Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFG |
Texto Completo: | http://repositorio.bc.ufg.br/tede/handle/tede/6245 |
Resumo: | The pre-heating and post-curing can improve the mechanical properties of composites, even though there be no studies of fiber reinforced composites. The aim of this study was to evaluate the effect of pre-heating and post-curing autoclave and microwave in flexural strength (FS), diametral tensile strength (DTS), knoop microhardness (KHN) and degree of conversion (DC) of a experimental fiber- reinfoced composite. The experimental material was prepared with 30% glass fibers (3 mm), 22.5% of the resin matrix (40/60 Bis-GMA / TEGDMA) and 47.5% barium silicate particles. Six experimental groups were created by the interaction between the factors under study: heating, on two levels (without heating and heating at 60°C) and post-curing in 3 levels (conventional curing without post-curing, autoclave (120°C for 15 minutes) and microwaves (540 W for 5 minutes) The groups were: F - curing at 1500 mW/cm2 for 40 seconds; F + M - curing and post- polymerization in microwave; F + A - curing and post-curing in an autoclave , AQ + F - the composite heating prior to curing, AQ + F + M - heating prior to curing and post-curing in microwave;. AQ + F + A - heating prior to curing and post-curing and autoclave heating was conducted digital oven for 5 minutes at 60°C. Ten samples of the RF dimensions 25 x 2 x 2 mm and DTS in dimensions of 3 x 6 mm were tested in a universal testing machine Instron 5965, 0.5 mm/min. the KHN test was performed on samples of 3 x 6 mm with a load of 50 g for 30 sec, totaling 50 indentations per group. GC was obtained by Spectroscopy Fourier Transform Infrared (FTIR) on 5 samples. Data were analyzed by a factorial 2x3 and general linear model ANOVA and Tukey tests (α = 0.05). Factor analysis showed significant interaction between the factors just for RTD (p = 0.0001); preheating was significant factor for RF (p = 0.0001), RTD (p = 0.020) and KHN (p = 0.0001); post-curing factor for KHN was significant (p = 0.0001). ANOVA and Tukey tests showed statistically significant differences between groups for DTS (p = 0.001: AQ + F ≥ AQ + F + M = F + A = AQ + F + A = F + M ≥ F), FS (p = 0.016: AQ + F + M ≥ AQ + F + A + F = AQ = AQ + A + M ≥ F ≥ F) and KHN (p = 0.0001: AQ + F + M ≥ AQ + A + F = F = F + A + M ≥ F ≥ M + AQ). GC results showed no statistically significant difference. Through the Pearson correlation coefficient was observed significant positive correlation between the GC and RTD (r = 0.473, p = 0.008) and between DTS and FS (r = 0.263, p = 0.042). The pre-heating and post- polymerization were shown to be favorable to promote better mechanical properties of fiber reinforced composite by studied, specific for each property being analyzed. |
id |
UFG-2_22a4072a9171ae0df5c2543e7d22ce68 |
---|---|
oai_identifier_str |
oai:repositorio.bc.ufg.br:tede/6245 |
network_acronym_str |
UFG-2 |
network_name_str |
Repositório Institucional da UFG |
repository_id_str |
|
spelling |
Fonseca, Rodrigo Borgeshttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?metodo=apresentar&id=K4770435A0Fonseca, Rodrigo BorgesSouza, João Batista deMenezes, Murilo de Souzahttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?metodo=apresentar&id=K4325692D3Almeida, Letícia Nunes de2016-09-21T13:45:21Z2016-02-25ALMEIDA, L. N. Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro. 2016.90 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Goiás,Goiânia, 2016.http://repositorio.bc.ufg.br/tede/handle/tede/6245ark:/38995/0013000000v3jThe pre-heating and post-curing can improve the mechanical properties of composites, even though there be no studies of fiber reinforced composites. The aim of this study was to evaluate the effect of pre-heating and post-curing autoclave and microwave in flexural strength (FS), diametral tensile strength (DTS), knoop microhardness (KHN) and degree of conversion (DC) of a experimental fiber- reinfoced composite. The experimental material was prepared with 30% glass fibers (3 mm), 22.5% of the resin matrix (40/60 Bis-GMA / TEGDMA) and 47.5% barium silicate particles. Six experimental groups were created by the interaction between the factors under study: heating, on two levels (without heating and heating at 60°C) and post-curing in 3 levels (conventional curing without post-curing, autoclave (120°C for 15 minutes) and microwaves (540 W for 5 minutes) The groups were: F - curing at 1500 mW/cm2 for 40 seconds; F + M - curing and post- polymerization in microwave; F + A - curing and post-curing in an autoclave , AQ + F - the composite heating prior to curing, AQ + F + M - heating prior to curing and post-curing in microwave;. AQ + F + A - heating prior to curing and post-curing and autoclave heating was conducted digital oven for 5 minutes at 60°C. Ten samples of the RF dimensions 25 x 2 x 2 mm and DTS in dimensions of 3 x 6 mm were tested in a universal testing machine Instron 5965, 0.5 mm/min. the KHN test was performed on samples of 3 x 6 mm with a load of 50 g for 30 sec, totaling 50 indentations per group. GC was obtained by Spectroscopy Fourier Transform Infrared (FTIR) on 5 samples. Data were analyzed by a factorial 2x3 and general linear model ANOVA and Tukey tests (α = 0.05). Factor analysis showed significant interaction between the factors just for RTD (p = 0.0001); preheating was significant factor for RF (p = 0.0001), RTD (p = 0.020) and KHN (p = 0.0001); post-curing factor for KHN was significant (p = 0.0001). ANOVA and Tukey tests showed statistically significant differences between groups for DTS (p = 0.001: AQ + F ≥ AQ + F + M = F + A = AQ + F + A = F + M ≥ F), FS (p = 0.016: AQ + F + M ≥ AQ + F + A + F = AQ = AQ + A + M ≥ F ≥ F) and KHN (p = 0.0001: AQ + F + M ≥ AQ + A + F = F = F + A + M ≥ F ≥ M + AQ). GC results showed no statistically significant difference. Through the Pearson correlation coefficient was observed significant positive correlation between the GC and RTD (r = 0.473, p = 0.008) and between DTS and FS (r = 0.263, p = 0.042). The pre-heating and post- polymerization were shown to be favorable to promote better mechanical properties of fiber reinforced composite by studied, specific for each property being analyzed.O aquecimento prévio à polimerização e a pós-polimerização podem melhorar propriedades mecânicas em compósitos, embora inexistam estudos em compósitos reforçados com fibra. O objetivo deste estudo foi avaliar o efeito do pré- aquecimento e da pós-polimerização em autoclave e microondas na resistência flexural (RF), resistência à tração diametral (RTD), microdureza knoop (KHN) e grau de conversão (GC) de um compósito experimental reforçado por fibra de vidro. O material experimental foi confeccionado com 30% de fibras de vidro (3 mm), 22,5% de matriz resinosa (40/60 Bis-GMA/TEGDMA) e 47,5% de partículas de silicato de bário. Seis grupos experimentais foram criados pela interação entre os fatores em estudo: aquecimento, em dois níveis (controle sem aquecimento e aquecimento a 60oC) e pós-polimerização, em 3 níveis (fotopolimerização convencional sem pós- polimerização, autoclave (120oC por 15 minutos) e microondas (540 W por 5 minutos). Os grupos foram: F - fotopolimerização à 1500 mW/cm2 por 40 segundos; F+M - fotopolimerização e pós- polimerização em microondas; F+A - fotopolimerizacão e pós-polimerização em autoclave; AQ+F - aquecimento do compósito previamente à fotopolimerização; AQ+F+M - aquecimento previamente à fotopolimerização e pós-polimerização em microondas; AQ+F+A - aquecimento previamente à fotopolimerização e pós-polimerização e autoclave. O aquecimento foi realizado em estufa digital por 5 minutos a 60oC. Dez amostras de RF nas dimensões