Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar

Detalhes bibliográficos
Autor(a) principal: Santos, Bruno Henrique dos
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFABC
Texto Completo: http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300
Resumo: Orientadora: Profa. Dra. Márcia Aparecida da Silva Spinacé
id UFBC_539b85e8bdbb98a69be7ed018eff98b1
oai_identifier_str oai:BDTD:122300
network_acronym_str UFBC
network_name_str Repositório Institucional da UFABC
repository_id_str
spelling Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcarMATERIAIS COMPÓSITOS POLIMÉRICOSAMIDO TERMOPLÁSTICOBAGAÇO DE CANA-DE-AÇÚCARPOLYMERIC COMPOSITESTHERMOPLASTIC STARCHSUGARCANE BAGASSEPROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABCOrientadora: Profa. Dra. Márcia Aparecida da Silva SpinacéDissertação (mestrado) - Universidade Federal do ABC, Programa de Pós-Graduação em Nanociências e Materiais Avançados, Santo André, 2020.O Brasil é um grande gerador de resíduos lignocelulósicos provenientes da agroindústria. Consequentemente, vêm aumentando as pesquisas visando destinar de forma ambientalmente aceitável esses resíduos. Uma alternativa é substituir as fibras sintéticas como fase dispersa em biocompósitos poliméricos. Nesse projeto, foram preparados os compósitos de TPS e resíduos de bagaço de cana de açúcar por extrusão e moldagem por compressão. Foram avaliados o efeito do uso de fibras com diferentes faixas de tamanho e do tratamento alcalino das fibras com hidróxido de sódio e sulfito de sódio nas propriedades dos compósitos. As faixas de tamanho usadas foram: < 0,595 mm, 0,595 - 0,297 mm, 0,297 - 0,250 mm e > 0,250 mm; e as fibras foram tratadas por 30, 60, 120 e 240 min. As fibras, o TPS e os compósitos foram caracterizados por meio de análises químicas, mecânicas, térmicas e morfológicas. As fibras com diferentes faixas de tamanho apresentaram a mesma composição química e propriedades térmicas similares. Porém, os valores de índice de cristalinidade e a razão de aspecto são maiores para as fibras com maior tamanho, e os valores de absorção e teor de umidade são maiores para as fibras menores. A variação do período de tratamento alcalino não alterou significativamente as propriedades térmicas, morfologia, teor de umidade ou composição química das fibras. Verificou-se que 30 min de tratamento foram suficientes para remover 56 % de hemicelulose e 73 % de lignina indicando a eficiência do tratamento alcalino, e não foi verificado aumento da remoção destes componentes após esse período. Os compósitos de TPS com 10 % em massa (m/m) de fibras de bagaço de cana com diferentes tamanhos apresentaram propriedades mecânicas similares às do TPS. No entanto, o compósito com fibras com menor tamanho (< 595 mm) apresentou tendência a obter melhores propriedades mecânicas. O compósito com 10 % m/m de fibra (< 595 mm) e tratada por 30 min apresentou propriedade semelhante ao compósito usando fibra sem tratamento. Foram preparados compósitos com 20, 30 e 40% m/m de fibra (< 595 mm) sem tratamento e compósitos com 20 e 30 % m/m com fibras (< 595 mm) tratadas por 30 min. O compósito com 30 % m/m de fibra (< 595 mm) tratada por 30 min. apresentou um aumento de 135 % na tensão máxima, aumento de 770 % no módulo elástico comparado ao TPS e estabilidade térmica de aproximadamente 20 °C superior ao TPS puro.Brazil is a major generator of lignocellulosic waste from agribusiness. Consequently, research has been increasing in order to dispose of these residues in an environmentally acceptable way. An alternative is to replace synthetic fibers as a dispersed phase in polymeric biocomposites. In this project, composites of TPS and sugarcane bagasse residues were prepared by extrusion and compression molding. The effect of using fibers with different size ranges and the alkaline treatment of fibers with sodium hydroxide and sodium sulfite on the properties of the composites were evaluated. The size ranges used were: < 0.595 mm, 0.595 - 0.297 mm, 0.297 - 0.250 mm and > 0.250 mm; and the fibers were treated for 30, 60, 120 and 240 min. The fibers, TPS and composites were characterized by chemical, mechanical, thermal and morphological analysis. The fibers with different size ranges showed the same chemical composition and similar thermal properties. However, the crystallinity index values and the aspect ratio are higher for the fibers with larger size, and the absorption values and moisture content are higher for the smaller