Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo
Autor(a) principal: | |
---|---|
Data de Publicação: | 2006 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/jspui/handle/123456789/12783 |
Resumo: | The metalceramic crowns are usually used in dentistry because they provide a resistant structure due to its metallic base and its aesthetics from the porcelain that recovers this structure. To manufacture these crowns, a series of stages should be accomplished in the prosthetic laboratories, and many variables can influence its success. Changes in these variables cause alterations in the metallic alloy and in the porcelain, so, as consequence, in the adhesion between them. The composition of the metal alloy can be modified by recasting alloys, a common practice in some prosthetic laboratories. The aim of this paper is to make a systematic study investigating metalceramic crowns as well as analyzing the effect of recasting Ni-Cr alloys. Another variable which can influence the mechanism of metalceramic union is the temperature used in firing porcelain procedure. Each porcelain has to be fired in a fixed temperature which is determined by the manufacturer and its change can cause serious damages. This research simulate situations that may occur on laboratory procedures and observe their consequences in the quality of the metalceramic union. A scanning eletron microscopy and an optic microscopy were accomplish to analyse the metal-ceramic interface. No differences have been found when remelting alloys were used. The microhardness were similar in Ni-Cr alloys casted once, twice and three times. A wettability test was accomplished using a software developed at the Laboratório de Processamento de Materiais por Plasma, on the Universidade Federal do Rio Grande do Norte. No differences were found in the contact angle between the solid surface (metallic substratum) and the tangencial plane to the liquid surface (opaque). To analyse if the temperature of porcelain firing procedure could influence the contact area between metal and porcelain, a variation in its final temperature was achieve from 980° to 955°C. Once more, no differences have been found |
id |
UFRN_05e0aaf3c7f59274b7fbe8f23122476d |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/12783 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Sá, Juliana Carvalhohttp://lattes.cnpq.br/7441669258580942Gomes, Uilame Umbelinohttp://lattes.cnpq.br/9858094266525225Guerra Neto, Custódio Leopoldino Britohttp://lattes.cnpq.br/5387010100082241Alves Júnior, Clodomiro2014-12-17T14:07:07Z2007-02-052014-12-17T14:07:07Z2006-03-14SÁ, Juliana Carvalho. Pilot study of the adhesion between Ni-Cr alloys and ceramics when prosthetic variables were accomplish. 2006. 103 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2006.https://repositorio.ufrn.br/jspui/handle/123456789/12783The metalceramic crowns are usually used in dentistry because they provide a resistant structure due to its metallic base and its aesthetics from the porcelain that recovers this structure. To manufacture these crowns, a series of stages should be accomplished in the prosthetic laboratories, and many variables can influence its success. Changes in these variables cause alterations in the metallic alloy and in the porcelain, so, as consequence, in the adhesion between them. The composition of the metal alloy can be modified by recasting alloys, a common practice in some prosthetic laboratories. The aim of this paper is to make a systematic study investigating metalceramic crowns as well as analyzing the effect of recasting Ni-Cr alloys. Another variable which can influence the mechanism of metalceramic union is the temperature used in firing porcelain procedure. Each porcelain has to be fired in a fixed temperature which is determined by the manufacturer and its change can cause serious damages. This research simulate situations that may occur on laboratory procedures and observe their consequences in the quality of the metalceramic union. A scanning eletron microscopy and an optic microscopy were accomplish to analyse the metal-ceramic interface. No differences have been found when remelting alloys were used. The microhardness were similar in Ni-Cr alloys casted once, twice and three times. A wettability test was accomplished using a software developed at the Laboratório de Processamento de Materiais por Plasma, on the Universidade Federal do Rio Grande do Norte. No differences were found in the contact angle between the solid surface (metallic substratum) and the tangencial plane to the liquid surface (opaque). To analyse if the temperature of porcelain firing procedure could influence the contact area between metal and porcelain, a variation in its final temperature was achieve from 980° to 955°C. Once more, no differences have been foundDurante o processo de confecção de coroas metalocerâmicas, é necessário que todas as informações passadas pelo fabricante sejam seguidas de forma