SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES
Autor(a) principal: | |
---|---|
Data de Publicação: | 2012 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional Universidade Franciscana |
Texto Completo: | http://tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/207 http://www.tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/300 |
Resumo: | The amount of wastewater generated with the growing concern about the scarcity of water resources in a short time, is a problem of public health and of the environment too. The effluents are composed of materials that provide a large amount of phenols, acids and enzymatic products. To purify water, the advanced oxidation processes (AOP) are the newest and promissor alternative between the scientists. The AOP form radicals that can oxide organic materials into carbon dioxide and water (CO2 and H2O) and other inorganic ions. The TiO2, mainly at anatase phase, has several features that make it a promising material in this area, since from its low toxicity until the fact that it is activated by light. For use in photocatalysis, TiO2 may be used as powder, crystal or thin film. What determines the form that it will be used is the application that will be made . To this study we produced TiO2 at anatase phase under the powder form and thin films (the characterization was made separately). We observe, after the characterization, that the powder produced was 100% under the anatase phase, with an average size of particles with 20 nm, zeta potential of -21.0 mV, PDI of 0.8, and a very large specific area of 60.446 m2 g-1. Furthermore, the thin films of TiO2 produced had a thickness of approximately 70 nm and a specific area of 0.1180 m2 g-1, about 30 times higher than the glass slide which was used as base to thw thin film. Finally, about the application of the material to degradation of dye and antibiotic we obtained positive results once it was possible to observe the gradual elimination of these substances. Unfortunately, the results of the antimicrobial activity of the TiO2 produced are insufficient, what inspires the need for the continuation of this study. |
id |
UFN-1_eae9b1187503e9ebda77c8ce2268598b |
---|---|
oai_identifier_str |
oai:tede.universidadefranciscana.edu.br:UFN-BDTD/300 |
network_acronym_str |
UFN-1 |
network_name_str |
Repositório Institucional Universidade Franciscana |
repository_id_str |
http://www.tede.universidadefranciscana.edu.br:8080/oai/request |
spelling |
Mortari, Sergio RobertoCPF:58768335091CPF:01208260464http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4216163H1Andrade, Cláudia Turra de2018-06-27T18:56:10Z2012-08-24ANDRADE, Cláudia Turra de. SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES. 2012. 79 f. Dissertação (Mestrado em Biociências e Nanomateriais) - Universidade Franciscana, Santa Maria, 2012.http://tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/207http://www.tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/300The amount of wastewater generated with the growing concern about the scarcity of water resources in a short time, is a problem of public health and of the environment too. The effluents are composed of materials that provide a large amount of phenols, acids and enzymatic products. To purify water, the advanced oxidation processes (AOP) are the newest and promissor alternative between the scientists. The AOP form radicals that can oxide organic materials into carbon dioxide and water (CO2 and H2O) and other inorganic ions. The TiO2, mainly at anatase phase, has several features that make it a promising material in this area, since from its low toxicity until the fact that it is activated by light. For use in photocatalysis, TiO2 may be used as powder, crystal or thin film. What determines the form that it will be used is the application that will be made . To this study we produced TiO2 at anatase phase under the powder form and thin films (the characterization was made separately). We observe, after the characterization, that the powder produced was 100% under the anatase phase, with an average size of particles with 20 nm, zeta potential of -21.0 mV, PDI of 0.8, and a very large specific area of 60.446 m2 g-1. Furthermore, the thin films of TiO2 produced had a thickness of approximately 70 nm and a specific area of 0.1180 m2 g-1, about 30 times higher than the glass slide which was used as base to thw thin film. Finally, about the application of the material to degradation of dye and antibiotic we obtained positive results once it was possible to