Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates.
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Outros Autores: | |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UFOP |
Texto Completo: | http://www.repositorio.ufop.br/handle/123456789/4870 http://dx.doi.org/10.1590/S1516-14392013005000189 |
Resumo: | The influence of the synthesis parameters on the crystalline structures of orthotantalate ceramics has been investigated. Powder materials were prepared by the solid-state reaction route. X-ray diffraction and Raman scattering measurements were employed to investigate the crystal structure of the produced materials. In this work, we analyzed three different examples in which the temperature and time were decisive on the final crystal structure of LnTaO4 compounds besides the lanthanide ionic size. Firstly, the thermal evolution for NdTaO4 samples showed that mixed crystal phases are formed up to 1100 °C, while well-crystallized M-NdTaO4 (I2/a) materials are obtained in temperatures higher than 1200 °C. Also, the influence of the synthesis time was investigated for the LaTaO4 ceramics: it was necessary 14 h to obtain samples in the P21/c structure. Finally, two polymorphs could be obtained for the DyTaO4 ceramics: P2/a and I2/a space groups were obtained at 1300 °C and 1500 °C, respectively. This study indicated that the temperature, time and lanthanide size are directly correlated with the crystalline arrangement of the orthotantalate materials. |
id |
UFOP_0edbca620786ba46c0d5c375a34e740b |
---|---|
oai_identifier_str |
oai:localhost:123456789/4870 |
network_acronym_str |
UFOP |
network_name_str |
Repositório Institucional da UFOP |
repository_id_str |
3233 |
spelling |
Siqueira, Kisla Prislen FélixDias, Anderson2015-04-01T17:16:41Z2015-04-01T17:16:41Z2014SIQUEIRA, K. P. F.; DIAS, A. Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. Materials Research, São Carlos, v. 17, p. 167-173, 2014. Disponível em: <http://www.scielo.br/scielo.php?pid=S1516-14392014000700027&script=sci_arttext>. Acesso em: 02 fev. 2015.1516-1439http://www.repositorio.ufop.br/handle/123456789/4870http://dx.doi.org/10.1590/S1516-14392013005000189The influence of the synthesis parameters on the crystalline structures of orthotantalate ceramics has been investigated. Powder materials were prepared by the solid-state reaction route. X-ray diffraction and Raman scattering measurements were employed to investigate the crystal structure of the produced materials. In this work, we analyzed three different examples in which the temperature and time were decisive on the final crystal structure of LnTaO4 compounds besides the lanthanide ionic size. Firstly, the thermal evolution for NdTaO4 samples showed that mixed crystal phases are formed up to 1100 °C, while well-crystallized M-NdTaO4 (I2/a) materials are obtained in temperatures higher than 1200 °C. Also, the influence of the synthesis time was investigated for the LaTaO4 ceramics: it was necessary 14 h to obtain samples in the P21/c structure. Finally, two polymorphs could be obtained for the DyTaO4 ceramics: P2/a and I2/a space groups were obtained at 1300 °C and 1500 °C, respectively. This study indicated that the temperature, time and lanthanide size are directly correlated with the crystalline arrangement of the orthotantalate materials.Solid-state processingLanthanide orthotantalatesCrystal structureRaman spectroscopyEffect of the processing parameters on the crystalline structure of lanthanide orthotantalates.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleO periódico Materials Research dá permissão ao RI/UFOP para depositar uma cópia eletrônica dos artigos publicados por esse periódico em que ao menos um dos autores é aluno ou professor da UFOP. Contato via email em 25 out. 2013.info:eu-repo/semantics/openAccessengreponame:Repositório Institucional da UFOPinstname:Universidade Federal de Ouro Preto (UFOP)instacron:UFOPLICENSElicense.txtlicense.txttext/plain; charset=utf-82636http://www.repositorio.ufop.br/bitstream/123456789/4870/2/license.txtc2ffdd99e58acf69202dff00d361f23aMD52ORIGINALARTIGO_EffectProcessingParameter.pdfARTIGO_EffectProcessingParameter.pdfapplication/pdf1625511http://www.repositorio.ufop.br/bitstream/123456789/4870/1/ARTIGO_EffectProcessingParameter.pdf27ee62b1ede3b3ada66b3d3eb2161382MD51123456789/48702019-07-02 13:54:33.937oai:localhost: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Repositório InstitucionalPUBhttp://www.repositorio.ufop.br/oai/requestrepositorio@ufop.edu.bropendoar:32332019-07-02T17:54:33Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP)false |
