Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding

Detalhes bibliográficos
Autor(a) principal: Bloemer, Paulo Rafael Alberton
Data de Publicação: 2021
Tipo de documento: Trabalho de conclusão de curso
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/223482
Resumo: TCC (graduação) - Universidade Federal de Santa Catarina. Campus Joinville. Engenharia Automotiva.
id UFSC_290c3f4dfda5ea11ba70190f614cc302
oai_identifier_str oai:repositorio.ufsc.br:123456789/223482
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser claddingLaser claddingInconel 625Reparo de chanfroGroove repairTCC (graduação) - Universidade Federal de Santa Catarina. Campus Joinville. Engenharia Automotiva.O reparo de componentes metálicos de elevado custo permite trazer peças danificadas de volta a operação de uma maneira rápida, efetiva e economicamente atraente. Além disso, este processo pode estender o ciclo de vida dos componentes, através de melhorias nas propriedades superficiais, como resistência a corrosão e desgaste, via reparo ou revestimento. Este trabalho avaliou a morfologia e integridade da deposição de pó metálico da superliga de níquel - Inconel 625, sobre os substratos de aço AISI 316L, para os ângulos de chanfro de 120°, 135° e 150º. Corpos de prova com três diferentes ângulos de chanfro foram fabricados, a fim de caracterizar a distorções provenientes do processo de reparo. Foram realizadas medições por escaneamento a laser, usando o braço de medição a laser da empresa Faro, antes e depois do procedimento de reparo. Para avaliar a microestrutura e morfologia, foram conduzidas análises no microscópio ótico. A composição do material depositado na região de reparo, foi avaliada por meio da análise de Espectroscopia de Energia Dispersiva (Energy Dispersive X-ray Spectroscopy - EDS), que fica acoplada no Microscópio Eletrônico de Varredura (MEV). Foram realizadas medições de dureza Vickers no perfil transversal da deposição. Os resultados das medições de distorção mostraram que, a intensidade de distorção na direção transversal é maior longitudinal em todas as condições avaliadas. Na contabilização de descontinuidades do perfil transversal, as regiões apresentaram os valores de (0,09 %, 0,22 %, 0,39%) para os ângulos de chanfro de 150°, 135° e 120° respectivamente. A respeito da microestrutura, a amostra selecionada com chanfro de 150° mostrou uma estrutura preferencialmente dendrítica do tipo equiaxial, com crescimento de algumas estruturas dendríticas colunares. Foi verificado que, maiores ângulos de chanfro são mais apropriados com respeito a morfologia, embora favoreçam níveis de distorção mais elevados, em decorrência da maior quantidade de calor fornecida durante o processo de deposição. Em relação a dureza, foi observado que a baixa concentração de carbono suprimiu o pico característico da zona termicamente afetada.Repairing high-cost metal components allows damaged parts to be brought back into operation in a fast, effective and economically attractive way. In addition, this process can extend the life cycle of components, through improvements in surface properties, such as corrosion and wear resistance, via repair or coating. This work will evaluate the morphology and integrity of the deposition of metallic powder of the nickel superalloy - Inconel 625, on AISI 316L steel substrates, for the notch angles of 120 °, 135 ° and 150 °. Specimens with three different groove angles were manufactured in order to characterize the deformations arising from the repair process. Measurements were made by laser scanning, using the laser measurement arm of the company Faro, before and after the repair procedure. To assess the microstructure and morphology, analyzes were performed under the optical microscope. To assess the microstructure and morphology, analyzes were performed under the optical microscope. The composition of the material deposited in the repair region was evaluated through the analysis of Energy Dispersive X-ray Spectroscopy (EDS), which is attached to the Scanning Electron Microscope (SEM). Vickers hardness measurements were made in the cross section of the deposition. The results of the deformation measurements showed that the intensity of deformation in the transverse direction is greater longitudinal in all evaluated conditions. In the account of discontinuities of the transversal profile, the regions presented the values of (0.09%, 0.22%, 0.39%) for the groove angles of 150 °, 135 ° and 120 ° respectively. Regarding the microstructure, the sample selected with a chamfer of 150 ° showed a preferentially dendritic structure of the equiaxial type, with the growth of some columnar dendritic structures. It was found that greater chamfer angles are more appropriate with respect to morphology, although they favor higher levels of deformation, due to the greater amount of heat provided during the deposition process. Regarding hardness, it was observed that the low carbon concentration suppressed the characteristic peak of the thermally affected zone.Joinville, SCDutra, Gabriel BenedetTeixeira, Moisés FelipeUniversidade Federal de Santa CatarinaBloemer, Paulo Rafael Alberton2021-05-20T20:34:39Z2021-05-20T20:34:39Z2021-04-30info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesis63 f.application/pdfhttps://repositorio.ufsc.br/handle/123456789/223482info:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSC2021-05-20T20:34:40Zoai:repositorio.ufsc.br:123456789/223482Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732021-05-20T20:34:40Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
title Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
spellingShingle Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
Bloemer, Paulo Rafael Alberton
Laser cladding
Inconel 625
Reparo de chanfro
Groove repair
title_short Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
title_full Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
title_fullStr Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
title_full_unstemmed Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
title_sort Influência do ângulo de chanfro na qualidade do reparo da liga AISI 316L com Inconel 625 através de laser cladding
author Bloemer, Paulo Rafael Alberton
author_facet Bloemer, Paulo Rafael Alberton
author_role author
dc.contributor.none.fl_str_mv Dutra, Gabriel Benedet
Teixeira, Moisés Felipe
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Bloemer, Paulo Rafael Alberton
dc.subject.por.fl_str_mv Laser cladding
Inconel 625
Reparo de chanfro
Groove repair
topic Laser cladding
Inconel 625
Reparo de chanfro
Groove repair
description TCC (graduação) - Universidade Federal de Santa Catarina. Campus Joinville. Engenharia Automotiva.
publishDate 2021
dc.date.none.fl_str_mv 2021-05-20T20:34:39Z
2021-05-20T20:34:39Z
2021-04-30
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/bachelorThesis
format bachelorThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/223482
url https://repositorio.ufsc.br/handle/123456789/223482
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 63 f.
application/pdf
dc.publisher.none.fl_str_mv Joinville, SC
publisher.none.fl_str_mv Joinville, SC
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652137779953664

Registros relacionados