Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura

Detalhes bibliográficos
Autor(a) principal: Araujo, Emanoel Cunha
Data de Publicação: 2022
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/81749
Resumo: Orientador: Prof. Dr. Marcelo Henrique de Farias Medeiros
id UFPR_10139574fd7b29254e3588c0cccd2ae0
oai_identifier_str oai:acervodigital.ufpr.br:1884/81749
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Pieralisi, Ricardo, 1989-Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia CivilMedeiros, Marcelo Henrique Farias de, 1976-Araujo, Emanoel Cunha2023-03-29T12:25:40Z2023-03-29T12:25:40Z2022https://hdl.handle.net/1884/81749Orientador: Prof. Dr. Marcelo Henrique de Farias MedeirosCoorientador: Prof. Dr. Ricardo PieralisiDissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia Civil. Defesa : Curitiba, 23/12/2022Inclui referências: p. 117-138Área de concentração: Materiais e EstruturasResumo: Materiais de reparo em vertedouros de barragem, pavimentação, ou ambientes em exposição à radiação solar estão submetidos à ciclos de aquecimento e resfriamento devido as variações de temperatura diárias, ocasionando tensões térmicas no compósito que podem acarretar a perda de aderência entre esse e o substrato de concreto, impactando na sua eficiência. Os nano materiais são partículas com dimensões nanométricas que atuam no refinamento do esqueleto granular de compósitos cimentícios melhorando suas propriedades físicas e mecânicas, assim como os parâmetros de durabilidade. O objetivo principal desse estudo é avaliar a eficiência de argamassas de reparo com nano partículas de nanotubos de carbono e nanossílica, combinadas com micropartículas de grafeno e sílica ativa e microfibras de polipropileno, avaliando-se suas propriedades mecânicas, durabilidade e microestrutura. Para tal, as argamassas foram caracterizadas no estado fresco pela densidade aparente e consistência. No estado endurecido, foram avaliadas à retração por secagem, absorção de água, resistência à compressão, resistência à tração na flexão, módulo de elasticidade estático, coeficiente de expansão térmica, resistividade elétrica superficial, aderência e microestrutura. Ademais, as argamassas foram submetidas ao envelhecimento higrotérmico e os efeitos nas propriedades supracitadas foram avaliadas. Os resultados apontaram que as partículas de grafeno e dos nanotubos foram as mais eficientes em termos de melhoria das propriedades mecânicas. Já quanto à durabilidade, as argamassas com sílica ativa apresentaram incrementos da resistividade de até 69,49% em relação à mistura de referência. A avaliação da microestrutura demonstrou interação e aglutinação entre os produtos de hidratação do cimento Portland e as nano partículas de nanotubo de carbono e micropartículas de grafeno. A argamassa com maior eficiência frente os ciclos higrotérmicos foi a mistura com 0,02% de nanotubos. Esta mistura não apresentou reduções nas propriedades físicas, nomeadamente, absorção, resistência à compressão, resistência à tração na flexão e módulo de elasticidade após a aplicação do envelhecimento higrotérmico.Abstract: Repair materials in dam spillways, pavements, or environments exposed to solar radiation are submitted to heating and cooling cycles due to daily temperature fluctuations. These phenomena cause thermal stresses in the composite that can lead to a loss of adhesion between it and the concrete substrate, impacting its efficiency. The nanomaterials are particles with nanometric dimensions that act on the packing of the cementitious composite granular skeleton, thus improving their physical and mechanical properties and durability parameters. The main objective of this study is to evaluate the efficiency concerned mechanical properties, durability, and microstructure of repair mortars with nanoparticles such as carbon nanotubes and nano-silica combined with microparticles of graphene and silica fume and polypropylene microfibers. The mortars were analyzed concerning their fresh state by bulk density and consistency. In the hardened state, the properties evaluated were the drying shrinkage, water absorption, compressive strength, flexural tensile strength, static modulus of elasticity, coefficient of thermal expansion, surface electrical resistivity, adhesion, and microstructure. Furthermore, the mortars were submitted to hygrothermal aging, and the effects on the aforementioned properties were evaluated. The results indicated that the graphene and nanotube particles were the most efficient in improving the mechanical properties. As for durability, the mortars with silica fume presented an increase in resistivity of up to 69.49% concerned with the reference mixture. The evaluation of the microstructure showed interaction and agglutination between the hydration products of Portland cement and carbon nanotube nanoparticles and graphene micro-particles. The mortar with the highest efficiency against hygrothermal cycles was the mixture with 0.02% of nanotubes. This mixture showed no reduction in physical properties, including absorption, compressive strength, flexural tensile strength, and modulus of elasticity after hygrothermal aging.1 recurso online : PDF.application/pdfNanotubos de carbonoGrafenoSílicaEngenharia CivilEficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestruturainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - D - EMANOEL CUNHA ARAUJO.pdfapplication/pdf18849638https://acervodigital.ufpr.br/bitstream/1884/81749/1/R%20-%20D%20-%20EMANOEL%20CUNHA%20ARAUJO.pdf7be43b56ea1ea2ebee704b9ade07eca6MD51open access1884/817492023-03-29 09:25:40.679open accessoai:acervodigital.ufpr.br:1884/81749Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082023-03-29T12:25:40Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
title Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
spellingShingle Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
Araujo, Emanoel Cunha
Nanotubos de carbono
Grafeno
Sílica
Engenharia Civil
title_short Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
title_full Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
title_fullStr Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
title_full_unstemmed Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
title_sort Eficiência de argamassas de reparo com nano materiais : propriedades mecânicas, durabilidade e com microestrutura
author Araujo, Emanoel Cunha
author_facet Araujo, Emanoel Cunha
author_role author
dc.contributor.other.pt_BR.fl_str_mv Pieralisi, Ricardo, 1989-
Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia Civil
dc.contributor.advisor1.fl_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
dc.contributor.author.fl_str_mv Araujo, Emanoel Cunha
contributor_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
dc.subject.por.fl_str_mv Nanotubos de carbono
Grafeno
Sílica
Engenharia Civil
topic Nanotubos de carbono
Grafeno
Sílica
Engenharia Civil
description Orientador: Prof. Dr. Marcelo Henrique de Farias Medeiros
publishDate 2022
dc.date.issued.fl_str_mv 2022
dc.date.accessioned.fl_str_mv 2023-03-29T12:25:40Z
dc.date.available.fl_str_mv 2023-03-29T12:25:40Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/81749
url https://hdl.handle.net/1884/81749
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 1 recurso online : PDF.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/81749/1/R%20-%20D%20-%20EMANOEL%20CUNHA%20ARAUJO.pdf
bitstream.checksum.fl_str_mv 7be43b56ea1ea2ebee704b9ade07eca6
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1813898899006423040

Registros relacionados