Electrodeposition of diamond-like carbon (DLC) films on Ti.
Autor(a) principal: | |
---|---|
Data de Publicação: | 2009 |
Outros Autores: | |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Institucional da UFOP |
Texto Completo: | http://www.repositorio.ufop.br/handle/123456789/4483 https://doi.org/10.1016/j.apsusc.2008.10.087 |
Resumo: | Diamond-like carbon films (DLC) were deposited on titanium substrates in acetonitrile and N,N-dimethyl formamide (DMF) liquids by the liquid-phase electrodeposition technique at ambient pressure and temperature. The applied voltage between the electrodes was high (1200 V) due to the use of resistive organic liquids. The surface morphology was examined by Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM). Corrosion performance of the coatings was investigated by potentiodynamic polararization tests in phosphate buffer saline solution. Raman spectroscopy analysis of the films revealed two broad bands at approximately 1360 cm_1 and 1580 cm_1, related to D and G-band of DLC, respectively. The coated Ti was tested in a ball-on-plate type wear test machine with Al2O3 balls. The films presented a low friction coefficient (about 0.1), and the films deposited from DMF presented the best wear resistance. |
id |
UFOP_50ca404af6490d7473fd2763b7e91430 |
---|---|
oai_identifier_str |
oai:localhost:123456789/4483 |
network_acronym_str |
UFOP |
network_name_str |
Repositório Institucional da UFOP |
repository_id_str |
3233 |
spelling |
Manhabosco, Taíse MatteMuller, Iduvirges Lourdes2015-02-25T16:04:30Z2015-02-25T16:04:30Z2009MANHABOSCO, T. M.; MULLER, I. L. Electrodeposition of diamond-like carbon (DLC) films on Ti. Applied Surface Science, v. 255, p. 4082-4086, 2009. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0169433208022551>. Acesso em: 24 fev. 2015.0169-4332http://www.repositorio.ufop.br/handle/123456789/4483https://doi.org/10.1016/j.apsusc.2008.10.087Diamond-like carbon films (DLC) were deposited on titanium substrates in acetonitrile and N,N-dimethyl formamide (DMF) liquids by the liquid-phase electrodeposition technique at ambient pressure and temperature. The applied voltage between the electrodes was high (1200 V) due to the use of resistive organic liquids. The surface morphology was examined by Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM). Corrosion performance of the coatings was investigated by potentiodynamic polararization tests in phosphate buffer saline solution. Raman spectroscopy analysis of the films revealed two broad bands at approximately 1360 cm_1 and 1580 cm_1, related to D and G-band of DLC, respectively. The coated Ti was tested in a ball-on-plate type wear test machine with Al2O3 balls. The films presented a low friction coefficient (about 0.1), and the films deposited from DMF presented the best wear resistance.ElectrodepositionDiamond like carbonOrganic liquidsElectrodeposition of diamond-like carbon (DLC) films on Ti.info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleO periódico Applied Surface Science concede permissão para depósito do artigo no Repositório Institucional da UFOP. Número da licença: 3566051000625.info:eu-repo/semantics/openAccessengreponame:Repositório Institucional da UFOPinstname:Universidade Federal de Ouro Preto (UFOP)instacron:UFOPLICENSElicense.txtlicense.txttext/plain; charset=utf-82636http://www.repositorio.ufop.br/bitstream/123456789/4483/2/license.txtc2ffdd99e58acf69202dff00d361f23aMD52ORIGINALARTIGO_ElectrodepositionDiamond-likeCarbon.pdfARTIGO_ElectrodepositionDiamond-likeCarbon.pdfapplication/pdf725182http://www.repositorio.ufop.br/bitstream/123456789/4483/1/ARTIGO_ElectrodepositionDiamond-likeCarbon.pdfc8cce2152400cc34de57c3579e12e1d4MD51123456789/44832019-06-24 08:04:21.87oai:localhost: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Repositório InstitucionalPUBhttp://www.repositorio.ufop.br/oai/requestrepositorio@ufop.edu.bropendoar:32332019-06-24T12:04:21Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP)false |
