Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados

Detalhes bibliográficos
Autor(a) principal: Facin, Fernanda
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/215899
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2020.
id UFSC_364e04fe281892d726209d7a13140044
oai_identifier_str oai:repositorio.ufsc.br:123456789/215899
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificadosEngenharia civilAsfaltoNanocompósitos (Materiais)Cimento portlandAcabamento de superfícies (Construção civil)Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2020.Recentemente, a nanotecnologia tem sido aplicada em pesquisas na área de pavimentação, apesar do risco potencial de nanomateriais (NMs) atuarem como contaminantes através da liberação para o ambiente. Essa liberação pode ocorrer por meio do desgaste superficial dos revestimentos pela ação do tráfego, intempéries, entre outros fatores. Tendo em vista essa problemática, o objetivo deste trabalho foi simular um cenário crítico, onde há o desgaste avançado do revestimento e maior suscetibilidade de liberação de nanomateriais, através do ensaio descrito na NBR 10005:2004. Deste modo, este trabalho avaliou a toxicidade do lixiviado proveniente de revestimentos de concreto de cimento Portland (CCP) nanomodificados com TiO2 (dióxido de titânio), TiO2/WO3 (dióxido de titânio dopado com óxido de tungstênio) e ZnO (óxido de zinco), e de revestimentos de concreto asfáltico (CA) (ligante CAP 50-70) nanomodificados com NTC (nanotubo de carbono) e NA (nano-argila montmorilonita). Após a obtenção do lixiviado, foram realizados ensaios de toxicidade aguda e crônica com o microcrustáceo Daphnia magna e toxicidade com a macrófita aquática Landoltia punctata, ambos de água doce. Os resultados demonstraram baixa toxicidade tanto no teste agudo quando no teste crônico com a D. magna. Nos testes crônicos com D. magna, parâmetros como longevidade e idade da primeira postura, não foram afetados pelos lixiviados contendo NMs, já o parâmetro tamanho teve efeito significativo com o lixiviado do revestimento de referência CCP (sem NM), e a reprodução foi afetada pelos lixiviados de CCP nanomodificados com TiO2/WO3 e ZnO. Tais resultados indicam a possibilidade de outros materiais presentes na mistura causarem efeitos negativos nos organismos. A L. punctata demonstrou menor sensibilidade aos lixiviados do que a D. magna, com todas as CE50 > 180 mL/L, demonstrando que as amostras de lixiviado não são tóxicas para a L. punctata nas condições testadas. As causas dos efeitos toxicológicos não puderam ser verificadas, contudo há indícios de que os NMs não foram responsáveis pelos efeitos, uma vez que o ICP-MS e FTIR demonstraram que grande parte dos NMs incorporados nos revestimentos permaneceu aderida mesmo após o processo de lixiviação.Abstract: Recently, nanotechnology has been applied to paving research, despite the potential risk of nanomaterials (NMs) acting as contaminants through release to the environment. This release can occur through the superficial wear of the coatings by the action of traffic, weather, among other factors. In view of this problem, the the objective of this work was to simulate a critical scenario, where there is an advanced wear of the coating and greater susceptibility to release of NMs, through the test described in NBR 10005:2004. Thus, this work evaluated the toxicity of leachate from nanomodified Portland cement concrete (CCP) coatings with TiO2 (titanium dioxide), TiO2/WO3 (titanium dioxide doped with tungsten oxide) and ZnO (zinc oxide), and asphalt concrete (CA) coatings (CAP 50-70 binder) nanomodified with NTC (carbon nanotube) and NA (nano-clay montmorillonite). After obtaining the leachate, acute and chronic toxicity tests were performed with the micro-crustacean Daphnia magna and toxicity with the aquatic macrophyte Landoltia punctata, both freshwater. The results showed low toxicity both in the acute test and in the chronic test with D. magna. In chronic tests with D. magna, parameters such as longevity and time until the first brood, were not affected by leachate containing NMs, whereas the size parameter had a significant effect with the leachate from the CCP reference coating (without NM), and reproduction was affected by the nanomodified CCP leachate. with TiO2/WO3 and ZnO. Such results indicate the possibility of other materials present in the mixture causing negative effects on the organisms. A L. punctata showed less sensitivity to leachate than D. magna, with all CE50>180 mL/L, demonstrating that the leachate samples are not toxic to L. punctata under the conditions tested. The causes of the toxicological effects could not be verified, however there is evidence that the NMs were not responsible for the effects, since the ICP-MS and FTIR demonstrated that a large part of the NMs incorporated in the coatings remained adhered even after the leaching process.Melo, João Victor Staub deMatias, William GersonUniversidade Federal de Santa CatarinaFacin, Fernanda2020-10-21T21:23:19Z2020-10-21T21:23:19Z2020info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis127 p.| il., tabs.application/pdf370227https://repositorio.ufsc.br/handle/123456789/215899porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2020-10-21T21:23:19Zoai:repositorio.ufsc.br:123456789/215899Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732020-10-21T21:23:19Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
title Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
spellingShingle Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
Facin, Fernanda
Engenharia civil
Asfalto
Nanocompósitos (Materiais)
Cimento portland
Acabamento de superfícies (Construção civil)
title_short Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
title_full Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
title_fullStr Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
title_full_unstemmed Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
title_sort Avaliação da toxicidade sob landoltia punctata e daphnia magna de lixiviados de revestimentos asfálticos e de concreto de cimento Portland nanomodificados
author Facin, Fernanda
author_facet Facin, Fernanda
author_role author
dc.contributor.none.fl_str_mv Melo, João Victor Staub de
Matias, William Gerson
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Facin, Fernanda
dc.subject.por.fl_str_mv Engenharia civil
Asfalto
Nanocompósitos (Materiais)
Cimento portland
Acabamento de superfícies (Construção civil)
topic Engenharia civil
Asfalto
Nanocompósitos (Materiais)
Cimento portland
Acabamento de superfícies (Construção civil)
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2020.
publishDate 2020
dc.date.none.fl_str_mv 2020-10-21T21:23:19Z
2020-10-21T21:23:19Z
2020
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 370227
https://repositorio.ufsc.br/handle/123456789/215899
identifier_str_mv 370227
url https://repositorio.ufsc.br/handle/123456789/215899
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 127 p.| il., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652194852896768

Registros relacionados