Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)

Detalhes bibliográficos
Autor(a) principal: Santos, Reinan Tiago Fernandes dos
Data de Publicação: 2023
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFS
Texto Completo: https://ri.ufs.br/jspui/handle/riufs/18776
Resumo: Pure niobium specimens were processed by equiangular channel pressing (ECAP) at room temperature in 1 pass, to investigate the effect of lubricants on microstructure, processing variables and hardness homogeneity. In addition, the Nb was deformed in 1, 2, 4, 6 and 8 passes by ECAP, in an ECAP matrix with a straight channel angle (Φ = 90º) using two bending angles (Ψ = 0º and Ψ = 30º). The results showed that the lubricants: anti-seize spray with polytetrafluoroethylene tape, MoS2 grease and MoS2 grease with polytetrafluoroethylene tape showed favorable processing conditions in relation to the ECAP matrix without lubrication. The analysis of the microstructure homogeneity revealed that the banded regions, a random shear flow and the presence of dead zones were determinant in the heterogeneity along the ECAP passes. It is apparent from the analysis of the homogeneity of microstructures and Vickers hardness in the samples, that the angle of curvature had a significant influence up to 4 passes and reducing its effect up to 8 passes. Regarding the homogeneity of hardness, the data do not show variation of Vickers hardness in the two angles of curvature analyzed. After 6 passes, in both matrix configurations, the hardness values were homogeneously distributed along the deformed specimen. The processing of pure Nb by ECAP was efficient to produce a homogeneous microstructure.
id UFS-2_2fedcfc22f3ed0a1aa946bbcca3b7a82
oai_identifier_str oai:ufs.br:riufs/18776
network_acronym_str UFS-2
network_name_str Repositório Institucional da UFS
repository_id_str
spelling Santos, Reinan Tiago Fernandes dosBatista, Wilton Walter2023-12-07T14:58:55Z2023-12-07T14:58:55Z2023-08-28SANTOS, Reinan Tiago Fernandes dos. Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP). 2023. 136 f. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de Sergipe, São Cristóvão, 2023.https://ri.ufs.br/jspui/handle/riufs/18776Pure niobium specimens were processed by equiangular channel pressing (ECAP) at room temperature in 1 pass, to investigate the effect of lubricants on microstructure, processing variables and hardness homogeneity. In addition, the Nb was deformed in 1, 2, 4, 6 and 8 passes by ECAP, in an ECAP matrix with a straight channel angle (Φ = 90º) using two bending angles (Ψ = 0º and Ψ = 30º). The results showed that the lubricants: anti-seize spray with polytetrafluoroethylene tape, MoS2 grease and MoS2 grease with polytetrafluoroethylene tape showed favorable processing conditions in relation to the ECAP matrix without lubrication. The analysis of the microstructure homogeneity revealed that the banded regions, a random shear flow and the presence of dead zones were determinant in the heterogeneity along the ECAP passes. It is apparent from the analysis of the homogeneity of microstructures and Vickers hardness in the samples, that the angle of curvature had a significant influence up to 4 passes and reducing its effect up to 8 passes. Regarding the homogeneity of hardness, the data do not show variation of Vickers hardness in the two angles of curvature analyzed. After 6 passes, in both matrix configurations, the hardness values were homogeneously distributed along the deformed specimen. The processing of pure Nb by ECAP was efficient to produce a homogeneous microstructure.Corpos de prova de Nióbio foram processados por prensagem em canais equiangulares (ECAP) à temperatura ambiente em 1 passe para investigar o efeito dos lubrificantes na microestrutura, variáveis de processamento e homogeneidade de dureza. Além disso, o Nb foi deformado em 1, 2, 4, 6 e 8 passes por ECAP, em matriz ECAP com ângulo com canal reto (Φ = 90º) empregando