Transformação química do glicerol via catálise heterogênea em fase gás

• Autor(a) principal: Silva Júnior, Moacir José da
• Data de Publicação: 2014
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Repositório Institucional da Universidade Federal do Ceará (UFC)
• Texto Completo: http://www.repositorio.ufc.br/handle/riufc/15674
• topic: Acetol; Metanol; Catálise heterogênea

In order to promote the dehydration/dehydrogenation of reaction of glycerol in a heterogeneous environment, different catalysts were synthesized comprising copper oxide dispersed on different supports: aluminum oxide, aluminum oxide containing iron oxide, aluminum oxide containing niobium oxide and, silicon oxide containing iron oxide. The synthesis route applied was the polymeric precursor method. Acetol was the main reaction production, but other products were observed in low content, such as methanol, ethanol, acrolein, acetone, amyl alcohol, 1-propanol , 1,2- propanediol and 1,3-propanediol. High selectivity for acrolein was observed using the catalyst comprising of copper, iron and aluminum oxides. The effect of calcination temperature on catalyst performance was observed with the catalyst comprising of copper, iron and silicon oxides, and the best results were obtained by calcination at 600 °C. The analysis by X-ray diffraction highlight the preferential formation of CuO phase, iron oxide and aluminum oxide phases were observed even after calcination at 600 °C. The analysis of temperature programmed reduction (TPR) indicate the formation of samples with significant interaction between the oxides, suggesting high dispersion of iron oxide. The reuse test (twice) showed stability in conversion capacity and selectivity. The analyzes carried out by thermogravimetry and infrared spectroscopy, performed after the catalytic test, point to the formation/retention alkoxides on the catalyst surface.