Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland

Detalhes bibliográficos
Autor(a) principal: Adorno, Cleberson dos Santos, 1983-
Data de Publicação: 2018
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/58490
Resumo: Orientador: Prof. Dr. Marcelo Henrique Farias de Medeiros
id UFPR_4e73980d1021671192be95d027194b59
oai_identifier_str oai:acervodigital.ufpr.br:1884/58490
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Adorno, Cleberson dos Santos, 1983-Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia CivilMedeiros, Marcelo Henrique Farias de, 1976-2021-07-12T18:30:47Z2021-07-12T18:30:47Z2018https://hdl.handle.net/1884/58490Orientador: Prof. Dr. Marcelo Henrique Farias de MedeirosDissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia de Construção Civil. Defesa : Curitiba, 29/06/2017Inclui referências: p.133-141Resumo: A reação álcali-sílica é um processo de degradação relevante na tecnologia do concreto, devido ao seu potencial de afetar a funcionalidade das estruturas atingidas. Seguindo este contexto, este projeto tem por objetivo investigar o grau de mitigação proporcionado por adições minerais em compósitos cimentícios submetidos aos ensaios preconizados na NBR 15577-5:2008 - Determinação da expansão em barras de argamassa pelo método acelerado e investigação da microestrutura dos compósitos pelos ensaios de difratometria de raios-X, fluorescência de raios-X, microscopia eletrônica de varredura, termogravimetria e porosimetria. A metodologia usada envolve a confecção de corpos de prova de argamassa com as seguintes adições: filer quartzoso, metacaulim, sílica ativa, cinza volante, sílica de casca de arroz e resíduos de material cerâmico, esta última adição com nível de finura de acordo com o tempo de moagem (90 minutos). Entre as adições minerais empregadas, existem representantes que são reconhecidamente pozolânicos, outras que possivelmente são pozolânicas e outros que são inertes. Este critério foi tomado para investigar se o efeito fíler também pode ser um parâmetro mitigador da reação álcali-sílica. Foram produzidos corpos de prova (25 mm x 25 mm x 285 mm) para as argamassas com cimento Portland CP V ARI e agregados encontrados na região de Curitiba. A relação água/aglomerante utilizada foi de 0,47. Para as adições minerais empregou-se um teor de substituição do cimento de 10% e, também foram confeccionados corpos de prova de referência, ou seja, com 100% de cimento CP V ARI. Ensaiou-se 42 corpos de prova no total, sendo 6 de cada uma das adições, destas barras de argamassa 3 de cada adição foram colocadas na solução de NaOH a 80 ºC conforme prescrito na NBR 15577-4:2008 e outras 3 foram colocadas em água destilada a 50ºC para serem referência. Com todas essas amostras foram realizados ensaios de DRX, FRX, MEV, Termogravimetria e Porosimetria. Os resultados indicam que o resíduo cerâmico apresentou resultados que não mitigam a expansão por reação álcali-sílica, em contrapartida todas as outras adições utilizadas colaboram para a redução da expansão por álcali-sílica, principalmente a sílica ativa. A minimização da expansão está relacionada à redução do teor de hidróxido de cálcio na argamassa, que diminui com o aumento da adição pozolânica no cimento. Palavras-chave: Reatividade álcali-sílica, Portlandita, Cimento Portland, Argamassa, Pozolana, Adição Mineral.Abstract: The alkali-silica reaction is a relevant degradation process in concrete technology, because of its potential to affect the functionality of the structures. Therefore, this Master's thesis aims to investigate the degree of mitigation provided by mineral additions in cement composites subjected to testing recommended in NBR 15577- 4:2008 - Determination of expansion in mortar bars by the accelerated method and investigation of the microstructure of the composites by X-ray diffraction, X-ray fluorescence, scanning electron microscopy, thermogravimetry and porosimetry. The method involves producing mortar specimens with the following mineral admixtures: quartz filler, metakaolin, silica fume, rice husk ash, fly ash and residue from ceramic bricks the latter with level of fineness according grinding time (90 minutes). Among the admixtures employed, some are pozzolanic, others who are possibly pozzolanic and other is inert. This criterion has been taken in order to investigate if the filler effect is also a parameter mitigating alkali-silica reaction. Test specimens (25 mm x 25 mm x 285 mm) were produced with Portland cement CP V ARI and aggregate from the metropolitan region of Curitiba. The water/binder ratio used was 0.47. A content of 10% of cement was replaced by mineral admixture and also a reference mortar was produced with of 100% cement CP V ARI. A total of 42 test bars were tested six of each of the following additions: 100% cement, quartz filer, metakaolin, silica fume, fly ash, rice husk silica and ceramic residue with milling time of 90 minutes of these mortar bars were 3 of each addition were placed in the 80 ºC NaOH solution as prescribed in NBR 15577-4:2008 and another 3 were placed in distilled water at 50 ºC for reference. With all these samples were performed XRD, FRX, MEV, thermogravimetry and porosimetry tests. The results indicate that the ceramic residue presented results that do not mitigate the expansion by alkali silica reaction, in contrast all the other additions used collaborate to reduce the expansion by alkali-silica, mainly the silica fume. Keywords: Alkali-silica reaction, Portland cement, Portlandite, Mortar bars, Pozzolan, Mineral admixture.156 p. : il. (algumas color.).application/pdfCimento portlandEngenharia CivilConcreto - CorrosãoArgamassaTesesEfeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portlandinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - D - CLEBERSON DOS SANTOS ADORNO.pdfapplication/pdf7104937https://acervodigital.ufpr.br/bitstream/1884/58490/1/R%20-%20D%20-%20CLEBERSON%20DOS%20SANTOS%20ADORNO.pdfb5f466fe15abf310563495f611bb0335MD51open access1884/584902021-07-12 15:30:48.061open accessoai:acervodigital.ufpr.br:1884/58490Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082021-07-12T18:30:48Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
title Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
spellingShingle Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
Adorno, Cleberson dos Santos, 1983-
Cimento portland
Engenharia Civil
Concreto - Corrosão
Argamassa
Teses
title_short Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
title_full Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
title_fullStr Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
title_full_unstemmed Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
title_sort Efeitos físico-químicos de adições minerais na reatividade álcali-agregado em compósitos de cimento portland
author Adorno, Cleberson dos Santos, 1983-
author_facet Adorno, Cleberson dos Santos, 1983-
author_role author
dc.contributor.other.pt_BR.fl_str_mv Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia Civil
dc.contributor.author.fl_str_mv Adorno, Cleberson dos Santos, 1983-
dc.contributor.advisor1.fl_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
contributor_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
dc.subject.por.fl_str_mv Cimento portland
Engenharia Civil
Concreto - Corrosão
Argamassa
Teses
topic Cimento portland
Engenharia Civil
Concreto - Corrosão
Argamassa
Teses
description Orientador: Prof. Dr. Marcelo Henrique Farias de Medeiros
publishDate 2018
dc.date.issued.fl_str_mv 2018
dc.date.accessioned.fl_str_mv 2021-07-12T18:30:47Z
dc.date.available.fl_str_mv 2021-07-12T18:30:47Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/58490
url https://hdl.handle.net/1884/58490
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 156 p. : il. (algumas color.).
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/58490/1/R%20-%20D%20-%20CLEBERSON%20DOS%20SANTOS%20ADORNO.pdf
bitstream.checksum.fl_str_mv b5f466fe15abf310563495f611bb0335
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1801860780411322368

Registros relacionados