Evaluation of the castability of a Co-Cr-Mo-W alloy varying the investing technique

• Autor(a) principal: Carreiro, Adriana da Fonte Porto
• Data de Publicação: 2005
• Outros Autores: Ribeiro, Ricardo Faria, Mattos, Maria da Gloria Chiarello de, Rodrigues, Renata Cristina Silveira
• Tipo de documento: Artigo
• Idioma: por
• Título da fonte: Repositório Institucional da UFRN
• Texto Completo: https://repositorio.ufrn.br/jspui/handle/123456789/20923
• topic: Castability; Chromium alloys; Investing technique

The purpose of this study was to compare the castability of Co-Cr-Mo-W (Remanium 2000), Ni-Cr (Durabond) and Co-Cr-Mo (Vera PDI) alloys invested with either conventional (phosphate- and silica-based) or mixed investing techniques. A 10 X 10 mm square-shaped nylon net containing 100 open squares served as a template for construction of wax patterns, which were invested with phosphate-based investment (Termocast), silica-based investment (Refrafil) and mixed investing technique (2-mm layer phosphate investment plus filling with silica investment). Forty-five cast specimens (5 per experimental condition) were obtained and sandblasted with aluminum oxide. The number of completely reproduced cast segments was counted to obtain a percentage designated "castability value", which indicated the accuracy of the alloy to reproduce mold details. Statistical analysis using two-way ANOVA and Tukey's test showed that, comparing the alloys, Remanium 2000 had statistically similar castability (p>0.05) to Vera PDI and lower than Durabond (p<0.05). Considering the mixed technique results, Remanium 2000 yielded lower castability value (p<0.05) than Durabond and Vera PDI alloys, which showed similar results to each other (p>0.05). In conclusion, the castability of the Co-Cr-Mo-W alloy (Remanium 2000) was comparable to that of the Co-Cr alloy (Vera PDI) and worse than that of the Ni-Cr alloy (Durabond). Except for Remanium 2000, the mixed investing technique considerably improved the accuracy of the alloys to reproduce cast details, compared to the phosphate-based investment. The mixed investing technique appears as a viable alternative to improve castability of base metal alloys without decreasing the surface quality of the metallic pieces.