Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Trabalho de conclusão de curso |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Monografias da UFMT |
Texto Completo: | http://bdm.ufmt.br/handle/1/2179 |
Resumo: | The volume of sawdust and plastic lead to many environmental impacts. An alternative is the reuse of these in wood-plastic composite, materials with good physical and mechanical characteristics. The objective was to evaluate the physical and mechanical properties of manufactured composites with different proportions of polypropylene (PP) and sawdust. 4 treatments were made with 4 repetitions, the variation was the ratio of PP and sawdust (90%, 80%, 70% and 60% of PP). The composites were characterized by physical tests of moisture content, density, water absorption and thickness swelling, and mechanical tests of static bending resistance (MOE and MOR) and Rockwell hardness. The values of moisture content was below 4%, the density ranged from 0,78 g/cm³ in the treatment 60%PP to 0,91 g/cm³ at 80%PP. The largest absorption was 5,3% and 13,5% higher swelling treatment in both 80%PP after 72 hours. In mechanical tests the MOE and hardness showed no differences between treatments with average 1544 MPa and 54 respectively HRL, treatment 70%PP had the highest MOR of 24 MPa. In the physical characterization all parameters were according the specification standards. For mechanical testing only the MOR and Rockwell hardness values were according to the standards specifications, the MOE values were below the minimum required by the rules. The wood-plastic panels can be an alternative to recycling of sawdust and polypropylene as decking, table tops, floors, inner walls, etc. |
id |
UFMT-1_f1793d9accc988f901c4801d160dfa5c |
---|---|
oai_identifier_str |
oai:localhost:1/2179 |
network_acronym_str |
UFMT-1 |
network_name_str |
Biblioteca Digital de Monografias da UFMT |
repository_id_str |
|
spelling |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropilenoCNPQ::CIENCIAS AGRARIAS::RECURSOS FLORESTAIS E ENGENHARIA FLORESTALPainéis de madeira-plásticoSerragens - reciclagemPolipropileno - reciclagemWood-plastic panelsSawdust - recyclingPolypropylene - recyclingThe volume of sawdust and plastic lead to many environmental impacts. An alternative is the reuse of these in wood-plastic composite, materials with good physical and mechanical characteristics. The objective was to evaluate the physical and mechanical properties of manufactured composites with different proportions of polypropylene (PP) and sawdust. 4 treatments were made with 4 repetitions, the variation was the ratio of PP and sawdust (90%, 80%, 70% and 60% of PP). The composites were characterized by physical tests of moisture content, density, water absorption and thickness swelling, and mechanical tests of static bending resistance (MOE and MOR) and Rockwell hardness. The values of moisture content was below 4%, the density ranged from 0,78 g/cm³ in the treatment 60%PP to 0,91 g/cm³ at 80%PP. The largest absorption was 5,3% and 13,5% higher swelling treatment in both 80%PP after 72 hours. In mechanical tests the MOE and hardness showed no differences between treatments with average 1544 MPa and 54 respectively HRL, treatment 70%PP had the highest MOR of 24 MPa. In the physical characterization all parameters were according the specification standards. For mechanical testing only the MOR and Rockwell hardness values were according to the standards specifications, the MOE values were below the minimum required by the rules. The wood-plastic panels can be an alternative to recycling of sawdust and polypropylene as decking, table tops, floors, inner walls, etc.O volume de serragens e de plásticos provocam muitos impactos ambientais. Uma alternativa é o reaproveitamento destes em compósitos de madeira-plástico, materiais com boas características físico-mecânicas. O objetivo foi avaliar as propriedades