| spelling |
Herman Sander MansurRodrigo Lambert OréficeMarivalda de Magalhaes PereiraEdel Figueiredo BarbosaMagda Francisca Goncalves Rocha2019-08-12T03:11:31Z2019-08-12T03:11:31Z2006-09-13http://hdl.handle.net/1843/BUOS-8DNK7ZO objetivo deste estudo foi caracterizar e comparar amostras de fornecedores distintos de polietileno de peso molecular ultra-elevado (UHMWPE) usadas em artroplastia total de joelho, através de Espectroscopia de Infravermelho por Transformada de Fourier(FTIR), Difração de Raios-X (DRX), Microscopia Eletrônica de Varredura (MEV) acoplada com espectrômetro de energia dispersiva de elétrons (EDS) e Ensaio de Tração. Avaliou-se duas amostras de UHMWPE, uma produzida no Brasil (AMN) e a outra no exterior (AMI), por MEV acoplado com EDS, DRX, FTIR e submetidas a ensaio de tração. Diferenças morfológicas entre elas poderam ser observadas a partir daAMI apresentando uma superfície homogênea com aparência tipo escama de peixe. Os difratogramas obtidos indicaram que as amostras submetidas à avaliação apresentaram graus similares de cristalinidade, endossados pelos resultados do FTIR. As análises espectrográficas por FTIR indicaram discreta diferença no índice deoxidação para as amostras, nas quais a AMI apresentou-se mais reticulada que a AMN. Somam-se a isso, as propriedades mecânicas compatíveis com alto grau de reticulação apresentadas pela AMI. As ligações cruzadas podem ter efeitos consideravelmente diversos na microestrutura e nas propriedades mecânicas do UHMWPE. As diferenças entre as duas amostras AMN e AMI evidenciaram comportamentos e propriedades distintas em caso de utilização de polímero de polietileno em artroplastia total de joelho.The aim of this study was to characterize and also to compare two samples of ultra high molecular weight polyethylene (UHMWPE) useful in total knee replacement using Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) coupled to EDS microprobe and uniaxial tensile test. Two samples of UHMWPE, one of them produced in Brazil (sample AMN) and the otherone produced in a foreign country (sample AMI), were evaluated by SEM coupled with EDS, XRD, FTIR and uniaxial tensile. Morphological differences between the samples were observed with sample AMI presenting a homogeneous surface with fish scales appearance. XRD patterns for both samples under evaluation have shown similardegrees of crystallinity, endorsed by FTIR results. FTIR spectroscopy results have indicated some slight differences on the oxidation for both samples where AMI was found to be more reticulated than AMN. In addition to that, AMI has presented mechanical properties compatible with high grade of reticulation. The effects of crosslinking would like having considerably different effects on the polymer microstructureand mechanical properties of UHMWPE. Based on the results, the differences between the two samples AMN and AMI have given strong evidences that one might expect different properties and behavior if these polymers of polyethylene are used in total knee replacement.Universidade Federal de Minas GeraisUFMGEngenharia metalúrgicaMateriais biomédicosCiência dos materiaisEngenharia Metalúrgica e de MinasAnálise e caracterização do polietileno de ultra-elevado peso molecular para aplicação em prótese total de joelhoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFMGinstname:Universidade Federal de Minas Gerais (UFMG)instacron:UFMGORIGINALmagda_francisca_gon_alves_rocha.pdfapplication/pdf6544716https://repositorio.ufmg.br/bitstream/1843/BUOS-8DNK7Z/1/magda_francisca_gon_alves_rocha.pdf2e604ab27ac5916613f7358305af93d9MD51TEXTmagda_francisca_gon_alves_rocha.pdf.txtmagda_francisca_gon_alves_rocha.pdf.txtExtracted texttext/plain168520https://repositorio.ufmg.br/bitstream/1843/BUOS-8DNK7Z/2/magda_francisca_gon_alves_rocha.pdf.txtab614024d9c6630d95b0752c34fd73ceMD521843/BUOS-8DNK7Z2019-11-14 07:08:15.732oai:repositorio.ufmg.br:1843/BUOS-8DNK7ZRepositório InstitucionalPUBhttps://repositorio.ufmg.br/oaiopendoar:2019-11-14T10:08:15Repositório Institucional da UFMG - Universidade Federal de Minas Gerais (UFMG)false
|