Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP
Autor(a) principal: | |
---|---|
Data de Publicação: | 2017 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFS |
Texto Completo: | http://ri.ufs.br/jspui/handle/riufs/7204 |
Resumo: | This work investigated the effect of different types of homogenization on the microstructure and the cold deformation behavior of Ti-35Nb-0,15Si alloy. Homogenization was performed under two conditions. Condition 1: treatment in ambient air at 1000 °C for 8, 24, 48, 72, 96 and 120 hours. Condition 2: treatment in argon atmosphere at 1000 °C for 8 hours. For the cold deformation study samples of the Ti-35Nb-0,15Si alloy and samples of Ti CP were deformed by ECAP with up to 8 passes, using the routes A and BC in a matrix with angle of intersection between the channels of Φ = 120º. The microstructural characterization was performed in the internal and external regions with the aid of optical microscopy, scanning electron microscopy and X-ray diffractograms. Vickers microhardness measurements were performed to evaluate the changes caused by deformation. In the ambient air atmosphere the samples showed the presence of the oxide layer influencing the hardness and the level of cold deformation. With the deformation of Ti-35Nb-0,15Si by ECAP it was possible to refine the structure and increase the hardness with increasing the number of passes. XRD analysis showed the presence of the α” phase induced by deformation. With the Ti CP deformed by ECAP, it was possible to analyze the microstructural evolution throughout the sample. |
id |
UFS-2_d1b6398905e854fb6852791c4ca4ce36 |
---|---|
oai_identifier_str |
oai:ufs.br:riufs/7204 |
network_acronym_str |
UFS-2 |
network_name_str |
Repositório Institucional da UFS |
repository_id_str |
|
spelling |
Silva, Késia Filadélfia DionizioBatista, Wilton Walter2018-01-16T21:54:38Z2018-01-16T21:54:38Z2017-10-04SILVA, Késia Filadélfia Dionizio. Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP. 2017. 104 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Sergipe, São Cristóvão, SE, 2017.http://ri.ufs.br/jspui/handle/riufs/7204This work investigated the effect of different types of homogenization on the microstructure and the cold deformation behavior of Ti-35Nb-0,15Si alloy. Homogenization was performed under two conditions. Condition 1: treatment in ambient air at 1000 °C for 8, 24, 48, 72, 96 and 120 hours. Condition 2: treatment in argon atmosphere at 1000 °C for 8 hours. For the cold deformation study samples of the Ti-35Nb-0,15Si alloy and samples of Ti CP were deformed by ECAP with up to 8 passes, using the routes A and BC in a matrix with angle of intersection between the channels of Φ = 120º. The microstructural characterization was performed in the internal and external regions with the aid of optical microscopy, scanning electron microscopy and X-ray diffractograms. Vickers microhardness measurements were performed to evaluate the changes caused by deformation. In the ambient air atmosphere the samples showed the presence of the oxide layer influencing the hardness and the level of cold deformation. With the deformation of Ti-35Nb-0,15Si by ECAP it was possible to refine the structure and increase the hardness with increasing the number of passes. XRD analysis showed the presence of the α” phase induced by deformation. With the Ti CP deformed by ECAP, it was possible to analyze the microstructural evolution throughout the sample.Este trabalho investigou o efeito de diferentes tipos de homogeneização sobre a microestrutura e o comportamento em deformação a frio da liga Ti-35Nb-0,15Si. A homogeneização foi realizada em duas condições. Condição 1: tratamento em atmosfera de ar ambiente na temperatura 1000 °C por 8, 24, 48, 72, 96 e 120 horas. Condição 2: tratamento em atmosfera inerte de argônio de 1000 °C por 8 horas. Para o estudo de deformação a frio, amostras da liga