EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%.
Autor(a) principal: | |
---|---|
Data de Publicação: | 2012 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da UFMA |
Texto Completo: | https://tedebc.ufma.br/jspui/handle/tede/tede/2707 |
Resumo: | The aim of this in vitro study was to evaluate the effect in different times of 3% phosphate ascorbyl gel (PA), onto the microshear bond strength of composite resin (CR) to bovine enamel treated with 35% hydrogen peroxide (HP). Thirty bovine incisors were selected. Thirty enamel blocks of 70mm2 were made and distributed into 5 groups (n = 6), which were made on three specimens (n = 18), according to treatment: G1: No bleaching + CR; G2: HP + CR after 15d; G3: HP + CR after 24h; G4: HP + PA 15m + CR after 24h; G5: HP + PA 2h + CR after 24h. The resin cylinders were filled with Filtek ™ Z-350 by Tygon matrices, with photoactivation of 40s. The specimens were stored with cotton soaked in distilled water at 37 ° C for 24h. Microshear bond strength test was performed using universal testing machine with a 50N load at a speed of 0.5 mm / min. Fracture modes were assessed by a stereomicroscope 40x. Microshear bond strength values were submitted to the ANOVA one way and Tukey test (p <0.05). G1 had the highest mean bond strength (15.52 ± 10.01 MPa) when compared to the G3 (5.76 ± 8.02 MPa) and G5 (4.78 ± 4.39 MPa) (p <0.01). However the other groups, G2, G3, G4 and G5 showed no significant differences between groups (p> 0.05). Failure modes were divided into adhesive and mixed, showing mainly adhesive failure (90%) in all groups. It was concluded that 3% phosphate ascorbyl gel applied in time of 15 minutes was able to improve the bond strength of composite resin to bleached bovine enamel. |
id |
UFMA_c2a3bdd37e69650a04225a5c57f6f4ff |
---|---|
oai_identifier_str |
oai:tede2:tede/2707 |
network_acronym_str |
UFMA |
network_name_str |
Biblioteca Digital de Teses e Dissertações da UFMA |
repository_id_str |
2131 |
spelling |
PEREIRA, Adriana de Fátima Vasconcelos459.761.713-20http://lattes.cnpq.br/5415067761503976LIMA, Darlon Martins729.427.543-20http://lattes.cnpq.br/9472478898441292PEREIRA, Adriana de Fátima Vasconcelos459.761.713-20http://lattes.cnpq.br/5415067761503976BANDÉCA, Matheus Coelhohttp://lattes.cnpq.br/5904587055548654SILVA, Ana Paula Britohttp://lattes.cnpq.br/1594623544672871961.293.953-53http://lattes.cnpq.br/4678529823108487CASTRO, Milena de Fátima Schalcher de2019-06-04T14:56:06Z2012-08-29CASTRO, Milena de Fátima Schalcher de. Efeito do gel de ascorbil fosfato 3% na resistência de união da resina composta ao esmalte clareado com peróxido de hidrogênio 35%.. 2012. 53 folhas. Dissertação( Programa de Pós-Graduação em Odontologia/CCBS) - Universidade Federal do Maranhão,São Luís.https://tedebc.ufma.br/jspui/handle/tede/tede/2707The aim of this in vitro study was to evaluate the effect in different times of 3% phosphate ascorbyl gel (PA), onto the microshear bond strength of composite resin (CR) to bovine enamel treated with 35% hydrogen peroxide (HP). Thirty bovine incisors were selected. Thirty enamel blocks of 70mm2 were made and distributed into 5 groups (n = 6), which were made on three specimens (n = 18), according to treatment: G1: No bleaching + CR; G2: HP + CR after 15d; G3: HP + CR after 24h; G4: HP + PA 15m + CR after 24h; G5: HP + PA 2h + CR after 24h. The resin cylinders were filled with Filtek ™ Z-350 by Tygon matrices, with photoactivation of 40s. The specimens were stored with cotton soaked in distilled water at 37 ° C for 24h. Microshear bond strength test was