criteriosa. Caso isto não ocorra, podem acontecer alterações tanto na liga metálica como na porcelana e como conseqüência, na adesão entre elas. Um fator que deve ser levado em consideração, consiste em analisar o efeito das refusões, uma vez que nos laboratórios protéticos torna-se comum a prática do reaproveitamento da ligas. Outro fator importante ao se preparar coroas metalocerâmicas é a temperatura de sinterização da porcelana. Sabe-se que a temperatura de sinterização pode influenciar na microestrutura, afetando diretamente suas propriedades físicas e mecânicas. Nesse trabalho, um estudo sistemático é realizado com o intuito de investigar a adesão metal-cerâmica em ligas Ni-Cr fundidas sob diferentes graus de reaproveitamento, assim como analisar o efeito de diferentes temperaturas de sinterização da porcelana. Procura-se aqui simular situações possíveis de ocorrer durante procedimentos laboratoriais protéticos e observar suas conseqüências na qualidade da adesão metal-cerâmica. Deste modo, coroas de ligas de níquel-cromo refundidas em 1 e 2 vezes, foram comparadas com aquelas apenas fundidas. Uma análise por microscopia óptica e eletrônica foi realizada para se avaliar o contato entre o metal e o opaco da porcelana. Além do mais, testes de microdureza sobre a liga metálica foram executados. Neste estudo, procurou-se também avaliar a molhabilidade da porcelana sobre ligas metálicas com diferentes estados de fusão, além de realizar uma sinterização da porcelana em diferentes temperaturas (980°C e 955°C). Como resultado encontrou-se que não houve diferença na interface entre as liga em diferentes estágios de fusão e a porcelana. Com relação à microdureza, os resultados indicaram que, na medida em que se aumenta o número de refusões, os valores de microdureza não se alteram e com relação à molhabilidade não houve diferença estatisticamente significativa entre as amostras. Também não se encontrou diferença entre as áreas de contato formadas entre a porcelana e a liga fundida quando a porcelana foi sinterizada em diferentes temperaturas, mostrando que uma diminuição de 25ºC na temperatura final de sinterização não interfere na união metal-cerâmicaCoordenação de Aperfeiçoamento de Pessoal de Nível Superiorapplication/pdfporUniversidade Federal do Rio Grande do NortePrograma de Pós-Graduação em Ciência e Engenharia de MateriaisUFRNBRProcessamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a partMetalocerâmicaRefusãoLigas odontológicasLigas MetálicasMetalceramic crownsRecasting alloysodontologic alloysCNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA INORGANICA::COMPOSTOS ORGANO-METALICOSEfeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromoPilot study of the adhesion between Ni-Cr alloys and ceramics when prosthetic variables were accomplishinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNORIGINALEfeitoVariáveisLaboratoriais_Sá_2006.pdfapplication/pdf1007525https://repositorio.ufrn.br/bitstream/123456789/12783/1/EfeitoVari%c3%a1veisLaboratoriais_S%c3%a1_2006.pdf74d4bf5035436a1b506b801dce77838fMD51TEXTJulianaCS.pdf.txtJulianaCS.pdf.txtExtracted texttext/plain149110https://repositorio.ufrn.br/bitstream/123456789/12783/6/JulianaCS.pdf.txt7a9aed8677f58ba1e7fc39b751adf119MD56EfeitoVariáveisLaboratoriais_Sá_2006.pdf.txtEfeitoVariáveisLaboratoriais_Sá_2006.pdf.txtExtracted texttext/plain149110https://repositorio.ufrn.br/bitstream/123456789/12783/8/EfeitoVari%c3%a1veisLaboratoriais_S%c3%a1_2006.pdf.txt7a9aed8677f58ba1e7fc39b751adf119MD58THUMBNAILJulianaCS.pdf.jpgJulianaCS.pdf.jpgIM Thumbnailimage/jpeg3195https://repositorio.ufrn.br/bitstream/123456789/12783/7/JulianaCS.pdf.jpg1ba380d2f5797e57efe620e972188ce2MD57EfeitoVariáveisLaboratoriais_Sá_2006.pdf.jpgEfeitoVariáveisLaboratoriais_Sá_2006.pdf.jpgIM Thumbnailimage/jpeg3195https://repositorio.ufrn.br/bitstream/123456789/12783/9/EfeitoVari%c3%a1veisLaboratoriais_S%c3%a1_2006.pdf.jpg1ba380d2f5797e57efe620e972188ce2MD59123456789/127832019-01-29 18:49:27.382oai:https://repositorio.ufrn.br:123456789/12783Repositório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2019-01-29T21:49:27Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.por.fl_str_mv |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
dc.title.alternative.eng.fl_str_mv |
Pilot study of the adhesion between Ni-Cr alloys and ceramics when prosthetic variables were accomplish |
title |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
spellingShingle |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo Sá, Juliana Carvalho Metalocerâmica Refusão Ligas odontológicas Ligas Metálicas Metalceramic crowns Recasting alloys odontologic alloys CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA INORGANICA::COMPOSTOS ORGANO-METALICOS |
title_short |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
title_full |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
title_fullStr |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
title_full_unstemmed |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
