Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento

Detalhes bibliográficos
Autor(a) principal: Sassi, Marco
Data de Publicação: 2006
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
Texto Completo: http://www.bdtd.uerj.br/handle/1/16522
Resumo: Nowadays, aesthetic restorations are very common among our dental practice. Dental Ceramics are the main indicated material, because of its functional and aesthetic characteristics. Commonly, the glaze layer is removed during finishing procedures. The purpose of this study was to evaluate the effect of four finishing and polishing procedures on the surface roughness of one feldspathic ceramic, EX-3 Noritake. The efficacy of polishing with felt discs and paste was also analyzed. Initially, 40 ceramic disks were divided into 5 groups (n=8): Group 1 – Control; Group 2 – Komet Burs; Group 3 – Komet Silicone Polishers; Group 4 - Ceramisté Points Shofu; Group 5 – Experimental Points. Average surface roughness (Ra) in micrometers was measured and the specimens received additional polishing with felt disks and paste. Then, 4 new groups were formed: Group 6 – Modified Komet Burs; Group 7 – Modified Ceramisté Points Shofu; Group 8 – Modified Komet Silicone Polishers; Group 9 – Modified Experimental Points. Average surface roughness (Ra) in micrometers was again measured and data were treated with ANOVA and Tuckey test, p< 0,05. Means and standard deviations were, respectively: Group 1: 0,34 ± 0,05; Group 2: 0,48 ± 0,06; Group 3: 0,64 ± 0,06; Group 4: 0,42 ± 0,06; Group 5: 0,63 ± 0,06; Group 6: 0,31 ± 0,04; Group 7: 0,33 ± 0,04; Group 8: 0,47 ± 0,10; Group 9: 0,35 ± 0,08. Data analysis showed that the additional polishing with felt discs and paste was determinant in reducing roughness levels. The Ceramisté points Shofu leaded to the smoothest surface without additional polishing
id UERJ_e917ef3d6235cf0247259451a7c3f215
oai_identifier_str oai:www.bdtd.uerj.br:1/16522
network_acronym_str UERJ
network_name_str Biblioteca Digital de Teses e Dissertações da UERJ
repository_id_str 2903
spelling Souza, Hilda Maria Montes Ribeiro dehttp://lattes.cnpq.br/8040991247472108Gouvêa, Cresus Vinicius Depes dehttp://lattes.cnpq.br/9924799549240650Sampaio Filho, Hélio Rodrigueshttp://lattes.cnpq.br/6120571127063735Silva, Paulo Sérgio Souza dahttp://lattes.cnpq.br/7197484985614645http://lattes.cnpq.br/2047398976780169Sassi, Marco2021-08-31T13:09:53Z2006-02-07SASSI, Marco. Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento. 2006. 47 f. Dissertação (Mestrado em Odontologia) - Faculdade de Odontologia, Universidade do Estado do Rio de Janeiro, Rio de Janeiro, 2006.http://www.bdtd.uerj.br/handle/1/16522Nowadays, aesthetic restorations are very common among our dental practice. Dental Ceramics are the main indicated material, because of its functional and aesthetic characteristics. Commonly, the glaze layer is removed during finishing procedures. The purpose of this study was to evaluate the effect of four finishing and polishing procedures on the surface roughness of one feldspathic ceramic, EX-3 Noritake. The efficacy of polishing with felt discs and paste was also analyzed. Initially, 40 ceramic disks were divided into 5 groups (n=8): Group 1 – Control; Group 2 – Komet Burs; Group 3 – Komet Silicone Polishers; Group 4 - Ceramisté Points Shofu; Group 5 – Experimental Points. Average surface roughness (Ra) in micrometers was measured and