Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos

Detalhes bibliográficos
Autor(a) principal: Pinto, Sabrina Requião, 1992-
Data de Publicação: 2019
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/60741
Resumo: Orientador: Prof. Dr. Ronaldo Alves de Medeiros-Junior
id UFPR_e16fee67d22cba9a8fd79f66224920fe
oai_identifier_str oai:acervodigital.ufpr.br:1884/60741
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Pinto, Sabrina Requião, 1992-Luz, Caroline Angulski daUniversidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia CivilMedeiros Junior, Ronaldo Alves de, 1988-2022-06-15T12:55:31Z2022-06-15T12:55:31Z2019https://hdl.handle.net/1884/60741Orientador: Prof. Dr. Ronaldo Alves de Medeiros-JuniorCoorientadora: Profa. Dra. Caroline Angulski da LuzDissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia de Construção Civil. Defesa : Curitiba, 18/03/2019Inclui referências: p.179-195Resumo: Um considerável esforço tem sido realizado pela indústria de cimento para reduzir os impactos ambientais associados à sua produção. Entretanto, o cimento Portland ainda se mantém como um material com elevada taxa de emissão de CO2. De forma paralela, houve o surgimento de um panorama de incentivo ao desenvolvimento tecnológico de alternativas mais sustentáveis ao cimento Portland, como o cimento supersulfatado. O cimento supersulfatado (CSS) é um aglomerante composto por alto teor de escória de alto forno (?75%), sulfato de cálcio (5-20%) e um ativador alcalino (?5%). Devido ao elevado consumo de subprodutos industriais, o CSS tem potencialidade de se apresentar como uma alternativa mais sustentável na produção de concretos. Entretanto, ainda há poucos estudos dedicados a essa tecnologia, principalmente nacionalmente. Diante disso, a presente pesquisa busca contribuir com o conhecimento sobre o CSS, sobretudo, em relação à durabilidade. Para isso, avaliou-se a durabilidade de compósitos cimentícios com CSS frente ao ataque por sulfatos, carbonatação e penetração de íons cloreto. Como comparativo, também foram empregados no estudo os cimentos Portland CP V ARI e CP III RS, e diferentes relações água/cimento (0,40; 0,46 e 0,52). Para a realização dos ensaios foram confeccionadas amostras de concreto, argamassa e pasta. Também foram realizados ensaios de resistência à compressão, velocidade de propagação de pulso ultrassônico e absorção de água por imersão e por capilaridade. Para uma exploração mais ampla sobre a microestrutura das matrizes cimentícias, foram utilizadas técnicas de microscopia eletrônica de varredura (MEV) e difração de raios X (DRX). Os resultados mostraram que o cimento supersulfatado apresentou penetrabilidade à íons cloreto muito baixa e excelente resistênica ao ataque por sulfato de sódio, demonstrada pela estabilidade dimensional e de massa. Por outro lado, em relação ao sulfato de magnésio, mostrou-se menos resistente quando comparado com os cimentos Portland. Apesar de apresentar menores resistências à carbonatação e à compressão, para uma relação a/c igual a 0,40 o CSS atendeu os requisitos para uso estrutural e de desempenho, quanto à vida útil. Portanto, isso fornece um novo âmbito de estudo sobre a durabilidade do CSS e para o desenvolvimento de concretos adequados com CSS. Palavras-chave: Cimento Supersulfatado. Cimento Portland. Durabilidade. Ataque por sulfatos. Carbonatação. Cloretos. Cimento sustentável.Abstract: A considerable effort has been made by the cement industry to reduce the environmental impacts associated with its production. Although, the Portland cement is still regarded a significant contributor to global CO2 emissions. In this respect, there is a motivating outlook to technological development of eco-friendly alternatives for the conventional Portland cement, such as supersulfated cement. Supersulfated cement (SSC) is a binder comprised of blast furnace slag (?75%), calcium sulfate (5-20%) and an alkaline activator (?5%). Despite the high consumption of industrial by-products, SSC is a potential "low-CO2" cement to use in concrete production. However, relatively few studies have focused on this technology, mainly nationally. In view of this, the aim of the present research is to contribute with knowledge about SSC, principally the durability performance. For this purpose, the durability of SSC cementitious composites was evaluated against sulfate attack, carbonation and chloride ingress. A comparative analysis was designed with Portland cement CP V ARI and CP III RS and different water/cement ratios (0.40, 0.46 and 0.52). The tests were conducted with concrete, mortar and paste samples. Moreover, compressive strength, ultrasonic pulse velocity and water absorption by immersion were also investigated. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used for a more extensive investigation of the microstructure of the cementitious matrix. The results revealed that the supersulfated cement has a very low chloride ion penetrability and excellent performance against sodium sulfate attack due to dimensional and mass stability. Although in the magnesium sulfate SSC was poor resistant than Portland cements. A clear increase in carbonation and decrease in compressive strength was observed in SSC concrete. In spite of this, an adequate SCC concrete, from a strength class and service life point of view, was achieved with a water to cement ratio of 0.40. Therefore, this provides new scope for durability investigation of SSC, and for developing appropriate SSC concrete. Keywords: Supersulfated cement. Portland cement. Durability. Sulfate attack. Carbonation. Chloride. Sustainable cement.198 p. : il. (algumas color.).application/pdfCimento portlandEngenharia CivilCarbonatosConcreto - CorrosãoDurabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretosinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - D - SABRINA REQUIAO PINTO.pdfapplication/pdf16400621https://acervodigital.ufpr.br/bitstream/1884/60741/1/R%20-%20D%20-%20SABRINA%20REQUIAO%20PINTO.pdf7cbd7564c015b2bd6ac07d4d24881009MD51open access1884/607412022-06-15 09:55:31.295open accessoai:acervodigital.ufpr.br:1884/60741Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082022-06-15T12:55:31Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
title Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
spellingShingle Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
Pinto, Sabrina Requião, 1992-
Cimento portland
Engenharia Civil
Carbonatos
Concreto - Corrosão
title_short Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
title_full Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
title_fullStr Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
title_full_unstemmed Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
title_sort Durabilidade de compósitos com cimento supersulfatado e de cimentos portland : ataque por sulfatos, carbonatação e penetração de cloretos
author Pinto, Sabrina Requião, 1992-
author_facet Pinto, Sabrina Requião, 1992-
author_role author
dc.contributor.other.pt_BR.fl_str_mv Luz, Caroline Angulski da
Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia Civil
dc.contributor.author.fl_str_mv Pinto, Sabrina Requião, 1992-
dc.contributor.advisor1.fl_str_mv Medeiros Junior, Ronaldo Alves de, 1988-
contributor_str_mv Medeiros Junior, Ronaldo Alves de, 1988-
dc.subject.por.fl_str_mv Cimento portland
Engenharia Civil
Carbonatos
Concreto - Corrosão
topic Cimento portland
Engenharia Civil
Carbonatos
Concreto - Corrosão
description Orientador: Prof. Dr. Ronaldo Alves de Medeiros-Junior
publishDate 2019
dc.date.issued.fl_str_mv 2019
dc.date.accessioned.fl_str_mv 2022-06-15T12:55:31Z
dc.date.available.fl_str_mv 2022-06-15T12:55:31Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/60741
url https://hdl.handle.net/1884/60741
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 198 p. : il. (algumas color.).
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/60741/1/R%20-%20D%20-%20SABRINA%20REQUIAO%20PINTO.pdf
bitstream.checksum.fl_str_mv 7cbd7564c015b2bd6ac07d4d24881009
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1801860552380645376

Registros relacionados