Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico
Autor(a) principal: | |
---|---|
Data de Publicação: | 2015 |
Tipo de documento: | Trabalho de conclusão de curso |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFRN |
Texto Completo: | https://repositorio.ufrn.br/handle/123456789/38950 |
Resumo: | To evaluate the effect of contact of calcium hydroxide cements with polyacrylic and phosphoric acids on select physical and mechanical properties of chemically activated calcium hydroxide cements. Methods: Cement calcium hydroxide base (Life and Hydro C) were examined after exposure to different strategies: (1) contact with any substance, control; (2) washing with water and drying; (3) contact with polyacrylic acid (POL), washing with water and drying; and (4) contact phosphoric acid (FOS), washing with water and drying. The surface roughness, impact resistance, and release of hydroxyl ions (pH) were evaluated after 07 days storage in water. Data were statistically evaluated by ANOVA 2 factors and Tukey post-test (p <0.05). Results: The contact of acids with cement not statistically influences the values of the impact strength. FOS promoted statistically lower release of hydroxyl ions in both cements (p <0.05). The surface roughness Hydro C was statistically increased after contact with FOS (p <0.01) and decreased after the Life contact POL and FOS (p <0.01). Conclusion: While the FOS negatively affects the physical properties of the tested cements, POL interfered only in the roughness of Hydro C. |
id |
UFRN_dac872053deeb328a103a835ec2f502f |
---|---|
oai_identifier_str |
oai:https://repositorio.ufrn.br:123456789/38950 |
network_acronym_str |
UFRN |
network_name_str |
Repositório Institucional da UFRN |
repository_id_str |
|
spelling |
Souza, Gustavo Fernandes deBorges, Boniek Castillo DutraDorini, André LuisFerreira, Isana Álvares2016-10-06T13:52:21Z2021-09-27T14:00:37Z2016-10-06T13:52:21Z2021-09-27T14:00:37Z2015-12-042011093235SOUZA, Gustavo Fernandes de. Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico. 2015. Monografia (Graduação) - Departamento de Odontologia, Universidade Federal do Rio Grande do Norte, Natal, 2015.https://repositorio.ufrn.br/handle/123456789/38950To evaluate the effect of contact of calcium hydroxide cements with polyacrylic and phosphoric acids on select physical and mechanical properties of chemically activated calcium hydroxide cements. Methods: Cement calcium hydroxide base (Life and Hydro C) were examined after exposure to different strategies: (1) contact with any substance, control; (2) washing with water and drying; (3) contact with polyacrylic acid (POL), washing with water and drying; and (4) contact phosphoric acid (FOS), washing with water and drying. The surface roughness, impact resistance, and release of hydroxyl ions (pH) were evaluated after 07 days storage in water. Data were statistically evaluated by ANOVA 2 factors and Tukey post-test (p <0.05). Results: The contact of acids with cement not statistically influences the values of the impact strength. FOS promoted statistically lower release of hydroxyl ions in both cements (p <0.05). The surface roughness Hydro C was statistically increased after contact with FOS (p <0.01) and decreased after the Life contact POL and FOS (p <0.01). Conclusion: While the FOS negatively affects the physical properties of the tested cements, POL interfered only in the roughness of Hydro C.Avaliar o efeito do contato de cimentos de hidróxido de cálcio com ácidos poliacrílico e fosfórico sobre seletas propriedades físico-mecânicas de cimentos de hidróxido de cálcio quimicamente ativados. Materiais e métodos: Cimentos a base de hidróxido de cálcio (Life e Hydro C) foram examinados após exposição a diferentes estratégias: (1) contato com nenhuma substancia, controle; (2) lavagem com água e secagem; (3) contato com ácido poliacrílico (POL), lavagem com água e secagem; e (4) contato com ácido fosfórico (FOS), lavagem com água e secagem. A rugosidade, resistência ao impacto, e liberação de íons Hidroxila (pH) foram avaliados após 07 dias de estocagem em água. Os dados foram estatisticamente avaliados através do teste ANOVA a 2 fatores e pós-teste de Tukey (p<0,05). Resultados: O contato dos ácidos com os cimentos não influenciou estatisticamente os valores da resistência ao impacto. O FOS promoveu estatisticamente menor liberação de íons hidroxila em ambos os cimentos (p<0,05). A rugosidade superficial do cimento Hydro C foi estatisticamente aumentada após contato com FOS (p< 0,01), e a do Life diminuiu após contato com FOS e POL (p< 0,01). Conclusão: Enquanto o FOS afetou negativamente as propriedades físicas dos cimentos testados, o POL interferiu apenas na rugosidade do Hydro C.Universidade Federal do Rio Grande do NorteUFRNBrasilOdontologiaDentística operatóriaHidróxido de cálcioPHTensile StrengthPropriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfóricoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesisinfo:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNTEXT[2015] PROPRIEDADES FÍSICO-MECÂNICAS DE CIMENTOS DE HIDRÓXIDO DE CÁLCIO EXPOSTOS AOS ÁCIDOS POLIACRÍLICO E FOSFÓRICO.pdf.txtExtracted texttext/plain41141https://repositorio.ufrn.br/bitstream/123456789/38950/1/%5b2015%5d%20PROPRIEDADES%20F%c3%8dSICO-MEC%c3%82NICAS%20DE%20CIMENTOS%20DE%20HIDR%c3%93XIDO%20DE%20C%c3%81LCIO%20EXPOSTOS%20AOS%20%c3%81CIDOS%20POLIACR%c3%8dLICO%20E%20FOSF%c3%93RICO.pdf.txt481de7de36028bd819ca8cc8b9c835f5MD51ORIGINALPropriedadesHidroxidosExpostos_Ferreira_2015.pdfTrabalho de conclusão de curso - odontologia 2015.2application/pdf648152https://repositorio.ufrn.br/bitstream/123456789/38950/2/PropriedadesHidroxidosExpostos_Ferreira_2015.pdfaacd3a7b2ec92a3d2b9d05d344090e47MD52LICENSElicense.txttext/plain756https://repositorio.ufrn.br/bitstream/123456789/38950/3/license.txta80a9cda2756d355b388cc443c3d8a43MD53123456789/389502023-05-02 11:18:52.677oai:https://repositorio.ufrn.br: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ório de PublicaçõesPUBhttp://repositorio.ufrn.br/oai/opendoar:2023-05-02T14:18:52Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)false |
