Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec)
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/jspui/handle/123456789/12840 |
Resumo: | The development of new materials to fill the demand of technological advances is a challenge for many researchers around the world. Strategies such as making blends and composites are promising alternatives to produce materials with different properties from those found in conventional polymers. The objective of this study is to evaluate the effect of adding the copolymer poly(ethylene methyl acrylate) (EMA) and cotton linter fibers (LB) on the properties of recycled poly(ethylene terephthalate) (PETrec) by the development of PETrec/EMA blend and PETrec/EMA/LB blend composite. In order to improve the properties of these materials were added as compatibilizers: Ethylene - methyl acrylate - glycidyl methacrylate terpolymer (EMA-GMA) and maleic anhydride grafted polyethylene (PE-g-MA). The samples were produced using a single screw extruder and then injection molded. The obtained materials were characterized by thermogravimetry (TG), melt flow index (MFI) mensurements, torque rheometry, pycnometry to determinate the density, tensile testing and scanning electron microscopy (SEM). The rheological results showed that the addition of the EMA copolymer increased the viscosity of the blend and LB reduces the viscosity of the blend composite. SEM analysis of the binary blend showed poor interfacial adhesion between the PETrec matrix and the EMA dispersed phase, as well as the blend composite of PETrec/EMA/LB also observed low adhesion with the LB fiber. The tensile tests showed that the increase of EMA percentage decreased the tensile strength and the Young s modulus, also lower EMA percentage samples had increased the elongation at break. The blend composite showed an increase in the tensile strength and in the Young`s modulus, and a decrease in the elongation at break. The blend formulations with lower EMA percentages showed better mechanical properties that agree with the particle size analysis which showed that these formulations presented a smaller diameter of the dispersed phase. The blend composite mechanical tests showed that this material is stronger and stiffer than the blend PETrec/EMA, whose properties have been reduced due to the presence of EMA rubbery phase. The use of EMA-GMA was effective in reducing the particle size of the EMA dispersed phase in the PETrec/EMA blend and PE-g-MA showed evidences of reaction with LB and physical mixture with the EMA |
id |
UFRN_63b6d6a9e5a2a999a4a66fcba18cf945 |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/12840 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Pereira, Laurenice Martinshttp://lattes.cnpq.br/4565222846393256http://lattes.cnpq.br/7249500407405478Nascimento, Maria Carolina Burgos Costa dohttp://lattes.cnpq.br/4409025248163428Bibbo, Ana Carolina Corrêahttp://lattes.cnpq.br/3369858890068027Ito, Edson Noriyuki2014-12-17T14:07:18Z2014-11-112014-12-17T14:07:18Z2014-12-28PEREIRA, Laurenice Martins. Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec). 2014. 130 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2014.https://repositorio.ufrn.br/jspui/handle/123456789/12840The development of new materials to fill the demand of technological advances is a challenge for many researchers around the world. Strategies such as making blends and composites are promising alternatives to produce materials with different properties from those found in conventional polymers. The objective of this study is to evaluate the effect of adding the copolymer poly(ethylene methyl acrylate) (EMA) and cotton linter fibers (LB) on the properties of recycled poly(ethylene terephthalate) (PETrec) by the development of PETrec/EMA blend and PETrec/EMA/LB blend composite. In order to improve the properties of these materials were added as compatibilizers: Ethylene - methyl acrylate - glycidyl methacrylate terpolymer (EMA-GMA) and maleic anhydride grafted polyethylene (PE-g-MA). The samples were produced using a single screw extruder and then injection molded. The