Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas
Autor(a) principal: | |
---|---|
Data de Publicação: | 2010 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/jspui/handle/123456789/12689 |
Resumo: | The continuous advances in ceramic systems for crowns and bridges infrastructure getting researchers and manufacturers looking for a material that has good mechanical properties and aesthetic. The purpose of this study was to verify in which composition and sintering temperature the ceramic system for infrastructure composed of alumina and zirconia would have the best mechanical properties. With this objective we made in UFRN laboratories 45 test bodies in the form of rectangular bars with the following dimensions: 30mm x 8mm x 3mm, where we separated by the sintering temperature: 1200°C, 1300ºC and 1400ºC, and by comp osition: 33% Zirconia + 67% Alumina; 50% Zirconia + 50% Alumina and 25% Zirconia + 75% Alumina, these test bodies were not infiltrated with glass. Also, were made nine test bodies by a technical from a laboratory with a commercial ceramic system: in the Ceram Zircônia (Vita - Zahnfabrik) with the following dimensions: 20mm x 10mm x 0.5mm, these test bodies following all recommendations of the manufacturer and were infiltrated with glass. Were realized optical and electronic microscopy analyses, hardness testing, resistance to bending in three points, porosity and bulk density. After analysis of the results we verified that with the increasing of sintering temperature, increased the value of resistance to bending, but with the same temperature there was no significant difference between the different compositions, samples made with the commercial ceramic that were infiltrated, presented a resistance to bending six times greater than the samples sintered to 1400°C and which have not been infiltra ted. There was no significant difference between the values of apparent porosity for the samples made in UFRN laboratories, but the samples of commercial ceramic obtained 0% in porosity apparent value. In tests of Rockwell Hardness there is an increase in the value of Hardness, with the increase of sintering temperature for the samples not infiltrated. Samples infiltrated showed similar values as the samples sintered in 1400°C. There was no significant difference between the values of apparent density among samples manufactured in UFRN laboratories and samples made with a commercial ceramic |
id |
UFRN_4525d037ac524b0161df1ec74f554ac4 |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/12689 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Silva, Cláudia Anglélica Melo dahttp://lattes.cnpq.br/3318871716111536Nascimento, Rubens Maribondo dohttp://lattes.cnpq.br/8671649752936793Barros, Joana Maria de Fariashttp://lattes.cnpq.br/1016070459137884Melo, Dulce Maria de Araújo2014-12-17T14:06:54Z2010-07-082014-12-17T14:06:54Z2010-03-29SILVA, Cláudia Anglélica Melo da. Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas. 2010. 84 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2010.https://repositorio.ufrn.br/jspui/handle/123456789/12689The continuous advances in ceramic systems for crowns and bridges infrastructure getting researchers and manufacturers looking for a material that has good mechanical properties and aesthetic. The purpose of this study was to verify in which composition and sintering temperature the ceramic system for infrastructure composed of alumina and zirconia would have the best mechanical properties. With this objective we made in UFRN laboratories 45 test bodies in the form of rectangular bars with the following dimensions: 30mm x 8mm x 3mm, where we separated by the sintering temperature: 1200°C, 1300ºC and 1400ºC, and by comp osition: 33% Zirconia + 67% Alumina; 50% Zirconia + 50% Alumina and 25% Zirconia + 75% Alumina, these test bodies were not infiltrated with glass. Also, were made nine test bodies by a technical from a laboratory with a commercial ceramic system: in the Ceram Zircônia (Vita - Zahnfabrik) with the following dimensions: 20mm x 10mm x 0.5mm, these test bodies following all recommendations of the manufacturer and were infiltrated with glass. Were realized optical and electronic microscopy analyses, hardness testing, resistance to bending in three points, porosity and bulk density. After analysis of the results we verified that with the increasing of sintering temperature, increased the value of resistance to bending, but with the same temperature there was no significant difference between the different compositions, samples made with the commercial ceramic that were infiltrated, presented a resistance to bending six times greater than the samples sintered to 1400°C and which have not been infiltra ted. There was no significant difference between the values of apparent porosity for the samples made in UFRN laboratories, but the samples of commercial ceramic obtained 0% in porosity apparent value. In tests of Rockwell Hardness there is an increase in the value of Hardness, with