Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.

Detalhes bibliográficos
Autor(a) principal: Roger Ribeiro Silva
Data de Publicação: 2009
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da UFC
Texto Completo: http://www.teses.ufc.br/tde_busca/arquivo.php?codArquivo=3990
Resumo: Dielectric resonators based on type structure compound Bi3TiNbO9 show singular characteristics for microwave applications, including high dielectric constants, low dissipation losses and low temperature coefficients. Single phase of the Bi3TiNbO9 powder was obtained by x-ray diffraction technique. The ceramics doped during manufacture, with lead oxide and bismuth oxide, were synthesized by solid state reaction at 950ÂC for two hours. Samples were analysed by Archimedes method and exhibited good levels of density for doped ceramics with bismuth and lead oxide. Grain morphology and stoichiometry of ceramics were investigated by scanning electron microscopy and energy dispersive spectroscopy technique. Far infrared spectroscopy identified large bands on the Bi3TiNbO9 structure by attenuated total reflection technique. Radiofrequency measurements showed that doped ceramics exhibited higher dielectric constants than pure phase. Microwave measurements were investigated by Hakki-Coleman and resonant cylindrical cavity. The ceramics called as BTNO3BiP, BTNO5BiP, BTNO10BiP, BTNO3PbG e BTNO5PbG, showed high dielectric constants and high quality factors demonstrating that they can be applied in dielectric antennas on microwave range.
id UFC_c690ee082c503133a884f35553b2d0df
oai_identifier_str oai:www.teses.ufc.br:2336
network_acronym_str UFC
network_name_str Biblioteca Digital de Teses e Dissertações da UFC
spelling info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisEstudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.Study of dielectric properties of the Bismuth Titanate Niobate, [Bi3TiNbO9 (BTNO)], doped with PbO and Bi2O3 for applications in antennas2009-02-19AntÃnio SÃrgio Bezerra Sombra11420618334http://lattes.cnpq.br/6034251420222926 Paulo de Tarso Cavalcante Freire2284693032500508166322Roger Ribeiro SilvaUniversidade Federal do CearÃPrograma de PÃs-GraduaÃÃo em FÃsicaUFCBR x-ray diffraction quality factors dielectric constantresonators Hakki-Coleman Hakki-Coleman difraÃÃo de raios X fatores de qualidade constante dielÃtricaressoadoresFISICA DA MATERIA CONDENSADADielectric resonators based on type structure compound Bi3TiNbO9 show singular characteristics for microwave applications, including high dielectric constants, low dissipation losses and low temperature coefficients. Single phase of the Bi3TiNbO9 powder was obtained by x-ray diffraction technique. The ceramics doped during manufacture, with lead oxide and bismuth oxide, were synthesized by solid state reaction at 950ÂC for two hours. Samples were analysed by Archimedes method and exhibited good levels of density for doped ceramics with bismuth and lead oxide. Grain morphology and stoichiometry of ceramics were investigated by scanning electron microscopy and energy dispersive spectroscopy technique. Far infrared spectroscopy identified large bands on the Bi3TiNbO9 structure by attenuated total reflection technique. Radiofrequency measurements showed that doped ceramics exhibited higher dielectric constants than pure phase. Microwave measurements were investigated by Hakki-Coleman and resonant cylindrical cavity. The ceramics called as BTNO3BiP, BTNO5BiP, BTNO10BiP, BTNO3PbG e BTNO5PbG, showed high dielectric constants and high quality factors demonstrating that they can be applied in dielectric antennas on microwave range.Ressoadores dielÃtricos baseados na estrutura do composto Bi3TiNbO9 apresentam caracterÃsticas singulares para aplicaÃÃes em microondas, incluindo altas constantes dielÃtricas, baixos fatores de dissipaÃÃo e baixos coeficientes de temperatura. Obteve-se a fase pura da amostra em pà de Bi3TiNbO9 pela tÃcnica de difraÃÃo de raios X. As amostras cerÃmicas dopadas durante a fabricaÃÃo, com Ãxido de chumbo e Ãxido de bismuto, foram sintetizadas pelo mÃtodo de reaÃÃo do estado sÃlido a 950ÂC por 2 horas. As amostras foram analisadas pelo mÃtodo de Arquimedes e apresentaram bons nÃveis de densidade nas dopagens com os Ãxidos de bismuto e chumbo. A