O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27

Detalhes bibliográficos
Autor(a) principal: Sardinha, Farley Correia
Data de Publicação: 2008
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
Texto Completo: http://repositorio.ufes.br/handle/10/6285
Resumo: In this work, magnetic entropy change of nonstoichiometric Ni54[Mn(1-x)Fex]19Ga27 Heusler alloys was experimentally verified by partial substitution (up to 50%) of the Mn atoms by magnetic Fe atoms. Such study was mainly concentrated in the magneto-structural transformation region, at low temperatures. The analysis of X-ray diffraction patterns indicate that the partial substitution of Mn atoms by Fe atoms causes predominance of the L21 -phase, however accompanied by spurious phases. The magnetization measurements as a function of the temperature in the low magnetic field reveals that, in all concentration range (0 x 0.5), the system presents a magnetic transition (Ferromagnetic Paramagnetic) at a temperature, TC, near the room temperature, when the material lay in the austenitic phase. Moreover, as many others Heusler alloys, the material undergoes a martensitic structural transition at low temperatures, TM. As the Fe concentration increases, the Curie temperature, TC, undergoes a little variation, increasing around 5%, while TM decreases slowly and monotonically. The magnetic entropy change, for a field of 5T, presents a maximum SM = - 9,3 J/kg.K, for x = 0.1, at a temperature of 250K, and than decreases for x 0.3, changing linearly with the maximum applied field.
id UFES_4279a60d09e45c9c81a9abcc8c8b7c25
oai_identifier_str oai:repositorio.ufes.br:10/6285
network_acronym_str UFES
network_name_str Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
repository_id_str 2108
spelling Takeuchi, Armando YoshihakiSardinha, Farley CorreiaPaduani, CledersonCunha, Alfredo GonçalvesLarica, CarlosTakeuchi, Armando Yoshihaki2016-12-23T14:20:01Z2008-06-172016-12-23T14:20:01Z2008-03-28In this work, magnetic entropy change of nonstoichiometric Ni54[Mn(1-x)Fex]19Ga27 Heusler alloys was experimentally verified by partial substitution (up to 50%) of the Mn atoms by magnetic Fe atoms. Such study was mainly concentrated in the magneto-structural transformation region, at low temperatures. The analysis of X-ray diffraction patterns indicate that the partial substitution of Mn atoms by Fe atoms causes predominance of the L21 -phase, however accompanied by spurious phases. The magnetization measurements as a function of the temperature in the low magnetic field reveals that, in all concentration range (0 x 0.5), the system presents a magnetic transition (Ferromagnetic Paramagnetic) at a temperature, TC, near the room temperature, when the material lay in the austenitic phase. Moreover, as many others Heusler alloys, the material undergoes a martensitic structural transition at low temperatures, TM. As the Fe concentration increases, the Curie temperature, TC, undergoes a little variation, increasing around 5%, while TM decreases slowly and monotonically. The magnetic entropy change, for a field of 5T, presents a maximum SM = - 9,3 J/kg.K, for x = 0.1, at a temperature of 250K, and than decreases for x 0.3, changing linearly with the maximum applied field.Neste trabalho, verificou-se experimentalmente a variação da entropia magnética nas ligas Heusler não-estequiométricas Ni54[Mn(1-x)Fex]19Ga27, substituindo-se parcialmente (até 50%) os átomos de Mn por átomos de Fe. Tal estudo focalizou-se principalmente na região de transformação magneto-estrutural a baixas temperaturas. A análise dos difratogramas de raios-X indica que a substituição parcial de Mn por Fe nessa faixa de concentração, ocasiona uma predominância da fase- L21, porém acompanhada de outras fases espúrias. As medidas de magnetização em função da temperatura realizadas a campos baixos revelam que, em toda a faixa de concentração estudada (0 x 0,5), o sistema apresenta uma transição magnética (Ferromagnético Paramagnético) ao atingir a temperatura de Curie, TC, um pouco acima da temperatura ambiente, quando o material se encontra na fase austenítica. E, assim como muitas outras ligas Heusler, o material sofre uma transição estrutural ao ser resfriado a temperaturas inferiores à temperatura de transição martensítica, TM. À medida que se aumenta a concentração de Fe, a temperatura de Curie, TC, sofre uma pequena variação, aumentando em torno de 5%, enquanto que TM diminui lenta e monotonicamente. A variação da entropia, para um campo de 5T, apresenta um máximo SM = - 9,3 J/kg.K para x = 0,1, a uma temperatura T = 250K e, então, diminui para x 0,3, variando linearmente com o campo aplicado.CAPES - Conselho Nacional de Desenvolvimento Científico e TecnológicoTextSARDINHA, Farley Correia. O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27. 2008. 93 f. Dissertação (Mestrado em Física) – Programa de Pós-Graduação em Física, Universidade Federal do Espírito Santo, Centro de Ciências Exatas e da Terra, Vitória, 2008.http://repositorio.ufes.br/handle/10/6285porUniversidade Federal do Espírito SantoMestrado em FísicaPrograma de Pós-Graduação em FísicaUFESBRCentro de Ciências ExatasMagnetic refrigerationMagnetocaloric effectHeusler alloysRefrigeração magnéticaEfeito magnetocalóricoLigas HeuslerMateriais magnéticosRefrigeraçãoFísica53O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27The magnetocaloric effect in the Heusler alloys Ni54[Mn(1-x)Fex]19Ga27info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)instname:Universidade Federal do Espírito Santo (UFES)instacron:UFESCAPES - Conselho Nacional de Desenvolvimento Científico e TecnológicoORIGINALFarleyCorreiaSardinha-2008-trabalho.pdfapplication/pdf1976712http://repositorio.ufes.br/bitstreams/396fd100-9f24-4dbc-9985-502e98f9dc4a/download54cbe3c62f71ef7121b79c6f4e1efaa0MD5110/62852024-06-28 18:06:26.68oai:repositorio.ufes.br:10/6285http://repositorio.ufes.brRepositório InstitucionalPUBhttp://repositorio.ufes.br/oai/requestopendoar:21082024-07-11T14:32:39.044472Repositório Institucional da Universidade Federal do Espírito Santo (riUfes) - Universidade Federal do Espírito Santo (UFES)false