físico-mecânicas de compósitos manufaturados com diferentes proporções de polipropileno (PP) e serragem. Foram feitos 4 tratamentos com 4 repetições, a variação foi à proporção de PP e serragem (90%, 80%, 70% e 60% de PP). Os compósitos foram caracterizados por ensaios físicos de teor de umidade, massa específica, absorção de água e inchamento em espessura, e mecânicos de resistência à flexão estática (MOE e MOR) e dureza Rockwell. Os valores do teor de umidade ficaram abaixo de 4%, a massa específica variou entre 0,78 g/cm³ no tratamento 60%PP a 0,91 g/cm³ no 80%PP. A maior absorção foi de 5,3% e o maior inchamento de 13,5% ambas no tratamento 80%PP após 72 horas. Nos ensaios mecânicos o MOE e a dureza não apresentaram diferenças entre os tratamentos com média de 1544 MPa e 54 HRL respectivamente, o tratamento 70%PP apresentou o maior MOR de 24 MPa. Na caracterização física todos os parâmetros ficaram dentro dos padrões de especificações. Para os ensaios mecânicos apenas o MOR e a dureza Rockwell apresentaram valores dentro das normas de especificações, os valores do MOE ficaram abaixo do mínimo exigido pelas normas. Os painéis de madeira-plástico podem ser uma alternativa para a reciclagem das serragens e de polipropileno como em decks, tampos de mesa, pisos, paredes internas, etc.Universidade Federal de Mato GrossoBrasilInstituto de Ciências Agrárias e Ambientais (ICAA) – SinopUFMT CUS - SinopEngenharia Florestal - CUSMelo, Rafael Rodolfo dehttp://lattes.cnpq.br/6281797821607307Melo, Rafael Rodolfo dehttp://lattes.cnpq.br/6281797821607307Santana, Ricardo Robinson Campomaneshttp://lattes.cnpq.br/4005610138735380Stangerlin, Diego Martinshttp://lattes.cnpq.br/8510628107164043Lima, Daiane Cristina De2022-03-03T14:16:20Z2016-04-042022-03-03T14:16:20Z2016-03-14info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesisinfo:eu-repo/semantics/datasetLIMA, Daiane Cristina De. Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno. 2015. 60f. Trabalho de Conclusão de Curso (Graduação em Engenharia Florestal) – Universidade Federal de Mato Grosso, Instituto de Ciências Agrárias e Ambientais, Sinop, 2015.http://bdm.ufmt.br/handle/1/2179porinfo:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Monografias da UFMTinstname:Universidade Federal de Mato Grosso (UFMT)instacron:UFMT2022-03-22T07:00:50Zoai:localhost:1/2179Biblioteca Digital de Monografiahttps://bdm.ufmt.br/PUBhttp://200.129.241.122/oai/requestopendoar:2022-03-22T07:00:50falseBiblioteca Digital de Monografiahttps://bdm.ufmt.br/PUBhttp://200.129.241.122/oai/requestbibliotecacentral@ufmt.br||opendoar:2022-03-22T07:00:50Biblioteca Digital de Monografias da UFMT - Universidade Federal de Mato Grosso (UFMT)false |
dc.title.none.fl_str_mv |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
title |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
spellingShingle |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno Lima, Daiane Cristina De CNPQ::CIENCIAS AGRARIAS::RECURSOS FLORESTAIS E ENGENHARIA FLORESTAL Painéis de madeira-plástico Serragens - reciclagem Polipropileno - reciclagem Wood-plastic panels Sawdust - recycling Polypropylene - recycling |
title_short |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
title_full |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
title_fullStr |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
title_full_unstemmed |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
title_sort |
Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno |
author |
Lima, Daiane Cristina De |
author_facet |
Lima, Daiane Cristina De |
author_role |
author |
dc.contributor.none.fl_str_mv |
Melo, Rafael Rodolfo de http://lattes.cnpq.br/6281797821607307 Melo, Rafael Rodolfo de http://lattes.cnpq.br/6281797821607307 Santana, Ricardo Robinson Campomanes http://lattes.cnpq.br/4005610138735380 Stangerlin, Diego Martins http://lattes.cnpq.br/8510628107164043 |