dc.title.pt_BR.fl_str_mv |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
title |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
spellingShingle |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. Siqueira, Kisla Prislen Félix Solid-state processing Lanthanide orthotantalates Crystal structure Raman spectroscopy |
title_short |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
title_full |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
title_fullStr |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
title_full_unstemmed |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
title_sort |
Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. |
author |
Siqueira, Kisla Prislen Félix |
author_facet |
Siqueira, Kisla Prislen Félix Dias, Anderson |
author_role |
author |
author2 |
Dias, Anderson |
author2_role |
author |
dc.contributor.author.fl_str_mv |
Siqueira, Kisla Prislen Félix Dias, Anderson |
dc.subject.por.fl_str_mv |
Solid-state processing Lanthanide orthotantalates Crystal structure Raman spectroscopy |
topic |
Solid-state processing Lanthanide orthotantalates Crystal structure Raman spectroscopy |
description |
The influence of the synthesis parameters on the crystalline structures of orthotantalate ceramics has been investigated. Powder materials were prepared by the solid-state reaction route. X-ray diffraction and Raman scattering measurements were employed to investigate the crystal structure of the produced materials. In this work, we analyzed three different examples in which the temperature and time were decisive on the final crystal structure of LnTaO4 compounds besides the lanthanide ionic size. Firstly, the thermal evolution for NdTaO4 samples showed that mixed crystal phases are formed up to 1100 °C, while well-crystallized M-NdTaO4 (I2/a) materials are obtained in temperatures higher than 1200 °C. Also, the influence of the synthesis time was investigated for the LaTaO4 ceramics: it was necessary 14 h to obtain samples in the P21/c structure. Finally, two polymorphs could be obtained for the DyTaO4 ceramics: P2/a and I2/a space groups were obtained at 1300 °C and 1500 °C, respectively. This study indicated that the temperature, time and lanthanide size are directly correlated with the crystalline arrangement of the orthotantalate materials. |
publishDate |
2014 |
dc.date.issued.fl_str_mv |
2014 |
dc.date.accessioned.fl_str_mv |
2015-04-01T17:16:41Z |
dc.date.available.fl_str_mv |
2015-04-01T17:16:41Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SIQUEIRA, K. P. F.; DIAS, A. Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. Materials Research, São Carlos, v. 17, p. 167-173, 2014. Disponível em: <http://www.scielo.br/scielo.php?pid=S1516-14392014000700027&script=sci_arttext>. Acesso em: 02 fev. 2015. |
dc.identifier.uri.fl_str_mv |
http://www.repositorio.ufop.br/handle/123456789/4870 |
dc.identifier.issn.none.fl_str_mv |
1516-1439 |
dc.identifier.doi.none.fl_str_mv |
http://dx.doi.org/10.1590/S1516-14392013005000189 |
identifier_str_mv |
SIQUEIRA, K. P. F.; DIAS, A. Effect of the processing parameters on the crystalline structure of lanthanide orthotantalates. Materials Research, São Carlos, v. 17, p. 167-173, 2014. Disponível em: <http://www.scielo.br/scielo.php?pid=S1516-14392014000700027&script=sci_arttext>. Acesso em: 02 fev. 2015. 1516-1439 |
url |
http://www.repositorio.ufop.br/handle/123456789/4870 http://dx.doi.org/10.1590/S1516-14392013005000189 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFOP instname:Universidade Federal de Ouro Preto (UFOP) instacron:UFOP |
instname_str |
Universidade Federal de Ouro Preto (UFOP) |
instacron_str |
UFOP |
institution |
UFOP |
reponame_str |
Repositório Institucional da UFOP |
collection |
Repositório Institucional da UFOP |
bitstream.url.fl_str_mv |
http://www.repositorio.ufop.br/bitstream/123456789/4870/2/license.txt http://www.repositorio.ufop.br/bitstream/123456789/4870/1/ARTIGO_EffectProcessingParameter.pdf |
bitstream.checksum.fl_str_mv |
c2ffdd99e58acf69202dff00d361f23a 27ee62b1ede3b3ada66b3d3eb2161382 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP) |
repository.mail.fl_str_mv |
repositorio@ufop.edu.br |
_version_ |
1801685757825384448 |