Complex eutectic growth and Bi precipitation in ternary Sn-Bi-Cu and Sn-Bi-Ag alloys

• Autor(a) principal: Silva, Bismarck Luiz
• Data de Publicação: 2017
• Outros Autores: Garcia, Amauri, Spinelli, José Eduardo
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Institucional da UFRN
• Texto Completo: https://repositorio.ufrn.br/handle/123456789/31851
• topic: Sn-Bi-(Ag/Cu) alloys; Ternary eutectic; Solidification; Microstructure; Eutectic spacing

Sn-34 wt%Bi, Sn-34 wt%Bi-2wt%Ag and Sn-34 wt%Bi-0.7 wt%Cu alloys have been directionally solidified (DS) under a broad range of solidification cooling rates. Microstructures have been characterized with emphasis on both eutectic growth and precipitation of Bi within the β-Sn dendritic matrix. The eutectic growth, for all alloys examined, is shown to be associated with the coexistence of coarse and fine lamellar structures with different length-scale of lamellar spacing (λ). Experimental growth relations of λ vs. the cooling rate have been proposed. The length-scale of the lamellae in the fine eutectic ranges from 0.8 to 2.5 μm while in the coarse eutectic from 1.8 to 4.0 μm. Taking as reference the Sn-Bi alloy, both the spacing between Bi precipitates (λp) and the fine eutectic spacing (λfine) increase with Cu and Ag additions, whereas λcoarse remains roughly unaltered. Both ternary Sn-Bi-Ag and Sn-Bi-Cu alloys are shown to have worse distributions of both lamellae in the fine eutectic and of precipitates within Sn-rich dendrites, which resulted in decrease in hardness