the specimens received additional polishing with felt disks and paste. Then, 4 new groups were formed: Group 6 – Modified Komet Burs; Group 7 – Modified Ceramisté Points Shofu; Group 8 – Modified Komet Silicone Polishers; Group 9 – Modified Experimental Points. Average surface roughness (Ra) in micrometers was again measured and data were treated with ANOVA and Tuckey test, p< 0,05. Means and standard deviations were, respectively: Group 1: 0,34 ± 0,05; Group 2: 0,48 ± 0,06; Group 3: 0,64 ± 0,06; Group 4: 0,42 ± 0,06; Group 5: 0,63 ± 0,06; Group 6: 0,31 ± 0,04; Group 7: 0,33 ± 0,04; Group 8: 0,47 ± 0,10; Group 9: 0,35 ± 0,08. Data analysis showed that the additional polishing with felt discs and paste was determinant in reducing roughness levels. The Ceramisté points Shofu leaded to the smoothest surface without additional polishingA busca por alternativas restauradoras estéticas é, nos dias de hoje, uma constante por parte dos que procuram os consultórios odontológicos. Neste contexto, as porcelanas odontológicas ocupam lugar de destaque, por suas propriedades funcionais e estéticas. Entretanto, freqüentemente, ajustes na superfície da restauração são necessários, removendo a camada superficial do glaze, especialmente em restaurações do tipo inlay/onlay, onde o ajuste só é possível após a cimentação. O controle da textura de superfície torna-se, então, especialmente importante, uma vez que superfícies cerâmicas rugosas têm sido relacionadas a problemas como desgaste da dentição antagonista, retenção do biofilme e até fratura da restauração. Este trabalho procurou comparar a rugosidade de superfície obtida por 4 diferentes sistemas de acabamento e polimento, além da porcelana glazeada (controle). As análises foram efetuadas por leitura em rugosímetro e análise em Microscopia Eletrônica de Varredura. A eficácia do uso de pastas de polimento também foi avaliada. 40 discos cerâmicos foram divididos inicialmente em 5 grupos: Grupo 1 – Controle; Grupo 2 – Brocas Komet; Grupo 3 – Pontas abrasivas Komet; Grupo 4 – Pontas Ceramisté Shofu; Grupo 5 – Experimental. Após a leitura da rugosidade de superfície (Ra), os corpos-de-prova dos grupos 2, 3, 4 e 5 receberam polimento adicional com discos de feltro e pasta para polimento, originando: Grupo 6 – Brocas Komet Modificado; Grupo 7 – Pontas Ceramisté Shofu modificado; Grupo 8 – Pontas abrasivas Komet Modificado; Grupo 9 – Experimental Modificado. Novas leituras de rugosidade de superfície foram, então, efetuadas. Os dados foram tratados com ANOVA e teste de Tuckey, levando às seguintes médias e desvios-padrão: Grupo 1: 0,34 ± 0,05; Grupo 2: 0,48 ± 0,06; Grupo 3: 0,64 ± 0,06; Grupo 4: 0,42 ± 0,06; Grupo 5: 0,63 ± 0,06; Grupo 6: 0,31 ± 0,04; Grupo 7: 0,33 ± 0,04; Grupo 8: 0,47 ± 0,10; Grupo 9: 0,35 ± 0,08. A análise dos dados mostrou que o polimento adicional com discos de feltro e pasta levou a valores menores de rugosidade superficial. O Sistema que proporcionou a superfície mais lisa sem o uso de pasta de polimento foram as Pontas Ceramisté ShofuSubmitted by Adriana CB/B (adrianajana@uerj.br) on 2021-08-31T13:09:53Z No. of bitstreams: 1 DISSERTAÇÃO - MARCO SASSI - 2006 -Completa.pdf: 1350869 bytes, checksum: b32306b35f060fa923a7ee67123279ce (MD5)Made available in DSpace on 2021-08-31T13:09:53Z (GMT). No. of bitstreams: 1 DISSERTAÇÃO - MARCO SASSI - 2006 -Completa.pdf: 1350869 bytes, checksum: b32306b35f060fa923a7ee67123279ce (MD5) Previous issue date: 2006-02-07application/pdfporUniversidade do Estado do Rio de JaneiroPrograma de Pós-Graduação em OdontologiaUERJBrasilCentro Biomédico::Faculdade de OdontologiaCeramicFinishingRoughnessDental PorcelainSurface PropertiesDental PolishingPorcelanaAcabamentoRugosidadePorcelana DentáriaPropriedades de SuperfíciePolimento DentárioCIENCIAS DA SAUDE::ODONTOLOGIA::MATERIAIS ODONTOLOGICOSAvaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimentoSurface roughness evaluation of one feldspathic ceramic submitted to four different finishing and polishing systemsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da UERJinstname:Universidade do Estado do Rio de Janeiro (UERJ)instacron:UERJORIGINALDissertação - Marco Sassi - 2006 - Completa.pdfDissertação - Marco Sassi - 2006 - Completa.pdfapplication/pdf1350869http://www.bdtd.uerj.br/bitstream/1/16522/2/Disserta%C3%A7%C3%A3o+-+Marco+Sassi+-+2006+-+Completa.pdfb32306b35f060fa923a7ee67123279ceMD52LICENSElicense.txtlicense.txttext/plain; charset=utf-82123http://www.bdtd.uerj.br/bitstream/1/16522/1/license.txte5502652da718045d7fcd832b79fca29MD511/165222024-02-26 20:13:06.845oai:www.bdtd.uerj.br:1/16522Tk9UQTogTElDRU7Dh0EgUkVERSBTSVJJVVMKRXN0YSBsaWNlbsOnYSBkZSBleGVtcGxvIMOpIGZvcm5lY2lkYSBhcGVuYXMgcGFyYSBmaW5zIGluZm9ybWF0aXZvcy4KCkxJQ0VOw4dBIERFIERJU1RSSUJVScOHw4NPIE7Dg08tRVhDTFVTSVZBCgpDb20gYSBhcHJlc2VudGHDp8OjbyBkZXN0YSBsaWNlbsOnYSwgdm9jw6ogKG8gYXV0b3IgKGVzKSBvdSBvIHRpdHVsYXIgZG9zIGRpcmVpdG9zIGRlIGF1dG9yKSBjb25jZWRlIMOgIFVuaXZlcnNpZGFkZSAKZG8gRXN0YWRvIGRvIFJpbyBkZSBKYW5laXJvIChVRVJKKSBvIGRpcmVpdG8gbsOjby1leGNsdXNpdm8gZGUgcmVwcm9kdXppciwgIHRyYWR1emlyIChjb25mb3JtZSBkZWZpbmlkbyBhYmFpeG8pLCBlL291IApkaXN0cmlidWlyIGEgc3VhIHRlc2Ugb3UgZGlzc2VydGHDp8OjbyAoaW5jbHVpbmRvIG8gcmVzdW1vKSBwb3IgdG9kbyBvIG11bmRvIG5vIGZvcm1hdG8gaW1wcmVzc28gZSBlbGV0csO0bmljbyBlIAplbSBxdWFscXVlciBtZWlvLCBpbmNsdWluZG8gb3MgZm9ybWF0b3Mgw6F1ZGlvIG91IHbDrWRlby4KClZvY8OqIGNvbmNvcmRhIHF1ZSBhIFVFUkogcG9kZSwgc2VtIGFsdGVyYXIgbyBjb250ZcO6ZG8sIHRyYW5zcG9yIGEgc3VhIHRlc2Ugb3UgZGlzc2VydGHDp8OjbyAKcGFyYSBxdWFscXVlciBtZWlvIG91IGZvcm1hdG8gcGFyYSBmaW5zIGRlIHByZXNlcnZhw6fDo28uCgpWb2PDqiB0YW1iw6ltIGNvbmNvcmRhIHF1ZSBhIFVFUkogcG9kZSBtYW50ZXIgbWFpcyBkZSB1bWEgY8OzcGlhIGEgc3VhIHRlc2Ugb3UgCmRpc3NlcnRhw6fDo28gcGFyYSBmaW5zIGRlIHNlZ3VyYW7Dp2EsIGJhY2stdXAgZSBwcmVzZXJ2YcOnw6NvLgoKVm9jw6ogZGVjbGFyYSBxdWUgYSBzdWEgdGVzZSBvdSBkaXNzZXJ0YcOnw6NvIMOpIG9yaWdpbmFsIGUgcXVlIHZvY8OqIHRlbSBvIHBvZGVyIGRlIGNvbmNlZGVyIG9zIGRpcmVpdG9zIGNvbnRpZG9zIApuZXN0YSBsaWNlbsOnYS4gVm9jw6ogdGFtYsOpbSBkZWNsYXJhIHF1ZSBvIGRlcMOzc2l0byBkYSBzdWEgdGVzZSBvdSBkaXNzZXJ0YcOnw6NvIG7Do28sIHF1ZSBzZWphIGRlIHNldSAKY29uaGVjaW1lbnRvLCBpbmZyaW5nZSBkaXJlaXRvcyBhdXRvcmFpcyBkZSBuaW5ndcOpbS4KCkNhc28gYSBzdWEgdGVzZSBvdSBkaXNzZXJ0YcOnw6NvIGNvbnRlbmhhIG1hdGVyaWFsIHF1ZSB2b2PDqiBuw6NvIHBvc3N1aSBhIHRpdHVsYXJpZGFkZSBkb3MgZGlyZWl0b3MgYXV0b3JhaXMsIHZvY8OqIApkZWNsYXJhIHF1ZSBvYnRldmUgYSBwZXJtaXNzw6NvIGlycmVzdHJpdGEgZG8gZGV0ZW50b3IgZG9zIGRpcmVpdG9zIGF1dG9yYWlzIHBhcmEgY29uY2VkZXIgw6AgVUVSSiBvcyBkaXJlaXRvcyBhcHJlc2VudGFkb3MgbmVzdGEgbGljZW7Dp2EsIGUgcXVlIGVzc2UgbWF0ZXJpYWwgZGUgcHJvcHJpZWRhZGUgZGUgdGVyY2Vpcm9zIGVzdMOhIGNsYXJhbWVudGUgCmlkZW50aWZpY2FkbyBlIHJlY29uaGVjaWRvIG5vIHRleHRvIG91IG5vIGNvbnRlw7pkbyBkYSB0ZXNlIG91IGRpc3NlcnRhw6fDo28gb3JhIGRlcG9zaXRhZGEuCgpDQVNPIEEgVEVTRSBPVSBESVNTRVJUQcOHw4NPIE9SQSBERVBPU0lUQURBIFRFTkhBIFNJRE8gUkVTVUxUQURPIERFIFVNIFBBVFJPQ8ONTklPIE9VIApBUE9JTyBERSBVTUEgQUfDik5DSUEgREUgRk9NRU5UTyBPVSBPVVRSTyBPUkdBTklTTU8gUVVFIE7Dg08gU0VKQSBFU1RBClVOSVZFUlNJREFERSwgVk9Dw4ogREVDTEFSQSBRVUUgUkVTUEVJVE9VIFRPRE9TIEUgUVVBSVNRVUVSIERJUkVJVE9TIERFIFJFVklTw4NPIENPTU8gClRBTULDiU0gQVMgREVNQUlTIE9CUklHQcOHw5VFUyBFWElHSURBUyBQT1IgQ09OVFJBVE8gT1UgQUNPUkRPLgoKQSBVbml2ZXJzaWRhZGUgZG8gRXN0YWRvIGRvIFJpbyBkZSBKYW5laXJvIChVRVJKKSBzZSBjb21wcm9tZXRlIGEgaWRlbnRpZmljYXIgY2xhcmFtZW50ZSBvIHNldSBub21lIChzKSBvdSBvKHMpIG5vbWUocykgZG8ocykgCmRldGVudG9yKGVzKSBkb3MgZGlyZWl0b3MgYXV0b3JhaXMgZGEgdGVzZSBvdSBkaXNzZXJ0YcOnw6NvLCBlIG7Do28gZmFyw6EgcXVhbHF1ZXIgYWx0ZXJhw6fDo28sIGFsw6ltIGRhcXVlbGFzIApjb25jZWRpZGFzIHBvciBlc3RhIGxpY2Vuw6dhLgo=Biblioteca Digital de Teses e Dissertaçõeshttp://www.bdtd.uerj.br/PUBhttps://www.bdtd.uerj.br:8443/oai/requestbdtd.suporte@uerj.bropendoar:29032024-02-26T23:13:06Biblioteca Digital de Teses e Dissertações da UERJ - Universidade do Estado do Rio de Janeiro (UERJ)false
dc.title.por.fl_str_mv Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
dc.title.alternative.eng.fl_str_mv Surface roughness evaluation of one feldspathic ceramic submitted to four different finishing and polishing systems
title Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
spellingShingle Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
Sassi, Marco
Ceramic
Finishing
Roughness
Dental Porcelain
Surface Properties
Dental Polishing
Porcelana
Acabamento
Rugosidade
Porcelana Dentária
Propriedades de Superfície
Polimento Dentário
CIENCIAS DA SAUDE::ODONTOLOGIA::MATERIAIS ODONTOLOGICOS
title_short Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
title_full Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
title_fullStr Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
title_full_unstemmed Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
title_sort Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento
author Sassi, Marco
author_facet Sassi, Marco
author_role author
dc.contributor.advisor1.fl_str_mv Souza, Hilda Maria Montes Ribeiro de
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/8040991247472108
dc.contributor.referee1.fl_str_mv Gouvêa, Cresus Vinicius Depes de
dc.contributor.referee1Lattes.fl_str_mv http://lattes.cnpq.br/9924799549240650
dc.contributor.referee2.fl_str_mv Sampaio Filho, Hélio Rodrigues
dc.contributor.referee2Lattes.fl_str_mv http://lattes.cnpq.br/6120571127063735
dc.contributor.referee3.fl_str_mv Silva, Paulo Sérgio Souza da
dc.contributor.referee3Lattes.fl_str_mv http://lattes.cnpq.br/7197484985614645
dc.contributor.authorLattes.fl_str_mv http://lattes.cnpq.br/2047398976780169
dc.contributor.author.fl_str_mv Sassi, Marco
contributor_str_mv Souza, Hilda Maria Montes Ribeiro de
Gouvêa, Cresus Vinicius Depes de
Sampaio Filho, Hélio Rodrigues
Silva, Paulo Sérgio Souza da
dc.subject.eng.fl_str_mv Ceramic
Finishing
Roughness
Dental Porcelain
Surface Properties
Dental Polishing
topic Ceramic
Finishing
Roughness
Dental Porcelain
Surface Properties
Dental Polishing
Porcelana
Acabamento
Rugosidade
Porcelana Dentária
Propriedades de Superfície
Polimento Dentário
CIENCIAS DA SAUDE::ODONTOLOGIA::MATERIAIS ODONTOLOGICOS
dc.subject.por.fl_str_mv Porcelana
Acabamento
Rugosidade
Porcelana Dentária
Propriedades de Superfície
Polimento Dentário
dc.subject.cnpq.fl_str_mv CIENCIAS DA SAUDE::ODONTOLOGIA::MATERIAIS ODONTOLOGICOS