Ti-35Nb-0,15Si e amostras de Ti CP foram deformadas via ECAP com até 8 passes, utilizando as rotas A e BC numa matriz com ângulo de intersecção entre os canais de Φ = 120º. A caracterização microestrutural foi realizada nas regiões internas e externas com o auxílio de microscopia óptica, microscopia eletrônica de varredura e difratogramas de raios-X. Medidas de microdureza Vickers foram realizadas para avaliar as mudanças ocasionadas pela deformação. Em atmosfera de ar ambiente as amostras apresentaram a presença da camada de óxido influenciando na dureza e no nível de deformação a frio. Com a deformação de Ti-35Nb-0,15Si por ECAP foi possível refinar a estrutura e aumentar a dureza com o aumento do número de passes. A análise de DRX mostrou a presença da fase α’’ induzida por deformação. Com o Ti CP deformado por ECAP foi possível analisar a evolução microestrutural ao longo da amostra.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESSão Cristóvão, SEporMateriaisLigas de titânioMetaisPropriedades mecânicasDeformações (Mecânica)Ti-35Nb-0,15SiTi CPDeformação plásticaMicroestruturaEqual channel angular pressing (ECAP)Plastic deformationMicrostructureENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAEfeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CPEffect of the ECAP process on the microstructure and mechanical properties of Ti-35Nb-0,15Si alloy and Ti CPinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisPós-Graduação em Ciência e Engenharia de Materiaisreponame:Repositório Institucional da UFSinstname:Universidade Federal de Sergipe (UFS)instacron:UFSinfo:eu-repo/semantics/openAccessLICENSElicense.txtlicense.txttext/plain; charset=utf-81475https://ri.ufs.br/jspui/bitstream/riufs/7204/1/license.txt098cbbf65c2c15e1fb2e49c5d306a44cMD51ORIGINALKESIA_FILADELFIA_DIONIZIO_SILVA.pdfKESIA_FILADELFIA_DIONIZIO_SILVA.pdfapplication/pdf7325356https://ri.ufs.br/jspui/bitstream/riufs/7204/2/KESIA_FILADELFIA_DIONIZIO_SILVA.pdff6d55e4aceb1cf021d331011b0b67c4dMD52TEXTKESIA_FILADELFIA_DIONIZIO_SILVA.pdf.txtKESIA_FILADELFIA_DIONIZIO_SILVA.pdf.txtExtracted texttext/plain176035https://ri.ufs.br/jspui/bitstream/riufs/7204/3/KESIA_FILADELFIA_DIONIZIO_SILVA.pdf.txt87b71c372005d560144fbb3161341559MD53THUMBNAILKESIA_FILADELFIA_DIONIZIO_SILVA.pdf.jpgKESIA_FILADELFIA_DIONIZIO_SILVA.pdf.jpgGenerated Thumbnailimage/jpeg1348https://ri.ufs.br/jspui/bitstream/riufs/7204/4/KESIA_FILADELFIA_DIONIZIO_SILVA.pdf.jpg80142a921de61564426b6de9a031389dMD54riufs/72042018-01-16 18:54:38.703oai:ufs.br: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Repositório InstitucionalPUBhttps://ri.ufs.br/oai/requestrepositorio@academico.ufs.bropendoar:2018-01-16T21:54:38Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS)false |
dc.title.pt_BR.fl_str_mv |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
dc.title.alternative.eng.fl_str_mv |
Effect of the ECAP process on the microstructure and mechanical properties of Ti-35Nb-0,15Si alloy and Ti CP |
title |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
spellingShingle |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP Silva, Késia Filadélfia Dionizio Materiais Ligas de titânio Metais Propriedades mecânicas Deformações (Mecânica) Ti-35Nb-0,15Si Ti CP Deformação plástica Microestrutura Equal channel angular pressing (ECAP) Plastic deformation Microstructure ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
title_full |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
title_fullStr |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
title_full_unstemmed |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
title_sort |
Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP |
author |
Silva, Késia Filadélfia Dionizio |
author_facet |
Silva, Késia Filadélfia Dionizio |
author_role |
author |
dc.contributor.author.fl_str_mv |
Silva, Késia Filadélfia Dionizio |
dc.contributor.advisor1.fl_str_mv |
Batista, Wilton Walter |
