Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM

Detalhes bibliográficos
Autor(a) principal: Rauber, Gabrielle Branco
Data de Publicação: 2019
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/206259
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2019
id UFSC_3aea787812abb241ba7aeb7ce04c2225
oai_identifier_str oai:repositorio.ufsc.br:123456789/206259
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAMOdontologiaCoroas (Odontologia)Materiais dentáriosFadigaTese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2019O objetivo deste estudo foi avaliar a influência do desenho de término do preparo (vertical versus horizontal) na resistência à fadiga de coroas CAD/CAM de cerâmica vítrea reforçada com dissilicato de lítio (IPS e.max CAD) e resina composta (Shofu Block HC). Cinquenta terceiros molares superiores humanos de três cúspides foram selecionados e divididos em 5 grupos (n = 10) de acordo com o desenho do término e material restaurador utilizado na confecção da coroa: GC - Grupo controle: dentes hígidos; GHD - Término horizontal + cerâmica vítrea reforçada com dissilicato de lítio; GHR - Término horizontal +resina composta CAD/CAM; GVD - Término vertical + cerâmica vítrea reforçada com dissilicato de lítio; GVR - Término vertical + resina composta CAD/CAM. Os dentes receberam preparos para coroa padronizados conforme o desenho do término. Após, os preparos foram escaneados e as coroas fabricadas por meio da tecnologia CAD/CAMcom anatomia e espessura padrão de 1 mm axial e de 1,5 a 2,0 mm oclusal. As coroas foram cimentadas com o cimento resinoso autopolimerizável Multilink N e a presença de trincas avaliada 24 h após a cimentação por meio de fotografias das amostras transiluminadas. As amostras foram submetidas ao ensaio de resistência à fadiga comfrequência de 5 Hz e carregamento de 200 N por 5.000 ciclos, seguido por cargas de 400, 600, 800, 1000, 1200 e 1400 N por 30.000 ciclos cada, totalizando 185.000 ciclos. A análise estatística foi realizada por meio da curva de sobrevivência de Kaplan-Meier e teste Log-hank. O modo de fratura foi avaliado e as amostras sobreviventes novamenteforam transiluminadas para avaliação da presença de trincas. Nenhum dos grupos obteve 100% de sobrevivência. A comparação individual dos grupos GHD (80%) e GVD (30%) apresentou diferença significativa na sobrevivência das amostras (p<0,05). Todas as amostras sobreviventes de GVD apresentaram trincas, sendo estas maiores do que 3 mm. Além disso, todas as fraturas foram classificadas como favoráveis, exceto para uma amostra de GHD. Concluiu-se que o preparo com término vertical influenciou na resistência à fadiga de coroas de cerâmica vítrea reforçada com dissilicato de lítio, porém não influenciou na resistência à fadiga das coroas de resina composta CAD/CAM. Coroas de dissilicato de lítio com término vertical apresentam propensão ao desenvolvimentode trincas. Além disso, a fratura das coroas não afetou o substrato dental, sendo favorável a confecção de uma nova coroa.Abstract: The aim of this study was to evaluate the influence of the cervical margin design (vertical versus horizontal) on fatigue strength of lithium disilicate glass ceramic (IPS e.max CAD) and composite resin (Shofu Block HC) CAD/CAM crowns. Fifty three cusp maxillary molars third were selected and divided into 5 groups (n = 10) according to margin design and crown restorative material: GC - Control group: higid teeth; GHD - Horizontal margin + lithium disilicate; GHR - Horizontal margin + composite resin; GVD - Vertical margin + lithium disilicate; GVR - Vertical margin + composite resin. The samples received standardized crown preparations according to the margin design. The preparations were scanned and the crowns manufactured using CAD/CAM technology with anatomy and standard thickness of 1 mm axial and between 1.5 to 2.0 mm occlusal. The crowns were luted using Multilink N resin cement and the presence of cracks evaluated 24 h after cementation by photographs of the transilluminated samples. The fatigue stress test were executed at a frequency of 5 Hz and loading at 200 N for 5,000 cycles, followed by 400, 600, 800, 1000, 1200 and 1400 N per 30,000 cycles, completing 185,000 cycles. Statistical analysis was performed using the Kaplan-Meier survival curve and Log-hank test. The fracture mode was evaluated and surviving samples were transilluminated to evaluate the presence of cracks. None of the groups achieved 100% survival. The individual comparison of the groups GHD (80%) and GVD (30%) showed a significant difference in the survival ofthe samples (p <0.05). All surviving GVD samples showed cracks, and this were greater than 3 mm. All the samples presented fractures classified as favorable, except one sample of GHD. It was concluded that the vertical margin design influence the fatigue strength of lithium disilicate glass ceramic crowns, but did not influence the fatigue resistance of composite resin crowns. Lithium disilicate glass ceramic crowns with vertical termination tend to be prone to crack development. In addition, the fracture of the crowns did not affect the dental substrate, being favorable to the execution of a new crown.Baratieri, Luiz NarcisoUniversidade Federal de Santa CatarinaRauber, Gabrielle Branco2020-03-31T15:09:14Z2020-03-31T15:09:14Z2019info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis102 p.| il., gráfs., tabs.application/pdf361000https://repositorio.ufsc.br/handle/123456789/206259porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2020-03-31T15:09:14Zoai:repositorio.ufsc.br:123456789/206259Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732020-03-31T15:09:14Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
title Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
spellingShingle Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
Rauber, Gabrielle Branco
Odontologia
Coroas (Odontologia)
Materiais dentários
Fadiga
title_short Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
title_full Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
title_fullStr Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
title_full_unstemmed Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
title_sort Preparo vertical versus horizontal : influência na resistência à fadiga de coroas CAD/CAM
author Rauber, Gabrielle Branco
author_facet Rauber, Gabrielle Branco
author_role author
dc.contributor.none.fl_str_mv Baratieri, Luiz Narciso
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Rauber, Gabrielle Branco
dc.subject.por.fl_str_mv Odontologia
Coroas (Odontologia)
Materiais dentários
Fadiga
topic Odontologia
Coroas (Odontologia)
Materiais dentários
Fadiga
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2019
publishDate 2019
dc.date.none.fl_str_mv 2019
2020-03-31T15:09:14Z
2020-03-31T15:09:14Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 361000
https://repositorio.ufsc.br/handle/123456789/206259
identifier_str_mv 361000
url https://repositorio.ufsc.br/handle/123456789/206259
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 102 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652329995468800

Registros relacionados