Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142

Detalhes bibliográficos
Autor(a) principal: Gonçalves, Henrique Barbosa
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFS
Texto Completo: https://ri.ufs.br/handle/riufs/6046
Resumo: The development of techniques that minimizes the effects caused by the corrosive processes, associated with the cost benefit of ecologically viable alternatives, is replaced by more relevant to society. The objective of this work was to prepare microemulsion systems (SME) as steel corrosion inhibitors AISI 4142 from the oil of Annona muricata (Annonaceae) (Am) (Soursop), and NaCl in an aqueous solution with a concentration of 3.5%, as aqueous phase, simulating the corrosive medium. In order to stabilize the system Tween 80 was used as surfactant (T) and ethanol as a cosurfactant (TOC). The rheological properties were evaluated, the structure and the potential inhibition were analyzed by small angle X-ray scattering and electrochemical tests, respectively. Rheological measurements showed that all systems showed typical Newtonian behavior of SME and confirmed by SAXS. From application models, the results demonstrate that the microemulsions showed ellipsoidal shape "core-shell" for all SME except for samples with 70% aqueous phase, 27% oil phase and 3% surfactant which showed structures elongated cylindrical. Electrochemical tests polarization by extrapolation of Tafel plots were performed and demonstrate that all EMS had good corrosion resistance. The efficiency obtained for the samples show a percentage inhibition of 14.7% ME1, ME2 14.7%, 13.4% ME3, ME4 12.2% and 10.7% for ME5, and also evidenced an offset the most positive potential compared with curves for the solution without microemulsion. The results showed that obtained from EMS of Annona muricata (Annonaceae) oil are potential corrosion inhibitors, ME2 and 14.7% inhibition and a bend located at higher current density values, the sample showing be best inhibitor.
id UFS-2_82c115b74e5ba8f9546d68d93b4dbdca
oai_identifier_str oai:ufs.br:riufs/6046
network_acronym_str UFS-2
network_name_str Repositório Institucional da UFS
repository_id_str
spelling Gonçalves, Henrique BarbosaSarmento, Victor Hugo VitorinoCosta, Emmanoel Vilaçahttp://lattes.cnpq.br/49630157690067032017-09-27T13:57:20Z2017-09-27T13:57:20Z2016-03-07Gonçalves, Henrique Barbosa. Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142. 2016. 93 f. Dissertação (Pós-Graduação em Química) - Universidade Federal de Sergipe, São Cristóvão, 2016.https://ri.ufs.br/handle/riufs/6046The development of techniques that minimizes the effects caused by the corrosive processes, associated with the cost benefit of ecologically viable alternatives, is replaced by more relevant to society. The objective of this work was to prepare microemulsion systems (SME) as steel corrosion inhibitors AISI 4142 from the oil of Annona muricata (Annonaceae) (Am) (Soursop), and NaCl in an aqueous solution with a concentration of 3.5%, as aqueous phase, simulating the corrosive medium. In order to stabilize the system Tween 80 was used as surfactant (T) and ethanol as a cosurfactant (TOC). The rheological properties were evaluated, the structure and the potential inhibition were analyzed by small angle X-ray scattering and electrochemical tests, respectively. Rheological measurements showed that all systems showed typical Newtonian behavior of SME and confirmed by SAXS. From application models, the results demonstrate that the microemulsions showed ellipsoidal shape "core-shell" for all SME except for samples with 70% aqueous phase, 27% oil phase and 3% surfactant which showed structures elongated cylindrical. Electrochemical tests polarization by extrapolation of Tafel plots were performed and demonstrate that all EMS had good corrosion resistance. The efficiency obtained for the samples show a percentage inhibition of 14.7% ME1, ME2 14.7%, 13.4% ME3, ME4 12.2% and 10.7% for ME5, and also evidenced an offset the most positive potential compared with curves for the solution without microemulsion. The results showed that obtained from EMS of Annona muricata (Annonaceae) oil are potential corrosion inhibitors, ME2 and 14.7% inhibition and a bend located at higher current density values, the