performed using universal testing machine with a 50N load at a speed of 0.5 mm / min. Fracture modes were assessed by a stereomicroscope 40x. Microshear bond strength values were submitted to the ANOVA one way and Tukey test (p <0.05). G1 had the highest mean bond strength (15.52 ± 10.01 MPa) when compared to the G3 (5.76 ± 8.02 MPa) and G5 (4.78 ± 4.39 MPa) (p <0.01). However the other groups, G2, G3, G4 and G5 showed no significant differences between groups (p> 0.05). Failure modes were divided into adhesive and mixed, showing mainly adhesive failure (90%) in all groups. It was concluded that 3% phosphate ascorbyl gel applied in time of 15 minutes was able to improve the bond strength of composite resin to bleached bovine enamel.O objetivo deste estudo foi avaliar in vitro o efeito da aplicação, em diferentes tempos, do gel antioxidante ascorbil fosfato (AF) a 3% sobre a resistência de união ao microcisalhamento da resina composta (RC) ao esmalte bovino tratado com peróxido de hidrogênio a 35% (PH). A partir de 30 incisivos bovinos, foram confeccionados trinta blocos de esmalte de 70mm2 e distribuídos em 5 grupos (n=6), sobre os quais foram feitos 3 corpos de prova (n= 18), de acordo com tratamento: G1: Sem clareamento + RC; G2: PH + RC após 15d; G3: PH + RC após 24h; G4: PH + AF 15m + RC após 24h; G5: PH + AF 2h + RC após 24h. OS cilindros de resina foram confeccionados com Filtek™ Z-350, através de matrizes de Tygon, com fotoativação de 40s. Os espécimes foram armazenados com algodões embebidos em água destilada a 37°C por 24h. O teste de microcisalhamento foi feito em máquina de ensaio universal com célula de carga de 50N e velocidade 0,5mm/min. Os tipos de fraturas foram observados em um estereomicroscópio com aumento de 40x. Os valores de resistência adesiva ao microcisalhamento foram submetidos aos testes ANOVA um critério e Tukey (p<0,05). G1 apresentou as maiores médias de resistência adesiva (15,52±10,01MPa), quando comparadas às dos grupos G3 (5,76± 8,02MPa) e G5 (4,78±4,39MPa) (p<0,01). Entretanto, os grupos G2, G3, G4 e G5 não apresentaram diferenças significativas entre si (p>0,05). As fraturas encontradas foram classificadas como adesivas e mistas, sendo a maioria adesiva (90%) em todos os grupos. Conclui-se que o gel de ascorbil a 3%, aplicado no tempo de 15min, foi capaz de melhorar a resistência adesiva da resina composta ao esmalte bovino clareado.Submitted by Maria Aparecida (cidazen@gmail.com) on 2019-06-04T14:56:06Z No. of bitstreams: 1 Milena de Fátima Schalcher.pdf: 932016 bytes, checksum: 04dd2a5f5f55d328796f6e9b9bb0f3b4 (MD5)Made available in DSpace on 2019-06-04T14:56:06Z (GMT). No. of bitstreams: 1 Milena de Fátima Schalcher.pdf: 932016 bytes, checksum: 04dd2a5f5f55d328796f6e9b9bb0f3b4 (MD5) Previous issue date: 2012-08-29application/pdfporUniversidade Federal do MaranhãoPROGRAMA DE PÓS-GRADUAÇÃO EM ODONTOLOGIA/CCBSUFMABrasilDEPARTAMENTO DE ODONTOLOGIA II/CCBSAntioxidantes; Clareamento dental; Peróxido de hidrogênio; Resinas compostas; Resistência ao cisalhamentoAntioxidants; Tooth bleaching; Hydrogen peroxide; Composite resins; Shear strengthClínica Odontológica.EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%.EFFECT OF THE ASCORBIL PHOSPHATE 3% GEL ON THE UNION RESISTANCE OF THE COMPOSITE RESIN TO THE ENAMEL BLEACHING WITH HYDROGEN PEROXIDE 35%.