dc.title.none.fl_str_mv O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
dc.title.alternative.none.fl_str_mv The magnetocaloric effect in the Heusler alloys Ni54[Mn(1-x)Fex]19Ga27
title O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
spellingShingle O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
Sardinha, Farley Correia
Magnetic refrigeration
Magnetocaloric effect
Heusler alloys
Refrigeração magnética
Efeito magnetocalórico
Ligas Heusler
Física
Materiais magnéticos
Refrigeração
53
title_short O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
title_full O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
title_fullStr O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
title_full_unstemmed O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
title_sort O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27
author Sardinha, Farley Correia
author_facet Sardinha, Farley Correia
author_role author
dc.contributor.advisor1.fl_str_mv Takeuchi, Armando Yoshihaki
dc.contributor.author.fl_str_mv Sardinha, Farley Correia
dc.contributor.referee1.fl_str_mv Paduani, Clederson
dc.contributor.referee2.fl_str_mv Cunha, Alfredo Gonçalves
dc.contributor.referee3.fl_str_mv Larica, Carlos
dc.contributor.referee4.fl_str_mv Takeuchi, Armando Yoshihaki
contributor_str_mv Takeuchi, Armando Yoshihaki
Paduani, Clederson
Cunha, Alfredo Gonçalves
Larica, Carlos
Takeuchi, Armando Yoshihaki
dc.subject.eng.fl_str_mv Magnetic refrigeration
Magnetocaloric effect
Heusler alloys
topic Magnetic refrigeration
Magnetocaloric effect
Heusler alloys
Refrigeração magnética
Efeito magnetocalórico
Ligas Heusler
Física
Materiais magnéticos
Refrigeração
53
dc.subject.por.fl_str_mv Refrigeração magnética
Efeito magnetocalórico
Ligas Heusler
dc.subject.cnpq.fl_str_mv Física
dc.subject.br-rjbn.none.fl_str_mv Materiais magnéticos
Refrigeração
dc.subject.udc.none.fl_str_mv 53
description In this work, magnetic entropy change of nonstoichiometric Ni54[Mn(1-x)Fex]19Ga27 Heusler alloys was experimentally verified by partial substitution (up to 50%) of the Mn atoms by magnetic Fe atoms. Such study was mainly concentrated in the magneto-structural transformation region, at low temperatures. The analysis of X-ray diffraction patterns indicate that the partial substitution of Mn atoms by Fe atoms causes predominance of the L21 -phase, however accompanied by spurious phases. The magnetization measurements as a function of the temperature in the low magnetic field reveals that, in all concentration range (0 x 0.5), the system presents a magnetic transition (Ferromagnetic Paramagnetic) at a temperature, TC, near the room temperature, when the material lay in the austenitic phase. Moreover, as many others Heusler alloys, the material undergoes a martensitic structural transition at low temperatures, TM. As the Fe concentration increases, the Curie temperature, TC, undergoes a little variation, increasing around 5%, while TM decreases slowly and monotonically. The magnetic entropy change, for a field of 5T, presents a maximum SM = - 9,3 J/kg.K, for x = 0.1, at a temperature of 250K, and than decreases for x 0.3, changing linearly with the maximum applied field.
publishDate 2008
dc.date.available.fl_str_mv 2008-06-17
2016-12-23T14:20:01Z
dc.date.issued.fl_str_mv 2008-03-28
dc.date.accessioned.fl_str_mv 2016-12-23T14:20:01Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv SARDINHA, Farley Correia. O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27. 2008. 93 f. Dissertação (Mestrado em Física) – Programa de Pós-Graduação em Física, Universidade Federal do Espírito Santo, Centro de Ciências Exatas e da Terra, Vitória, 2008.
dc.identifier.uri.fl_str_mv http://repositorio.ufes.br/handle/10/6285
identifier_str_mv SARDINHA, Farley Correia. O efeito magnetocalórico nas ligas Heusler Ni54[Mn(1-x)Fex]19Ga27. 2008. 93 f. Dissertação (Mestrado em Física) – Programa de Pós-Graduação em Física, Universidade Federal do Espírito Santo, Centro de Ciências Exatas e da Terra, Vitória, 2008.
url http://repositorio.ufes.br/handle/10/6285
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv Text
dc.publisher.none.fl_str_mv Universidade Federal do Espírito Santo
Mestrado em Física
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Física
dc.publisher.initials.fl_str_mv UFES
dc.publisher.country.fl_str_mv BR
dc.publisher.department.fl_str_mv Centro de Ciências Exatas
publisher.none.fl_str_mv Universidade Federal do Espírito Santo
Mestrado em Física
dc.source.none.fl_str_mv reponame:Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
instname:Universidade Federal do Espírito Santo (UFES)
instacron:UFES
instname_str Universidade Federal do Espírito Santo (UFES)
instacron_str UFES
institution UFES
reponame_str Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
collection Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
bitstream.url.fl_str_mv http://repositorio.ufes.br/bitstreams/396fd100-9f24-4dbc-9985-502e98f9dc4a/download
bitstream.checksum.fl_str_mv 54cbe3c62f71ef7121b79c6f4e1efaa0
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da Universidade Federal do Espírito Santo (riUfes) - Universidade Federal do Espírito Santo (UFES)
repository.mail.fl_str_mv
_version_ 1813022608205021184