Efeito de um primer autocondicionante na resistência ao cisalhamento de bráquetes com compósito pré-incorporado

• Autor(a) principal: Cal Neto, Julio Orrico de Aragão Pedra e
• Data de Publicação: 2005
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Biblioteca Digital de Teses e Dissertações da UERJ
• Texto Completo: http://www.bdtd.uerj.br/handle/1/14120
• topic: Adhesives; Dental acid etching; Dental enamel; Orthodontics; Adesivos; Condicionamento; Ácido dentário; Esmalte Dentário; Ortodontia; Adesivos dentários; Braquetes ortodônticos; Resistência ao cisalhamento; CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA::ORTODONTIA

The use of self-etching primers and precoated brackets are presented as alternatives to shorten the clinical bonding steps. The aim of this study was to evaluate the influence of a self-etching primer - SEP (Transbond Plus SEP, 3M Unitek) on shear bond strength of adhesive uncoated and precoated Victory brackets (3M Unitek). The sample group consisted of 23 patients with 4 premolars each one, equally divided in four different groups according to the bracket and enamel preparation. Brackets were bonded in vivo, by the same operator, using a split mouth random technique: Group 1- 37% Phosphoric acid + primer + composite + conventional Victory bracket; Group 2- 37% Phosphoric acid + primer + precoated Victory bracket; Group 3- SEP + composite + conventional bracket; Group 4- SEP + precoated bracket. After 30 days premolars were extracted for orthodontic reasons, and a Universal Testing Machine was used to apply an occlusal shear force directly to the enamel-bracket interface at a speed of 0.5 mm/min. Mean results and standard deviation for the groups were: Group 1 = 11,35 (2,36) MPa; Group 2 = 9,77 (2,49) MPa; Group 3 = 10,89 (2,60) MPa; e Group 4 = 10,16 (2,75) MPa. The groups were compared using 2-way ANOVA. No difference was observed while a conventional etching and primer or self-etching primer was used (p = 0.948). But, it was indicated significant differences in bond strength between uncoated and precoated brackets (p = 0.032). However, it could be concluded that the self etching primer combined with adhesive precoated brackets showed adequate shear bond strength, and may be suitable for clinical use.