dc.title.pt_BR.fl_str_mv |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
title |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
spellingShingle |
Electrodeposition of diamond-like carbon (DLC) films on Ti. Manhabosco, Taíse Matte Electrodeposition Diamond like carbon Organic liquids |
title_short |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
title_full |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
title_fullStr |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
title_full_unstemmed |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
title_sort |
Electrodeposition of diamond-like carbon (DLC) films on Ti. |
author |
Manhabosco, Taíse Matte |
author_facet |
Manhabosco, Taíse Matte Muller, Iduvirges Lourdes |
author_role |
author |
author2 |
Muller, Iduvirges Lourdes |
author2_role |
author |
dc.contributor.author.fl_str_mv |
Manhabosco, Taíse Matte Muller, Iduvirges Lourdes |
dc.subject.por.fl_str_mv |
Electrodeposition Diamond like carbon Organic liquids |
topic |
Electrodeposition Diamond like carbon Organic liquids |
description |
Diamond-like carbon films (DLC) were deposited on titanium substrates in acetonitrile and N,N-dimethyl formamide (DMF) liquids by the liquid-phase electrodeposition technique at ambient pressure and temperature. The applied voltage between the electrodes was high (1200 V) due to the use of resistive organic liquids. The surface morphology was examined by Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM). Corrosion performance of the coatings was investigated by potentiodynamic polararization tests in phosphate buffer saline solution. Raman spectroscopy analysis of the films revealed two broad bands at approximately 1360 cm_1 and 1580 cm_1, related to D and G-band of DLC, respectively. The coated Ti was tested in a ball-on-plate type wear test machine with Al2O3 balls. The films presented a low friction coefficient (about 0.1), and the films deposited from DMF presented the best wear resistance. |
publishDate |
2009 |
dc.date.issued.fl_str_mv |
2009 |
dc.date.accessioned.fl_str_mv |
2015-02-25T16:04:30Z |
dc.date.available.fl_str_mv |
2015-02-25T16:04:30Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
MANHABOSCO, T. M.; MULLER, I. L. Electrodeposition of diamond-like carbon (DLC) films on Ti. Applied Surface Science, v. 255, p. 4082-4086, 2009. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0169433208022551>. Acesso em: 24 fev. 2015. |
dc.identifier.uri.fl_str_mv |
http://www.repositorio.ufop.br/handle/123456789/4483 |
dc.identifier.issn.none.fl_str_mv |
0169-4332 |
dc.identifier.doi.none.fl_str_mv |
https://doi.org/10.1016/j.apsusc.2008.10.087 |
identifier_str_mv |
MANHABOSCO, T. M.; MULLER, I. L. Electrodeposition of diamond-like carbon (DLC) films on Ti. Applied Surface Science, v. 255, p. 4082-4086, 2009. Disponível em: <http://www.sciencedirect.com/science/article/pii/S0169433208022551>. Acesso em: 24 fev. 2015. 0169-4332 |
url |
http://www.repositorio.ufop.br/handle/123456789/4483 https://doi.org/10.1016/j.apsusc.2008.10.087 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFOP instname:Universidade Federal de Ouro Preto (UFOP) instacron:UFOP |
instname_str |
Universidade Federal de Ouro Preto (UFOP) |
instacron_str |
UFOP |
institution |
UFOP |
reponame_str |
Repositório Institucional da UFOP |
collection |
Repositório Institucional da UFOP |
bitstream.url.fl_str_mv |
http://www.repositorio.ufop.br/bitstream/123456789/4483/2/license.txt http://www.repositorio.ufop.br/bitstream/123456789/4483/1/ARTIGO_ElectrodepositionDiamond-likeCarbon.pdf |
bitstream.checksum.fl_str_mv |
c2ffdd99e58acf69202dff00d361f23a c8cce2152400cc34de57c3579e12e1d4 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFOP - Universidade Federal de Ouro Preto (UFOP) |
repository.mail.fl_str_mv |
repositorio@ufop.edu.br |
_version_ |
1801685709851983872 |