morfologia dos grÃos e a estequiometria das amostras cerÃmicas foram investigadas pelas tÃcnicas de microscopia eletrÃnica de varredura e anÃlise por energia dispersiva de raios X. A espectroscopia no infravermelho distante identificou bandas largas na estrutura do Bi3TiNbO9 pela tÃcnica de reflexÃo total atenuada. As medidas de constante dielÃtrica e perda dielÃtrica em radiofreqÃÃncia demonstraram que as dopagens com chumbo e bismuto exibiram maiores constantes dielÃtricas em relaÃÃo à cerÃmica pura. As medidas em microondas foram estudadas pelos mÃtodos Hakki-Coleman e a cavidade ressonante metÃlica. As cerÃmicas denominadas como BTNO3BiP, BTNO5BiP, BTNO10BiP, BTNO3PbG e BTNO5PbG, apresentaram altas constantes dielÃtricas e altos fatores de qualidade, demonstrando que podem ser aplicadas em antenas dielÃtricas na faixa de microondas. Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgicohttp://www.teses.ufc.br/tde_busca/arquivo.php?codArquivo=3990application/pdfinfo:eu-repo/semantics/openAccessporreponame:Biblioteca Digital de Teses e Dissertações da UFCinstname:Universidade Federal do Cearáinstacron:UFC2019-01-21T11:18:00Zmail@mail.com -
dc.title.pt.fl_str_mv Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
dc.title.alternative..fl_str_mv Study of dielectric properties of the Bismuth Titanate Niobate, [Bi3TiNbO9 (BTNO)], doped with PbO and Bi2O3 for applications in antennas
title Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
spellingShingle Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
Roger Ribeiro Silva
Hakki-Coleman
difraÃÃo de raios X
fatores de qualidade
constante dielÃtrica
ressoadores
FISICA DA MATERIA CONDENSADA
title_short Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
title_full Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
title_fullStr Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
title_full_unstemmed Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
title_sort Estudo das propriedades dielÃtricas do Niobato de Bismuto e TitÃnio dopado com PbO e Bi2O3 para aplicaÃÃes em antenas.
author Roger Ribeiro Silva
author_facet Roger Ribeiro Silva
author_role author
dc.contributor.advisor1.fl_str_mv AntÃnio SÃrgio Bezerra Sombra
dc.contributor.advisor1ID.fl_str_mv 11420618334
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/6034251420222926
dc.contributor.referee1.fl_str_mv Paulo de Tarso Cavalcante Freire
dc.contributor.referee1ID.fl_str_mv 22846930325
dc.contributor.authorID.fl_str_mv 00508166322
dc.contributor.author.fl_str_mv Roger Ribeiro Silva
contributor_str_mv AntÃnio SÃrgio Bezerra Sombra
Paulo de Tarso Cavalcante Freire
dc.subject.por.fl_str_mv Hakki-Coleman
difraÃÃo de raios X
fatores de qualidade
constante dielÃtrica
ressoadores
topic Hakki-Coleman
difraÃÃo de raios X
fatores de qualidade
constante dielÃtrica
ressoadores
FISICA DA MATERIA CONDENSADA
dc.subject.cnpq.fl_str_mv FISICA DA MATERIA CONDENSADA
dc.description.sponsorship.fl_txt_mv Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico
dc.description.abstract..fl_txt_mv Dielectric resonators based on type structure compound Bi3TiNbO9 show singular characteristics for microwave applications, including high dielectric constants, low dissipation losses and low temperature coefficients. Single phase of the Bi3TiNbO9 powder was obtained by x-ray diffraction technique. The ceramics doped during manufacture, with lead oxide and bismuth oxide, were synthesized by solid state reaction at 950ÂC for two hours. Samples were analysed by Archimedes method and exhibited good levels of density for doped ceramics with bismuth and lead oxide. Grain morphology and stoichiometry of ceramics were investigated by scanning electron microscopy and energy dispersive spectroscopy technique. Far infrared spectroscopy identified large bands on the Bi3TiNbO9 structure by attenuated total reflection technique. Radiofrequency measurements showed that doped ceramics exhibited higher dielectric constants than pure phase. Microwave measurements were investigated by Hakki-Coleman and resonant cylindrical cavity. The ceramics called as BTNO3BiP, BTNO5BiP, BTNO10BiP, BTNO3PbG e BTNO5PbG, showed high dielectric constants and high quality factors demonstrating that they can be applied in dielectric antennas on microwave range.