sample showing be best inhibitor.O desenvolvimento de técnicas que possam ajudar a minimizar os efeitos causados pelos processos corrosivos, associados ao custo benefício de alternativas ecologicamente viáveis, passa a ter maior relevância para a sociedade. O objetivo deste trabalho foi preparar sistemas microemulsionados (SME) como inibidores de corrosão em aço AISI 4142 a partir do óleo da Annona muricata (Annonaceae) (Am) (Graviola), tendo NaCl em uma solução aquosa com concentração de 3,5%, como fase aquosa, simulando o meio corrosivo. Para estabilização do sistema foram utilizados o Tween 80 como tensoativo (T) e etanol como cotensoativo (COT). As propriedades reológicas foram avaliadas, a estrutura e o potencial de inibição foram analisados por espalhamento de Raios X a baixo ângulo e ensaios eletroquímicos, respectivamente. As medidas reológicas mostraram que todos os sistemas apresentaram comportamento newtoniano típico de SME e confirmados por SAXS. A partir de aplicação de modelos, os resultados demonstraram que as microemulsões apresentaram formato elipsoidal “casca-caroço” para todas as amostras com exceção de SME com 70% de fase aquosa, 27% de fase oleosa e 3% de tensoativo que apresentou formato cilíndrico alongado. Ensaios eletroquímicos de polarização por extrapolação das curvas de Tafel foram realizados e demonstram que todos os SME apresentaram boa resistência à corrosão. Os valores de eficiência obtidos para as amostras apresentam percentual de inibição de 14,7% ME1, 14,7% ME2, 13,4% ME3, 12,2% ME4 e 10,7% para a ME5, sendo também evidenciado um deslocamento das curvas para potenciais mais positivos em comparação com a solução sem microemulsão. Os resultados mostraram que SME obtidos a partir do óleo da Annona muricata (Annonaceae) são potenciais inibidores de corrosão, sendo a ME2 com 14,7% de inibição e com uma curva localizada em maiores valores de densidade de corrente, a amostra que apresentou ser a melhor inibidora.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfporUniversidade Federal de SergipePós-Graduação em QuímicaUFSBrasilQuímicaReologiaAnonna muricataAnonnaceaeGraviolaEssências e óleos essenciaisSAXSAçoCorrosãoInibidor de corrosãoRheologyCorrosion inhibitorCIENCIAS EXATAS E DA TERRA::QUIMICASistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSinstname:Universidade Federal de Sergipe (UFS)instacron:UFSORIGINALHENRIQUE_BARBOSA_GONCALVES.pdfapplication/pdf10960416https://ri.ufs.br/jspui/bitstream/riufs/6046/1/HENRIQUE_BARBOSA_GONCALVES.pdf37fd63c8a316750edec805c3a67a5a02MD51TEXTHENRIQUE_BARBOSA_GONCALVES.pdf.txtHENRIQUE_BARBOSA_GONCALVES.pdf.txtExtracted texttext/plain116568https://ri.ufs.br/jspui/bitstream/riufs/6046/2/HENRIQUE_BARBOSA_GONCALVES.pdf.txt64b7c7bfc76be5a3873ee6ac35a3d64fMD52THUMBNAILHENRIQUE_BARBOSA_GONCALVES.pdf.jpgHENRIQUE_BARBOSA_GONCALVES.pdf.jpgGenerated Thumbnailimage/jpeg1470https://ri.ufs.br/jspui/bitstream/riufs/6046/3/HENRIQUE_BARBOSA_GONCALVES.pdf.jpga9f3e65db8015b18f96e1c6b84ec7954MD53riufs/60462018-01-16 19:59:41.982oai:ufs.br:riufs/6046Repositório InstitucionalPUBhttps://ri.ufs.br/oai/requestrepositorio@academico.ufs.bropendoar:2018-01-16T22:59:41Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS)false
dc.title.por.fl_str_mv Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
title Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
spellingShingle Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
Gonçalves, Henrique Barbosa
Química
Reologia
Anonna muricata
Anonnaceae
Graviola
Essências e óleos essenciais
SAXS
Aço
Corrosão
Inibidor de corrosão
Rheology
Corrosion inhibitor
CIENCIAS EXATAS E DA TERRA::QUIMICA
title_short Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
title_full Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
title_fullStr Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
title_full_unstemmed Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
title_sort Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142
author Gonçalves, Henrique Barbosa
author_facet Gonçalves, Henrique Barbosa
author_role author
dc.contributor.author.fl_str_mv Gonçalves, Henrique Barbosa
dc.contributor.advisor1.fl_str_mv Sarmento, Victor Hugo Vitorino
dc.contributor.advisor-co1.fl_str_mv Costa, Emmanoel Vilaça
