Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives
Autor(a) principal: | |
---|---|
Data de Publicação: | 2020 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UFLA |
Texto Completo: | http://repositorio.ufla.br/jspui/handle/1/48063 |
Resumo: | This work aimed to evaluate the physical and mechanical behavior of glued laminated timber (GLT) - glulam pieces of Hevea brasiliensis treated with chromed copper arsenate (CCA), chromed copper borate (CCB) and pyrethroid in the production of GLT. The pieces were produced using three wooden laminae with dimensions of 60 x 20 x 1200 mm, (width x thickness x length), joined with epoxy adhesive under 1.0 MPa pressure for 24h at room temperature. The rubberwood had an apparent density of 0.624 g cm-3, a value close to that of Eucalyptus grandis wood, a species traditionally used in the manufacture of GLT. Regarding the GLT parts, it was observed that the preservative treatment with CCA and CCB influenced negatively the values of the mechanical properties. For resistance modulus (MOR), a reduction of 75.44 MPa to 62.36 and 58.57 MPa was found for the parts untreated and treated with CCA and CCB, respectively. There was no statistical difference for surface treatment with pyrethroid. The photomicrographs of the glue line showed that the reduction in these values was mainly due to the penetration of preservative solutions into the wood structure (cell lumens and vessels or pores), impairing the anchoring of the adhesive. |
id |
UFLA_c36c3914c98e6e3ae764f39b7390fa99 |
---|---|
oai_identifier_str |
oai:localhost:1/48063 |
network_acronym_str |
UFLA |
network_name_str |
Repositório Institucional da UFLA |
repository_id_str |
|
spelling |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservativesComportamento físico e mecânico de vigas laminadas coladas produzidas com madeira de seringueira tratada com preservativosAdhesive wood bondingStatic bendingDelaminationPreservative treatmentLigação madeira adesivoFlexão estáticaDelaminaçãoTratamento preservativoThis work aimed to evaluate the physical and mechanical behavior of glued laminated timber (GLT) - glulam pieces of Hevea brasiliensis treated with chromed copper arsenate (CCA), chromed copper borate (CCB) and pyrethroid in the production of GLT. The pieces were produced using three wooden laminae with dimensions of 60 x 20 x 1200 mm, (width x thickness x length), joined with epoxy adhesive under 1.0 MPa pressure for 24h at room temperature. The rubberwood had an apparent density of 0.624 g cm-3, a value close to that of Eucalyptus grandis wood, a species traditionally used in the manufacture of GLT. Regarding the GLT parts, it was observed that the preservative treatment with CCA and CCB influenced negatively the values of the mechanical properties. For resistance modulus (MOR), a reduction of 75.44 MPa to 62.36 and 58.57 MPa was found for the parts untreated and treated with CCA and CCB, respectively. There was no statistical difference for surface treatment with pyrethroid. The photomicrographs of the glue line showed that the reduction in these values was mainly due to the penetration of preservative solutions into the wood structure (cell lumens and vessels or pores), impairing the anchoring of the adhesive.Esse trabalho teve por objetivo avaliar o comportamento físico e mecânico de madeira laminada colada (MLC) de Hevea brasiliensis tratada com arseniato de cobre cromatado (CCA), borato de cobre cromatado (CCB) e piretróide na produção de MLC. As peças foram produzidas com três lâminas com dimensões de 60 x 20 x 1200 mm (largura x espessura x comprimento), unidas com adesivo epóxi sob 1,0 MPa de pressão durante 24h à temperatura ambiente. A madeira de seringueira tinha densidade aparente de 0,624 g cm-3, valor próximo ao da madeira de Eucalyptus grandis, espécie utilizada tradicionalmente na fabricação de MLC. Em relação às peças de MLC, observou-se que o tratamento preservativo com CCA e CCB influenciou nos valores das propriedades mecânicas. Para o módulo de ruptura (MOR), foi verificado redução de 75,44 MPa para 62,36 e 58,57 MPa para as peças sem tratamento e tratadas com CCA e CCB, respectivamente. Já para o tratamento superficial com piretróide não houve diferenças estatísticas. As fotomicrografias da linha de cola mostraram que a redução desses valores ocorreu sobretudo pela penetração das soluções preservativas na estrutura da madeira (lume celular, vasos ou poros), prejudicando a ancoragem do adesivo.Universidade Federal de Lavras2021-09-06T19:34:37Z2021-09-06T19:34:37Z2020-11info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleapplication/pdfFARIA, D. L. et al. Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives. Ciência e Agrotecnologia, Lavras, v. 44, e012020, 2020. DOI: http://dx.doi.org/10.1590/1413-7054202044012020.http://repositorio.ufla.br/jspui/handle/1/48063Ciência e Agrotecnologiareponame:Repositório Institucional da UFLAinstname:Universidade Federal de Lavras (UFLA)instacron:UFLAhttp://creativecommons.org/licenses/by/4.0/info:eu-repo/semantics/openAccessFaria, Douglas LamounierCruz, Thiago MoreiraDias, Matheus CordazzoDuarte, Paulo JunioMendes, Lourival MarinGuimarães Junior, José Beneditoeng2021-09-06T19:34:53Zoai:localhost:1/48063Repositório InstitucionalPUBhttp://repositorio.ufla.br/oai/requestnivaldo@ufla.br || repositorio.biblioteca@ufla.bropendoar:2021-09-06T19:34:53Repositório Institucional da UFLA - Universidade Federal de Lavras (UFLA)false |