description Nowadays, aesthetic restorations are very common among our dental practice. Dental Ceramics are the main indicated material, because of its functional and aesthetic characteristics. Commonly, the glaze layer is removed during finishing procedures. The purpose of this study was to evaluate the effect of four finishing and polishing procedures on the surface roughness of one feldspathic ceramic, EX-3 Noritake. The efficacy of polishing with felt discs and paste was also analyzed. Initially, 40 ceramic disks were divided into 5 groups (n=8): Group 1 – Control; Group 2 – Komet Burs; Group 3 – Komet Silicone Polishers; Group 4 - Ceramisté Points Shofu; Group 5 – Experimental Points. Average surface roughness (Ra) in micrometers was measured and the specimens received additional polishing with felt disks and paste. Then, 4 new groups were formed: Group 6 – Modified Komet Burs; Group 7 – Modified Ceramisté Points Shofu; Group 8 – Modified Komet Silicone Polishers; Group 9 – Modified Experimental Points. Average surface roughness (Ra) in micrometers was again measured and data were treated with ANOVA and Tuckey test, p< 0,05. Means and standard deviations were, respectively: Group 1: 0,34 ± 0,05; Group 2: 0,48 ± 0,06; Group 3: 0,64 ± 0,06; Group 4: 0,42 ± 0,06; Group 5: 0,63 ± 0,06; Group 6: 0,31 ± 0,04; Group 7: 0,33 ± 0,04; Group 8: 0,47 ± 0,10; Group 9: 0,35 ± 0,08. Data analysis showed that the additional polishing with felt discs and paste was determinant in reducing roughness levels. The Ceramisté points Shofu leaded to the smoothest surface without additional polishing
publishDate 2006
dc.date.issued.fl_str_mv 2006-02-07
dc.date.accessioned.fl_str_mv 2021-08-31T13:09:53Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv SASSI, Marco. Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento. 2006. 47 f. Dissertação (Mestrado em Odontologia) - Faculdade de Odontologia, Universidade do Estado do Rio de Janeiro, Rio de Janeiro, 2006.
dc.identifier.uri.fl_str_mv http://www.bdtd.uerj.br/handle/1/16522
identifier_str_mv SASSI, Marco. Avaliação da rugosidade superficial de uma porcelana feldspática frente ao uso de diferentes sistemas de acabamento e polimento. 2006. 47 f. Dissertação (Mestrado em Odontologia) - Faculdade de Odontologia, Universidade do Estado do Rio de Janeiro, Rio de Janeiro, 2006.
url http://www.bdtd.uerj.br/handle/1/16522
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Universidade do Estado do Rio de Janeiro
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Odontologia
dc.publisher.initials.fl_str_mv UERJ
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Centro Biomédico::Faculdade de Odontologia
publisher.none.fl_str_mv Universidade do Estado do Rio de Janeiro
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da UERJ
instname:Universidade do Estado do Rio de Janeiro (UERJ)
instacron:UERJ
instname_str Universidade do Estado do Rio de Janeiro (UERJ)
instacron_str UERJ
institution UERJ
reponame_str Biblioteca Digital de Teses e Dissertações da UERJ
collection Biblioteca Digital de Teses e Dissertações da UERJ
bitstream.url.fl_str_mv http://www.bdtd.uerj.br/bitstream/1/16522/2/Disserta%C3%A7%C3%A3o+-+Marco+Sassi+-+2006+-+Completa.pdf
http://www.bdtd.uerj.br/bitstream/1/16522/1/license.txt
bitstream.checksum.fl_str_mv b32306b35f060fa923a7ee67123279ce
e5502652da718045d7fcd832b79fca29
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da UERJ - Universidade do Estado do Rio de Janeiro (UERJ)
repository.mail.fl_str_mv bdtd.suporte@uerj.br
_version_ 1792352345766494208

Registros relacionados