Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo
Autor(a) principal: | |
---|---|
Data de Publicação: | 2007 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/jspui/handle/123456789/12862 |
Resumo: | The development of activities in the oil and gas sector has been promoting the search for materials more adequate to oilwell cementing operation. In the state of Rio Grande do Norte, the cement sheath integrity tend to fail during steam injection operation which is necessary to increase oil recovery in reservoir with heavy oil. Geopolymer is a material that can be used as alternative cement. It has been used in manufacturing of fireproof compounds, construction of structures and for controlling of toxic or radioactive waste. Latex is widely used in Portland cement slurries and its characteristic is the increase of compressive strength of cement slurries. Sodium Tetraborate is used in dental cement as a retarder. The addition of this additive aim to improve the geopolymeric slurries properties for oilwell cementing operation. The slurries studied are constituted of metakaolinite, potassium silicate, potassium hydroxide, non-ionic latex and sodium tetraborate. The properties evaluated were: viscosity, compressive strength, thickening time, density, fluid loss control, at ambient temperature (27 ºC) and at cement specification temperature. The tests were carried out in accordance to the practical recommendations of the norm API RP 10B. The slurries with sodium tetraborate did not change either their rheological properties or their mechanical properties or their density in relation the slurry with no additive. The increase of the concentration of sodium tetraborate increased the water loss at both temperatures studied. The best result obtained with the addition of sodium tetraborate was thickening time, which was tripled. The addition of latex in the slurries studied diminished their rheological properties and their density, however, at ambient temperature, it increased their compressive strength and it functioned as an accelerator. The increase of latex concentration increased the presence of water and then diminished the density of the slurries and increased the water loss. From the results obtained, it was concluded that sodium tetraborate and non-ionic latex are promising additives for geopolymer slurries to be used in oilwell cementing operation |
id |
UFRN_5be8858296709a81f75d0ff6860b8880 |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/12862 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Pinto, Erica Natasche de Medeiros Gurgelhttp://lattes.cnpq.br/6531020251306710http://lattes.cnpq.br/3318871716111536Martinelli, Antônio Eduardohttp://lattes.cnpq.br/0022988322449627Melo, Marcus Antônio de Freitashttp://lattes.cnpq.br/5840621182000517Marinho, érika Pintohttp://lattes.cnpq.br/1192938961586608Melo, Dulce Maria de Araújo2014-12-17T14:07:20Z2007-11-192014-12-17T14:07:20Z2007-04-23PINTO, Erica Natasche de Medeiros Gurgel. Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo. 2007. 96 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2007.https://repositorio.ufrn.br/jspui/handle/123456789/12862The development of activities in the oil and gas sector has been promoting the search for materials more adequate to oilwell cementing operation. In the state of Rio Grande do Norte, the cement sheath integrity tend to fail during steam injection operation which is necessary to increase oil recovery in reservoir with heavy oil. Geopolymer is a material that can be used as alternative cement. It has been used in manufacturing of fireproof compounds, construction of structures and for controlling of toxic or radioactive waste. Latex is widely used in Portland cement slurries and its characteristic is the increase of compressive strength of cement slurries. Sodium Tetraborate is used in dental cement as a retarder. The addition of this additive aim to improve the geopolymeric slurries properties for oilwell cementing operation. The slurries studied are constituted of metakaolinite, potassium silicate, potassium hydroxide, non-ionic latex and sodium tetraborate. The properties evaluated were: viscosity, compressive strength, thickening time, density, fluid loss control, at ambient temperature (27 ºC) and at cement specification temperature. The tests were carried out in accordance to the practical recommendations of the norm API RP 10B. The slurries with sodium tetraborate did not change either their rheological properties or their mechanical properties or their density in relation the slurry with no additive. The increase of the concentration of sodium tetraborate increased the water loss at both temperatures studied. The best result obtained with the addition of sodium tetraborate was thickening time, which was tripled. The addition of latex in the slurries studied diminished their rheological properties and their density, however, at ambient temperature, it increased their compressive strength and it functioned as an accelerator. The increase of latex concentration increased the presence of water and then diminished the density of the slurries and increased the water loss. From the results obtained, it was concluded that sodium tetraborate and non-ionic latex are promising