Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)

Detalhes bibliográficos
Autor(a) principal: Tavora, Mauro Vitor Greco, 1989-
Data de Publicação: 2019
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/62518
Resumo: Orientador: Prof. Dr. Marcelo Henrique Farias de Medeiros
id UFPR_7131290d92369f36877023d896fc07f2
oai_identifier_str oai:acervodigital.ufpr.br:1884/62518
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Tavora, Mauro Vitor Greco, 1989-Matos, Jorge Luis Monteiro de, 1960-Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia CivilMedeiros, Marcelo Henrique Farias de, 1976-2021-07-12T17:44:41Z2021-07-12T17:44:41Z2019https://hdl.handle.net/1884/62518Orientador: Prof. Dr. Marcelo Henrique Farias de MedeirosCoorientador: Prof. Dr. Jorge Luis Monteiro de MatosDissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia de Construção Civil. Defesa : Curitiba, 10/04/2019Inclui referências: p. 79-89Área de concentração: Materiais e EstruturasResumo: O presente trabalho teve como objetivo avaliar a aptidão da madeira de Pinus taeda L. termomodificada para a função de lamelas e posterior confecção de produtos de madeira laminada colada. O material foi termomodificado em três patamares de temperatura (160, 180 e 200°C), respeitando as diretrizes do documento de patente: Processo de modificação térmica por irradiação de calor, para a melhora da estabilidade dimensional e da durabilidade biológica de madeira sólida (INPI - PI0902138-8 A2). Na sequência, foram determinadas as propriedades físicas (perda de massa, teor de umidade de equilíbrio, estabilidade dimensional, densidade aparente e molhabilidade) e mecânicas (resistência à compressão, resistência à flexão e resistência ao cisalhamento) das amostras testemunha e do material termomodificado. Também foram aplicadas as técnicas não-destrutivas de ultrassom e ondas de tensão, visando estabelecer correlações com propriedades das madeiras termomodificadas determinadas pelos ensaios mecânicos destrutivos. Foi observada uma redução no teor de umidade de equilíbrio para todas as temperaturas aplicadas, alteração positiva que indica uma redução da higroscopicidade do material. Somente o tratamento a 200°C resultou em uma melhora na estabilidade dimensional do material, o qual ocasionou uma menor taxa de absorção de água e variação volumétrica. O tratamento a 200°C também se destacou na alteração da molhabilidade do material, evidenciado pelo aumento nos ângulos de contato. A densidade aparente a 0% de umidade do material não se alterou entre os diferentes tratamentos térmicos. Em relação às propriedades mecânicas foi observado um aumento na resistência à compressão paralela às fibras, apesar do módulo de ruptura (MOR) e o módulo de elasticidade (MOE), na flexão estática, não se alterarem devido à modificação térmica. Apenas o tratamento a 200°C foi prejudicial à adesividade do material, enquanto que a modificação térmica a 160 e 180°C não ocasionou reduções na resistência ao cisalhamento na linha de cola, indicando a possibilidade de uso de material termomodificado em produtos de madeira que passem por processo de colagem. Além disso, os valores de módulo de elasticidade dinâmico determinados a partir das técnicas não-destrutivas de ultrassom e ondas de tensão (Stress Wave Timer) apresentaram fortes correlações com o módulo de elasticidade estático (MOE), determinado pelo ensaio destrutivo de resistência à flexão estática, evidenciando a possibilidade de utilizar tais técnicas para a estimativa de propriedades mecânicas de madeiras nas quais tenha sido aplicado um processo de modificação térmica. Palavras-chaves: Modificação térmica. Propriedades físicas e mecânicas. Adesividade.Abstract: The present work aims to evaluate the ability of thermally modified Pinus taeda L. wood for the function of lamellae and later confection of glulam products. The material was heated in three temperature stages (160°C, 180°C and 200°C), respecting the guidelines of the patent document: Thermal modifying process by heat irradiation, for the improvement of dimensional stability and durability solid wood (INPI - PI0902138-8 A2). Afterwards, physical properties (mass loss, equilibrium moisture content, dimensional stability, apparent density at 0% moisture content and wettability) and mechanical properties (compression parallel to grain strength, static bending