fibers. The variation in the alkaline treatment period did not significantly change the thermal properties, morphology, moisture content or chemical composition of the fibers. It was found that 30 min of treatment was sufficient to remove 56 % of hemicellulose and 73 % of lignin indicating the efficiency of the alkaline treatment, and there was no increase in the removal of these components after this period. TPS composites with 10 % by weight (wt%) of sugarcane bagasse fibers with different sizes showed similar mechanical properties to those of TPS. However, the composite with smaller fibers (<595 mm) tended to obtain better mechanical properties. The composite with 10 wt% fiber (<595 mm) and treated for 30 min showed similar properties to the composite using untreated fiber. Composites with 20, 30 and 40 wt% fiber (<595 mm) were prepared without treatment and composites with 20 and 30 wt% fiber (<595 mm) treated for 30 min. The composite with 30 wt% fiber (<595 mm) treated for 30 min. presented an increase of 135 % in the maximum tension, 770 % increase in the elastic modulus compared to TPS and thermal stability of 20 °C superior to pure TPS.Spinacé, Márcia Aparecida da SilvaBonse, Baltus CornelisFerreira, Mathilde Julienne Gisele ChampeauSantos, Bruno Henrique dos2020info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdf116 f. : il.http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300&midiaext=79615http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300&midiaext=79616Cover: http://biblioteca.ufabc.edu.br/php/capa.php?obra=122300Titanium dioxide recovery from paint manufacturing wash waterporreponame:Repositório Institucional da UFABCinstname:Universidade Federal do ABC (UFABC)instacron:UFABCinfo:eu-repo/semantics/openAccess2022-04-13T10:59:44Zoai:BDTD:122300Repositório InstitucionalPUBhttp://www.biblioteca.ufabc.edu.br/oai/oai.phpopendoar:2022-04-13T10:59:44Repositório Institucional da UFABC - Universidade Federal do ABC (UFABC)false
dc.title.none.fl_str_mv Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
title Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
spellingShingle Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
Santos, Bruno Henrique dos
MATERIAIS COMPÓSITOS POLIMÉRICOS
AMIDO TERMOPLÁSTICO
BAGAÇO DE CANA-DE-AÇÚCAR
POLYMERIC COMPOSITES
THERMOPLASTIC STARCH
SUGARCANE BAGASSE
PROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABC
title_short Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
title_full Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
title_fullStr Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
title_full_unstemmed Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
title_sort Caracterização de compósitos de amido termoplástico com fibras de bagaço de cana-de-açúcar
author Santos, Bruno Henrique dos
author_facet Santos, Bruno Henrique dos
author_role author
dc.contributor.none.fl_str_mv Spinacé, Márcia Aparecida da Silva
Bonse, Baltus Cornelis
Ferreira, Mathilde Julienne Gisele Champeau
dc.contributor.author.fl_str_mv Santos, Bruno Henrique dos
dc.subject.por.fl_str_mv MATERIAIS COMPÓSITOS POLIMÉRICOS
AMIDO TERMOPLÁSTICO
BAGAÇO DE CANA-DE-AÇÚCAR
POLYMERIC COMPOSITES
THERMOPLASTIC STARCH
SUGARCANE BAGASSE
PROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABC
topic MATERIAIS COMPÓSITOS POLIMÉRICOS
AMIDO TERMOPLÁSTICO
BAGAÇO DE CANA-DE-AÇÚCAR
POLYMERIC COMPOSITES
THERMOPLASTIC STARCH
SUGARCANE BAGASSE
PROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABC
description Orientadora: Profa. Dra. Márcia Aparecida da Silva Spinacé
publishDate 2020
dc.date.none.fl_str_mv 2020
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300
url http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300&midiaext=79615
http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=122300&midiaext=79616
Cover: http://biblioteca.ufabc.edu.br/php/capa.php?obra=122300
Titanium dioxide recovery from paint manufacturing wash water
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
116 f. : il.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFABC
instname:Universidade Federal do ABC (UFABC)
instacron:UFABC
instname_str Universidade Federal do ABC (UFABC)
instacron_str UFABC
institution UFABC
reponame_str Repositório Institucional da UFABC
collection Repositório Institucional da UFABC
repository.name.fl_str_mv Repositório Institucional da UFABC - Universidade Federal do ABC (UFABC)
repository.mail.fl_str_mv
_version_ 1801502108134932480

Registros relacionados