contributor_str_mv |
Batista, Wilton Walter |
dc.subject.por.fl_str_mv |
Materiais Ligas de titânio Metais Propriedades mecânicas Deformações (Mecânica) Ti-35Nb-0,15Si Ti CP Deformação plástica Microestrutura |
topic |
Materiais Ligas de titânio Metais Propriedades mecânicas Deformações (Mecânica) Ti-35Nb-0,15Si Ti CP Deformação plástica Microestrutura Equal channel angular pressing (ECAP) Plastic deformation Microstructure ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.eng.fl_str_mv |
Equal channel angular pressing (ECAP) Plastic deformation Microstructure |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
This work investigated the effect of different types of homogenization on the microstructure and the cold deformation behavior of Ti-35Nb-0,15Si alloy. Homogenization was performed under two conditions. Condition 1: treatment in ambient air at 1000 °C for 8, 24, 48, 72, 96 and 120 hours. Condition 2: treatment in argon atmosphere at 1000 °C for 8 hours. For the cold deformation study samples of the Ti-35Nb-0,15Si alloy and samples of Ti CP were deformed by ECAP with up to 8 passes, using the routes A and BC in a matrix with angle of intersection between the channels of Φ = 120º. The microstructural characterization was performed in the internal and external regions with the aid of optical microscopy, scanning electron microscopy and X-ray diffractograms. Vickers microhardness measurements were performed to evaluate the changes caused by deformation. In the ambient air atmosphere the samples showed the presence of the oxide layer influencing the hardness and the level of cold deformation. With the deformation of Ti-35Nb-0,15Si by ECAP it was possible to refine the structure and increase the hardness with increasing the number of passes. XRD analysis showed the presence of the α” phase induced by deformation. With the Ti CP deformed by ECAP, it was possible to analyze the microstructural evolution throughout the sample. |
publishDate |
2017 |
dc.date.issued.fl_str_mv |
2017-10-04 |
dc.date.accessioned.fl_str_mv |
2018-01-16T21:54:38Z |
dc.date.available.fl_str_mv |
2018-01-16T21:54:38Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SILVA, Késia Filadélfia Dionizio. Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP. 2017. 104 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Sergipe, São Cristóvão, SE, 2017. |
dc.identifier.uri.fl_str_mv |
http://ri.ufs.br/jspui/handle/riufs/7204 |
identifier_str_mv |
SILVA, Késia Filadélfia Dionizio. Efeito do processo ECAP sobre a microestrutura e as propriedades mecânicas da liga Ti-35Nb-0,15Si e do Ti CP. 2017. 104 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal de Sergipe, São Cristóvão, SE, 2017. |
url |
http://ri.ufs.br/jspui/handle/riufs/7204 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.publisher.program.fl_str_mv |
Pós-Graduação em Ciência e Engenharia de Materiais |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFS instname:Universidade Federal de Sergipe (UFS) instacron:UFS |
instname_str |
Universidade Federal de Sergipe (UFS) |
instacron_str |
UFS |
institution |
UFS |
reponame_str |
Repositório Institucional da UFS |
collection |
Repositório Institucional da UFS |
bitstream.url.fl_str_mv |
https://ri.ufs.br/jspui/bitstream/riufs/7204/1/license.txt https://ri.ufs.br/jspui/bitstream/riufs/7204/2/KESIA_FILADELFIA_DIONIZIO_SILVA.pdf https://ri.ufs.br/jspui/bitstream/riufs/7204/3/KESIA_FILADELFIA_DIONIZIO_SILVA.pdf.txt https://ri.ufs.br/jspui/bitstream/riufs/7204/4/KESIA_FILADELFIA_DIONIZIO_SILVA.pdf.jpg |
bitstream.checksum.fl_str_mv |
098cbbf65c2c15e1fb2e49c5d306a44c f6d55e4aceb1cf021d331011b0b67c4d 87b71c372005d560144fbb3161341559 80142a921de61564426b6de9a031389d |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFS - Universidade Federal de Sergipe (UFS) |
repository.mail.fl_str_mv |
repositorio@academico.ufs.br |
_version_ |
1802110787389489152 |