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da UFMAinstname:Universidade Federal do Maranhão (UFMA)instacron:UFMAORIGINALMilena de Fátima Schalcher.pdfMilena de Fátima Schalcher.pdfapplication/pdf932016http://tedebc.ufma.br:8080/bitstream/tede/2707/2/Milena+de+F%C3%A1tima+Schalcher.pdf04dd2a5f5f55d328796f6e9b9bb0f3b4MD52LICENSElicense.txtlicense.txttext/plain; charset=utf-82255http://tedebc.ufma.br:8080/bitstream/tede/2707/1/license.txt97eeade1fce43278e63fe063657f8083MD51tede/27072019-06-04 11:56:06.541oai:tede2: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Biblioteca Digital de Teses e Dissertaçõeshttps://tedebc.ufma.br/jspui/PUBhttp://tedebc.ufma.br:8080/oai/requestrepositorio@ufma.br||repositorio@ufma.bropendoar:21312019-06-04T14:56:06Biblioteca Digital de Teses e Dissertações da UFMA - Universidade Federal do Maranhão (UFMA)false |
dc.title.por.fl_str_mv |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
dc.title.alternative.eng.fl_str_mv |
EFFECT OF THE ASCORBIL PHOSPHATE 3% GEL ON THE UNION RESISTANCE OF THE COMPOSITE RESIN TO THE ENAMEL BLEACHING WITH HYDROGEN PEROXIDE 35%. |
title |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
spellingShingle |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. CASTRO, Milena de Fátima Schalcher de Antioxidantes; Clareamento dental; Peróxido de hidrogênio; Resinas compostas; Resistência ao cisalhamento Antioxidants; Tooth bleaching; Hydrogen peroxide; Composite resins; Shear strength Clínica Odontológica. |
title_short |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
title_full |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
title_fullStr |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
title_full_unstemmed |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
title_sort |
EFEITO DO GEL DE ASCORBIL FOSFATO 3% NA RESISTÊNCIA DE UNIÃO DA RESINA COMPOSTA AO ESMALTE CLAREADO COM PERÓXIDO DE HIDROGÊNIO 35%. |
author |
CASTRO, Milena de Fátima Schalcher de |
author_facet |
CASTRO, Milena de Fátima Schalcher de |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
PEREIRA, Adriana de Fátima Vasconcelos |
dc.contributor.advisor1ID.fl_str_mv |
459.761.713-20 |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/5415067761503976 |
dc.contributor.advisor-co1.fl_str_mv |
LIMA, Darlon Martins |
dc.contributor.advisor-co1ID.fl_str_mv |
729.427.543-20 |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://lattes.cnpq.br/9472478898441292 |
dc.contributor.referee1.fl_str_mv |
PEREIRA, Adriana de Fátima Vasconcelos |
dc.contributor.referee1ID.fl_str_mv |
459.761.713-20 |
dc.contributor.referee1Lattes.fl_str_mv |
http://lattes.cnpq.br/5415067761503976 |
dc.contributor.referee2.fl_str_mv |
BANDÉCA, Matheus Coelho |
dc.contributor.referee2Lattes.fl_str_mv |
http://lattes.cnpq.br/5904587055548654 |
dc.contributor.referee3.fl_str_mv |
SILVA, Ana Paula Brito |
dc.contributor.referee3Lattes.fl_str_mv |
http://lattes.cnpq.br/1594623544672871 |
dc.contributor.authorID.fl_str_mv |
961.293.953-53 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/4678529823108487 |
dc.contributor.author.fl_str_mv |
CASTRO, Milena de Fátima Schalcher de |
contributor_str_mv |
PEREIRA, Adriana de Fátima Vasconcelos LIMA, Darlon Martins PEREIRA, Adriana de Fátima Vasconcelos BANDÉCA, Matheus Coelho SILVA, Ana Paula Brito |
dc.subject.por.fl_str_mv |
Antioxidantes; Clareamento dental; Peróxido de hidrogênio; Resinas compostas; Resistência ao cisalhamento |
topic |
Antioxidantes; Clareamento dental; Peróxido de hidrogênio; Resinas compostas; Resistência ao cisalhamento Antioxidants; Tooth bleaching; Hydrogen peroxide; Composite resins; Shear strength Clínica Odontológica. |
dc.subject.eng.fl_str_mv |
Antioxidants; Tooth bleaching; Hydrogen peroxide; Composite resins; Shear strength |
dc.subject.cnpq.fl_str_mv |
Clínica Odontológica. |
description |
