Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários

Detalhes bibliográficos
Autor(a) principal: Godinho, Jayson Pereira
Data de Publicação: 2023
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/85755
Resumo: Orientador: Prof. Dr. Marcelo Henrique Farias de Medeiros
id UFPR_9b0262fe485d3699974b02c8f71e66ed
oai_identifier_str oai:acervodigital.ufpr.br:1884/85755
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia CivilMedeiros, Marcelo Henrique Farias de, 1976-Godinho, Jayson Pereira2023-12-21T14:39:38Z2023-12-21T14:39:38Z2023https://hdl.handle.net/1884/85755Orientador: Prof. Dr. Marcelo Henrique Farias de MedeirosTese (doutorado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia Civil. Defesa : Curitiba, 31/05/2023Inclui referênciasÁrea de concentração: Materiais e EstruturasResumo: É fundamental investigar a degradação do concreto causada pelo ácido sulfúrico de origem biogênica devido a vários fatores, incluindo questões sociais, ambientais e econômicas. Além disso, há uma falta de normas brasileiras e poucos estudos no país que identifiquem a melhor composição do concreto para resistir a esse tipo de ataque ou as soluções mais eficazes para proteger as estruturas de concreto quando expostas a esse agente agressivo. Deste modo, o objetivo do estudo foi avaliar o efeito de cristalizantes comerciais e da solução de silicato de sódio neutro (Na2SiO3) no aumento da durabilidade do concreto armado, submetido ao ataque sulfúrico de origem biogênica em uma ETE e de origem química em laboratório. Para atingir esse objetivo, foi realizada primeiramente a caracterização do concreto da ETE, no qual os testemunhos foram testados com ensaios microestruturais e mecânicos. Também foi definido em experimentos preliminares o teor ótimo da solução de silicato de sódio neutro, e ao final, foram moldados diferentes corpos de prova para a realização de diversos ensaios como velocidade de pulso ultrassônico (VPU), resistência à tração na flexão e à compressão, profundidade de neutralização, variação dimensional e de massa do concreto, microscopia eletrônica de varredura (MEV) e espectroscopia de energia dispersiva (EDS), difratometria de raios X (DRX), espectroscopia Raman e espectroscopia de infravermelho por transformada de Fourier (FTIR). Como resultados em relação ao Capítulo 4, foi possível notar que o pH do interior das lajes se manteve acima da faixa de viragem da solução de fenolftaleína, a resistência à compressão se manteve acima daquela especificada em projeto, e por meio das análises microestruturais, foi possível identificar a presença de etringita e gipsita ao longo de toda a profundidade do testemunho da laje. Em relação ao Capítulo 5, somente foi possível verificar a influência do ataque ácido na VPU e resistência à compressão uniaxial após 56 dias de exposição, onde todos os concretos tiveram redução dos parâmetros mecânicos aos 91 dias. Ao final do estudo no Capítulo 6, foi constatado que a velocidade de deterioração e perda de massa são os melhores indicadores da durabilidade a longo prazo do concreto exposto ao ácido sulfúrico. Os concretos com cinza volante e cristalizantes comerciais apresentaram valores mais baixos desses parâmetros, indicando maior durabilidade. Os ensaios eletroquímicos de densidade de corrente de corrosão e potencial de corrosão foram eficazes na avaliação da durabilidade dos corpos de prova armados, com os mesmos resultados favoráveis aos concretos com as adições mencionadasAbstract: It is essential to investigate the degradation of concrete caused by biogenic sulfuric acid due to various factors, including social, environmental, and economic issues. In addition, there is a lack of Brazilian standards and few studies in the country that identify the best concrete composition to resist this type of attack or the most effective solutions to protect concrete structures when exposed to this aggressive agent. Thus, the objective of the study was to evaluate the effect of commercial crystallizers and neutral sodium silicate solution (Na2SiO3) on increasing the durability of reinforced concrete subjected to biogenic sulfuric acid attack in an ETE and chemical sulfuric acid attack in the laboratory. To achieve this objective, the concrete of the ETE was first characterized, where the specimens were tested with microstructural and mechanical tests. The optimal content of the neutral sodium silicate