Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural

Detalhes bibliográficos
Autor(a) principal: Seniski, Anelize, 1989-
Data de Publicação: 2021
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/71601
Resumo: Orientador: Prof. Dr. Kleber Franke Portella
id UFPR_f8cdca50636c2cab82f7c41c2e464c49
oai_identifier_str oai:acervodigital.ufpr.br:1884/71601
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Seniski, Anelize, 1989-Bragança, Mariana D'Orey Gaivão Portella, 1986-Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia e Ciência dos Materiais - PIPEPortella, Kleber Franke2021-09-09T14:38:34Z2021-09-09T14:38:34Z2021https://hdl.handle.net/1884/71601Orientador: Prof. Dr. Kleber Franke PortellaCoorientadora: Prof.a. Dr.a Mariana d’Orey Gaivão Portella BragançaTese (doutorado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia e Ciência dos Materiais – PIPE. Defesa : Curitiba, 08/03/2021Inclui referências: p. 117-132Resumo: Ligas de aço carbono possuem uma vasta gama de utilização, pois apresentam baixo custo de produção. Porém, essas ligas são suscetíveis a corrosão, quando expostas a atmosfera. O processo corrosivo depende de uma série de fatores, como o tempo de superfície úmida, o pH do eletrólito, a temperatura ambiente e demais condições de exposição, os poluentes atmosféricos, entre outros. Uma estratégia utilizada no controle da corrosão é a utilização de revestimentos orgânicos, pois funcionam como uma barreira entre o metal e o meio. As propriedades de barreira (proteção passiva) também funcionam inibindo o deslocamento de íons agressivos até a superfície metálica. Durante a vida útil do sistema, no entanto, essa propriedade pode ser alterada, levando a falhas no revestimento, consequentemente expondo o substrato metálico e iniciando o processo corrosivo. A fim de estender a vida útil desses materiais e melhorara a eficiência de proteção, vem sendo estudados revestimentos que permitem a proteção ativa de superfícies metálicas. São adicionados a esses revestimentos, nano e microrreservatórios que possuem, intercalados em suas lamelas, um inibidor de corrosão. Os hidróxidos duplos lamelares (LDH) são denominados compostos do tipo hidrotalcita, que são permutadores de íons. Estruturalmente, consistem em lamelas de hidróxido de metais misturados, separadas por ânions e moléculas de água. Com a exposição a meios agressivos, os LDHs tendem a trocar íons com o meio, capturando o íon agressivo e liberando o inibidor de corrosão intercalado nas lamelas. Assim, essa pesquisa teve como objetivo investigar o multiestressamento de origem ambiental, natural e artificial, de revestimentos epoxídicos, contendo LDH intercalado com inibidor de corrosão nitrito. Foram investigados LDH do tipo Zn-Al-NO2. Quando livre em solução proporcionou a formação de um óxido compacto e insolúvel na superfície do aço carbono, o que não ocorreu na amostra de referência, que apresentou um óxido solúvel, que ocasionou na perda de massa do metal. Os LDH foram, então, adicionados em revestimentos epoxídicos na proporção de 5% (m/m). Esses revestimentos foram expostos em solução de NaCl, com diferentes espessuras, e avaliados pela técnica de EIS, quanto as suas propriedades de barreira. Foram expostas, também, placas de aço carbono revestidas com resina epóxi e resina epóxi com LDH de Zn-Al-NO2 em câmara de nevoa salina, sulfato e weather O-meter, para avaliar o comportamento desses materiais em campo e para adicionar os dados em um modelo de rede neural artificial (ANN). As placas, também, foram expostas em cinco localidades no Pará e no Maranhão, obtendo-se dados para alimentar a ANN, juntamente com os parâmetros meteorológicos obtidos para cada localidade. Pela análise dos resultados obtidos pela técnica de EIS, (laboratório e campo) constatouse que a adição de LDH no revestimento aumentou a proteção ativa do sistema de pintura. O resultado do modelo de ANN, mostrou que a adição de LDH em revestimento epoxídico foi viável e que o LDH proporcionou um aumento da vida útil de 1,1 vez, quando comparado com a amostra de referência, desses materiais em campo. Palavras-chave: Proteção Contra a Corrosão. Aço Carbono 1010. Espectroscopia de Impedância Eletroquímica. Hidróxidos Duplos Lamelares. Nitrito.Abstract: Carbon steel alloys have a wide range of use, because they present a low production cost. However, these alloys are corrosion susceptible when exposed to the atmosphere. The corrosion process depends on a series of factors such as time of wet surface, electrolyte pH, temperature, exposure condition, atmospheric pollutants, among others. An utilized strategy on the corrosion control is the application of organic coatings, because they work as a barrier between the metal surface and the environment. The barrier properties (passive protection) also limit the reaching of aggressive ions until to the metallic surface. However, during lifetime of these materials, their