The aim of this in vitro study was to evaluate the effect in different times of 3% phosphate ascorbyl gel (PA), onto the microshear bond strength of composite resin (CR) to bovine enamel treated with 35% hydrogen peroxide (HP). Thirty bovine incisors were selected. Thirty enamel blocks of 70mm2 were made and distributed into 5 groups (n = 6), which were made on three specimens (n = 18), according to treatment: G1: No bleaching + CR; G2: HP + CR after 15d; G3: HP + CR after 24h; G4: HP + PA 15m + CR after 24h; G5: HP + PA 2h + CR after 24h. The resin cylinders were filled with Filtek ™ Z-350 by Tygon matrices, with photoactivation of 40s. The specimens were stored with cotton soaked in distilled water at 37 ° C for 24h. Microshear bond strength test was performed using universal testing machine with a 50N load at a speed of 0.5 mm / min. Fracture modes were assessed by a stereomicroscope 40x. Microshear bond strength values were submitted to the ANOVA one way and Tukey test (p <0.05). G1 had the highest mean bond strength (15.52 ± 10.01 MPa) when compared to the G3 (5.76 ± 8.02 MPa) and G5 (4.78 ± 4.39 MPa) (p <0.01). However the other groups, G2, G3, G4 and G5 showed no significant differences between groups (p> 0.05). Failure modes were divided into adhesive and mixed, showing mainly adhesive failure (90%) in all groups. It was concluded that 3% phosphate ascorbyl gel applied in time of 15 minutes was able to improve the bond strength of composite resin to bleached bovine enamel. |
publishDate |
2012 |
dc.date.issued.fl_str_mv |
2012-08-29 |
dc.date.accessioned.fl_str_mv |
2019-06-04T14:56:06Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
CASTRO, Milena de Fátima Schalcher de. Efeito do gel de ascorbil fosfato 3% na resistência de união da resina composta ao esmalte clareado com peróxido de hidrogênio 35%.. 2012. 53 folhas. Dissertação( Programa de Pós-Graduação em Odontologia/CCBS) - Universidade Federal do Maranhão,São Luís. |
dc.identifier.uri.fl_str_mv |
https://tedebc.ufma.br/jspui/handle/tede/tede/2707 |
identifier_str_mv |
CASTRO, Milena de Fátima Schalcher de. Efeito do gel de ascorbil fosfato 3% na resistência de união da resina composta ao esmalte clareado com peróxido de hidrogênio 35%.. 2012. 53 folhas. Dissertação( Programa de Pós-Graduação em Odontologia/CCBS) - Universidade Federal do Maranhão,São Luís. |
url |
https://tedebc.ufma.br/jspui/handle/tede/tede/2707 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal do Maranhão |
dc.publisher.program.fl_str_mv |
PROGRAMA DE PÓS-GRADUAÇÃO EM ODONTOLOGIA/CCBS |
dc.publisher.initials.fl_str_mv |
UFMA |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
DEPARTAMENTO DE ODONTOLOGIA II/CCBS |
publisher.none.fl_str_mv |
Universidade Federal do Maranhão |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da UFMA instname:Universidade Federal do Maranhão (UFMA) instacron:UFMA |
instname_str |
Universidade Federal do Maranhão (UFMA) |
instacron_str |
UFMA |
institution |
UFMA |
reponame_str |
Biblioteca Digital de Teses e Dissertações da UFMA |
collection |
Biblioteca Digital de Teses e Dissertações da UFMA |
bitstream.url.fl_str_mv |
http://tedebc.ufma.br:8080/bitstream/tede/2707/2/Milena+de+F%C3%A1tima+Schalcher.pdf http://tedebc.ufma.br:8080/bitstream/tede/2707/1/license.txt |
bitstream.checksum.fl_str_mv |
04dd2a5f5f55d328796f6e9b9bb0f3b4 97eeade1fce43278e63fe063657f8083 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da UFMA - Universidade Federal do Maranhão (UFMA) |
repository.mail.fl_str_mv |
repositorio@ufma.br||repositorio@ufma.br |
_version_ |
1800303797468135424 |