Influência do lodo de ETE na massa para fabricação de cerâmica vermelha
Autor(a) principal: | |
---|---|
Data de Publicação: | 2008 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/jspui/handle/123456789/12670 |
Resumo: | The WTP produce many kinds of residue on your treatment stages, but the sludge is the more problematic from the final disposition point view. The actual rate of residue production deriving from technological evolution and the crescent population needs prevents the subtle equilibrium generation between consumption and recycling/reuse, creating problems of pollution resulting from inappropriate management of residues. Thus, is necessary achieve a new equilibrium between the grow from raw materials and energy and the residue generation. This equilibrium should be achieved by technical and economic feasibility of environmental supported models through recycling and reuse. The red ceramic industry stand out in residue absorption question as raw material due their clay mass heterogeneity, constituted by clay minerals and non-clay minerals with wide mineralogical variation, allowing residue inclusion which act like plastic or non-plastic materials, contributing to retain heavy metals contained in residues in the vitreous mass formed during the burning of the ceramic bodies. This work propose the study of the influence of incorporation of 25 wt.% sludge from wastewater treatment plant, according preliminary results, in the mass to produce ceramic bodies. The raw materials was characterized through chemical composition analyses by XRF, mineralogical analyses by XRD, thermal analyses by TG and DTA, Atterberg limits and thermodilatometry. Subsequently was composed the mass with 75 wt.% of clay and 25 wt.% of dried wastewater sludge from UFRN WWTP. Samples with 6,0 x 2,0 x 0,5 cm was produced with unidirectional compacting under pressure of 20MPa and burned in temperatures between 950 and 1,200ºC. After fired, the ceramic bodies have been submitted to physical and mechanical analyses through the measure of firing shrinkage, water absorption, density, apparent porosity and flexural strength; crystallographic analyses through XRD and microstructure analyses by SEM. The technological properties obtained was satisfactory to production of roof tiles with 25 wt.% at 1,200 ºC, but the production of others products at lower temperatures was not feasible |
id |
UFRN_d8293fb37c5105eaff8aa50a6ec48b25 |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/12670 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Araújo, Franciolli da Silva Dantas dehttp://lattes.cnpq.br/5460040602567184Gomes, Uilame Umbelinohttp://lattes.cnpq.br/9858094266525225Diniz, Marcus Alexandrehttp://lattes.cnpq.br/5997887290230186Paes Júnior, Herval Ramoshttp://lattes.cnpq.br/9034804887420018Acchar, Wilson2014-12-17T14:06:49Z2009-03-112014-12-17T14:06:49Z2008-08-05ARAÚJO, Franciolli da Silva Dantas de. Influência do lodo de ETE na massa para fabricação de cerâmica vermelha. 2008. 91 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2008.https://repositorio.ufrn.br/jspui/handle/123456789/12670The WTP produce many kinds of residue on your treatment stages, but the sludge is the more problematic from the final disposition point view. The actual rate of residue production deriving from technological evolution and the crescent population needs prevents the subtle equilibrium generation between consumption and recycling/reuse, creating problems of pollution resulting from inappropriate management of residues. Thus, is necessary achieve a new equilibrium between the grow from raw materials and energy and the residue generation. This equilibrium should be achieved by technical and economic feasibility of environmental supported models through recycling and reuse. The red ceramic industry stand out in residue absorption question as raw material due their clay mass heterogeneity, constituted by clay minerals and non-clay minerals with wide mineralogical variation, allowing residue inclusion which act like plastic or non-plastic materials, contributing to retain heavy metals contained in residues in the vitreous mass formed during the burning of the ceramic bodies. This work propose the study of the influence of incorporation of 25 wt.% sludge from wastewater treatment plant, according preliminary results, in the mass to produce ceramic bodies. The raw materials was characterized through chemical composition analyses by XRF, mineralogical analyses by XRD, thermal analyses by TG and DTA, Atterberg limits and thermodilatometry. Subsequently was composed the mass with 75 wt.% of clay and 25 wt.% of dried wastewater sludge from UFRN WWTP. Samples with 6,0 x 2,0 x 0,5 cm was produced with unidirectional compacting under pressure of 20MPa and burned in temperatures between 950 and 1,200ºC. After fired, the ceramic bodies have been submitted to physical and mechanical analyses through the measure of firing shrinkage, water absorption, density, apparent porosity and flexural strength; crystallographic analyses through XRD and microstructure analyses by SEM. The technological properties obtained was satisfactory to production of roof tiles with 25 wt.