio, devido a sua propriedade de ser infinitamente reciclável pode, a cada ciclo de reciclagem, acumular impurezas indesejáveis influenciando a qualidade do produto final e, principalmente, nas folhas de alumínio para uso doméstico que são utilizadas indiscriminadamente pelos consumidores por falta de conhecimento ou incentivo das associações de alumínio. Com o passar do tempo, ou seja, com um maior ciclo de reciclagem, a quantidade de impurezas a quantidade de impurezas aumenta e pode-se chegar a um limite para o alumínio secundário (a partir da sucata) tornando-se impróprio para as indústrias. Para verificar essas impurezas utilizou-se a análise XRF. Cinco amostras foram utilizadas, quatro produzidas no Brasil e uma produzida na Itália e triplicadas em um total de quinze amostras. A análise por XRF foram feitas com o equipamento Epsilon 1 da Panalytical. A norma da Associação Brasileira de Normas Técnicas (ABNT) sobre a liga de alumínio 8011, rica em ferro e silício para a produção das folhas de alumínio de uso doméstico, a análise XRF detectou e quantificou impurezas de quatro a cinco vezes maior que o limite tolerável para a liga. A norma da Agência Nacional de Vigilância Sanitária (Anvisa) sobre materiais metálicos em contato com alimentos, todas as amostras estavam no limite do tolerável, porém esta norma inclui todos os metais indiscriminadamente. O regulamento do Parlamento Europeu de 2004 sobre alumínio em contato com alimentos e bebidas desde utensílios de cozinha a maquinários para processamento de alimentos, apenas a amostra italiana excedeu o limite em ferro. Uma maior fiscalização da ANVISA nas fábricas de folhas de alumínio para uso doméstico é proposta.Submitted by Pâmela CTC/E (pamela.flegr@uerj.br) on 2021-08-18T12:56:35Z No. of bitstreams: 1 Dissertação - Carlos Augusto da Mata Bittencourt Junior - 2021 - Completa.pdf: 2408159 bytes, checksum: 311d7cae1186ee978afceaa3f799298c (MD5)Made available in DSpace on 2021-08-18T12:56:35Z (GMT). No. of bitstreams: 1 Dissertação - Carlos Augusto da Mata Bittencourt Junior - 2021 - Completa.pdf: 2408159 bytes, checksum: 311d7cae1186ee978afceaa3f799298c (MD5) Previous issue date: 2020-03-05Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfporUniversidade do Estado do Rio de JaneiroPrograma de Pós-Graduação em Ciência e Tecnologia de MateriaisUERJBrasilCentro de Tecnologia e Ciências::Instituto PolitécnicoAluminumAluminum alloy 8011Aluminum foilX-Ray FluorescenceAlumínioLiga de alumínio 8011Folhas de alumínioFluorescência de raios XTensões residuaisENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA::ESTRUTURA DOS METAIS E LIGASCaracterização de folhas de alumínio de uso doméstico por XRFCharacterization of household aluminum foils by XRFinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da UERJinstname:Universidade do Estado do Rio de Janeiro (UERJ)instacron:UERJORIGINALDissertação - Carlos Augusto da Mata Bittencourt Junior - 2021 - Completa.pdfDissertação - Carlos Augusto da Mata Bittencourt Junior - 2021 - Completa.pdfapplication/pdf2408159http://www.bdtd.uerj.br/bitstream/1/16462/2/Disserta%C3%A7%C3%A3o+-+Carlos+Augusto+da+Mata+Bittencourt+Junior+-+2021+-+Completa.pdf311d7cae1186ee978afceaa3f799298cMD52LICENSElicense.txtlicense.txttext/plain; charset=utf-82123http://www.bdtd.uerj.br/bitstream/1/16462/1/license.txte5502652da718045d7fcd832b79fca29MD511/164622024-02-27 14:29:38.715oai:www.bdtd.uerj.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://www.bdtd.uerj.br/PUBhttps://www.bdtd.uerj.br:8443/oai/requestbdtd.suporte@uerj.bropendoar:29032024-02-27T17:29:38Biblioteca Digital de Teses e Dissertações da UERJ - Universidade do Estado do Rio de Janeiro (UERJ)false |
dc.title.por.fl_str_mv |
Caracterização de folhas de alumínio de uso doméstico por XRF |
dc.title.alternative.eng.fl_str_mv |
Characterization of household aluminum foils by XRF |
title |
Caracterização de folhas de alumínio de uso doméstico por XRF |
spellingShingle |
Caracterização de folhas de alumínio de uso doméstico por XRF Bittencourt Junior, Carlos Augusto da Mata Aluminum Aluminum alloy 8011 Aluminum foil X-Ray Fluorescence Alumínio Liga de alumínio 8011 Folhas de alumínio Fluorescência de raios X Tensões residuais ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA::ESTRUTURA DOS METAIS E LIGAS |
title_short |
Caracterização de folhas de alumínio de uso doméstico por XRF |
title_full |
Caracterização de folhas de alumínio de uso doméstico por XRF |
title_fullStr |
Caracterização de folhas de alumínio de uso doméstico por XRF |
title_full_unstemmed |
Caracterização de folhas de alumínio de uso doméstico por XRF |
title_sort |
Caracterização de folhas de alumínio de uso doméstico por XRF |
author |
Bittencourt Junior, Carlos Augusto da Mata |
author_facet |