dois ângulos de curvatura (Ψ = 0º e Ψ = 30º). Os resultados mostraram que os lubrificantes: spray desengripante com fita de politetrafluoretileno, graxa de MoS2 e graxa de MoS2 com fita de politetrafluoretileno apresentaram condições de processamento favoráveis em relação à matriz ECAP sem lubrificação. A análise da homogeneidade da microestrutura revelou que, as regiões bandeadas, um fluxo cisalhante aleatório e a presença de zonas mortas foram determinantes na heterogeneidade ao longo dos passes ECAP. É aparente pela análise da homogeneidade das microestruturas e durezas Vickers nas amostras, que o ângulo de curvatura apresentou influência significativa até 4 passes e reduzindo seu efeito até 8 passes. Em relação a homogeneidade de dureza, os dados não apresentam variação de dureza Vickers nos nos dois ângulos de curvatura analisados. A partir de 6 passes, em ambas as configurações de matriz, os valores de dureza foram distribuídos de forma homogênea ao longo do corpo de prova deformado. O processamento do Nb puro por ECAP, foi eficiente para produzir uma microestrutura homogênea.Fundação de Apoio a Pesquisa e à Inovação Tecnológica do Estado de Sergipe - FAPITEC/SESão CristóvãoporPrensas mecânicasNióbioMetais – propriedades mecânicasPrensagem em canais equiangularesÂngulo de curvatura ECAPHomogeneidade de durezaHomogeneidade microestruturalPressing in equiangular channelsPure niobiumECAP camber angleHardness homogeneityMicrostructural homogeneityENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAEfeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)Effect of bending angle on microstructural homogeneity and hardness of pure niobium processed by pressing in equiangular channels (ECAP)info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisPós-Graduação em Ciência e Engenharia de MateriaisUniversidade Federal de Sergipe (UFS)reponame:Repositório Institucional da UFSinstname:Universidade Federal de Sergipe (UFS)instacron:UFSinfo:eu-repo/semantics/openAccessLICENSElicense.txtlicense.txttext/plain; charset=utf-81475https://ri.ufs.br/jspui/bitstream/riufs/18776/1/license.txt098cbbf65c2c15e1fb2e49c5d306a44cMD51ORIGINALREINAN_TIAGO_FERNANDES_SANTOS.pdfREINAN_TIAGO_FERNANDES_SANTOS.pdfapplication/pdf9439533https://ri.ufs.br/jspui/bitstream/riufs/18776/2/REINAN_TIAGO_FERNANDES_SANTOS.pdfe4a49d764f612ffc5160221ef9b74e65MD52riufs/187762023-12-07 11:59:01.44oai:ufs.br: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Repositório InstitucionalPUBhttps://ri.ufs.br/oai/requestrepositorio@academico.ufs.bropendoar:2023-12-07T14:59:01Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS)false
dc.title.pt_BR.fl_str_mv Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
dc.title.alternative.eng.fl_str_mv Effect of bending angle on microstructural homogeneity and hardness of pure niobium processed by pressing in equiangular channels (ECAP)
title Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
spellingShingle Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
Santos, Reinan Tiago Fernandes dos
Prensas mecânicas
Nióbio
Metais – propriedades mecânicas
Prensagem em canais equiangulares
Ângulo de curvatura ECAP
Homogeneidade de dureza
Homogeneidade microestrutural
Pressing in equiangular channels
Pure niobium
ECAP camber angle
Hardness homogeneity
Microstructural homogeneity
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
title_short Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
title_full Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
title_fullStr Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
title_full_unstemmed Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
title_sort Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP)
author Santos, Reinan Tiago Fernandes dos
author_facet Santos, Reinan Tiago Fernandes dos
author_role author
dc.contributor.author.fl_str_mv Santos, Reinan Tiago Fernandes dos
dc.contributor.advisor1.fl_str_mv Batista, Wilton Walter