% at 1,200 ºC, but the production of others products at lower temperatures was not feasibleAs ETE produzem vários tipos de resíduos em suas etapas de tratamento, mas o lodo é o resíduo mais problemático do ponto de vista de disposição final. A atual taxa de geração de resíduos, acarretada da evolução tecnológica e da crescente demanda populacional, impede a geração de um equilíbrio hábil entre o consumo e a reciclagem/reuso, gerando problemas de poluição resultantes da gestão inadequada dos resíduos. Dessa forma, é necessário atingir um novo equilíbrio entre o crescimento das demandas por matérias e energia e a geração de resíduos. Este equilíbrio, só pode ser alcançado através da viabilização técnica e econômica de modelos de sustentabilidade ambiental, através da reciclagem e do reuso. A indústria de cerâmica vermelha se destaca no quesito absorção de resíduos como matéria-prima em virtude da heterogeneidade das massas argilosas, constituídas de argilominerais e minerais não argilosos com ampla variação mineralógica, permitindo a inclusão de resíduos que atuem como plastificantes ou desplastificantes, e contribuindo também para a retenção de metais pesados presentes nos resíduos na massa vítrea formada nos corpos cerâmicos. Este trabalho propõe estudar a influência da incorporação de 25% de lodo de estação de tratamento de esgoto, baseado em resultados preliminares, à massa para produção de corpos cerâmicos. As matérias-primas foram caracterizadas através de análise da composição química por FRX, análise mineralógica por DRX, análise térmica por TG e DTA, análise dos limites de Atterberg e análise dilatométrica. Em seguida foi composta a massa com 75% de argila e 25% em peso de lodo da ETE UFRN. Foram prensados corpos-de-prova com dimensões 6,0 x 2,0 x 0,5 cm através de prensagem uniaxial sob pressão de 20MPa e queimadas nas temperaturas entre 950 e 1200ºC. Após a sinterização, os corpos-de-prova foram submetidos a ensaios físico-mecânicos através de medida de retração linear, absorção de água, massa específica aparente, porosidade aparente e tensão de ruptura à flexão; análise cristalográfica através de DRX e análise microestrutural através de MEV. As propriedades tecnológicas obtidas mostraram-se satisfatórias para fabricação de telhas com 25% de lodo na temperatura de queima de 1.200 ºC, não sendo viável a fabricação de outros produtos em temperaturas inferioresapplication/pdfporUniversidade Federal do Rio Grande do NortePrograma de Pós-Graduação em Ciência e Engenharia de MateriaisUFRNBRProcessamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a partReciclagem industrialLodoArgilaCerâmica vermelhaIndustrial recyclingSewage sludgeClayRed ceramicCNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAInfluência do lodo de ETE na massa para fabricação de cerâmica vermelhainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNORIGINALnfluênciaIodoETE_Araujo_2008.pdfapplication/pdf2363369https://repositorio.ufrn.br/bitstream/123456789/12670/1/nflu%c3%aanciaIodoETE_Araujo_2008.pdf60110371e06857963dc0f1bfade49f3aMD51TEXTFranciolliSDA.pdf.txtFranciolliSDA.pdf.txtExtracted texttext/plain147932https://repositorio.ufrn.br/bitstream/123456789/12670/6/FranciolliSDA.pdf.txt0ce02f3114bcdee8c416af1d484faea6MD56nfluênciaIodoETE_Araujo_2008.pdf.txtnfluênciaIodoETE_Araujo_2008.pdf.txtExtracted texttext/plain147932https://repositorio.ufrn.br/bitstream/123456789/12670/8/nflu%c3%aanciaIodoETE_Araujo_2008.pdf.txt0ce02f3114bcdee8c416af1d484faea6MD58THUMBNAILFranciolliSDA.pdf.jpgFranciolliSDA.pdf.jpgIM Thumbnailimage/jpeg3482https://repositorio.ufrn.br/bitstream/123456789/12670/7/FranciolliSDA.pdf.jpg030f21e6aa9a5312c97d3fdfceceefdaMD57nfluênciaIodoETE_Araujo_2008.pdf.jpgnfluênciaIodoETE_Araujo_2008.pdf.jpgIM Thumbnailimage/jpeg3480https://repositorio.ufrn.br/bitstream/123456789/12670/9/nflu%c3%aanciaIodoETE_Araujo_2008.pdf.jpg2a7ec9dcee3686ce51d706a087abcf43MD59123456789/126702019-01-29 17:42:25.589oai:https://repositorio.ufrn.br:123456789/12670Repositório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2019-01-29T20:42:25Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.por.fl_str_mv |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
title |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
spellingShingle |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha Araújo, Franciolli da Silva Dantas de Reciclagem industrial Lodo Argila Cerâmica vermelha Industrial recycling Sewage sludge Clay Red ceramic CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
title_full |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
title_fullStr |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
title_full_unstemmed |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
title_sort |
Influência do lodo de ETE na massa para fabricação de cerâmica vermelha |
author |
Araújo, Franciolli da Silva Dantas de |
author_facet |
Araújo, Franciolli da Silva Dantas de |
author_role |
