Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica

Detalhes bibliográficos
Autor(a) principal: Sato, Hebert Hiroshi
Data de Publicação: 2015
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/54472
Resumo: Orientadora: Profª. Drª. Neide Kazue Kuromoto
id UFPR_ca6d26e53745f93e03071e247837dbb0
oai_identifier_str oai:acervodigital.ufpr.br:1884/54472
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia MecânicaKuromoto, Neide Kazue, 1954-Sato, Hebert Hiroshi2024-07-25T19:17:18Z2024-07-25T19:17:18Z2015https://hdl.handle.net/1884/54472Orientadora: Profª. Drª. Neide Kazue KuromotoDissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia Mecânica. Defesa: Curitiba, 13/03/2015Inclui referências : fls. 77-84Resumo: O titânio (Ti) e suas ligas são bastante utilizados para fabricação de implantes dentários e próteses ortopédicas. Uma alternativa para o emprego de biomateriais metálicos na ortopedia são as ligas de titânio-nióbio (Ti-Nb), devido a sua excelente biocompatibilidade, e do ponto de vista econômico, devido à produção do Nb no Brasil em alta escala. Para estas aplicações específicas os metais devem possuir propriedades adequadas, tais como toxicidade zero, boas propriedades mecânicas (módulo de elasticidade próximo ao do osso humano), e de resistência à corrosão. Outro fator relevante a ser considerado é a recuperação rápida do paciente, que é conseguida através da diminuição do tempo de osseointegração entre o implante metálico e o osso, isto é, a superficie que estará em contato com o osso deverá ser bioativa para induzir o crescimento das células. Existem vários métodos para aumentar a bioatividade do Ti de forma a diminuir o tempo de convalescença do paciente. Esses tratamentos superficiais resultam em superfícies com morfologias, rugosidades e propriedades mecânicas diferentes. O presente estudo teve como objetivo modificar a superfície de uma liga de Ti-Nb com a intenção de torná-la bioativa usando a técnica a oxidação anódica (OA), que foi realizada usando o ácido fosfórico 1mol/L, sob modo potenciostático (250V/60s). Foram avaliadas a morfologia do filme anódico e elementos químicos presentes (MEV), as fases presentes (DRX e espectroscopia Raman), as propriedades mecânicas (indentação instrumentada), tribológicas (análise da taxa de desgaste e coeficiente de atrito) e de bioatividade in vitro (SBF). A superfície oxidada se apresentou com morfologia rugosa e porosa e enriquecida com P. Verificou-se que as ligas Ti-Nb apresentaram durezas mais elevadas e módulos de elasticidade mais baixos quando comparadas ao Ti comercialmente puro. Com relação aos testes tribológicos, não foram observadas diferenças significativas no coeficiente de atrito das várias superfícies analisadas e verificou-se que a taxa de desgaste foi mais baixa para a liga com 10% de Nb em relação a liga com 20% de Nb. Além da baixa taxa de desgaste essa liga se mostrou mais bioativa em solução de SBF do que a liga contendo 20% de Nb.Abstract: Titanium (Ti) and its alloys are widely used for the manufacture of dental implants and orthopedic prostheses. An alternative to the use of metallic biomaterials in orthopedics are the titanium-niobium alloy (Ti-Nb) due to its excellent biocompatibility, and from the economic point of view, due to the production of Nb in Brazil on a large scale. For these specific applications the metal must have suitable properties such as zero toxicity, good mechanical properties (elastic modulus close to that of human bone) and corrosion resistance. Another important factor to be considered is the quick recovery of the patient, which is achieved by reducing the osseointegration time between the metal implant and bone, i.e. the surface that will be in contact with the bone must be bioactive to induce growth cells. There are several methods to increase the bioactivity of Ti in way to decrease the recovery of the patient. These surface treatments result in surfaces morphologies, different roughness and mechanical properties. This study aimed to modify the surface of Ti- Nb alloy with the intention of making it bioactive using the anodic oxidation (OA) technique, which was performed using phosphoric acid 1 mol / L, under potentiostatic mode (250V / 60s). It was evaluated the morphology and chemical elements present on the anodic film (SEM), the crystalline structure (XRD and Raman spectroscopy), mechanical (instrumented indentation) and tribological properties (analysis of the wear rate and friction coefficient) and the surface bioactivity in vitro (SBF). The oxidized surface presented rough and porous morphology, enriched with P and without great differences with increasing Nb content. It was found that the Ti-Nb alloys exhibited higher hardness and lower elastic modulus when compared to commercially pure Ti. Concerning the tribological tests, no significant differences were observed in the friction coefficient of the various surfaces studied and it was found that the wear rate was lower for the alloy with 10% Nb compared with 20% of Nb. Besides the low wear rate this alloy was more bioactive in SBF solution than the alloy containing 20% Nb.84 f. : il., algumas color, gráfs., tabs.application/pdfDisponível em formato digitalEngenharia mecânicaDesgaste mecanicoTitanioElasticidadePropriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médicainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - D - HEBERT HIROSHI SATO.pdfapplication/pdf6615996https://acervodigital.ufpr.br/bitstream/1884/54472/1/R%20-%20D%20-%20HEBERT%20HIROSHI%20SATO.pdfb1a68ae43c05f84287450293f4d0bf53MD51open access1884/544722024-07-25 16:17:18.647open accessoai:acervodigital.ufpr.br:1884/54472Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082024-07-25T19:17:18Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
title Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
spellingShingle Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
Sato, Hebert Hiroshi
Engenharia mecânica
Desgaste mecanico
Titanio
Elasticidade
title_short Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
title_full Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
title_fullStr Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
title_full_unstemmed Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
title_sort Propriedades mecânicas e tribológicas das ligas de Ti-Nb anodizadas para aplicação médica
author Sato, Hebert Hiroshi
author_facet Sato, Hebert Hiroshi
author_role author
dc.contributor.other.pt_BR.fl_str_mv Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia Mecânica
dc.contributor.advisor1.fl_str_mv Kuromoto, Neide Kazue, 1954-
dc.contributor.author.fl_str_mv Sato, Hebert Hiroshi
contributor_str_mv Kuromoto, Neide Kazue, 1954-
dc.subject.por.fl_str_mv Engenharia mecânica
Desgaste mecanico
Titanio
Elasticidade
topic Engenharia mecânica
Desgaste mecanico
Titanio
Elasticidade
description Orientadora: Profª. Drª. Neide Kazue Kuromoto
publishDate 2015
dc.date.issued.fl_str_mv 2015
dc.date.accessioned.fl_str_mv 2024-07-25T19:17:18Z
dc.date.available.fl_str_mv 2024-07-25T19:17:18Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/54472
url https://hdl.handle.net/1884/54472
dc.language.iso.fl_str_mv por
language por
dc.relation.pt_BR.fl_str_mv Disponível em formato digital
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 84 f. : il., algumas color, gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/54472/1/R%20-%20D%20-%20HEBERT%20HIROSHI%20SATO.pdf
bitstream.checksum.fl_str_mv b1a68ae43c05f84287450293f4d0bf53
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1813898670318288896

Registros relacionados