dc.description.abstract.por.fl_txt_mv Ressoadores dielÃtricos baseados na estrutura do composto Bi3TiNbO9 apresentam caracterÃsticas singulares para aplicaÃÃes em microondas, incluindo altas constantes dielÃtricas, baixos fatores de dissipaÃÃo e baixos coeficientes de temperatura. Obteve-se a fase pura da amostra em pà de Bi3TiNbO9 pela tÃcnica de difraÃÃo de raios X. As amostras cerÃmicas dopadas durante a fabricaÃÃo, com Ãxido de chumbo e Ãxido de bismuto, foram sintetizadas pelo mÃtodo de reaÃÃo do estado sÃlido a 950ÂC por 2 horas. As amostras foram analisadas pelo mÃtodo de Arquimedes e apresentaram bons nÃveis de densidade nas dopagens com os Ãxidos de bismuto e chumbo. A morfologia dos grÃos e a estequiometria das amostras cerÃmicas foram investigadas pelas tÃcnicas de microscopia eletrÃnica de varredura e anÃlise por energia dispersiva de raios X. A espectroscopia no infravermelho distante identificou bandas largas na estrutura do Bi3TiNbO9 pela tÃcnica de reflexÃo total atenuada. As medidas de constante dielÃtrica e perda dielÃtrica em radiofreqÃÃncia demonstraram que as dopagens com chumbo e bismuto exibiram maiores constantes dielÃtricas em relaÃÃo à cerÃmica pura. As medidas em microondas foram estudadas pelos mÃtodos Hakki-Coleman e a cavidade ressonante metÃlica. As cerÃmicas denominadas como BTNO3BiP, BTNO5BiP, BTNO10BiP, BTNO3PbG e BTNO5PbG, apresentaram altas constantes dielÃtricas e altos fatores de qualidade, demonstrando que podem ser aplicadas em antenas dielÃtricas na faixa de microondas.
description Dielectric resonators based on type structure compound Bi3TiNbO9 show singular characteristics for microwave applications, including high dielectric constants, low dissipation losses and low temperature coefficients. Single phase of the Bi3TiNbO9 powder was obtained by x-ray diffraction technique. The ceramics doped during manufacture, with lead oxide and bismuth oxide, were synthesized by solid state reaction at 950ÂC for two hours. Samples were analysed by Archimedes method and exhibited good levels of density for doped ceramics with bismuth and lead oxide. Grain morphology and stoichiometry of ceramics were investigated by scanning electron microscopy and energy dispersive spectroscopy technique. Far infrared spectroscopy identified large bands on the Bi3TiNbO9 structure by attenuated total reflection technique. Radiofrequency measurements showed that doped ceramics exhibited higher dielectric constants than pure phase. Microwave measurements were investigated by Hakki-Coleman and resonant cylindrical cavity. The ceramics called as BTNO3BiP, BTNO5BiP, BTNO10BiP, BTNO3PbG e BTNO5PbG, showed high dielectric constants and high quality factors demonstrating that they can be applied in dielectric antennas on microwave range.
publishDate 2009
dc.date.issued.fl_str_mv 2009-02-19
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
status_str publishedVersion
format masterThesis
dc.identifier.uri.fl_str_mv http://www.teses.ufc.br/tde_busca/arquivo.php?codArquivo=3990
url http://www.teses.ufc.br/tde_busca/arquivo.php?codArquivo=3990
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Universidade Federal do CearÃ
dc.publisher.program.fl_str_mv Programa de PÃs-GraduaÃÃo em FÃsica
dc.publisher.initials.fl_str_mv UFC
dc.publisher.country.fl_str_mv BR
publisher.none.fl_str_mv Universidade Federal do CearÃ
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da UFC
instname:Universidade Federal do Ceará
instacron:UFC
reponame_str Biblioteca Digital de Teses e Dissertações da UFC
collection Biblioteca Digital de Teses e Dissertações da UFC
instname_str Universidade Federal do Ceará
instacron_str UFC
institution UFC
repository.name.fl_str_mv -
repository.mail.fl_str_mv mail@mail.com
_version_ 1643295142143066112

Registros relacionados