obtained materials were characterized by thermogravimetry (TG), melt flow index (MFI) mensurements, torque rheometry, pycnometry to determinate the density, tensile testing and scanning electron microscopy (SEM). The rheological results showed that the addition of the EMA copolymer increased the viscosity of the blend and LB reduces the viscosity of the blend composite. SEM analysis of the binary blend showed poor interfacial adhesion between the PETrec matrix and the EMA dispersed phase, as well as the blend composite of PETrec/EMA/LB also observed low adhesion with the LB fiber. The tensile tests showed that the increase of EMA percentage decreased the tensile strength and the Young s modulus, also lower EMA percentage samples had increased the elongation at break. The blend composite showed an increase in the tensile strength and in the Young`s modulus, and a decrease in the elongation at break. The blend formulations with lower EMA percentages showed better mechanical properties that agree with the particle size analysis which showed that these formulations presented a smaller diameter of the dispersed phase. The blend composite mechanical tests showed that this material is stronger and stiffer than the blend PETrec/EMA, whose properties have been reduced due to the presence of EMA rubbery phase. The use of EMA-GMA was effective in reducing the particle size of the EMA dispersed phase in the PETrec/EMA blend and PE-g-MA showed evidences of reaction with LB and physical mixture with the EMAO desenvolvimento de novos materiais para atender as necessidades dos avanços tecnológicos é um desafio enfrentado por pesquisadores de todo o mundo. No que diz respeito aos materiais poliméricos, estratégias como a confecção de blendas e compósitos são alternativas promissoras para atender a demanda por materiais com propriedades diferentes das encontradas nos polímeros convencionais. O objetivo deste trabalho é avaliar o efeito da adição do copolímero poli(etileno-acrilato de metila) (EMA) e da fibra de linter de algodão (LB) nas propriedades do poli(tereftalato de etileno) reciclado (PETrec). Para isto, foram desenvolvidos a blenda PETrec/EMA e o compósito da blenda PETrec/EMA/LB. Com o intuito de melhorar as propriedades destes materiais foram adicionados agentes compatibilizantes: terpolímero etileno-acrilato de metila-metacrilato de glicidila (EMA-GMA) e o polietileno enxertado com anidrido maléico (PE-g-MA). As misturas foram produzidas por meio de uma extrusora monorosca e, em seguida, moldados por injeção. As caracterizações realizadas foram termogravimetria (TG), medida de índice de fluidez (MFI), reometria de torque, determinação da densidade por picnometria, ensaio de tração uniaxial e microscopia eletrônica de varredura (MEV). Os resultados reológicos mostraram que a adição do copolímero EMA aumentou a viscosidade da mistura e o LB reduziu a viscosidade da blenda PETrec/EMA. A análise por MEV da blenda binária mostrou baixa adesão interfacial entre a matriz de PETrec e a fase dispersa de EMA, assim como no compósito da blenda PETrec/EMA/LB, também observou-se uma baixa adesão com a fibra de LB. Os ensaios de tração mostraram que o aumento da porcentagem de EMA diminuiu a resistência máxima e o módulo de elasticidade, e, para as formulações com menor porcentagem de EMA verificou-se um aumento do alongamento na ruptura. O compósito da blenda apresentou um aumento na resistência máxima e no módulo de elasticidade, e uma redução no alongamento de ruptura. As formulações da blenda com menores porcentagens de EMA apresentaram propriedades mecânicas melhores, que corrobora com as análises de tamanho de partícula que mostraram que estas formulações apresentaram menor diâmetro médio de fase dispersa. Os resultados de ensaios mecânicos do compósito da blenda mostraram que essa mistura resultou em um material com maior resistência mecânica e rigidez do que a blenda PETrec/EMA, cujas propriedades foram reduzidas em função da fase borrachosa EMA. O uso do EMA-GMA foi eficiente na redução do tamanho de partículas da fase dispersa do EMA na blenda PETrec/EMA e o PE-g-MA