de 25 x 2 x 2 mm e de RTD nas dimensões de 3 x 6 mm foram testadas em máquina de ensaio universal Instron 5965, a 0,5mm/min. O teste de KHN foi realizado em amostras de 3 x 6 mm com carga de 50 g por 30 s, totalizando 50 indentações por grupo. O GC foi obtido através de Espectroscopia de Infravermelho por Transformada de Fourrier (FTIR) em cinco amostras. Os dados foram analisados por um modelo linear geral fatorial 2x3 e testes de ANOVA e Tukey (α=0,05). A análise fatorial mostrou interação significativa entre os fatores apenas para RTD (p=0,0001); o fator pré-aquecimento foi significante para RF (p=0,0001), RTD (p=0,020) e KHN (p=0,0001); o fator pós-polimerização foi significante para KHN (p=0,0001). Os testes de ANOVA e Tukey mostraram diferença estatística entre os grupos para RTD (p = 0,001: AQ+F ≥ AQ+F+M = F+A = AQ+F+A = F+M ≥ F), RF (p = 0,016: AQ+F+M ≥ AQ+F+A = AQ+F = AQ+A ≥ F+M ≥ F) e KHN (p = 0,0001: AQ+F+M ≥ AQ+F+A = F+A= F+M ≥ AQ+F ≥ F). Os resultados de GC não apresentaram diferença estatisticamente significante. Através do coeficiente de correlação de Pearson foi possível observar correlação positiva significante entre o GC e RTD (r = 0,473, p = 0,008) e entre RTD e RF (r = 0,263, p = 0,042) . O pré- aquecimento e a pós-polimerização mostraram-se favoráveis para promover melhores propriedades mecânicas do compósito reforçado por fibra estudado, sendo específicos para cada propriedade analisada.Submitted by Marlene Santos (marlene.bc.ufg@gmail.com) on 2016-09-21T13:42:33Z No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-09-21T13:45:21Z (GMT) No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)Made available in DSpace on 2016-09-21T13:45:21Z (GMT). No. of bitstreams: 2 Dissertação - Letícia Nunes de Almeida - 2016.pdf: 4956536 bytes, checksum: ff3b7edcf1cb8b45c40f2292cb032676 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2016-02-25Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfporUniversidade Federal de GoiásPrograma de Pós-graduação em Odontologia (FO)UFGBrasilFaculdade de Odontologia - FO (RG)http://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessCompósitos reforçados por fibraGrau de conversãoPós-polimerizaçãoPropriedades mecânicasPinos intrarradicularesFiber-reinforced compositesDegree of conversionPost-curingMechanical propertiesIntrarradicular postCIENCIAS DA SAUDE::ODONTOLOGIAEfeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidroEffect of pre-heating and post-curing on mechanical properties and degree of conversion of an experimental composite reinforced with glass fiberinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-2325576619034292269600600600600-5569154581575113691-20704984698792443492075167498588264571reponame:Repositório Institucional da UFGinstname:Universidade Federal de Goiás (UFG)instacron:UFGORIGINALDissertação - Letícia Nunes de Almeida - 2016.pdfDissertação - Letícia Nunes de Almeida - 2016.pdfapplication/pdf4956536http://repositorio.bc.ufg.br/tede/bitstreams/0b32b8df-4c4d-430e-ba60-79e2b6f82473/downloadff3b7edcf1cb8b45c40f2292cb032676MD55LICENSElicense.txtlicense.txttext/plain; charset=utf-82165http://repositorio.bc.ufg.br/tede/bitstreams/f2fc7126-b9dc-4881-a43b-db9e3ddbe9c5/downloadbd3efa91386c1718a7f26a329fdcb468MD51CC-LICENSElicense_urllicense_urltext/plain; charset=utf-849http://repositorio.bc.ufg.br/tede/bitstreams/a0def759-e288-4952-a4f4-9e32c3aaa156/download4afdbb8c545fd630ea7db775da747b2fMD52license_textlicense_texttext/html; charset=utf-80http://repositorio.bc.ufg.br/tede/bitstreams/979cf687-ed20-46a9-85ee-5dda3c61d140/downloadd41d8cd98f00b204e9800998ecf8427eMD53license_rdflicense_rdfapplication/rdf+xml; charset=utf-80http://repositorio.bc.ufg.br/tede/bitstreams/6e26cff3-2e2c-445a-96a0-eeb5a9d24dfc/downloadd41d8cd98f00b204e9800998ecf8427eMD54tede/62452016-09-21 10:45:21.1http://creativecommons.org/licenses/by-nc-nd/4.0/Acesso Abertoopen.accessoai:repositorio.bc.ufg.br:tede/6245http://repositorio.bc.ufg.br/tedeRepositório InstitucionalPUBhttp://repositorio.bc.ufg.br/oai/requesttasesdissertacoes.bc@ufg.bropendoar:2016-09-21T13:45:21Repositório Institucional da UFG - Universidade Federal de Goiás (UFG)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 |