dc.contributor.author.fl_str_mv |
Lima, Daiane Cristina De |
dc.subject.por.fl_str_mv |
CNPQ::CIENCIAS AGRARIAS::RECURSOS FLORESTAIS E ENGENHARIA FLORESTAL Painéis de madeira-plástico Serragens - reciclagem Polipropileno - reciclagem Wood-plastic panels Sawdust - recycling Polypropylene - recycling |
topic |
CNPQ::CIENCIAS AGRARIAS::RECURSOS FLORESTAIS E ENGENHARIA FLORESTAL Painéis de madeira-plástico Serragens - reciclagem Polipropileno - reciclagem Wood-plastic panels Sawdust - recycling Polypropylene - recycling |
description |
The volume of sawdust and plastic lead to many environmental impacts. An alternative is the reuse of these in wood-plastic composite, materials with good physical and mechanical characteristics. The objective was to evaluate the physical and mechanical properties of manufactured composites with different proportions of polypropylene (PP) and sawdust. 4 treatments were made with 4 repetitions, the variation was the ratio of PP and sawdust (90%, 80%, 70% and 60% of PP). The composites were characterized by physical tests of moisture content, density, water absorption and thickness swelling, and mechanical tests of static bending resistance (MOE and MOR) and Rockwell hardness. The values of moisture content was below 4%, the density ranged from 0,78 g/cm³ in the treatment 60%PP to 0,91 g/cm³ at 80%PP. The largest absorption was 5,3% and 13,5% higher swelling treatment in both 80%PP after 72 hours. In mechanical tests the MOE and hardness showed no differences between treatments with average 1544 MPa and 54 respectively HRL, treatment 70%PP had the highest MOR of 24 MPa. In the physical characterization all parameters were according the specification standards. For mechanical testing only the MOR and Rockwell hardness values were according to the standards specifications, the MOE values were below the minimum required by the rules. The wood-plastic panels can be an alternative to recycling of sawdust and polypropylene as decking, table tops, floors, inner walls, etc. |
publishDate |
2016 |
dc.date.none.fl_str_mv |
2016-04-04 2016-03-14 2022-03-03T14:16:20Z 2022-03-03T14:16:20Z |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/publishedVersion info:eu-repo/semantics/bachelorThesis info:eu-repo/semantics/dataset |
format |
bachelorThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
LIMA, Daiane Cristina De. Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno. 2015. 60f. Trabalho de Conclusão de Curso (Graduação em Engenharia Florestal) – Universidade Federal de Mato Grosso, Instituto de Ciências Agrárias e Ambientais, Sinop, 2015. http://bdm.ufmt.br/handle/1/2179 |
identifier_str_mv |
LIMA, Daiane Cristina De. Compósitos madeira-plástico confeccionados com serragem de cambará (Qualea sp.) e resíduos de polipropileno. 2015. 60f. Trabalho de Conclusão de Curso (Graduação em Engenharia Florestal) – Universidade Federal de Mato Grosso, Instituto de Ciências Agrárias e Ambientais, Sinop, 2015. |
url |
http://bdm.ufmt.br/handle/1/2179 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de Mato Grosso Brasil Instituto de Ciências Agrárias e Ambientais (ICAA) – Sinop UFMT CUS - Sinop Engenharia Florestal - CUS |
publisher.none.fl_str_mv |
Universidade Federal de Mato Grosso Brasil Instituto de Ciências Agrárias e Ambientais (ICAA) – Sinop UFMT CUS - Sinop Engenharia Florestal - CUS |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Monografias da UFMT instname:Universidade Federal de Mato Grosso (UFMT) instacron:UFMT |
instname_str |
Universidade Federal de Mato Grosso (UFMT) |
instacron_str |
UFMT |
institution |
UFMT |
reponame_str |
Biblioteca Digital de Monografias da UFMT |
collection |
Biblioteca Digital de Monografias da UFMT |
repository.name.fl_str_mv |
Biblioteca Digital de Monografias da UFMT - Universidade Federal de Mato Grosso (UFMT) |
repository.mail.fl_str_mv |
bibliotecacentral@ufmt.br|| |
_version_ |
1804658251514511360 |