solution was also defined in preliminary experiments, and different specimens were molded for various tests, such as ultrasonic pulse velocity (UPV), flexural and compressive strength, neutralization depth, concrete dimensional and mass variation, scanning electron microscopy (SEM), energydispersive spectroscopy (EDS), X-ray diffraction (XRD), Raman spectroscopy, and Fourier transform infrared spectroscopy (FTIR). As results in relation to Chapter 4, it was observed that the pH inside the slabs remained above the phenolphthalein turning range, the compressive strength remained above that specified in the project, and through microstructural analysis, the presence of ettringite and gypsum was identified throughout the depth of the slab specimen. In relation to Chapter 5, it was only possible to verify the influence of acid attack on UPV and compressive uniaxial strength after 56 days of exposure, where all concretes had a reduction in mechanical parameters after 91 days. At the end of the study in Chapter 6, it was observed that Portland cement composites with the addition of neutral sodium silicate were also susceptible to sulfuric acid degradation, but to a lesser extent when compared to those with the addition of alkaline sodium silicate. At the end of the study, it was found that the speed of deterioration and mass loss are the best indicators of long-term durability of concrete exposed to sulfuric acid. Concretes with fly ash and commercial crystallizers showed lower values of these parameters, indicating greater durability. Electrochemical tests of corrosion current density and corrosion potential were effective in evaluating the durability of reinforced specimens, with the same favorable results for concretes with the mentioned additions1 recurso online : PDF.application/pdfConstrução de concreto armadoAcido sulfuricoÁguas residuaisEsgotos - TratamentoEngenharia CivilEfeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitáriosinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - T - JAYSON PEREIRA GODINHO.pdfapplication/pdf33400349https://acervodigital.ufpr.br/bitstream/1884/85755/1/R%20-%20T%20-%20JAYSON%20PEREIRA%20GODINHO.pdf28f3d6befdb859b6204a5cb4dbdcb3b9MD51open access1884/857552023-12-21 11:39:39.004open accessoai:acervodigital.ufpr.br:1884/85755Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082023-12-21T14:39:39Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
title Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
spellingShingle Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
Godinho, Jayson Pereira
Construção de concreto armado
Acido sulfurico
Águas residuais
Esgotos - Tratamento
Engenharia Civil
title_short Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
title_full Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
title_fullStr Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
title_full_unstemmed Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
title_sort Efeito de cristalizantes na durabilidade do concreto armado submetido ao ataque por ácido sulfúrico biogênico gerado em estação municipai de tratamento de esgotos sanitários
author Godinho, Jayson Pereira
author_facet Godinho, Jayson Pereira
author_role author
dc.contributor.other.pt_BR.fl_str_mv Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia Civil
dc.contributor.advisor1.fl_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
dc.contributor.author.fl_str_mv Godinho, Jayson Pereira
contributor_str_mv Medeiros, Marcelo Henrique Farias de, 1976-
dc.subject.por.fl_str_mv Construção de concreto armado
Acido sulfurico
Águas residuais
Esgotos - Tratamento
Engenharia Civil
topic Construção de concreto armado
Acido sulfurico
Águas residuais
Esgotos - Tratamento
Engenharia Civil
description Orientador: Prof. Dr. Marcelo Henrique Farias de Medeiros
publishDate 2023
dc.date.accessioned.fl_str_mv 2023-12-21T14:39:38Z
dc.date.available.fl_str_mv 2023-12-21T14:39:38Z
dc.date.issued.fl_str_mv 2023
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/85755
url https://hdl.handle.net/1884/85755
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 1 recurso online : PDF.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/85755/1/R%20-%20T%20-%20JAYSON%20PEREIRA%20GODINHO.pdf
bitstream.checksum.fl_str_mv 28f3d6befdb859b6204a5cb4dbdcb3b9
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1813898877705650176

Registros relacionados