dc.title.por.fl_str_mv |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
dc.title.alternative.eng.fl_str_mv |
Effect of pre-heating and post-curing on mechanical properties and degree of conversion of an experimental composite reinforced with glass fiber |
title |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
spellingShingle |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro Almeida, Letícia Nunes de Compósitos reforçados por fibra Grau de conversão Pós-polimerização Propriedades mecânicas Pinos intrarradiculares Fiber-reinforced composites Degree of conversion Post-curing Mechanical properties Intrarradicular post CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
title_full |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
title_fullStr |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
title_full_unstemmed |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
title_sort |
Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro |
author |
Almeida, Letícia Nunes de |
author_facet |
Almeida, Letícia Nunes de |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Fonseca, Rodrigo Borges |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?metodo=apresentar&id=K4770435A0 |
dc.contributor.referee1.fl_str_mv |
Fonseca, Rodrigo Borges |
dc.contributor.referee2.fl_str_mv |
Souza, João Batista de |
dc.contributor.referee3.fl_str_mv |
Menezes, Murilo de Souza |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?metodo=apresentar&id=K4325692D3 |
dc.contributor.author.fl_str_mv |
Almeida, Letícia Nunes de |
contributor_str_mv |
Fonseca, Rodrigo Borges Fonseca, Rodrigo Borges Souza, João Batista de Menezes, Murilo de Souza |
dc.subject.por.fl_str_mv |
Compósitos reforçados por fibra Grau de conversão Pós-polimerização Propriedades mecânicas Pinos intrarradiculares |
topic |
Compósitos reforçados por fibra Grau de conversão Pós-polimerização Propriedades mecânicas Pinos intrarradiculares Fiber-reinforced composites Degree of conversion Post-curing Mechanical properties Intrarradicular post CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Fiber-reinforced composites Degree of conversion Post-curing Mechanical properties Intrarradicular post |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
The pre-heating and post-curing can improve the mechanical properties of composites, even though there be no studies of fiber reinforced composites. The aim of this study was to evaluate the effect of pre-heating and post-curing autoclave and microwave in flexural strength (FS), diametral tensile strength (DTS), knoop microhardness (KHN) and degree of conversion (DC) of a experimental fiber- reinfoced composite. The experimental material was prepared with 30% glass fibers (3 mm), 22.5% of the resin matrix (40/60 Bis-GMA / TEGDMA) and 47.5% barium silicate particles. Six experimental groups were created by the interaction between the factors under study: heating, on two levels (without heating and heating at 60°C) and post-curing in 3 levels (conventional curing without post-curing, autoclave (120°C for 15 minutes) and microwaves (540 W for 5 minutes) The groups were: F - curing at 1500 mW/cm2 for 40 seconds; F + M - curing and post- polymerization in microwave; F + A - curing and post-curing in an autoclave , AQ + F - the composite heating prior to curing, AQ + F + M - heating prior to curing and post-curing in microwave;. AQ + F + A - heating prior to curing and post-curing and autoclave heating was conducted digital oven for 5 minutes at 60°C. Ten samples of the RF dimensions 