Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFMG |
Texto Completo: | http://hdl.handle.net/1843/RAOA-BAULKW |
Resumo: | The present study proposes to find the mortar that promotes the best performance in a structural masonry of concrete blocks. It was compared industrialized mortars, mortars dosed on site without additive and mortars dosed on site with additives. Tests were performed in fresh and hardened state (standardized and nonstandardized). For the adherence analysis the existing standards did not predict the pullout situation according to the efforts in the structural masonry, making it impossible to evaluate. The potential adherence test was adapted and a test for shear strength was created. In addition, considering that this is study with a practical application, the normative parameters limiting the mechanical strength tests (compression) for mortars were verified, which, in the case of the blocks tested, is 8,3 MPa. Thus it was realized that the dosages on site 1:0,5:6 and 1:0,5:9 with and without additives were not applicable for the tested blocks. The evaluation of the mortars, with compressive strength lower than the limit imposed by the standard, by the graph scale method, the one that obtained the best performance was the mortar measured on site without plasticizer additive with 1:0,5:9 dosage for use in structural masonry composed of concrete blocks with estimated compressive strength (in relation to the net area) of 9,9MPa |
id |
UFMG_fd9147c35c47bf0b89f5f2acb45dfc72 |
---|---|
oai_identifier_str |
oai:repositorio.ufmg.br:1843/RAOA-BAULKW |
network_acronym_str |
UFMG |
network_name_str |
Repositório Institucional da UFMG |
repository_id_str |
|
spelling |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenhoArgamassaAlvenaria estruturalDesempenhoArgamassaConstrução civilAlvenariaDesempenhoThe present study proposes to find the mortar that promotes the best performance in a structural masonry of concrete blocks. It was compared industrialized mortars, mortars dosed on site without additive and mortars dosed on site with additives. Tests were performed in fresh and hardened state (standardized and nonstandardized). For the adherence analysis the existing standards did not predict the pullout situation according to the efforts in the structural masonry, making it impossible to evaluate. The potential adherence test was adapted and a test for shear strength was created. In addition, considering that this is study with a practical application, the normative parameters limiting the mechanical strength tests (compression) for mortars were verified, which, in the case of the blocks tested, is 8,3 MPa. Thus it was realized that the dosages on site 1:0,5:6 and 1:0,5:9 with and without additives were not applicable for the tested blocks. The evaluation of the mortars, with compressive strength lower than the limit imposed by the standard, by the graph scale method, the one that obtained the best performance was the mortar measured on site without plasticizer additive with 1:0,5:9 dosage for use in structural masonry composed of concrete blocks with estimated compressive strength (in relation to the net area) of 9,9MPaO presente estudo propõe encontrar a argamassa que promova o melhor desempenho num sistema em alvenaria estrutural de blocos de concreto. Comparou-se argamassas industrializadas, argamassas dosadas em obra sem aditivo e argamassas dosadas em obras com aditivos. Realizou-se ensaios no estado fresco e no estado endurecido (normatizados e não normatizados). Para análise da aderência as normas existentes não previam a situação de arrancamento de acordo com os esforços existentes na alvenaria estrutural impossibilitando a avaliação. Adaptou-se assim o ensaio de aderência potencial à tração e criou-se um ensaio para resistência ao cisalhamento. Além disso, considerando tratar-se de estudo de aplicação prática, foram verificados os parâmetros normativos que delimitam os ensaios de resistência mecânica (compressão), que, no caso dos blocos ensaiados o limite é 8,3 MPa. Percebeu-se assim, que os traços 1:0,5:6 e 1:0,5:8 dosados em obra com e sem aditivos não são aplicáveis para os blocos utilizados. A avaliação das argamassas, com resistência à compressão inferior ao limite imposto pela norma, deu-se pelo método da escala gráfica e a que obteve melhor desempenho foi a argamassa