observe the gradual elimination of these substances. Unfortunately, the results of the antimicrobial activity of the TiO2 produced are insufficient, what inspires the need for the continuation of this study.A quantidade de efluente gerada atualmente somado-se à crescente preocupação com a escassez de recursos hídricos em pouco tempo, se mostram um problema não só de saúde pública como também ambiental. Os efluentes são compostos de materiais que propiciam uma grande quantidade de fenóis, ácidos e produtos enzimáticos. Para obter água purificada, os processos oxidativos avançados (POA) se destacam no cenário científico. Os POA formam radicais capazes de oxidar diversos materiais orgânicos em gás carbônico e água (CO2 e H2O) e outros íons inorgânicos. O TiO2 (principalmente na fase anatase) apresenta várias características que fazem dele um material promissor nesta área, que incluem desde sua comprovada baixa toxicidade até o fato de ser ativado pela luz. Para a utilização em fotocatálise, o TiO2 pode ser usado na forma de pó, cristal ou filme fino. O que determina a forma a ser utilizada é a aplicação que será feita. Para o estudo realizado neste trabalho, foram produzidos pó na fase anatase e filmes finos de TiO2 que foram caracterizados separadamente. Verificou-se, após a caracterização, que o pó produzido apresentava 100% da fase anatase em sua composição, apresentando um tamanho médio de partícula de 20 nm, potencial zeta de -21,0 mV, Índice de Polidispersão de 0,8, além de uma área específica bastante grande, de 60,446 m2 g-1. Além disso, os filmes finos de TiO2 se mostraram com uma espessura de aproximadamente 70 nm e uma área específica de 0,1180 m2 g-1, cerca de 30 vezes maior do que a da lâmina de vidro que serviu como sua base. Por fim, no que diz respeito à aplicação do material na degradação tanto de corante quanto de antibiótico, obtivemos resultados positivos, uma vez que foi possível observar a eliminação gradual das substâncias citadas. Infelizmente, os resultados da atividade antimicrobiana do composto produzido se mostraram insuficientes, o que inspira a necessidade da continuação deste estudo.Made available in DSpace on 2018-06-27T18:56:10Z (GMT). No. of bitstreams: 2 CLAUDIA TURRA DE ANDRADE.pdf: 18738699 bytes, checksum: 132776bfd28c6c670c7642740fce4b69 (MD5) CLAUDIA TURRA DE ANDRADE.pdf.jpg: 3628 bytes, checksum: d1495cc4a8a7a2109f7fc01af2ba0996 (MD5) Previous issue date: 2012-08-24Coordenação de Aperfeiçoamento de Pessoal de Nível Superiorapplication/pdfhttp://tede.universidadefranciscana.edu.br:8080/retrieve/455/CLAUDIA%20TURRA%20DE%20ANDRADE.pdf.jpgporUniversidade FranciscanaMestrado Acadêmico em NanociênciasUFNBRBiociências e Nanomateriaisnanotecnologiadióxido de titâniofotocatálisenanotechnologytitanium dioxidephotocatalysisCNPQ::ENGENHARIASSÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTESinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional Universidade Franciscanainstname:Universidade Franciscana (UFN)instacron:UFNORIGINALCLAUDIA TURRA DE ANDRADE.pdfapplication/pdf18738699http://tede.universidadefranciscana.edu.br:8080/bitstream/UFN-BDTD/300/1/CLAUDIA+TURRA+DE+ANDRADE.pdf132776bfd28c6c670c7642740fce4b69MD51THUMBNAILCLAUDIA TURRA DE ANDRADE.pdf.jpgimage/jpeg3628http://tede.universidadefranciscana.edu.br:8080/bitstream/UFN-BDTD/300/2/CLAUDIA+TURRA+DE+ANDRADE.pdf.jpgd1495cc4a8a7a2109f7fc01af2ba0996MD52UFN-BDTD/3002018-06-27 15:56:10.182oai:tede.universidadefranciscana.edu.br:UFN-BDTD/300Repositório de Publicaçõeshttp://www.tede.universidadefranciscana.edu.br:8080/http://www.tede.universidadefranciscana.edu.br:8080/oai/requestopendoar:2018-06-27T18:56:10Repositório Institucional Universidade Franciscana - Universidade Franciscana (UFN)false |
dc.title.por.fl_str_mv |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
title |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
spellingShingle |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES Andrade, Cláudia Turra de nanotecnologia dióxido de titânio fotocatálise nanotechnology titanium dioxide photocatalysis CNPQ::ENGENHARIAS |
title_short |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
title_full |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
title_fullStr |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
title_full_unstemmed |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
title_sort |
SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES |
author |
Andrade, Cláudia Turra de |
author_facet |
Andrade, Cláudia Turra de |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Mortari, Sergio Roberto |