strength and shear strength in the glue line) were determined for thermally treated and untreated material. Non-destructive techniques of ultrasound and Stress Wave Timer were also applied in order to establish correlations with the modified woods mechanical properties determined by destructive mechanical tests. A reduction in equilibrium moisture content was observed for allapplied temperature, a positive change indicating a reduction in the hygroscopicity of the material. Only the treatment at 200°C resulted in an improvement in the dimensional stability of the material, which a lower rate of water absorption and volumetric variation. The treatment at 200°C also altered the wettability of the material, evidenced by the increase in the contact angles. The apparent density at 0% moisture content of the material did not change due to the different heat treatments. Regarding mechanical properties, an increase in the compressive strength parallel to the fibers was observed with the heat treatment although the modulus of rupture (MOR) and modulus of elasticity (MOE), at static bending, did not change due the thermal modification. Only the treatment at200°C was detrimental to the adhesiveness of the material, whereas the thermal modification at 160 and 180°C did not cause reductions in the shear strength in the glue line, indicating the possibility of using thermo-modified material in wood products that pass through a bonding process. Besides that, dynamic modulus of elasticity values, determined from the nondestructive techniques of ultrasound and Stress Wave Timer had strong correlations with the static modulus of elasticity (MOE), determined by the destructive test of static bending, showing the possibility of using such techniques for the estimation of mechanical properties of heat-treated wood. Keywords: Thermal modification. Physical and Mechanical properties. Adhesion.89 p. : il. (algumas color.).application/pdfPinus taedaLâminas de madeiraEngenharia CivilEngenharia termicaAptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - D - MAURO VITOR GRECO TAVORA.pdfapplication/pdf2652453https://acervodigital.ufpr.br/bitstream/1884/62518/1/R%20-%20D%20-%20%20MAURO%20VITOR%20GRECO%20TAVORA.pdf9dbd558b9fd75f56d2843c11ac45a74eMD51open access1884/625182021-07-12 14:44:42.139open accessoai:acervodigital.ufpr.br:1884/62518Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082021-07-12T17:44:42Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
title Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
spellingShingle Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
Tavora, Mauro Vitor Greco, 1989-
Pinus taeda
Lâminas de madeira
Engenharia Civil
Engenharia termica
title_short Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
title_full Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
title_fullStr Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
title_full_unstemmed Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
title_sort Aptidão de lamelas termo-modificadas de Pinus taeda L. para a produção de madeira laminada colada (MLC)
author Tavora, Mauro Vitor Greco, 1989-
author_facet Tavora, Mauro Vitor Greco, 1989-
author_role author
dc.contributor.other.pt_BR.fl_str_mv Matos, Jorge Luis Monteiro de, 1960-
Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia Civil
dc.contributor.author.fl_str_mv Tavora, Mauro Vitor Greco, 1989-
dc.contributor.advisor1.fl_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
contributor_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
dc.subject.por.fl_str_mv Pinus taeda
Lâminas de madeira
Engenharia Civil
Engenharia termica
topic Pinus taeda
Lâminas de madeira
Engenharia Civil
Engenharia termica
description Orientador: Prof. Dr. Marcelo Henrique Farias de Medeiros
publishDate 2019
dc.date.issued.fl_str_mv 2019
dc.date.accessioned.fl_str_mv 2021-07-12T17:44:41Z
dc.date.available.fl_str_mv 2021-07-12T17:44:41Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/62518
url https://hdl.handle.net/1884/62518
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 89 p. : il. (algumas color.).
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/62518/1/R%20-%20D%20-%20%20MAURO%20VITOR%20GRECO%20TAVORA.pdf
bitstream.checksum.fl_str_mv 9dbd558b9fd75f56d2843c11ac45a74e
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1801860357348655104

Registros relacionados