Zeólita NaA sintetizada sobre fibra de vidro como estratégia para otimização do abrandamento de águas duras

• Autor(a) principal: Oliveira, Edipo Silva de
• Data de Publicação: 2022
• Outros Autores: Alves, Conceição Regina Fernandes, França, Antonia Mayza de Morais, Nascimento, Ronaldo Ferreira do, Sasaki, José Marcos, Loiola, Adonay Rodrigues
• Tipo de documento: Artigo
• Idioma: por
• Título da fonte: Repositório Institucional da Universidade Federal do Ceará (UFC)
• Texto Completo: http://www.repositorio.ufc.br/handle/riufc/69389
• topic: Zeolite A; Fiber glass; Hierarchical material; Water softening

Zeolite NaA has been successfully synthesized over glass fiber surface previously activated by alkaline treatment. By varying the time of the treatment and the amount of silica and alumina precursors used in the reaction mixture, a sample with higher zeolite concentration could be obtained. This material was evaluated for water softening process as an alternative substitute for the use of the zeolite in its powder form, in which several drawbacks related to recovery and reuse limit its application. Water softening experiments, carried out in a continuous flow system, with a column containing the glass fiber-zeolite NaA, showed high performance in decreasing the Ca2+ ions, with complete removal achieved for 20 mL of simulated hard water (Ca2+ 100.0 mg L– ¹) by using 200 mg of the sample in form of column (10 mm diameter × 300 mm high). The sample maintained this performance in a wide range of pH (3.0-9.0), and also presented a feasible regenerability, with no decrease in its performance during the first four cycles of use, reaching 87.3% of efficiency over the tenth cycle.