dosada em obra sem aditivo plastificante com traço 1:0,5:9 para emprego em alvenarias estruturais compostas por blocos de concreto com resistência à compressão estimada (em relação à área líquida) de 9,9MPaUniversidade Federal de Minas GeraisUFMGAntonio Neves de Carvalho JuniorEduardo ChahudEdna Alves OliveiraLuiz Antonio Melgaco Nunes BrancoNatalia Souza Diniz Alves2019-08-12T18:21:46Z2019-08-12T18:21:46Z2018-02-27info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/1843/RAOA-BAULKWinfo:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFMGinstname:Universidade Federal de Minas Gerais (UFMG)instacron:UFMG2019-11-14T22:13:27Zoai:repositorio.ufmg.br:1843/RAOA-BAULKWRepositório InstitucionalPUBhttps://repositorio.ufmg.br/oairepositorio@ufmg.bropendoar:2019-11-14T22:13:27Repositório Institucional da UFMG - Universidade Federal de Minas Gerais (UFMG)false |
dc.title.none.fl_str_mv |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
title |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
spellingShingle |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho Natalia Souza Diniz Alves Argamassa Alvenaria estrutural Desempenho Argamassa Construção civil Alvenaria Desempenho |
title_short |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
title_full |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
title_fullStr |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
title_full_unstemmed |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
title_sort |
Argamassa de assentamento em blocos de concreto para alvenaria estrutural estudo de desempenho |
author |
Natalia Souza Diniz Alves |
author_facet |
Natalia Souza Diniz Alves |
author_role |
author |
dc.contributor.none.fl_str_mv |
Antonio Neves de Carvalho Junior Eduardo Chahud Edna Alves Oliveira Luiz Antonio Melgaco Nunes Branco |
dc.contributor.author.fl_str_mv |
Natalia Souza Diniz Alves |
dc.subject.por.fl_str_mv |
Argamassa Alvenaria estrutural Desempenho Argamassa Construção civil Alvenaria Desempenho |
topic |
Argamassa Alvenaria estrutural Desempenho Argamassa Construção civil Alvenaria Desempenho |
description |
The present study proposes to find the mortar that promotes the best performance in a structural masonry of concrete blocks. It was compared industrialized mortars, mortars dosed on site without additive and mortars dosed on site with additives. Tests were performed in fresh and hardened state (standardized and nonstandardized). For the adherence analysis the existing standards did not predict the pullout situation according to the efforts in the structural masonry, making it impossible to evaluate. The potential adherence test was adapted and a test for shear strength was created. In addition, considering that this is study with a practical application, the normative parameters limiting the mechanical strength tests (compression) for mortars were verified, which, in the case of the blocks tested, is 8,3 MPa. Thus it was realized that the dosages on site 1:0,5:6 and 1:0,5:9 with and without additives were not applicable for the tested blocks. The evaluation of the mortars, with compressive strength lower than the limit imposed by the standard, by the graph scale method, the one that obtained the best performance was the mortar measured on site without plasticizer additive with 1:0,5:9 dosage for use in structural masonry composed of concrete blocks with estimated compressive strength (in relation to the net area) of 9,9MPa |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-02-27 2019-08-12T18:21:46Z 2019-08-12T18:21:46Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://hdl.handle.net/1843/RAOA-BAULKW |
url |
http://hdl.handle.net/1843/RAOA-BAULKW |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Minas Gerais UFMG |
publisher.none.fl_str_mv |
Universidade Federal de Minas Gerais UFMG |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFMG instname:Universidade Federal de Minas Gerais (UFMG) instacron:UFMG |
instname_str |
Universidade Federal de Minas Gerais (UFMG) |
instacron_str |
UFMG |
institution |
UFMG |
reponame_str |
Repositório Institucional da UFMG |
collection |
Repositório Institucional da UFMG |
repository.name.fl_str_mv |
Repositório Institucional da UFMG - Universidade Federal de Minas Gerais (UFMG) |
repository.mail.fl_str_mv |
repositorio@ufmg.br |
_version_ |
1816829784820285440 |