Bittencourt Junior, Carlos Augusto da Mata |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Assis, Joaquim Teixeira de |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/7307238902576135 |
dc.contributor.referee1.fl_str_mv |
Anjos, Marcelino José dos |
dc.contributor.referee1Lattes.fl_str_mv |
http://lattes.cnpq.br/8175635608970623 |
dc.contributor.referee2.fl_str_mv |
Oliveira, Davi Ferreira de |
dc.contributor.referee2Lattes.fl_str_mv |
http://lattes.cnpq.br/6571271495588914 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/5205153803194761 |
dc.contributor.author.fl_str_mv |
Bittencourt Junior, Carlos Augusto da Mata |
contributor_str_mv |
Assis, Joaquim Teixeira de Anjos, Marcelino José dos Oliveira, Davi Ferreira de |
dc.subject.eng.fl_str_mv |
Aluminum Aluminum alloy 8011 Aluminum foil X-Ray Fluorescence |
topic |
Aluminum Aluminum alloy 8011 Aluminum foil X-Ray Fluorescence Alumínio Liga de alumínio 8011 Folhas de alumínio Fluorescência de raios X Tensões residuais ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA::ESTRUTURA DOS METAIS E LIGAS |
dc.subject.por.fl_str_mv |
Alumínio Liga de alumínio 8011 Folhas de alumínio Fluorescência de raios X Tensões residuais |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::METALURGIA FISICA::ESTRUTURA DOS METAIS E LIGAS |
description |
The aluminum metal, due to its property of being infinitely recyclable, can, in each recycling cycle, accumulate undesirable impurities influencing the quality of the final product and, mainly, in aluminum sheets for domestic use that are used indiscriminately by consumers due to lack of knowledge. or incentive from aluminum associations. Over time, that is, with a longer recycling cycle, the amount of impurities the amount of impurities increases and a limit can be reached for secondary aluminum (from scrap) becoming unsuitable for industries. To check these impurities, XRF analysis was used. Five samples were used, four produced in Brazil and one produced in Italy and tripled in a total of fifteen samples. The XRF analysis was performed with the Epsilon 1 equipment from Panalytical. The norm of the Brazilian Association of Technical Standards (ABNT) on aluminum alloy 8011, rich in iron and silicon for the production of aluminum sheets for domestic use, the XRF analysis detected and quantified impurities four to five times greater than the limit tolerable for the alloy. The norm of the National Health Surveillance Agency (Anvisa) on metallic materials in contact with food, all samples were within the tolerable limit, however this norm includes all metals indiscriminately. The European Parliament's 2004 regulation on aluminum in contact with food and beverages from kitchen utensils to machinery for food processing, only the Italian sample exceeded the iron limit. Greater inspection by ANVISA in aluminum foil factories for domestic use is proposed. |
publishDate |
2020 |
dc.date.issued.fl_str_mv |
2020-03-05 |
dc.date.accessioned.fl_str_mv |
2021-08-18T12:56:35Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
BITTENCOURT JUNIOR, Carlos Augusto da Mata. Caracterização de folhas de alumínio de uso doméstico por XRF. 2020. 68 f. Dissertação (Mestrado em Ciência e Tecnologia de Materiais) - Universidade do Estado do Rio de Janeiro, Nova Friburgo, 2020. |
dc.identifier.uri.fl_str_mv |
http://www.bdtd.uerj.br/handle/1/16462 |
identifier_str_mv |
BITTENCOURT JUNIOR, Carlos Augusto da Mata. Caracterização de folhas de alumínio de uso doméstico por XRF. 2020. 68 f. Dissertação (Mestrado em Ciência e Tecnologia de Materiais) - Universidade do Estado do Rio de Janeiro, Nova Friburgo, 2020. |
url |
http://www.bdtd.uerj.br/handle/1/16462 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade do Estado do Rio de Janeiro |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Tecnologia de Materiais |
dc.publisher.initials.fl_str_mv |
UERJ |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Centro de Tecnologia e Ciências::Instituto Politécnico |
publisher.none.fl_str_mv |
Universidade do Estado do Rio de Janeiro |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da UERJ instname:Universidade do Estado do Rio de Janeiro (UERJ) instacron:UERJ |
instname_str |
Universidade do Estado do Rio de Janeiro (UERJ) |
instacron_str |
UERJ |
institution |
UERJ |
reponame_str |
Biblioteca Digital de Teses e Dissertações da UERJ |
collection |
Biblioteca Digital de Teses e Dissertações da UERJ |
bitstream.url.fl_str_mv |
http://www.bdtd.uerj.br/bitstream/1/16462/2/Disserta%C3%A7%C3%A3o+-+Carlos+Augusto+da+Mata+Bittencourt+Junior+-+2021+-+Completa.pdf http://www.bdtd.uerj.br/bitstream/1/16462/1/license.txt |
bitstream.checksum.fl_str_mv |
311d7cae1186ee978afceaa3f799298c e5502652da718045d7fcd832b79fca29 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da UERJ - Universidade do Estado do Rio de Janeiro (UERJ) |
repository.mail.fl_str_mv |
bdtd.suporte@uerj.br |
_version_ |
1792352344842698752 |