additives for geopolymer slurries to be used in oilwell cementing operationO desenvolvimento das atividades do setor petróleo e gás tem promovido a busca de materiais mais adequados para cimentação de poços de petróleo. No estado do RN, a integridade da bainha cimentante tende a ser prejudicada durante a injeção de vapor, procedimento necessário para aumentar a recuperação do petróleo em reservatórios com óleo de alta viscosidade. O geopolímero é um material que pode ser utilizado como cimento alternativo, uma vez que vem sendo empregado na produção de componentes resistentes ao fogo, na construção de estruturas, e para o controle de resíduos tóxicos ou radioativos. O látex é extensamente usado em pastas de cimento Portland e tem como característica o aumento significativo da resistência à compressão das pastas. O tetraborato de sódio é usado em cimentos odontológicos como retardador de pega em resinas. A adição deste aditivo tem a finalidade de melhorar a propriedades das pastas geopoliméricas para cimentação de poços de petróleo. As pastas estudadas são constituídas de metacaulim, silicato de potássio, hidróxido de potássio, látex não iônico e tetraborato de sódio. As propriedades avaliadas foram: viscosidade, resistência mecânica, tempo de espessamento, densidade e controle de filtrado, na temperatura ambiente (27°C) e de especificação de cimento. Os testes foram realizados seguindo as recomendações práticas da norma API RP 10B. As pastas aditivadas com tetraborato de sódio não modificaram as propriedades reológicas em relação a pasta sem aditivo, assim como não modificaram as propriedades mecânicas e a densidade das pastas. O aumento da concentração de tetraborato de sódio aumentou o volume de filtrado das pastas nas duas temperaturas estudadas. A propriedade que o tetraborato de sódio obteve o melhor desempenho foi em relação ao tempo de pega, onde a adição do aditivo conseguiu triplicar o tempo de espessamento das pastas. Com relação às pastas aditivadas com látex observou-se que a adição desse aditivo diminuiu as propriedades reológicas e a densidade do sistema. Na temperatura ambiente, o aditivo funcionou como acelerador de pega e aumentou a resistência mecânica das pastas. A presença de água reduziu a densidade das pastas e aumentou o volume de filtrado a medida que aumentou a concentração do aditivo. A partir dos resultados obtidos concluiu-se que o tetraborato de sódio e o látex não iônico são aditivos promissores para pastas geopoliméricas para cimentação de poços de petróleoapplication/pdfporUniversidade Federal do Rio Grande do NortePrograma de Pós-Graduação em Ciência e Engenharia de MateriaisUFRNBRProcessamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a partGeopolímeroLátex não-iônicoTetraborato de sódioCimentação de poços de petróleoGeopolymerNon-ionic LatexSodium TetraborateOilwell Cementing OperationCNPQ::CIENCIAS EXATAS E DA TERRAAditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNORIGINALAditivacaoPastasGeopoliméricas_Pinto_2007.pdfapplication/pdf6433422https://repositorio.ufrn.br/bitstream/123456789/12862/1/AditivacaoPastasGeopolim%c3%a9ricas_Pinto_2007.pdfbf4255596957765009ee816c080d6b9aMD51TEXTEricaNMGP.pdf.txtEricaNMGP.pdf.txtExtracted texttext/plain131389https://repositorio.ufrn.br/bitstream/123456789/12862/6/EricaNMGP.pdf.txt48a428211d3c515652fb05c76c986ec6MD56AditivacaoPastasGeopoliméricas_Pinto_2007.pdf.txtAditivacaoPastasGeopoliméricas_Pinto_2007.pdf.txtExtracted texttext/plain131389https://repositorio.ufrn.br/bitstream/123456789/12862/8/AditivacaoPastasGeopolim%c3%a9ricas_Pinto_2007.pdf.txt48a428211d3c515652fb05c76c986ec6MD58THUMBNAILEricaNMGP.pdf.jpgEricaNMGP.pdf.jpgIM Thumbnailimage/jpeg2819https://repositorio.ufrn.br/bitstream/123456789/12862/7/EricaNMGP.pdf.jpg684582a6b227c096e7b1deab9218bea0MD57AditivacaoPastasGeopoliméricas_Pinto_2007.pdf.jpgAditivacaoPastasGeopoliméricas_Pinto_2007.pdf.jpgIM Thumbnailimage/jpeg2827https://repositorio.ufrn.br/bitstream/123456789/12862/9/AditivacaoPastasGeopolim%c3%a9ricas_Pinto_2007.pdf.jpga29fc1b8769c9fc4c87ff8a54fc0dd6aMD59123456789/128622019-01-29 18:52:29.559oai:https://repositorio.ufrn.br:123456789/12862Repositório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2019-01-29T21:52:29Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.por.fl_str_mv |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
title |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
spellingShingle |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo Pinto, Erica Natasche de Medeiros Gurgel Geopolímero Látex não-iônico Tetraborato de sódio Cimentação de poços de petróleo Geopolymer Non-ionic Latex Sodium Tetraborate Oilwell Cementing Operation CNPQ::CIENCIAS EXATAS E DA TERRA |
title_short |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
title_full |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
title_fullStr |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
title_full_unstemmed |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
title_sort |
Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo |
author |
Pinto, Erica Natasche de Medeiros Gurgel |
author_facet |
Pinto, Erica Natasche de Medeiros Gurgel |
author_role |
author |
dc.contributor.authorID.por.fl_str_mv |
|