dc.contributor.advisor1ID.fl_str_mv |
CPF:58768335091 |
dc.contributor.authorID.fl_str_mv |
CPF:01208260464 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4216163H1 |
dc.contributor.author.fl_str_mv |
Andrade, Cláudia Turra de |
contributor_str_mv |
Mortari, Sergio Roberto |
dc.subject.por.fl_str_mv |
nanotecnologia dióxido de titânio fotocatálise |
topic |
nanotecnologia dióxido de titânio fotocatálise nanotechnology titanium dioxide photocatalysis CNPQ::ENGENHARIAS |
dc.subject.eng.fl_str_mv |
nanotechnology titanium dioxide photocatalysis |
dc.subject.cnpq.fl_str_mv |
CNPQ::ENGENHARIAS |
description |
The amount of wastewater generated with the growing concern about the scarcity of water resources in a short time, is a problem of public health and of the environment too. The effluents are composed of materials that provide a large amount of phenols, acids and enzymatic products. To purify water, the advanced oxidation processes (AOP) are the newest and promissor alternative between the scientists. The AOP form radicals that can oxide organic materials into carbon dioxide and water (CO2 and H2O) and other inorganic ions. The TiO2, mainly at anatase phase, has several features that make it a promising material in this area, since from its low toxicity until the fact that it is activated by light. For use in photocatalysis, TiO2 may be used as powder, crystal or thin film. What determines the form that it will be used is the application that will be made . To this study we produced TiO2 at anatase phase under the powder form and thin films (the characterization was made separately). We observe, after the characterization, that the powder produced was 100% under the anatase phase, with an average size of particles with 20 nm, zeta potential of -21.0 mV, PDI of 0.8, and a very large specific area of 60.446 m2 g-1. Furthermore, the thin films of TiO2 produced had a thickness of approximately 70 nm and a specific area of 0.1180 m2 g-1, about 30 times higher than the glass slide which was used as base to thw thin film. Finally, about the application of the material to degradation of dye and antibiotic we obtained positive results once it was possible to observe the gradual elimination of these substances. Unfortunately, the results of the antimicrobial activity of the TiO2 produced are insufficient, what inspires the need for the continuation of this study. |
publishDate |
2012 |
dc.date.issued.fl_str_mv |
2012-08-24 |
dc.date.accessioned.fl_str_mv |
2018-06-27T18:56:10Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
ANDRADE, Cláudia Turra de. SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES. 2012. 79 f. Dissertação (Mestrado em Biociências e Nanomateriais) - Universidade Franciscana, Santa Maria, 2012. |
dc.identifier.uri.fl_str_mv |
http://tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/207 http://www.tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/300 |
identifier_str_mv |
ANDRADE, Cláudia Turra de. SÍNTESE, CARACTERIZAÇÃO E APLICAÇÃO DE TiO2 NANOESTRUTURADO PARA O TRATAMENTO DE EFLUENTES. 2012. 79 f. Dissertação (Mestrado em Biociências e Nanomateriais) - Universidade Franciscana, Santa Maria, 2012. |
url |
http://tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/207 http://www.tede.universidadefranciscana.edu.br:8080/handle/UFN-BDTD/300 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Franciscana |
dc.publisher.program.fl_str_mv |
Mestrado Acadêmico em Nanociências |
dc.publisher.initials.fl_str_mv |
UFN |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Biociências e Nanomateriais |
publisher.none.fl_str_mv |
Universidade Franciscana |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional Universidade Franciscana instname:Universidade Franciscana (UFN) instacron:UFN |
instname_str |
Universidade Franciscana (UFN) |
instacron_str |
UFN |
institution |
UFN |
reponame_str |
Repositório Institucional Universidade Franciscana |
collection |
Repositório Institucional Universidade Franciscana |
bitstream.url.fl_str_mv |
http://tede.universidadefranciscana.edu.br:8080/bitstream/UFN-BDTD/300/1/CLAUDIA+TURRA+DE+ANDRADE.pdf http://tede.universidadefranciscana.edu.br:8080/bitstream/UFN-BDTD/300/2/CLAUDIA+TURRA+DE+ANDRADE.pdf.jpg |
bitstream.checksum.fl_str_mv |
132776bfd28c6c670c7642740fce4b69 d1495cc4a8a7a2109f7fc01af2ba0996 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional Universidade Franciscana - Universidade Franciscana (UFN) |
repository.mail.fl_str_mv |
|
_version_ |
1809269396314521600 |