Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico

Detalhes bibliográficos
Autor(a) principal: Oliveira, Leandro Antonio de
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFABC
Texto Completo: http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082
Resumo: Orientador: Prof. Dr. Renato Altobelli Antunes
id UFBC_bdd826e6f7cfed3ab8714ade89bdc2e2
oai_identifier_str oai:BDTD:106082
network_acronym_str UFBC
network_name_str Repositório Institucional da UFABC
repository_id_str
spelling Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológicoCORROSÃOFILMES ANÓDICOSELETROQUÍMICACORROSIONANODIC FILMSELECTROCHEMISTRYPROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABCOrientador: Prof. Dr. Renato Altobelli AntunesDissertação (mestrado) - Universidade Federal do ABC, Programa de Pós-Graduação em Nanociências e Materiais Avançados, 2016.O fenômeno da corrosão é uma das maiores ameaças à integridadedos aços de alta resistência e baixa liga (ARBL) utilizados para transporte de petróleo e gás.No presente trabalho, investigou-sea estabilidade de filmes anódicos formados sobre o aço API 5L X80 em eletrólitos utilizados para testes de inibidores de corrosão, variando o pH da solução, o potencial de formação na técnica de voltametria cíclica, e a formação espontânea dos filmes por ensaios de imersão. Explorando outro objetivo, foram produzidos filmes anódicos por polarização potenciostática com o intuito de formar uma camada de proteção contra a corrosão do aço API 5L X80. Estes experimentos foram conduzidos em solução de metassilicato de sódio.Neste caso otempo de exposição da amostra aumpotencial fixode formaçãofoi variadoe, como forma de estabelecer um comparativo, foram formados filmes espontaneamente sobre o eletrodo por ensaios de imersão.A caracterização do comportamento eletroquímico foi investigadausando espectroscopia de impedância eletroquímica(EIE)epolarização potenciodinâmica. As propriedades eletrônicas dos filmes anódicos foram analisadas pela abordagem de Mott-Schottky. A morfologia dos produtos de corrosão foi observada com auxílio de microscopia confocal a laser e microscopia eletrônica de varredura (MEV). A composição das camadas de óxido foi identificada com auxílio de espectroscopia Raman. Os resultadosmostraramque os filmesformados em solução alcalina foram mais resistentes àdissolução,menos defeituosos e mais estáveis do que aqueles formados em solução ácida.O produto de corrosão formado por voltametria cíclica tanto emeletrólitode caráter ácido quanto em eletrólitode caráter básico foi identificado como sendo hematita,enquanto a composição doproduto de corrosão formadopor imersãoem eletrólito de caráter básico indicouumadiversidade de compostos, especialmente quando o tempo de imersão foi maior, sendo possível identificar outros compostos além de hematita.A caracterização do comportamento eletroquímico dos filmes obtidos em solução de metassilicato de sódiomostrou que tanto apolarização potenciostáticaquanto a produçãoespontâneados filmes(ensaios de imersão)apresentaram poucos defeitos,alta estabilidade superficiale um aumentosignificativoda resistência à corrosão.A respeito da sua composição química, os filmes formados por cronoamperometria em solução de metassilicato de sódio apresentaram compostos à base de óxidos e oxihidróxidosde ferro, embora a análise de EDS sugerisse a presença de silíciona composição dosfilmes. Por sua vez, a composição dos filmes formados por imersão, em especial o espectro do filme imerso pelo maior período detempo, não foi possível deser identificada com precisão por espectroscopia Raman.Corrosion is a major threat to the integrity ofhigh strength low alloy (HSLA) steels usedaspipelinesfor oil and gas transportation. In this study, we investigated the stability of the formed anodic films on API 5L X80 steel in electrolytes used for testing corrosion inhibitors, varying the pH of the solution, the formation potential in cyclic voltammetry technique and the spontaneous formation of films by immersion tests. Exploring another objective,anodic films were produced by potentiostatic polarization in order to form a protective layer against corrosion of the API 5L X80 steel. These experiments were conducted in a sodium metasilicate solution. In this case,the exposure time of the sample at a fixed formation potential was varied and, in order to establish a comparison, films were formed spontaneously on the electrode by immersion tests. The characterization of the electrochemical behavior was carried outusing electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The