dc.title.none.fl_str_mv |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives Comportamento físico e mecânico de vigas laminadas coladas produzidas com madeira de seringueira tratada com preservativos |
title |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives |
spellingShingle |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives Faria, Douglas Lamounier Adhesive wood bonding Static bending Delamination Preservative treatment Ligação madeira adesivo Flexão estática Delaminação Tratamento preservativo |
title_short |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives |
title_full |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives |
title_fullStr |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives |
title_full_unstemmed |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives |
title_sort |
Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives |
author |
Faria, Douglas Lamounier |
author_facet |
Faria, Douglas Lamounier Cruz, Thiago Moreira Dias, Matheus Cordazzo Duarte, Paulo Junio Mendes, Lourival Marin Guimarães Junior, José Benedito |
author_role |
author |
author2 |
Cruz, Thiago Moreira Dias, Matheus Cordazzo Duarte, Paulo Junio Mendes, Lourival Marin Guimarães Junior, José Benedito |
author2_role |
author author author author author |
dc.contributor.author.fl_str_mv |
Faria, Douglas Lamounier Cruz, Thiago Moreira Dias, Matheus Cordazzo Duarte, Paulo Junio Mendes, Lourival Marin Guimarães Junior, José Benedito |
dc.subject.por.fl_str_mv |
Adhesive wood bonding Static bending Delamination Preservative treatment Ligação madeira adesivo Flexão estática Delaminação Tratamento preservativo |
topic |
Adhesive wood bonding Static bending Delamination Preservative treatment Ligação madeira adesivo Flexão estática Delaminação Tratamento preservativo |
description |
This work aimed to evaluate the physical and mechanical behavior of glued laminated timber (GLT) - glulam pieces of Hevea brasiliensis treated with chromed copper arsenate (CCA), chromed copper borate (CCB) and pyrethroid in the production of GLT. The pieces were produced using three wooden laminae with dimensions of 60 x 20 x 1200 mm, (width x thickness x length), joined with epoxy adhesive under 1.0 MPa pressure for 24h at room temperature. The rubberwood had an apparent density of 0.624 g cm-3, a value close to that of Eucalyptus grandis wood, a species traditionally used in the manufacture of GLT. Regarding the GLT parts, it was observed that the preservative treatment with CCA and CCB influenced negatively the values of the mechanical properties. For resistance modulus (MOR), a reduction of 75.44 MPa to 62.36 and 58.57 MPa was found for the parts untreated and treated with CCA and CCB, respectively. There was no statistical difference for surface treatment with pyrethroid. The photomicrographs of the glue line showed that the reduction in these values was mainly due to the penetration of preservative solutions into the wood structure (cell lumens and vessels or pores), impairing the anchoring of the adhesive. |
publishDate |
2020 |
dc.date.none.fl_str_mv |
2020-11 2021-09-06T19:34:37Z 2021-09-06T19:34:37Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
FARIA, D. L. et al. Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives. Ciência e Agrotecnologia, Lavras, v. 44, e012020, 2020. DOI: http://dx.doi.org/10.1590/1413-7054202044012020. http://repositorio.ufla.br/jspui/handle/1/48063 |
identifier_str_mv |
FARIA, D. L. et al. Physical and mechanical behavior of glulam beams produced with rubberwood treated with preservatives. Ciência e Agrotecnologia, Lavras, v. 44, e012020, 2020. DOI: http://dx.doi.org/10.1590/1413-7054202044012020. |
url |
http://repositorio.ufla.br/jspui/handle/1/48063 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.rights.driver.fl_str_mv |
http://creativecommons.org/licenses/by/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by/4.0/ |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Lavras |
publisher.none.fl_str_mv |
Universidade Federal de Lavras |
dc.source.none.fl_str_mv |
Ciência e Agrotecnologia reponame:Repositório Institucional da UFLA instname:Universidade Federal de Lavras (UFLA) instacron:UFLA |
instname_str |
Universidade Federal de Lavras (UFLA) |
instacron_str |
UFLA |
institution |
UFLA |
reponame_str |
Repositório Institucional da UFLA |
collection |
Repositório Institucional da UFLA |
repository.name.fl_str_mv |
Repositório Institucional da UFLA - Universidade Federal de Lavras (UFLA) |
repository.mail.fl_str_mv |
nivaldo@ufla.br || repositorio.biblioteca@ufla.br |
_version_ |
1807835093965733888 |