Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UFMG |
Texto Completo: | https://doi.org/10.4103%2F0976-237X.188543 http://hdl.handle.net/1843/55585 |
Resumo: | Objectives: This study aimed to evaluate the influence of the incorporation of pigments on surface hardness of four acrylic resins subjected to thermocycling and analyze their elemental composition using energy dispersive X-ray spectroscopy (EDS). Materials and Methods: Twenty-one discs of each resin were fabricated, whereas seven had no additive, seven had 3% of nanoscale pigments and last seven had 10% of them. The percentage was obtained by measuring the total weight of each resin disc. Besides, seven discs composed by only nanoscale pigments were also fabricated, totalizing 91 discs. The pigment was weighed by using an analytical balance (BEL Analytical Equipment, SP, Brazil). The surface hardness was measured through a hardness tester machine before and after thermocycling (5–55°C, for 2000 cycles). Data were analyzed by ANOVA and Tukey's test (P < 0.05). The chemical composition of the discs composed only by nanoscale pigments was analyzed with EDS test. Results: Hardness of all resins decreased after thermocycling. The lowest values were observed on the discs with 3% of nanoscale pigments and discs fabricated only with them. EDS showed the presence of titanium dioxide. Conclusion: Discs with 7% of pigments (after thermocycling) showed higher hardness values. |
id |
UFMG_413f32e8ac25a357087baec89a72aab3 |
---|---|
oai_identifier_str |
oai:repositorio.ufmg.br:1843/55585 |
network_acronym_str |
UFMG |
network_name_str |
Repositório Institucional da UFMG |
repository_id_str |
|
spelling |
2023-06-30T11:50:37Z2023-06-30T11:50:37Z20167307311https://doi.org/10.4103%2F0976-237X.1885430976237Xhttp://hdl.handle.net/1843/55585Objectives: This study aimed to evaluate the influence of the incorporation of pigments on surface hardness of four acrylic resins subjected to thermocycling and analyze their elemental composition using energy dispersive X-ray spectroscopy (EDS). Materials and Methods: Twenty-one discs of each resin were fabricated, whereas seven had no additive, seven had 3% of nanoscale pigments and last seven had 10% of them. The percentage was obtained by measuring the total weight of each resin disc. Besides, seven discs composed by only nanoscale pigments were also fabricated, totalizing 91 discs. The pigment was weighed by using an analytical balance (BEL Analytical Equipment, SP, Brazil). The surface hardness was measured through a hardness tester machine before and after thermocycling (5–55°C, for 2000 cycles). Data were analyzed by ANOVA and Tukey's test (P < 0.05). The chemical composition of the discs composed only by nanoscale pigments was analyzed with EDS test. Results: Hardness of all resins decreased after thermocycling. The lowest values were observed on the discs with 3% of nanoscale pigments and discs fabricated only with them. EDS showed the presence of titanium dioxide. Conclusion: Discs with 7% of pigments (after thermocycling) showed higher hardness values.engUniversidade Federal de Minas GeraisUFMGBrasilFAO - DEPARTAMENTO DE CLÍNICAContemporary Clinical DentistryAcrylic resinsGeriatricsDenture basesHardnessSpectrometry, x-ray emissionEffect of nanoscale particles incorporation on microhardness of polymers for oral prosthesisinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articlehttps://www.ncbi.nlm.nih.gov/pmc/articles/PMC5004541/Marcelo Coelho GoiatoBruna Carolina Rossatti ZuccolottiAmália MorenoAljomar José Vechiato FilhoMarcela Borghi PauliniDaniela Micheline dos Santosinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFMGinstname:Universidade Federal de Minas Gerais (UFMG)instacron:UFMGORIGINALEffect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis.pdfEffect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis.pdfapplication/pdf926986https://repositorio.ufmg.br/bitstream/1843/55585/2/Effect%20of%20nanoscale%20particles%20incorporation%20on%20microhardness%20of%20polymers%20for%20oral%20prosthesis.pdf7046e672f08227a3a05584923e13201fMD52LICENSELicense.txtLicense.txttext/plain; charset=utf-82042https://repositorio.ufmg.br/bitstream/1843/55585/1/License.txtfa505098d172de0bc8864fc1287ffe22MD511843/555852023-06-30 08:50:37.83oai:repositorio.ufmg.br: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Repositório de PublicaçõesPUBhttps://repositorio.ufmg.br/oaiopendoar:2023-06-30T11:50:37Repositório Institucional da UFMG - Universidade Federal de Minas Gerais (UFMG)false |