contributor_str_mv Batista, Wilton Walter
dc.subject.por.fl_str_mv Prensas mecânicas
Nióbio
Metais – propriedades mecânicas
Prensagem em canais equiangulares
Ângulo de curvatura ECAP
Homogeneidade de dureza
Homogeneidade microestrutural
topic Prensas mecânicas
Nióbio
Metais – propriedades mecânicas
Prensagem em canais equiangulares
Ângulo de curvatura ECAP
Homogeneidade de dureza
Homogeneidade microestrutural
Pressing in equiangular channels
Pure niobium
ECAP camber angle
Hardness homogeneity
Microstructural homogeneity
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
dc.subject.eng.fl_str_mv Pressing in equiangular channels
Pure niobium
ECAP camber angle
Hardness homogeneity
Microstructural homogeneity
dc.subject.cnpq.fl_str_mv ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
description Pure niobium specimens were processed by equiangular channel pressing (ECAP) at room temperature in 1 pass, to investigate the effect of lubricants on microstructure, processing variables and hardness homogeneity. In addition, the Nb was deformed in 1, 2, 4, 6 and 8 passes by ECAP, in an ECAP matrix with a straight channel angle (Φ = 90º) using two bending angles (Ψ = 0º and Ψ = 30º). The results showed that the lubricants: anti-seize spray with polytetrafluoroethylene tape, MoS2 grease and MoS2 grease with polytetrafluoroethylene tape showed favorable processing conditions in relation to the ECAP matrix without lubrication. The analysis of the microstructure homogeneity revealed that the banded regions, a random shear flow and the presence of dead zones were determinant in the heterogeneity along the ECAP passes. It is apparent from the analysis of the homogeneity of microstructures and Vickers hardness in the samples, that the angle of curvature had a significant influence up to 4 passes and reducing its effect up to 8 passes. Regarding the homogeneity of hardness, the data do not show variation of Vickers hardness in the two angles of curvature analyzed. After 6 passes, in both matrix configurations, the hardness values were homogeneously distributed along the deformed specimen. The processing of pure Nb by ECAP was efficient to produce a homogeneous microstructure.
publishDate 2023
dc.date.accessioned.fl_str_mv 2023-12-07T14:58:55Z
dc.date.available.fl_str_mv 2023-12-07T14:58:55Z
dc.date.issued.fl_str_mv 2023-08-28
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv SANTOS, Reinan Tiago Fernandes dos. Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP). 2023. 136 f. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de Sergipe, São Cristóvão, 2023.
dc.identifier.uri.fl_str_mv https://ri.ufs.br/jspui/handle/riufs/18776
identifier_str_mv SANTOS, Reinan Tiago Fernandes dos. Efeito do ângulo de curvatura na homogeneidade microestrutural e de dureza do nióbio puro processado por prensagem em canais equiangulares (ECAP). 2023. 136 f. Tese (Doutorado em Ciência e Engenharia de Materiais) – Universidade Federal de Sergipe, São Cristóvão, 2023.
url https://ri.ufs.br/jspui/handle/riufs/18776
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.publisher.program.fl_str_mv Pós-Graduação em Ciência e Engenharia de Materiais
dc.publisher.initials.fl_str_mv Universidade Federal de Sergipe (UFS)
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFS
instname:Universidade Federal de Sergipe (UFS)
instacron:UFS
instname_str Universidade Federal de Sergipe (UFS)
instacron_str UFS
institution UFS
reponame_str Repositório Institucional da UFS
collection Repositório Institucional da UFS
bitstream.url.fl_str_mv https://ri.ufs.br/jspui/bitstream/riufs/18776/1/license.txt
https://ri.ufs.br/jspui/bitstream/riufs/18776/2/REINAN_TIAGO_FERNANDES_SANTOS.pdf
bitstream.checksum.fl_str_mv 098cbbf65c2c15e1fb2e49c5d306a44c
e4a49d764f612ffc5160221ef9b74e65
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS)
repository.mail.fl_str_mv repositorio@academico.ufs.br
_version_ 1802110658112651264

Registros relacionados