author |
dc.contributor.authorID.por.fl_str_mv |
|
dc.contributor.advisorID.por.fl_str_mv |
|
dc.contributor.advisorLattes.por.fl_str_mv |
http://lattes.cnpq.br/5460040602567184 |
dc.contributor.referees1.pt_BR.fl_str_mv |
Gomes, Uilame Umbelino |
dc.contributor.referees1ID.por.fl_str_mv |
|
dc.contributor.referees1Lattes.por.fl_str_mv |
http://lattes.cnpq.br/9858094266525225 |
dc.contributor.referees2.pt_BR.fl_str_mv |
Diniz, Marcus Alexandre |
dc.contributor.referees2ID.por.fl_str_mv |
|
dc.contributor.referees2Lattes.por.fl_str_mv |
http://lattes.cnpq.br/5997887290230186 |
dc.contributor.referees3.pt_BR.fl_str_mv |
Paes Júnior, Herval Ramos |
dc.contributor.referees3ID.por.fl_str_mv |
|
dc.contributor.referees3Lattes.por.fl_str_mv |
http://lattes.cnpq.br/9034804887420018 |
dc.contributor.author.fl_str_mv |
Araújo, Franciolli da Silva Dantas de |
dc.contributor.advisor1.fl_str_mv |
Acchar, Wilson |
contributor_str_mv |
Acchar, Wilson |
dc.subject.por.fl_str_mv |
Reciclagem industrial Lodo Argila Cerâmica vermelha |
topic |
Reciclagem industrial Lodo Argila Cerâmica vermelha Industrial recycling Sewage sludge Clay Red ceramic CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
Industrial recycling Sewage sludge Clay Red ceramic |
dc.subject.cnpq.fl_str_mv |
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
The WTP produce many kinds of residue on your treatment stages, but the sludge is the more problematic from the final disposition point view. The actual rate of residue production deriving from technological evolution and the crescent population needs prevents the subtle equilibrium generation between consumption and recycling/reuse, creating problems of pollution resulting from inappropriate management of residues. Thus, is necessary achieve a new equilibrium between the grow from raw materials and energy and the residue generation. This equilibrium should be achieved by technical and economic feasibility of environmental supported models through recycling and reuse. The red ceramic industry stand out in residue absorption question as raw material due their clay mass heterogeneity, constituted by clay minerals and non-clay minerals with wide mineralogical variation, allowing residue inclusion which act like plastic or non-plastic materials, contributing to retain heavy metals contained in residues in the vitreous mass formed during the burning of the ceramic bodies. This work propose the study of the influence of incorporation of 25 wt.% sludge from wastewater treatment plant, according preliminary results, in the mass to produce ceramic bodies. The raw materials was characterized through chemical composition analyses by XRF, mineralogical analyses by XRD, thermal analyses by TG and DTA, Atterberg limits and thermodilatometry. Subsequently was composed the mass with 75 wt.% of clay and 25 wt.% of dried wastewater sludge from UFRN WWTP. Samples with 6,0 x 2,0 x 0,5 cm was produced with unidirectional compacting under pressure of 20MPa and burned in temperatures between 950 and 1,200ºC. After fired, the ceramic bodies have been submitted to physical and mechanical analyses through the measure of firing shrinkage, water absorption, density, apparent porosity and flexural strength; crystallographic analyses through XRD and microstructure analyses by SEM. The technological properties obtained was satisfactory to production of roof tiles with 25 wt.% at 1,200 ºC, but the production of others products at lower temperatures was not feasible |
publishDate |
2008 |
dc.date.issued.fl_str_mv |
2008-08-05 |
dc.date.available.fl_str_mv |
2009-03-11 2014-12-17T14:06:49Z |
dc.date.accessioned.fl_str_mv |
2014-12-17T14:06:49Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
ARAÚJO, Franciolli da Silva Dantas de. Influência do lodo de ETE na massa para fabricação de cerâmica vermelha. 2008. 91 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2008. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/jspui/handle/123456789/12670 |
identifier_str_mv |
ARAÚJO, Franciolli da Silva Dantas de. Influência do lodo de ETE na massa para fabricação de cerâmica vermelha. 2008. 91 f. Dissertação (Mestrado em Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part) - Universidade Federal do Rio Grande do Norte, Natal, 2008. |
url |
https://repositorio.ufrn.br/jspui/handle/123456789/12670 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/12670/1/nflu%c3%aanciaIodoETE_Araujo_2008.pdf https://repositorio.ufrn.br/bitstream/123456789/12670/6/FranciolliSDA.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12670/8/nflu%c3%aanciaIodoETE_Araujo_2008.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/12670/7/FranciolliSDA.pdf.jpg https://repositorio.ufrn.br/bitstream/123456789/12670/9/nflu%c3%aanciaIodoETE_Araujo_2008.pdf.jpg |
bitstream.checksum.fl_str_mv |
60110371e06857963dc0f1bfade49f3a 0ce02f3114bcdee8c416af1d484faea6 0ce02f3114bcdee8c416af1d484faea6 030f21e6aa9a5312c97d3fdfceceefda 2a7ec9dcee3686ce51d706a087abcf43 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1802117767493582848 |