dc.title.pt_BR.fl_str_mv |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
title |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
spellingShingle |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis Marcelo Coelho Goiato Acrylic resins Geriatrics Denture bases Hardness Spectrometry, x-ray emission |
title_short |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
title_full |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
title_fullStr |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
title_full_unstemmed |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
title_sort |
Effect of nanoscale particles incorporation on microhardness of polymers for oral prosthesis |
author |
Marcelo Coelho Goiato |
author_facet |
Marcelo Coelho Goiato Bruna Carolina Rossatti Zuccolotti Amália Moreno Aljomar José Vechiato Filho Marcela Borghi Paulini Daniela Micheline dos Santos |
author_role |
author |
author2 |
Bruna Carolina Rossatti Zuccolotti Amália Moreno Aljomar José Vechiato Filho Marcela Borghi Paulini Daniela Micheline dos Santos |
author2_role |
author author author author author |
dc.contributor.author.fl_str_mv |
Marcelo Coelho Goiato Bruna Carolina Rossatti Zuccolotti Amália Moreno Aljomar José Vechiato Filho Marcela Borghi Paulini Daniela Micheline dos Santos |
dc.subject.other.pt_BR.fl_str_mv |
Acrylic resins Geriatrics Denture bases Hardness Spectrometry, x-ray emission |
topic |
Acrylic resins Geriatrics Denture bases Hardness Spectrometry, x-ray emission |
description |
Objectives: This study aimed to evaluate the influence of the incorporation of pigments on surface hardness of four acrylic resins subjected to thermocycling and analyze their elemental composition using energy dispersive X-ray spectroscopy (EDS). Materials and Methods: Twenty-one discs of each resin were fabricated, whereas seven had no additive, seven had 3% of nanoscale pigments and last seven had 10% of them. The percentage was obtained by measuring the total weight of each resin disc. Besides, seven discs composed by only nanoscale pigments were also fabricated, totalizing 91 discs. The pigment was weighed by using an analytical balance (BEL Analytical Equipment, SP, Brazil). The surface hardness was measured through a hardness tester machine before and after thermocycling (5–55°C, for 2000 cycles). Data were analyzed by ANOVA and Tukey's test (P < 0.05). The chemical composition of the discs composed only by nanoscale pigments was analyzed with EDS test. Results: Hardness of all resins decreased after thermocycling. The lowest values were observed on the discs with 3% of nanoscale pigments and discs fabricated only with them. EDS showed the presence of titanium dioxide. Conclusion: Discs with 7% of pigments (after thermocycling) showed higher hardness values. |
publishDate |
2016 |
dc.date.issued.fl_str_mv |
2016 |
dc.date.accessioned.fl_str_mv |
2023-06-30T11:50:37Z |
dc.date.available.fl_str_mv |
2023-06-30T11:50:37Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://hdl.handle.net/1843/55585 |
dc.identifier.doi.pt_BR.fl_str_mv |
https://doi.org/10.4103%2F0976-237X.188543 |
dc.identifier.issn.pt_BR.fl_str_mv |
0976237X |
url |
https://doi.org/10.4103%2F0976-237X.188543 http://hdl.handle.net/1843/55585 |
identifier_str_mv |
0976237X |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.ispartof.pt_BR.fl_str_mv |
Contemporary Clinical Dentistry |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de Minas Gerais |
dc.publisher.initials.fl_str_mv |
UFMG |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
FAO - DEPARTAMENTO DE CLÍNICA |
publisher.none.fl_str_mv |
Universidade Federal de Minas Gerais |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFMG instname:Universidade Federal de Minas Gerais (UFMG) instacron:UFMG |
instname_str |
Universidade Federal de Minas Gerais (UFMG) |
instacron_str |
UFMG |
institution |
UFMG |
reponame_str |
Repositório Institucional da UFMG |
collection |
Repositório Institucional da UFMG |
bitstream.url.fl_str_mv |
https://repositorio.ufmg.br/bitstream/1843/55585/2/Effect%20of%20nanoscale%20particles%20incorporation%20on%20microhardness%20of%20polymers%20for%20oral%20prosthesis.pdf https://repositorio.ufmg.br/bitstream/1843/55585/1/License.txt |
bitstream.checksum.fl_str_mv |
7046e672f08227a3a05584923e13201f fa505098d172de0bc8864fc1287ffe22 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFMG - Universidade Federal de Minas Gerais (UFMG) |
repository.mail.fl_str_mv |
|
_version_ |
1803589446657900544 |