Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Trabalho de conclusão de curso |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/handle/123456789/38907 |
Resumo: | With the concern of contemporary society with environmental issues, new legislations, more stringent control of pollutants emissions of and more effective techniques for wastewater treatment has been implemented. In this context, heterogeneous photocatalysis is presented as a powerful alternative to be a rapid and efficient method for a complete contaminants mineralization. At recent years, ceramic materials have been receiving much focus on various studies and research due to its various properties such as: high melting points, mixed conductivity, high stability, among others and applications as, for example, the study of semiconductor materials, electrodes in technological devices and in particular in heterogeneous photocatalysis. This work deals with the synthesis and characterization of molybdate Strontium (SrMoO4) doped with copper, cobalt and zinc at the site A in the structure of this material (AMoO4, A = 0.9 Strontium + 0.1 dopant). The products were synthesized by complexation method EDTA / Citrate, with basic mean(pH ≈ 9), through thermal pretreatment for removing water and ammonia at 230 °C during 180 minutes and heating rate of 10 ° C.min- ¹ obtaining an amorphous precursor of the final powder. The precursors were then submited to heat treatment of 650 ° C with a fixed level of 180 minutes and a heating rate of 10 ° C min-¹. For the characterization of the products obtained were used Thermogravimetric Analysis (TG), X-Ray Diffraction (XRD), Particle size distribution by laser diffraction, Spectroscopy in the UV-Visible region, Energy Dispersive Spectroscopy (EDS) and Scanning Electron Microscopy (SEM). Finally, was carried out a brief study of the photocatalytic properties of these materials in a batch reactor under agitation. |
id |
UFRN_813534859237c2304f170ff9360d1561 |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/38907 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Dutra, Fabíola BezerraAndré Luís Lopes MoriyamaMoriyama, André Luís LopesSilva, Maitê Medeiros de Santana eSouza, Carlson Pereira de2016-06-16T18:02:18Z2021-09-27T12:25:21Z2016-06-16T18:02:18Z2021-09-27T12:25:21Z2016-06-152012039610DUTRA, Fabíola Bezerra. Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos.. 2016. 71f. Trabalho de Conclusão de Curso (Graduação em Engenharia Química), Departamento de Engenharia Química, Universidade Federal do Rio Grande do Norte, Natal, 2016.https://repositorio.ufrn.br/handle/123456789/38907With the concern of contemporary society with environmental issues, new legislations, more stringent control of pollutants emissions of and more effective techniques for wastewater treatment has been implemented. In this context, heterogeneous photocatalysis is presented as a powerful alternative to be a rapid and efficient method for a complete contaminants mineralization. At recent years, ceramic materials have been receiving much focus on various studies and research due to its various properties such as: high melting points, mixed conductivity, high stability, among others and applications as, for example, the study of semiconductor materials, electrodes in technological devices and in particular in heterogeneous photocatalysis. This work deals with the synthesis and characterization of molybdate Strontium (SrMoO4) doped with copper, cobalt and zinc at the site A in the structure of this material (AMoO4, A = 0.9 Strontium + 0.1 dopant). The products were synthesized by complexation method EDTA / Citrate, with basic mean(pH ≈ 9), through thermal pretreatment for removing water and ammonia at 230 °C during 180 minutes and heating rate of 10 ° C.min- ¹ obtaining an amorphous precursor of the final powder. The precursors were then submited to heat treatment of 650 ° C with a fixed level of 180 minutes and a heating rate of 10 ° C min-¹. For the characterization of the products obtained were used Thermogravimetric Analysis (TG), X-Ray Diffraction (XRD), Particle size distribution by laser diffraction, Spectroscopy in the UV-Visible region, Energy Dispersive Spectroscopy (EDS) and Scanning Electron Microscopy (SEM). Finally, was carried out a brief study of the photocatalytic properties of these materials in a batch reactor under agitation.Com a grande preocupação da sociedade contemporânea com os problemas ambientais, novas legislações, controle mais rigorosos de emissões de poluentes e técnicas mais eficazes de tratamento de efluentes vem sendo implementadas. Nesse contexto, a fotocatálise heterogênea apresenta-se como uma potente alternativa por ser um método rápido e eficiente para a completa mineralização de contaminantes. Nos últimos anos, os materiais cerâmicos vêm recebendo grande enfoque em diversos estudos e pesquisas devido as suas diversas propriedades, como altos pontos de fusão, condutividade mista, alta estabilidade, entre outros e aplicações como no estudo de materiais semicondutores, eletrodos, dispositivos tecnológicos e em particular, na fotocatálise heterogênea. O presente trabalho trata da síntese e caracterização do Molibdato de Estrôncio (SrMoO4) dopado com Cobre, Cobalto e Zinco no sitio A na estrutura deste material (AMoO4, A= 0,9 Estrôncio + 0,1 dopante). Os compostos foram sintetizados através do método de complexação EDTA/Citrato em meio básico (pH ≈ 9) passando por prévio tratamento térmico para eliminação de água e amônia a 230°C, por 180 minutos e taxa de aquecimento de 10°C.min-¹, obtendo-se um precursor amorfo do pó final. Os precursores então foram submetidos a tratamento térmico de 650°C com patamar fixo de 180 minutos e taxa de aquecimento de 10°C.min-¹. Para a caracterização dos produtos obtidos foram utilizadas as técnicas de Análise Termogravimétrica (TG), Difração de Raios-X (DRX), Granulometria por difração a laser, Espectroscopia na Região do UV-Visível, Espectroscopia de Energia Dispersiva (EDS), e Microscopia Eletrônica de Varredura (MEV). Por fim, foi realizado um breve estudo das propriedades fotocatalíticas desses materiais em um reator batelada sob agitação.Universidade Federal do Rio Grande do NorteUFRNBrasilEngenharia QuímicaSínteseCaracterizaçãoMateriais dopantesFotocatálise heterogêneaEngenharias.Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticosinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesisinfo:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNTEXTSinteseecaracterizacao_Monografia.txtExtracted texttext/plain88521https://repositorio.ufrn.br/bitstream/123456789/38907/1/Sinteseecaracterizacao_Monografia.txtc13d7a9fcfd109a8247582dcdc716b4eMD51ORIGINALSinteseecaracterizacao_MonografiaMonografiaapplication/octet-stream3360730https://repositorio.ufrn.br/bitstream/123456789/38907/2/Sinteseecaracterizacao_Monografia60e3852ff400ae7c55fb07030151d413MD52LICENSElicense.txttext/plain756https://repositorio.ufrn.br/bitstream/123456789/38907/3/license.txta80a9cda2756d355b388cc443c3d8a43MD53123456789/389072021-09-27 09:25:21.455oai:https://repositorio.ufrn.br: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ório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2021-09-27T12:25:21Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.pr_BR.fl_str_mv |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
title |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
spellingShingle |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos Dutra, Fabíola Bezerra Síntese Caracterização Materiais dopantes Fotocatálise heterogênea Engenharias. |
title_short |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
title_full |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
title_fullStr |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
title_full_unstemmed |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
title_sort |
Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos |
author |
Dutra, Fabíola Bezerra |
author_facet |
Dutra, Fabíola Bezerra |
author_role |
author |
dc.contributor.referees1.none.fl_str_mv |
Moriyama, André Luís Lopes |
dc.contributor.referees2.none.fl_str_mv |
Silva, Maitê Medeiros de Santana e |
dc.contributor.author.fl_str_mv |
Dutra, Fabíola Bezerra |
dc.contributor.advisor-co1.fl_str_mv |
André Luís Lopes Moriyama |
dc.contributor.advisor1.fl_str_mv |
Souza, Carlson Pereira de |
contributor_str_mv |
André Luís Lopes Moriyama Souza, Carlson Pereira de |
dc.subject.pr_BR.fl_str_mv |
Síntese Caracterização Materiais dopantes Fotocatálise heterogênea |
topic |
Síntese Caracterização Materiais dopantes Fotocatálise heterogênea Engenharias. |
dc.subject.cnpq.fl_str_mv |
Engenharias. |
description |
With the concern of contemporary society with environmental issues, new legislations, more stringent control of pollutants emissions of and more effective techniques for wastewater treatment has been implemented. In this context, heterogeneous photocatalysis is presented as a powerful alternative to be a rapid and efficient method for a complete contaminants mineralization. At recent years, ceramic materials have been receiving much focus on various studies and research due to its various properties such as: high melting points, mixed conductivity, high stability, among others and applications as, for example, the study of semiconductor materials, electrodes in technological devices and in particular in heterogeneous photocatalysis. This work deals with the synthesis and characterization of molybdate Strontium (SrMoO4) doped with copper, cobalt and zinc at the site A in the structure of this material (AMoO4, A = 0.9 Strontium + 0.1 dopant). The products were synthesized by complexation method EDTA / Citrate, with basic mean(pH ≈ 9), through thermal pretreatment for removing water and ammonia at 230 °C during 180 minutes and heating rate of 10 ° C.min- ¹ obtaining an amorphous precursor of the final powder. The precursors were then submited to heat treatment of 650 ° C with a fixed level of 180 minutes and a heating rate of 10 ° C min-¹. For the characterization of the products obtained were used Thermogravimetric Analysis (TG), X-Ray Diffraction (XRD), Particle size distribution by laser diffraction, Spectroscopy in the UV-Visible region, Energy Dispersive Spectroscopy (EDS) and Scanning Electron Microscopy (SEM). Finally, was carried out a brief study of the photocatalytic properties of these materials in a batch reactor under agitation. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-06-16T18:02:18Z 2021-09-27T12:25:21Z |
dc.date.available.fl_str_mv |
2016-06-16T18:02:18Z 2021-09-27T12:25:21Z |
dc.date.issued.fl_str_mv |
2016-06-15 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/bachelorThesis |
format |
bachelorThesis |
status_str |
publishedVersion |
dc.identifier.pr_BR.fl_str_mv |
2012039610 |
dc.identifier.citation.fl_str_mv |
DUTRA, Fabíola Bezerra. Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos.. 2016. 71f. Trabalho de Conclusão de Curso (Graduação em Engenharia Química), Departamento de Engenharia Química, Universidade Federal do Rio Grande do Norte, Natal, 2016. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/handle/123456789/38907 |
identifier_str_mv |
2012039610 DUTRA, Fabíola Bezerra. Síntese e caracterização do molibdato de estrôncio dopado com cobre, cobalto e zinco para fins fotocatalíticos.. 2016. 71f. Trabalho de Conclusão de Curso (Graduação em Engenharia Química), Departamento de Engenharia Química, Universidade Federal do Rio Grande do Norte, Natal, 2016. |
url |
https://repositorio.ufrn.br/handle/123456789/38907 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Engenharia Química |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/38907/1/Sinteseecaracterizacao_Monografia.txt https://repositorio.ufrn.br/bitstream/123456789/38907/2/Sinteseecaracterizacao_Monografia https://repositorio.ufrn.br/bitstream/123456789/38907/3/license.txt |
bitstream.checksum.fl_str_mv |
c13d7a9fcfd109a8247582dcdc716b4e 60e3852ff400ae7c55fb07030151d413 a80a9cda2756d355b388cc443c3d8a43 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1802117624681725952 |