Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA

Detalhes bibliográficos
Autor(a) principal: Pirola, Fernanda Carvalho
Data de Publicação: 2012
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: http://repositorio.ufsc.br/xmlui/handle/123456789/95668
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2011
id UFSC_02f27a5ad924e61d80a084060757e29b
oai_identifier_str oai:repositorio.ufsc.br:123456789/95668
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPAEngenharia civilBlocos de concretoProduçãoAvaliaçãoPavimentosDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2011A utilização de pavimentos com blocos pré-moldados de concreto de 50MPa vem crescendo nos últimos anos, fato este comprovado pelo aumento do número de fabricantes. Este aumento do consumo se deve a diversos fatores, entre eles: facilidade na execução deste pavimento, bom desempenho do mesmo frente ao uso, maior permeabilidade, grande variedade de cores e modelos, facilidade de manutenção e reciclagem. Porém, apesar desta crescente expansão, constata-se que ainda são poucas as fábricas que conseguem garantir as resistências características preconizadas pela norma NBR 9781 (ABNT, 1987) e poucos são os estudos realizados na área dos concretos #secos# utilizados na produção destas peças. Em função disso, o presente trabalho teve como objetivo principal estudar a influência de algumas variáveis do processo produtivo de PCP de 50MPa na resistência mecânica e energia de compactação destas peças. As variáveis analisadas foram: traço, teor de sólidos, teor de brita 0, umidade, tipo de areia grossa e teor de areia fina. Além disso, avaliou-se a relação entre os resultados de energia e resistência à compressão obtidos em laboratório (com corpos-de-prova 9x8cm) e os dos equipamentos de vibro-compressão. Os estudos mostraram que é possível a previsão de resistência à compressão das PCP, bem como de sua textura e energia demandadas para fabricação, através de corpos-de-prova cilíndricos de 9x8cm moldados por meio do soquete de compactação. Os resultados mostraram, ainda, que todas as variáveis estudadas influenciam significativamente na resistência a compressão e energia de compactação das PCP com nível de confiabilidade superior a 95%. A areia de britagem estudada de uma maneira geral, mostrou-se ineficiente para a fabricação de PCP de 50MPa, pois, além de não aumentar significativamente a resistência à compressão das peças, aumentou bastante a energia de compactação demandada. Também o controle da variável umidade mostrou-se de extrema importância para o alcance das propriedades desejadas. O entendimento destas influências permitiu conceber uma solução de produção de peças com menores custos, menor desgaste dos equipamentos e com o máximo de constância possível quanto a textura e resistência mecânica, mostrando que o controle destas variáveis torna-se fundamental para o alcance das exigências preconizadas por norma e para a obtenção de produtos mais homogêneos na produção de PCP com Fpk = 50 MPa.The use of pavements made from precast concrete blocks (pavers) of 50MPa has been growing in recent years, a fact borne out by the increase in the number of manufacturers. This increase in use is due to various factors, amongst them: ease of application, performance in use, greater permeability, large variety of colours and models, easy maintenance and recyclability. However, whilst there is large expansion, there continues to be few manufacturers who can guarantee the accepted and recommended resistance characteristics which conform to NBR 9781 (ABNT, 1987) and little research carried out in the area of #dry. concrete used in the production of these pieces. In response to this, the main objective of this work is to study the influence of some varied production processes of PCP 50MPa regarding mechanical resistance and the energy required to compact these pieces. The parameters analysed were: mix proportions, solids content, quantity of crushed stone, humidity, type of coarse sand and quantity of fine sand. As well as this it evaluates the relationship between energy results and compressive strength obtained in the laboratory (using 9x8cm specimens as reference) and of vibro-compression equipment. The studies demonstrate that it is possible to predict the compressive strength of PCP, as well as its texture and energy required for manufacture, using cylindrical specimens of 9x8cm, moulded through a compaction hammer as reference. Moreover the studies showed that, all the parameters studied significantly influence the compressive strength and the compaction energy of PCP with a level of reliability higher than 95%. A general study of crushed stone demonstrated its inefficiency for the manufacture of PCP 50MPa, since although not significantly increasing the resistance to the compression of the specimens tested, it significantly increased the compacting energy required. The control of moisture content was also shown to be extremely important in achieving the desired properties. Understanding these influences, is was possible to arrive at a solution for production of pavers with less cost, less stress on equipment and with the maximum possible consistency regarding texture and mechanical resistance. It was also shown that the control of these parameters becomes fundamental to comply with market demands and standard requirements for achieving the most homogeneous products in the production of PCP with Fpk = 50 MPa.Prudencio Junior, Luiz RobertoUniversidade Federal de Santa CatarinaPirola, Fernanda Carvalho2012-10-26T04:41:16Z2012-10-26T04:41:16Z2012-10-26T04:41:16Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis85 p.| il., grafs., tabs.application/pdf296868http://repositorio.ufsc.br/xmlui/handle/123456789/95668porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2013-05-02T21:00:53Zoai:repositorio.ufsc.br:123456789/95668Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732013-05-02T21:00:53Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
title Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
spellingShingle Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
Pirola, Fernanda Carvalho
Engenharia civil
Blocos de concreto
Produção
Avaliação
Pavimentos
title_short Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
title_full Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
title_fullStr Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
title_full_unstemmed Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
title_sort Contribuição para o estudo de concreto seco utilizado na fabricação de peças de concreto para pavimentação de 50MPA
author Pirola, Fernanda Carvalho
author_facet Pirola, Fernanda Carvalho
author_role author
dc.contributor.none.fl_str_mv Prudencio Junior, Luiz Roberto
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Pirola, Fernanda Carvalho
dc.subject.por.fl_str_mv Engenharia civil
Blocos de concreto
Produção
Avaliação
Pavimentos
topic Engenharia civil
Blocos de concreto
Produção
Avaliação
Pavimentos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2011
publishDate 2012
dc.date.none.fl_str_mv 2012-10-26T04:41:16Z
2012-10-26T04:41:16Z
2012-10-26T04:41:16Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 296868
http://repositorio.ufsc.br/xmlui/handle/123456789/95668
identifier_str_mv 296868
url http://repositorio.ufsc.br/xmlui/handle/123456789/95668
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 85 p.| il., grafs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808651884986105856

Registros relacionados