apresentou indício de reação com o LB e mistura física com o EMACoordenação de Aperfeiçoamento de Pessoal de Nível Superiorapplication/pdfporUniversidade Federal do Rio Grande do NortePrograma de Pós-Graduação em Ciência e Engenharia de MateriaisUFRNBRProcessamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a partCompósito de blenda polimérica. Politereftalato de etileno. Polietileno acrilato de metila e linter de algodãoComposite polymer blend. Polyethylene terephthalate. Polyethylene methyl acrylate. And cotton linterCNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAEfeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec)info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNORIGINALEfeitoAdicaoPoli_Pereira_2014.pdfapplication/pdf7523564https://repositorio.ufrn.br/bitstream/123456789/12840/1/EfeitoAdicaoPoli_Pereira_2014.pdf3bb1b06da6a21522b0974a84935760a3MD51TEXTLaureniceMP_DISSERT.pdf.txtLaureniceMP_DISSERT.pdf.txtExtracted texttext/plain183647https://repositorio.ufrn.br/bitstream/123456789/12840/6/LaureniceMP_DISSERT.pdf.txt413c9ea6cc257004d8e158929a721cc2MD56EfeitoAdicaoPoli_Pereira_2014.pdf.txtEfeitoAdicaoPoli_Pereira_2014.pdf.txtExtracted texttext/plain183647https://repositorio.ufrn.br/bitstream/123456789/12840/8/EfeitoAdicaoPoli_Pereira_2014.pdf.txt413c9ea6cc257004d8e158929a721cc2MD58THUMBNAILLaureniceMP_DISSERT.pdf.jpgLaureniceMP_DISSERT.pdf.jpgIM Thumbnailimage/jpeg3901https://repositorio.ufrn.br/bitstream/123456789/12840/7/LaureniceMP_DISSERT.pdf.jpgecedee64a073ef66824c1a847e2ed61aMD57EfeitoAdicaoPoli_Pereira_2014.pdf.jpgEfeitoAdicaoPoli_Pereira_2014.pdf.jpgIM Thumbnailimage/jpeg3901https://repositorio.ufrn.br/bitstream/123456789/12840/9/EfeitoAdicaoPoli_Pereira_2014.pdf.jpgecedee64a073ef66824c1a847e2ed61aMD59123456789/128402019-01-29 18:50:21.559oai:https://repositorio.ufrn.br:123456789/12840Repositório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2019-01-29T21:50:21Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.por.fl_str_mv |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
title |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
spellingShingle |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) Pereira, Laurenice Martins Compósito de blenda polimérica. Politereftalato de etileno. Polietileno acrilato de metila e linter de algodão Composite polymer blend. Polyethylene terephthalate. Polyethylene methyl acrylate. And cotton linter CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
title_full |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
title_fullStr |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
title_full_unstemmed |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
title_sort |
Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec) |
author |
Pereira, Laurenice Martins |
author_facet |
Pereira, Laurenice Martins |
author_role |
author |
dc.contributor.authorID.por.fl_str_mv |
|
dc.contributor.authorLattes.por.fl_str_mv |
http://lattes.cnpq.br/4565222846393256 |
dc.contributor.advisorID.por.fl_str_mv |
|
dc.contributor.advisorLattes.por.fl_str_mv |
http://lattes.cnpq.br/7249500407405478 |
dc.contributor.referees1.pt_BR.fl_str_mv |
Nascimento, Maria Carolina Burgos Costa do |
dc.contributor.referees1ID.por.fl_str_mv |
|
dc.contributor.referees1Lattes.por.fl_str_mv |
http://lattes.cnpq.br/4409025248163428 |
dc.contributor.referees2.pt_BR.fl_str_mv |
Bibbo, Ana Carolina Corrêa |
dc.contributor.referees2ID.por.fl_str_mv |
|
dc.contributor.referees2Lattes.por.fl_str_mv |
http://lattes.cnpq.br/3369858890068027 |
dc.contributor.author.fl_str_mv |
Pereira, Laurenice Martins |
dc.contributor.advisor1.fl_str_mv |
Ito, Edson Noriyuki |
contributor_str_mv |
Ito, Edson Noriyuki |
dc.subject.por.fl_str_mv |
Compósito de blenda polimérica. Politereftalato de etileno. Polietileno acrilato de metila e linter de algodão |
topic |
Compósito de blenda polimérica. Politereftalato de etileno. Polietileno acrilato de metila e linter de algodão Composite polymer blend. Polyethylene terephthalate. Polyethylene methyl acrylate. And cotton linter CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
