Caracterización de revestimientos de niobio formados por aspersión térmica a plasma sobre acero API 5l X65

• Autor(a) principal: Matos Mandujano, José Fidel
• Data de Publicação: 2012
• Outros Autores: Motta, Felipe Piccinini, Rieder, Ester Schmidt, Malfatti, Célia de Fraga
• Tipo de documento: Artigo
• Idioma: spa
• Título da fonte: Repositório Institucional da UFRGS
• Texto Completo: http://hdl.handle.net/10183/263095
• topic: Revestimentos anti-corrosivos; Nióbio; Aço; Niobium; Thermal spray; Corrosion resistance; Coating; Niobio; Aspersión térmica; Resistencia a la corrosión; Revestimiento

The morphology and electrochemical behavior of niobium coating obtained by thermal plasma spray process on a substrate of steel API 5L X65 was evaluated. The coating was obtained, using electrical current of 500 A, 15 g/min of powder and 2.0 L/min of argon gas. The preparation of the substrate surface was performed with preheating and abrasive blasting with alumina. After thermal spraying, the morphology of the coating was analyzed by scanning electron microscopy (SEM), while the surface roughness was evaluated by profilometry, hardness by Vickers microhardness test and adhesion by bending at 180 °. The corrosion resistance of the coating was evaluated from the polarization test in 3.5% NaVl solution. The results show that the coating presented cracking and lack of padding between the plates sprayed, relative high hardness and deficient adhesion to the substrate. However, the values of current density carried by the system compared to uncoated steel were reduced.