the increase of sintering temperature for the samples not infiltrated. Samples infiltrated showed similar values as the samples sintered in 1400°C. There was no significant difference between the values of apparent density among samples manufactured in UFRN laboratories and samples made with a commercial ceramicOs avanços constantes dos sistemas cerâmicos para infra-estruturas de coroas e pontes fazem com que os pesquisadores e fabricantes busquem um material que tenha boas propriedades mecânicas e estéticas. O intuito deste trabalho foi verificar em qual composição e temperatura de sinterização o sistema cerâmico a base de alumina e zircônia para infra-estrutura teria as melhores propriedades mecânicas. Com este objetivo confeccionamos nos laboratórios da UFRN 45 corpos-e-prova em forma de barras retangulares com as seguintes dimensões: 30mm x 8mm x 3mm, onde os separamos por temperatura de sinterização: 1200ºC, 1300ºC e 1400ºC; e por composição: 33% Zircônia + 67% Alumina; 50% Zircônia + 50% Alumina e 25% Zircônia + 75% Alumina, estes corpos-de-prova não foram infiltrados com vidro. Foram confeccionados ainda nove corpos- e-prova por um técnico de laboratório com um sistema cerâmico comercial o In Ceram Zircônia (Vita Zahnfabrik) com as seguintes dimensões: 20mm x 10mm x 0,5mm, estes corpos-de-prova seguiram todas as recomendações do fabricante e foram infiltrados com vidro. Foram realizadas análises por microscopia ótica e eletrônica, ensaios de dureza, de resistência á flexão em três pontos, porosidade e densidade aparente. Após a análise dos resultados verificamos que com o aumento da temperatura de sinterização, aumentamos o valor da resistência á flexão, sendo que dentro da mesma temperatura não houve diferença significante entre as diferentes composições, as amostras confeccionadas com a cerâmica comercial e que foram infiltradas apresentaram uma resistência á flexão seis vezes maior que as amostras sinterizadas á 1400ºC e que não foram infiltradas. Não houve diferença significante entre os valores da porosidade aparente para as amostras confeccionadas nos laboratórios da UFRN, já as amostras da cerâmica comercial obtiveram um valor de 0% de porosidade aparente. Nos ensaios de Dureza Rockwell verifica-se um aumento no valor da Dureza, com o aumento da temperatura de sinterização das amostras não infiltradas. As amostras infiltradas apresentaram valores similares aos das amostras sinterizadas á 1400ºC. Não houve diferença significante entre os valores de densidade aparente entre as amostras confeccionadas nos laboratórios da UFRN e as amostras confeccionadas com a cerâmica comercialapplication/pdfporUniversidade Federal do Rio Grande do NortePrograma de Pós-Graduação em Ciência e Engenharia de MateriaisUFRNBRProcessamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a partAluminaZircôniaCerâmicas OdontológicasAluminaZirconiaOdontological ceramicsCNPQ::ENGENHARIASEstruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixasinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNORIGINALEstruturasCerâmicasBase_Silva_2010.pdfapplication/pdf2577371https://repositorio.ufrn.br/bitstream/123456789/12689/1/EstruturasCer%c3%a2micasBase_Silva_2010.pdf741bbb91aaccd5dd4b233f1b8017a831MD51TEXTClaudiaAMS_DISSERT.pdf.txtClaudiaAMS_DISSERT.pdf.txtExtracted texttext/plain128139https://repositorio.ufrn.br/bitstream/123456789/12689/6/ClaudiaAMS_DISSERT.pdf.txt56e70b84eeba9fb49f1b8bea35536dbbMD56EstruturasCerâmicasBase_Silva_2010.pdf.txtEstruturasCerâmicasBase_Silva_2010.pdf.txtExtracted texttext/plain128139https://repositorio.ufrn.br/bitstream/123456789/12689/8/EstruturasCer%c3%a2micasBase_Silva_2010.pdf.txt56e70b84eeba9fb49f1b8bea35536dbbMD58THUMBNAILClaudiaAMS_DISSERT.pdf.jpgClaudiaAMS_DISSERT.pdf.jpgIM Thumbnailimage/jpeg4301https://repositorio.ufrn.br/bitstream/123456789/12689/7/ClaudiaAMS_DISSERT.pdf.jpgcc9768f2930ec7380e21f8de76dc6820MD57EstruturasCerâmicasBase_Silva_2010.pdf.jpgEstruturasCerâmicasBase_Silva_2010.pdf.jpgIM Thumbnailimage/jpeg4301https://repositorio.ufrn.br/bitstream/123456789/12689/9/EstruturasCer%c3%a2micasBase_Silva_2010.pdf.jpgcc9768f2930ec7380e21f8de76dc6820MD59123456789/126892019-01-29 17:59:38.698oai:https://repositorio.ufrn.br:123456789/12689Repositório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2019-01-29T20:59:38Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.por.fl_str_mv |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
title |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
spellingShingle |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas Silva, Cláudia Anglélica Melo da Alumina Zircônia Cerâmicas Odontológicas Alumina Zirconia Odontological ceramics CNPQ::ENGENHARIAS |
title_short |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
title_full |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
title_fullStr |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
title_full_unstemmed |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
title_sort |
Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas |
author |
Silva, Cláudia Anglélica Melo da |
author_facet |
Silva, Cláudia Anglélica Melo da |
author_role |
author |
dc.contributor.authorID.por.fl_str_mv |
|
dc.contributor.advisorID.por.fl_str_mv |
|
dc.contributor.advisorLattes.por.fl_str_mv |
http://lattes.cnpq.br/3318871716111536 |
dc.contributor.advisor-co1ID.por.fl_str_mv |
|
dc.contributor.referees1.pt_BR.fl_str_mv |
Barros, Joana Maria de Farias |
dc.contributor.referees1ID.por.fl_str_mv |
|
dc.contributor.referees1Lattes.por.fl_str_mv |
http://lattes.cnpq.br/1016070459137884 |
dc.contributor.author.fl_str_mv |
Silva, Cláudia Anglélica Melo da |
dc.contributor.advisor-co1.fl_str_mv |
Nascimento, Rubens Maribondo do |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://lattes.cnpq.br/8671649752936793 |
dc.contributor.advisor1.fl_str_mv |
Melo, Dulce Maria de Araújo |
contributor_str_mv |
Nascimento, Rubens Maribondo do Melo, Dulce Maria de Araújo |
dc.subject.por.fl_str_mv |
Alumina Zircônia Cerâmicas Odontológicas |
topic |
Alumina Zircônia Cerâmicas Odontológicas Alumina Zirconia Odontological ceramics CNPQ::ENGENHARIAS |
dc.subject.eng.fl_str_mv |
Alumina Zirconia Odontological ceramics |
dc.subject.cnpq.fl_str_mv |
CNPQ::ENGENHARIAS |
description |
The continuous advances in ceramic systems for crowns and bridges infrastructure getting researchers and manufacturers looking for a material that has good mechanical properties and aesthetic. The purpose of this study was to verify in which composition and sintering temperature the ceramic system for infrastructure composed of alumina and zirconia would have the best mechanical properties. With this objective we made in UFRN laboratories 45 test bodies in the form of rectangular bars with the following dimensions: 30mm x 8mm x 3mm, where we separated by the sintering temperature: 1200°C, 1300ºC and 1400ºC, and by comp osition: 33% Zirconia + 67% Alumina; 50% Zirconia + 50% Alumina and 25% Zirconia + 75% Alumina, these test bodies were not infiltrated with glass. Also, were made nine test bodies by a technical from a laboratory with a commercial ceramic system: in the Ceram Zircônia (Vita - Zahnfabrik) with the following dimensions: 20mm x 10mm x 0.5mm, these test bodies following all recommendations of the manufacturer and were infiltrated with glass. Were realized optical and electronic microscopy analyses, hardness testing, resistance to bending in three points, porosity and bulk density. After analysis of the results we verified that with the increasing of sintering temperature, increased the value of resistance to bending, but with the same temperature there was no significant difference between the different compositions, samples made with the commercial ceramic that were infiltrated, presented a resistance to bending six times greater than the samples sintered to 1400°C and which have not been infiltra ted. There was no significant difference between the values of apparent porosity for the samples made in UFRN laboratories, but the samples of commercial ceramic obtained 0% in porosity apparent value. In tests of Rockwell Hardness there is an increase in the value of Hardness, with the increase of sintering temperature for the samples not infiltrated. Samples infiltrated showed similar values as the samples sintered in 1400°C. There was no significant difference between the values of apparent density among samples manufactured in UFRN laboratories and samples made with a commercial ceramic |
publishDate |
2010 |
dc.date.available.fl_str_mv |
2010-07-08 2014-12-17T14:06:54Z |
dc.date.issued.fl_str_mv |
2010-03-29 |
dc.date.accessioned.fl_str_mv |
2014-12-17T14:06:54Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SILVA, Cláudia Anglélica Melo da. Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas. 2010. 84 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2010. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/jspui/handle/123456789/12689 |
identifier_str_mv |
SILVA, Cláudia Anglélica Melo da. Estruturas cerâmicas a base de zircônia e alumina utilizadas na confecção de infra - estruturas para coroas e pontes fixas. 2010. 84 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2010. |
url |
https://repositorio.ufrn.br/jspui/handle/123456789/12689 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/12689/1/EstruturasCer%c3%a2micasBase_Silva_2010.pdf https://repositorio.ufrn.br/bitstream/123456789/12689/6/ClaudiaAMS_DISSERT.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12689/8/EstruturasCer%c3%a2micasBase_Silva_2010.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12689/7/ClaudiaAMS_DISSERT.pdf.jpg https://repositorio.ufrn.br/bitstream/123456789/12689/9/EstruturasCer%c3%a2micasBase_Silva_2010.pdf.jpg |
bitstream.checksum.fl_str_mv |
741bbb91aaccd5dd4b233f1b8017a831 56e70b84eeba9fb49f1b8bea35536dbb 56e70b84eeba9fb49f1b8bea35536dbb cc9768f2930ec7380e21f8de76dc6820 cc9768f2930ec7380e21f8de76dc6820 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1814833073968119808 |