electronic properties of anodic films were assessedbytheMott-Schottky approach. The morphology of corrosion products was observed with the aid of confocal laser scanning microscopy and scanning electron microscopy (SEM). The composition of the oxide layers was identified with the aid of Raman spectroscopy. The results showed that the films formed in alkaline solutions were more resistant to dissolution, less defective and more stable than those formed in acidicsolution. The corrosion product formed by cyclic voltammetry in both the acidic and alkaline solutionswas identified as hematite, while the corrosion product composition formed by immersion in the alkaline solutionindicated a diversity of compounds.Especially whenthe immersiontime was longer, it waspossible to identify other compounds in addition to hematite. The characterization of the electrochemical behavior of the films obtained in the sodium metasilicate solution showed that both the potentiostatic polarizationandthe spontaneous production of films (immersion test) produced layers withfew defects, high surface stability and significantlyincreased corrosion resistance. Regarding its chemical composition, the films formed by chronoamperometry insodium metasilicate solution presented iron oxides and oxyhydroxides, althoughEDS analysis suggested the presence of silicon in the composition of the films. In turn, the composition of thefilms formed upon immersion, in particular the spectrum of the film immersed forthe longest time, could not be reliably determined using Raman spectroscopy.Antunes, Renato AltobelliTriveño Rios, CarlosAoki, Idalina VieiraOliveira, Leandro Antonio de2016info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdf128 f. : il.http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082&midiaext=74300http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082&midiaext=74301Cover: http://biblioteca.ufabc.edu.br/php/capa.php?obra=106082porreponame:Repositório Institucional da UFABCinstname:Universidade Federal do ABC (UFABC)instacron:UFABCinfo:eu-repo/semantics/openAccess2022-03-24T11:25:26Zoai:BDTD:106082Repositório InstitucionalPUBhttp://www.biblioteca.ufabc.edu.br/oai/oai.phpopendoar:2022-03-24T11:25:26Repositório Institucional da UFABC - Universidade Federal do ABC (UFABC)false
dc.title.none.fl_str_mv Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
title Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
spellingShingle Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
Oliveira, Leandro Antonio de
CORROSÃO
FILMES ANÓDICOS
ELETROQUÍMICA
CORROSION
ANODIC FILMS
ELECTROCHEMISTRY
PROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABC
title_short Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
title_full Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
title_fullStr Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
title_full_unstemmed Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
title_sort Desenvolvimento de filmes anódicos sobre o aço API 5l X80 e caracterização de seu comportamento eletroquímico e morfológico
author Oliveira, Leandro Antonio de
author_facet Oliveira, Leandro Antonio de
author_role author
dc.contributor.none.fl_str_mv Antunes, Renato Altobelli
Triveño Rios, Carlos
Aoki, Idalina Vieira
dc.contributor.author.fl_str_mv Oliveira, Leandro Antonio de
dc.subject.por.fl_str_mv CORROSÃO
FILMES ANÓDICOS
ELETROQUÍMICA
CORROSION
ANODIC FILMS
ELECTROCHEMISTRY
PROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABC
topic CORROSÃO
FILMES ANÓDICOS
ELETROQUÍMICA
CORROSION
ANODIC FILMS
ELECTROCHEMISTRY
PROGRAMA DE PÓS-GRADUAÇÃO EM NANOCIÊNCIAS E MATERIAIS AVANÇADOS - UFABC
description Orientador: Prof. Dr. Renato Altobelli Antunes
publishDate 2016
dc.date.none.fl_str_mv 2016
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082
url http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082&midiaext=74300
http://biblioteca.ufabc.edu.br/index.php?codigo_sophia=106082&midiaext=74301
Cover: http://biblioteca.ufabc.edu.br/php/capa.php?obra=106082
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
128 f. : il.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFABC
instname:Universidade Federal do ABC (UFABC)
instacron:UFABC
instname_str Universidade Federal do ABC (UFABC)
instacron_str UFABC
institution UFABC
reponame_str Repositório Institucional da UFABC
collection Repositório Institucional da UFABC
repository.name.fl_str_mv Repositório Institucional da UFABC - Universidade Federal do ABC (UFABC)
repository.mail.fl_str_mv
_version_ 1813263941686525952

Registros relacionados