title_sort |
Efeito das variáveis laboratoriais protéticas na adesão da porcelana com ligas de níquel-cromo |
author |
Sá, Juliana Carvalho |
author_facet |
Sá, Juliana Carvalho |
author_role |
author |
dc.contributor.authorID.por.fl_str_mv |
|
dc.contributor.advisorID.por.fl_str_mv |
|
dc.contributor.advisorLattes.por.fl_str_mv |
http://lattes.cnpq.br/7441669258580942 |
dc.contributor.referees1.pt_BR.fl_str_mv |
Gomes, Uilame Umbelino |
dc.contributor.referees1ID.por.fl_str_mv |
|
dc.contributor.referees1Lattes.por.fl_str_mv |
http://lattes.cnpq.br/9858094266525225 |
dc.contributor.referees2.pt_BR.fl_str_mv |
Guerra Neto, Custódio Leopoldino Brito |
dc.contributor.referees2ID.por.fl_str_mv |
|
dc.contributor.referees2Lattes.por.fl_str_mv |
http://lattes.cnpq.br/5387010100082241 |
dc.contributor.author.fl_str_mv |
Sá, Juliana Carvalho |
dc.contributor.advisor1.fl_str_mv |
Alves Júnior, Clodomiro |
contributor_str_mv |
Alves Júnior, Clodomiro |
dc.subject.por.fl_str_mv |
Metalocerâmica Refusão Ligas odontológicas Ligas Metálicas |
topic |
Metalocerâmica Refusão Ligas odontológicas Ligas Metálicas Metalceramic crowns Recasting alloys odontologic alloys CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA INORGANICA::COMPOSTOS ORGANO-METALICOS |
dc.subject.eng.fl_str_mv |
Metalceramic crowns Recasting alloys odontologic alloys |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA INORGANICA::COMPOSTOS ORGANO-METALICOS |
description |
The metalceramic crowns are usually used in dentistry because they provide a resistant structure due to its metallic base and its aesthetics from the porcelain that recovers this structure. To manufacture these crowns, a series of stages should be accomplished in the prosthetic laboratories, and many variables can influence its success. Changes in these variables cause alterations in the metallic alloy and in the porcelain, so, as consequence, in the adhesion between them. The composition of the metal alloy can be modified by recasting alloys, a common practice in some prosthetic laboratories. The aim of this paper is to make a systematic study investigating metalceramic crowns as well as analyzing the effect of recasting Ni-Cr alloys. Another variable which can influence the mechanism of metalceramic union is the temperature used in firing porcelain procedure. Each porcelain has to be fired in a fixed temperature which is determined by the manufacturer and its change can cause serious damages. This research simulate situations that may occur on laboratory procedures and observe their consequences in the quality of the metalceramic union. A scanning eletron microscopy and an optic microscopy were accomplish to analyse the metal-ceramic interface. No differences have been found when remelting alloys were used. The microhardness were similar in Ni-Cr alloys casted once, twice and three times. A wettability test was accomplished using a software developed at the Laboratório de Processamento de Materiais por Plasma, on the Universidade Federal do Rio Grande do Norte. No differences were found in the contact angle between the solid surface (metallic substratum) and the tangencial plane to the liquid surface (opaque). To analyse if the temperature of porcelain firing procedure could influence the contact area between metal and porcelain, a variation in its final temperature was achieve from 980° to 955°C. Once more, no differences have been found |
publishDate |
2006 |
dc.date.issued.fl_str_mv |
2006-03-14 |
dc.date.available.fl_str_mv |
2007-02-05 2014-12-17T14:07:07Z |
dc.date.accessioned.fl_str_mv |
2014-12-17T14:07:07Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SÁ, Juliana Carvalho. Pilot study of the adhesion between Ni-Cr alloys and ceramics when prosthetic variables were accomplish. 2006. 103 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2006. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/jspui/handle/123456789/12783 |
identifier_str_mv |
SÁ, Juliana Carvalho. Pilot study of the adhesion between Ni-Cr alloys and ceramics when prosthetic variables were accomplish. 2006. 103 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2006. |
url |
https://repositorio.ufrn.br/jspui/handle/123456789/12783 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/12783/1/EfeitoVari%c3%a1veisLaboratoriais_S%c3%a1_2006.pdf https://repositorio.ufrn.br/bitstream/123456789/12783/6/JulianaCS.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12783/8/EfeitoVari%c3%a1veisLaboratoriais_S%c3%a1_2006.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12783/7/JulianaCS.pdf.jpg https://repositorio.ufrn.br/bitstream/123456789/12783/9/EfeitoVari%c3%a1veisLaboratoriais_S%c3%a1_2006.pdf.jpg |
bitstream.checksum.fl_str_mv |
74d4bf5035436a1b506b801dce77838f 7a9aed8677f58ba1e7fc39b751adf119 7a9aed8677f58ba1e7fc39b751adf119 1ba380d2f5797e57efe620e972188ce2 1ba380d2f5797e57efe620e972188ce2 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1802117565450813440 |