dc.contributor.authorLattes.fl_str_mv http://lattes.cnpq.br/4963015769006703
contributor_str_mv Sarmento, Victor Hugo Vitorino
Costa, Emmanoel Vilaça
dc.subject.por.fl_str_mv Química
Reologia
Anonna muricata
Anonnaceae
Graviola
Essências e óleos essenciais
SAXS
Aço
Corrosão
Inibidor de corrosão
topic Química
Reologia
Anonna muricata
Anonnaceae
Graviola
Essências e óleos essenciais
SAXS
Aço
Corrosão
Inibidor de corrosão
Rheology
Corrosion inhibitor
CIENCIAS EXATAS E DA TERRA::QUIMICA
dc.subject.eng.fl_str_mv Rheology
Corrosion inhibitor
dc.subject.cnpq.fl_str_mv CIENCIAS EXATAS E DA TERRA::QUIMICA
description The development of techniques that minimizes the effects caused by the corrosive processes, associated with the cost benefit of ecologically viable alternatives, is replaced by more relevant to society. The objective of this work was to prepare microemulsion systems (SME) as steel corrosion inhibitors AISI 4142 from the oil of Annona muricata (Annonaceae) (Am) (Soursop), and NaCl in an aqueous solution with a concentration of 3.5%, as aqueous phase, simulating the corrosive medium. In order to stabilize the system Tween 80 was used as surfactant (T) and ethanol as a cosurfactant (TOC). The rheological properties were evaluated, the structure and the potential inhibition were analyzed by small angle X-ray scattering and electrochemical tests, respectively. Rheological measurements showed that all systems showed typical Newtonian behavior of SME and confirmed by SAXS. From application models, the results demonstrate that the microemulsions showed ellipsoidal shape "core-shell" for all SME except for samples with 70% aqueous phase, 27% oil phase and 3% surfactant which showed structures elongated cylindrical. Electrochemical tests polarization by extrapolation of Tafel plots were performed and demonstrate that all EMS had good corrosion resistance. The efficiency obtained for the samples show a percentage inhibition of 14.7% ME1, ME2 14.7%, 13.4% ME3, ME4 12.2% and 10.7% for ME5, and also evidenced an offset the most positive potential compared with curves for the solution without microemulsion. The results showed that obtained from EMS of Annona muricata (Annonaceae) oil are potential corrosion inhibitors, ME2 and 14.7% inhibition and a bend located at higher current density values, the sample showing be best inhibitor.
publishDate 2016
dc.date.issued.fl_str_mv 2016-03-07
dc.date.accessioned.fl_str_mv 2017-09-27T13:57:20Z
dc.date.available.fl_str_mv 2017-09-27T13:57:20Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv Gonçalves, Henrique Barbosa. Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142. 2016. 93 f. Dissertação (Pós-Graduação em Química) - Universidade Federal de Sergipe, São Cristóvão, 2016.
dc.identifier.uri.fl_str_mv https://ri.ufs.br/handle/riufs/6046
identifier_str_mv Gonçalves, Henrique Barbosa. Sistemas microemulsionados a base de Anonna muricata (Anonnaceae) como inibidores de corrosão em aço AISI 4142. 2016. 93 f. Dissertação (Pós-Graduação em Química) - Universidade Federal de Sergipe, São Cristóvão, 2016.
url https://ri.ufs.br/handle/riufs/6046
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Universidade Federal de Sergipe
dc.publisher.program.fl_str_mv Pós-Graduação em Química
dc.publisher.initials.fl_str_mv UFS
dc.publisher.country.fl_str_mv Brasil
publisher.none.fl_str_mv Universidade Federal de Sergipe
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFS
instname:Universidade Federal de Sergipe (UFS)
instacron:UFS
instname_str Universidade Federal de Sergipe (UFS)
instacron_str UFS
institution UFS
reponame_str Repositório Institucional da UFS
collection Repositório Institucional da UFS
bitstream.url.fl_str_mv https://ri.ufs.br/jspui/bitstream/riufs/6046/1/HENRIQUE_BARBOSA_GONCALVES.pdf
https://ri.ufs.br/jspui/bitstream/riufs/6046/2/HENRIQUE_BARBOSA_GONCALVES.pdf.txt
https://ri.ufs.br/jspui/bitstream/riufs/6046/3/HENRIQUE_BARBOSA_GONCALVES.pdf.jpg
bitstream.checksum.fl_str_mv 37fd63c8a316750edec805c3a67a5a02
64b7c7bfc76be5a3873ee6ac35a3d64f
a9f3e65db8015b18f96e1c6b84ec7954
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
repository.name.fl_str_mv Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS)
repository.mail.fl_str_mv repositorio@academico.ufs.br
_version_ 1802110815112790016