properties can be altered, leading to coating failure, consequently exposing the metallic substrate and starting the corrosion process. In order to extend the lifetime and improve the protection efficiency of these materials, coatings that allow the active protection to metallic surfaces have been studied. Nano and microcontainers that possess corrosion inhibitors intercalated between layers are added to this coating. The double layered hydroxides (LDH) are denominated hydrotalcite-like compounds and they are ions exchangers. Their structure consists in layers of mixed metal hydroxides, separated by anions and water molecules. In aggressive environments, the LDHs exchange ions with the media, capturing the aggressive ions and releasing the corrosion inhibitor. Thus, the present research has as objective investigation of natural, artificial and environmental multistressing of coating with and without LDH intercalated with nitrite corrosion inhibitors (Zn-Al-NO2). Were investigated LDH Zn-Al- NO2 like. The free LDH in solution provided the formation of a compact and insoluble oxide on carbon steel surface, which did not occur in the reference sample. In this case, a soluble oxide was found instead, leading to mass loss. The LDH were added to epoxy matrix in the proportion 5 wt%. This coating was exposed to a NaCl solution, with different coating thicknesses, and evaluated by the EIS technique, as for their barrier properties. Plates of coated carbon steel with epoxy resin and epoxy resin with LDH Zn-Al-NO2 were also exposed in salt spray, sulfate and weather o-meter chambers, to evaluate the behavior of these materials in conditions close to field conditions and to add data in an artificial neural network (ANN) model. The samples were also exposed in five locations on Pará and Maranhão and these data were also used to feed the ANN, together with the meteorological data, obtained for each location. The data obtained by EIS technique (laboratory and field) revealed that the addition of LDH to the coating increased the active protection of the painting system. The ANN results showed that the LDH addition to an epoxy coating was feasible and that the LDH provided a 1.1 time increase in the useful life of these materials in the field. Keywords: Corrosion Protection. 1010 Carbon Steel. Electrochemical Impedance. Spectroscopy. Layered Double Hydroxides. Nitrite.1 arquivo (132 p.) : il.application/pdfAço - CorrosãoEngenharia de Materiais e MetalurgiaNitritosHidroxidosInvestigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e naturalinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - T - ANELIZE SENISKI SILVA.pdfapplication/pdf11158900https://acervodigital.ufpr.br/bitstream/1884/71601/1/R%20-%20T%20-%20ANELIZE%20SENISKI%20SILVA.pdf0d8cb355aecd3d9de4aa7f32994a58bbMD51open access1884/716012021-09-09 11:38:34.614open accessoai:acervodigital.ufpr.br:1884/71601Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082021-09-09T14:38:34Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
title Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
spellingShingle Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
Seniski, Anelize, 1989-
Aço - Corrosão
Engenharia de Materiais e Metalurgia
Nitritos
Hidroxidos
title_short Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
title_full Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
title_fullStr Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
title_full_unstemmed Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
title_sort Investigação de revestimentos à base de resina epóxi e hidróxidos duplos lamelares na prevenção à corrosão de aço carbono 1010 expostos a intemperismos artificial e natural
author Seniski, Anelize, 1989-
author_facet Seniski, Anelize, 1989-
author_role author
dc.contributor.other.pt_BR.fl_str_mv Bragança, Mariana D'Orey Gaivão Portella, 1986-
Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia e Ciência dos Materiais - PIPE
dc.contributor.author.fl_str_mv Seniski, Anelize, 1989-
dc.contributor.advisor1.fl_str_mv Portella, Kleber Franke
contributor_str_mv Portella, Kleber Franke
dc.subject.por.fl_str_mv Aço - Corrosão
Engenharia de Materiais e Metalurgia
Nitritos
Hidroxidos
topic Aço - Corrosão
Engenharia de Materiais e Metalurgia
Nitritos
Hidroxidos
description Orientador: Prof. Dr. Kleber Franke Portella
publishDate 2021
dc.date.accessioned.fl_str_mv 2021-09-09T14:38:34Z
dc.date.available.fl_str_mv 2021-09-09T14:38:34Z
dc.date.issued.fl_str_mv 2021
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/71601
url https://hdl.handle.net/1884/71601
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 1 arquivo (132 p.) : il.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/71601/1/R%20-%20T%20-%20ANELIZE%20SENISKI%20SILVA.pdf
bitstream.checksum.fl_str_mv 0d8cb355aecd3d9de4aa7f32994a58bb
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1813898867877347328

Registros relacionados