dc.title.pr_BR.fl_str_mv |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
title |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
spellingShingle |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico Souza, Gustavo Fernandes de Dentística operatória Hidróxido de cálcio PH Tensile Strength |
title_short |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
title_full |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
title_fullStr |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
title_full_unstemmed |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
title_sort |
Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico |
author |
Souza, Gustavo Fernandes de |
author_facet |
Souza, Gustavo Fernandes de |
author_role |
author |
dc.contributor.referees1.none.fl_str_mv |
Borges, Boniek Castillo Dutra |
dc.contributor.referees2.none.fl_str_mv |
Dorini, André Luis |
dc.contributor.author.fl_str_mv |
Souza, Gustavo Fernandes de |
dc.contributor.advisor1.fl_str_mv |
Ferreira, Isana Álvares |
contributor_str_mv |
Ferreira, Isana Álvares |
dc.subject.pr_BR.fl_str_mv |
Dentística operatória Hidróxido de cálcio PH Tensile Strength |
topic |
Dentística operatória Hidróxido de cálcio PH Tensile Strength |
description |
To evaluate the effect of contact of calcium hydroxide cements with polyacrylic and phosphoric acids on select physical and mechanical properties of chemically activated calcium hydroxide cements. Methods: Cement calcium hydroxide base (Life and Hydro C) were examined after exposure to different strategies: (1) contact with any substance, control; (2) washing with water and drying; (3) contact with polyacrylic acid (POL), washing with water and drying; and (4) contact phosphoric acid (FOS), washing with water and drying. The surface roughness, impact resistance, and release of hydroxyl ions (pH) were evaluated after 07 days storage in water. Data were statistically evaluated by ANOVA 2 factors and Tukey post-test (p <0.05). Results: The contact of acids with cement not statistically influences the values of the impact strength. FOS promoted statistically lower release of hydroxyl ions in both cements (p <0.05). The surface roughness Hydro C was statistically increased after contact with FOS (p <0.01) and decreased after the Life contact POL and FOS (p <0.01). Conclusion: While the FOS negatively affects the physical properties of the tested cements, POL interfered only in the roughness of Hydro C. |
publishDate |
2015 |
dc.date.issued.fl_str_mv |
2015-12-04 |
dc.date.accessioned.fl_str_mv |
2016-10-06T13:52:21Z 2021-09-27T14:00:37Z |
dc.date.available.fl_str_mv |
2016-10-06T13:52:21Z 2021-09-27T14:00:37Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/bachelorThesis |
format |
bachelorThesis |
status_str |
publishedVersion |
dc.identifier.pr_BR.fl_str_mv |
2011093235 |
dc.identifier.citation.fl_str_mv |
SOUZA, Gustavo Fernandes de. Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico. 2015. Monografia (Graduação) - Departamento de Odontologia, Universidade Federal do Rio Grande do Norte, Natal, 2015. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufrn.br/handle/123456789/38950 |
identifier_str_mv |
2011093235 SOUZA, Gustavo Fernandes de. Propriedades físico-mecânicas de cimentos de hidróxido de cálcio expostos aos ácidos poliacrílico e fosfórico. 2015. Monografia (Graduação) - Departamento de Odontologia, Universidade Federal do Rio Grande do Norte, Natal, 2015. |
url |
https://repositorio.ufrn.br/handle/123456789/38950 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.publisher.initials.fl_str_mv |
UFRN |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Odontologia |
publisher.none.fl_str_mv |
Universidade Federal do Rio Grande do Norte |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFRN instname:Universidade Federal do Rio Grande do Norte (UFRN) instacron:UFRN |
instname_str |
Universidade Federal do Rio Grande do Norte (UFRN) |
instacron_str |
UFRN |
institution |
UFRN |
reponame_str |
Repositório Institucional da UFRN |
collection |
Repositório Institucional da UFRN |
bitstream.url.fl_str_mv |
https://repositorio.ufrn.br/bitstream/123456789/38950/1/%5b2015%5d%20PROPRIEDADES%20F%c3%8dSICO-MEC%c3%82NICAS%20DE%20CIMENTOS%20DE%20HIDR%c3%93XIDO%20DE%20C%c3%81LCIO%20EXPOSTOS%20AOS%20%c3%81CIDOS%20POLIACR%c3%8dLICO%20E%20FOSF%c3%93RICO.pdf.txt https://repositorio.ufrn.br/bitstream/123456789/38950/2/PropriedadesHidroxidosExpostos_Ferreira_2015.pdf https://repositorio.ufrn.br/bitstream/123456789/38950/3/license.txt |
bitstream.checksum.fl_str_mv |
481de7de36028bd819ca8cc8b9c835f5 aacd3a7b2ec92a3d2b9d05d344090e47 a80a9cda2756d355b388cc443c3d8a43 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN) |
repository.mail.fl_str_mv |
|
_version_ |
1802117767489388544 |