25 x 2 x 2 mm and DTS in dimensions of 3 x 6 mm were tested in a universal testing machine Instron 5965, 0.5 mm/min. the KHN test was performed on samples of 3 x 6 mm with a load of 50 g for 30 sec, totaling 50 indentations per group. GC was obtained by Spectroscopy Fourier Transform Infrared (FTIR) on 5 samples. Data were analyzed by a factorial 2x3 and general linear model ANOVA and Tukey tests (α = 0.05). Factor analysis showed significant interaction between the factors just for RTD (p = 0.0001); preheating was significant factor for RF (p = 0.0001), RTD (p = 0.020) and KHN (p = 0.0001); post-curing factor for KHN was significant (p = 0.0001). ANOVA and Tukey tests showed statistically significant differences between groups for DTS (p = 0.001: AQ + F ≥ AQ + F + M = F + A = AQ + F + A = F + M ≥ F), FS (p = 0.016: AQ + F + M ≥ AQ + F + A + F = AQ = AQ + A + M ≥ F ≥ F) and KHN (p = 0.0001: AQ + F + M ≥ AQ + A + F = F = F + A + M ≥ F ≥ M + AQ). GC results showed no statistically significant difference. Through the Pearson correlation coefficient was observed significant positive correlation between the GC and RTD (r = 0.473, p = 0.008) and between DTS and FS (r = 0.263, p = 0.042). The pre-heating and post- polymerization were shown to be favorable to promote better mechanical properties of fiber reinforced composite by studied, specific for each property being analyzed. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-09-21T13:45:21Z |
dc.date.issued.fl_str_mv |
2016-02-25 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
ALMEIDA, L. N. Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro. 2016.90 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Goiás,Goiânia, 2016. |
dc.identifier.uri.fl_str_mv |
http://repositorio.bc.ufg.br/tede/handle/tede/6245 |
dc.identifier.dark.fl_str_mv |
ark:/38995/0013000000v3j |
identifier_str_mv |
ALMEIDA, L. N. Efeito do pré-aquecimento e da pós-polimerização nas propriedades mecânicas e grau de conversão de um compósito experimental reforçado com fibra de vidro. 2016.90 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Goiás,Goiânia, 2016. ark:/38995/0013000000v3j |
url |
http://repositorio.bc.ufg.br/tede/handle/tede/6245 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-2325576619034292269 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 |
dc.relation.department.fl_str_mv |
-5569154581575113691 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Goiás |
dc.publisher.program.fl_str_mv |
Programa de Pós-graduação em Odontologia (FO) |
dc.publisher.initials.fl_str_mv |
UFG |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Odontologia - FO (RG) |
publisher.none.fl_str_mv |
Universidade Federal de Goiás |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFG instname:Universidade Federal de Goiás (UFG) instacron:UFG |
instname_str |
Universidade Federal de Goiás (UFG) |
instacron_str |
UFG |
institution |
UFG |
reponame_str |
Repositório Institucional da UFG |
collection |
Repositório Institucional da UFG |
bitstream.url.fl_str_mv |
http://repositorio.bc.ufg.br/tede/bitstreams/0b32b8df-4c4d-430e-ba60-79e2b6f82473/download http://repositorio.bc.ufg.br/tede/bitstreams/f2fc7126-b9dc-4881-a43b-db9e3ddbe9c5/download http://repositorio.bc.ufg.br/tede/bitstreams/a0def759-e288-4952-a4f4-9e32c3aaa156/download http://repositorio.bc.ufg.br/tede/bitstreams/979cf687-ed20-46a9-85ee-5dda3c61d140/download http://repositorio.bc.ufg.br/tede/bitstreams/6e26cff3-2e2c-445a-96a0-eeb5a9d24dfc/download |
bitstream.checksum.fl_str_mv |
ff3b7edcf1cb8b45c40f2292cb032676 bd3efa91386c1718a7f26a329fdcb468 4afdbb8c545fd630ea7db775da747b2f d41d8cd98f00b204e9800998ecf8427e d41d8cd98f00b204e9800998ecf8427e |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFG - Universidade Federal de Goiás (UFG) |
repository.mail.fl_str_mv |
tasesdissertacoes.bc@ufg.br |
_version_ |
1811721324803915776 |