Composite polymer blend. Polyethylene terephthalate. Polyethylene methyl acrylate. And cotton linter |
dc.subject.cnpq.fl_str_mv |
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
The development of new materials to fill the demand of technological advances is a challenge for many researchers around the world. Strategies such as making blends and composites are promising alternatives to produce materials with different properties from those found in conventional polymers. The objective of this study is to evaluate the effect of adding the copolymer poly(ethylene methyl acrylate) (EMA) and cotton linter fibers (LB) on the properties of recycled poly(ethylene terephthalate) (PETrec) by the development of PETrec/EMA blend and PETrec/EMA/LB blend composite. In order to improve the properties of these materials were added as compatibilizers: Ethylene - methyl acrylate - glycidyl methacrylate terpolymer (EMA-GMA) and maleic anhydride grafted polyethylene (PE-g-MA). The samples were produced using a single screw extruder and then injection molded. The obtained materials were characterized by thermogravimetry (TG), melt flow index (MFI) mensurements, torque rheometry, pycnometry to determinate the density, tensile testing and scanning electron microscopy (SEM). The rheological results showed that the addition of the EMA copolymer increased the viscosity of the blend and LB reduces the viscosity of the blend composite. SEM analysis of the binary blend showed poor interfacial adhesion between the PETrec matrix and the EMA dispersed phase, as well as the blend composite of PETrec/EMA/LB also observed low adhesion with the LB fiber. The tensile tests showed that the increase of EMA percentage decreased the tensile strength and the Young s modulus, also lower EMA percentage samples had increased the elongation at break. The blend composite showed an increase in the tensile strength and in the Young`s modulus, and a decrease in the elongation at break. The blend formulations with lower EMA percentages showed better mechanical properties that agree with the particle size analysis which showed that these formulations presented a smaller diameter of the dispersed phase. The blend composite mechanical tests showed that this material is stronger and stiffer than the blend PETrec/EMA, whose properties have been reduced due to the presence of EMA rubbery phase. The use of EMA-GMA was effective in reducing the particle size of the EMA dispersed phase in the PETrec/EMA blend and PE-g-MA showed evidences of reaction with LB and physical mixture with the EMA |
publishDate |
2014 |
dc.date.accessioned.fl_str_mv |
2014-12-17T14:07:18Z |
dc.date.available.fl_str_mv |
2014-11-11 2014-12-17T14:07:18Z |
dc.date.issued.fl_str_mv |
2014-12-28 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
PEREIRA, Laurenice Martins. Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec). 2014. 130 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2014. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/jspui/handle/123456789/12840 |
identifier_str_mv |
PEREIRA, Laurenice Martins. Efeito da adição do poli(etileno acrilato de metila) (ema) e da fibra de linter de algodão nas propriedades do poli(tereftalato de etileno) reciclado (petrec). 2014. 130 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2014. |
url |
https://repositorio.ufrn.br/jspui/handle/123456789/12840 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/12840/1/EfeitoAdicaoPoli_Pereira_2014.pdf https://repositorio.ufrn.br/bitstream/123456789/12840/6/LaureniceMP_DISSERT.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12840/8/EfeitoAdicaoPoli_Pereira_2014.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12840/7/LaureniceMP_DISSERT.pdf.jpg https://repositorio.ufrn.br/bitstream/123456789/12840/9/EfeitoAdicaoPoli_Pereira_2014.pdf.jpg |
bitstream.checksum.fl_str_mv |
3bb1b06da6a21522b0974a84935760a3 413c9ea6cc257004d8e158929a721cc2 413c9ea6cc257004d8e158929a721cc2 ecedee64a073ef66824c1a847e2ed61a ecedee64a073ef66824c1a847e2ed61a |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1802117774545256448 |