dc.contributor.authorLattes.por.fl_str_mv |
http://lattes.cnpq.br/6531020251306710 |
dc.contributor.advisorID.por.fl_str_mv |
|
dc.contributor.advisorLattes.por.fl_str_mv |
http://lattes.cnpq.br/3318871716111536 |
dc.contributor.advisor-co1ID.por.fl_str_mv |
|
dc.contributor.referees1.pt_BR.fl_str_mv |
Melo, Marcus Antônio de Freitas |
dc.contributor.referees1ID.por.fl_str_mv |
|
dc.contributor.referees1Lattes.por.fl_str_mv |
http://lattes.cnpq.br/5840621182000517 |
dc.contributor.referees2.pt_BR.fl_str_mv |
Marinho, érika Pinto |
dc.contributor.referees2ID.por.fl_str_mv |
|
dc.contributor.referees2Lattes.por.fl_str_mv |
http://lattes.cnpq.br/1192938961586608 |
dc.contributor.author.fl_str_mv |
Pinto, Erica Natasche de Medeiros Gurgel |
dc.contributor.advisor-co1.fl_str_mv |
Martinelli, Antônio Eduardo |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://lattes.cnpq.br/0022988322449627 |
dc.contributor.advisor1.fl_str_mv |
Melo, Dulce Maria de Araújo |
contributor_str_mv |
Martinelli, Antônio Eduardo Melo, Dulce Maria de Araújo |
dc.subject.por.fl_str_mv |
Geopolímero Látex não-iônico Tetraborato de sódio Cimentação de poços de petróleo |
topic |
Geopolímero Látex não-iônico Tetraborato de sódio Cimentação de poços de petróleo Geopolymer Non-ionic Latex Sodium Tetraborate Oilwell Cementing Operation CNPQ::CIENCIAS EXATAS E DA TERRA |
dc.subject.eng.fl_str_mv |
Geopolymer Non-ionic Latex Sodium Tetraborate Oilwell Cementing Operation |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS EXATAS E DA TERRA |
description |
The development of activities in the oil and gas sector has been promoting the search for materials more adequate to oilwell cementing operation. In the state of Rio Grande do Norte, the cement sheath integrity tend to fail during steam injection operation which is necessary to increase oil recovery in reservoir with heavy oil. Geopolymer is a material that can be used as alternative cement. It has been used in manufacturing of fireproof compounds, construction of structures and for controlling of toxic or radioactive waste. Latex is widely used in Portland cement slurries and its characteristic is the increase of compressive strength of cement slurries. Sodium Tetraborate is used in dental cement as a retarder. The addition of this additive aim to improve the geopolymeric slurries properties for oilwell cementing operation. The slurries studied are constituted of metakaolinite, potassium silicate, potassium hydroxide, non-ionic latex and sodium tetraborate. The properties evaluated were: viscosity, compressive strength, thickening time, density, fluid loss control, at ambient temperature (27 ºC) and at cement specification temperature. The tests were carried out in accordance to the practical recommendations of the norm API RP 10B. The slurries with sodium tetraborate did not change either their rheological properties or their mechanical properties or their density in relation the slurry with no additive. The increase of the concentration of sodium tetraborate increased the water loss at both temperatures studied. The best result obtained with the addition of sodium tetraborate was thickening time, which was tripled. The addition of latex in the slurries studied diminished their rheological properties and their density, however, at ambient temperature, it increased their compressive strength and it functioned as an accelerator. The increase of latex concentration increased the presence of water and then diminished the density of the slurries and increased the water loss. From the results obtained, it was concluded that sodium tetraborate and non-ionic latex are promising additives for geopolymer slurries to be used in oilwell cementing operation |
publishDate |
2007 |
dc.date.available.fl_str_mv |
2007-11-19 2014-12-17T14:07:20Z |
dc.date.issued.fl_str_mv |
2007-04-23 |
dc.date.accessioned.fl_str_mv |
2014-12-17T14:07:20Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
PINTO, Erica Natasche de Medeiros Gurgel. Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo. 2007. 96 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2007. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/jspui/handle/123456789/12862 |
identifier_str_mv |
PINTO, Erica Natasche de Medeiros Gurgel. Aditivação de pastas geopoliméricas com tetraborato de sódio e látex não iônico para cimentação de Poços de Petróleo. 2007. 96 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2007. |
url |
https://repositorio.ufrn.br/jspui/handle/123456789/12862 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/12862/1/AditivacaoPastasGeopolim%c3%a9ricas_Pinto_2007.pdf https://repositorio.ufrn.br/bitstream/123456789/12862/6/EricaNMGP.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12862/8/AditivacaoPastasGeopolim%c3%a9ricas_Pinto_2007.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12862/7/EricaNMGP.pdf.jpg https://repositorio.ufrn.br/bitstream/123456789/12862/9/AditivacaoPastasGeopolim%c3%a9ricas_Pinto_2007.pdf.jpg |
bitstream.checksum.fl_str_mv |
bf4255596957765009ee816c080d6b9a 48a428211d3c515652fb05c76c986ec6 48a428211d3c515652fb05c76c986ec6 684582a6b227c096e7b1deab9218bea0 a29fc1b8769c9fc4c87ff8a54fc0dd6a |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1797777029035196416 |