Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser

Detalhes bibliográficos
Autor(a) principal: Bandeira, Vítor Freire
Data de Publicação: 2021
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/229154
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2021.
id UFSC_4affaf6c80833aefd84b1aa6e45d3fc0
oai_identifier_str oai:repositorio.ufsc.br:123456789/229154
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaBandeira, Vítor FreireMikowski, Alexandre2021-10-14T19:29:19Z2021-10-14T19:29:19Z2021373310https://repositorio.ufsc.br/handle/123456789/229154Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2021.Este trabalho trata da caracterização de corpos de prova retirados de uma estrutura interna soldada a laser de um trocador de calor casco-placa (Plate and Shell Heat Exchanger - PSHE) e propõe um tratamento térmico para alívio de tensões residuais (decorrentes dos processos de laminação e soldagem), cuja duração é de uma hora a 455 ? em forno mufla. O material do qual são fabricadas as placas é um aço inoxidável austenítico de baixo teor de carbono (AISI 316L). Por meio de técnicas de microscopia óptica e eletrônica de varredura, pontos de concentração de tensão, decorrentes do processo de capilaridade da zona fundida, foram observados na região de junta da solda. Após o processo de tratamento térmico, ocorreu a formação de carbetos de cromo, em pequena quantidade, principalmente na região de interface e metal solda. Na matriz austenítica do material base, houve redução nas marcas de laminação, além de maior definição dos contornos de grãos. Além do mais, após o processo térmico para alívio de tensões, verificou-se que há aumento no valor médio da dureza Vickers (de 186 GPa para 1,94 GPa) e na dureza média obtida por nanoindentação instrumentada (de 2,10 GPa para 2,42 GPa). Ainda, a média do módulo de elasticidade do material passou de 184,81 GPa para 199,17 GPa após o tratamento térmico. Alterações nas impressões obtidas pelo ensaio de risco, como desprendimento de material ao redor das trilhas, indicam um decréscimo na ductilidade do material após o tratamento, bem como um acréscimo na resistência à deformação plástica. Caracterizou-se também a estrutura soldada por meio de ensaios mecânicos de tração não convencionais antes e após o processo de tratamento térmico, obtendo um comportamento de maior resistência às solicitações mecânicas. Cabe ressaltar que novas geometrias de corpos de prova foram propostas para realização dos ensaios mecânicos de tração. O limite de resistência à tração da condição \"como recebida\", em que a linha do cordão de solda é perpendicular ao sentido de tração longitudinal, foi validado, confirmando a efetividade do ensaio proposto. Finalmente, por meio destas análises comparativas, entendeu-se que o tratamento térmico para alívio de tensões pode viabilizar melhorias no comportamento mecânico da estrutura de placas corrugadas e soldadas a laser de aço AISI 316L.Abstract: This work addresses the characterization of specimens taken from an internal structure welded by laser of a Plate and Shell Heat Exchanger (PSHE) and proposes a thermal treatment to relieve residual stresses (due to the lamination and welding processes), whose duration is one hour at 455 ? in a muffle furnace. The material from which the plates are manufactured is a low carbon austenitic stainless steel (AISI 316L). Through optical and scanning electron microscopy techniques, stress concentration points, resulting from the capillary process of the molten zone, were observed in the weld joint region. After the heat treatment process, a small amount of chromium carbides was formed, mainly in the interface and weld metal region. In the austenitic matrix of the base material, there was a reduction in the rolling marks, in addition to a greater definition of grain boundaries. Furthermore, after the thermal process for stress relief, it was found that there is an increase in the mean value of Vickers hardness (from 186 GPa to 1.94 GPa) and in the mean hardness obtained by instrumented nanoindentation (from 2.10 GPa to 2.42 GPa). Also, the mean modulus of elasticity of the material went from 184.81 GPa to 199.17 GPa after heat treatment. Changes in the impressions obtained by the scratch test, such as material detachment around the tracks, indicate a decrease in the ductility of the material after treatment, as well as an increase in the resistance to plastic deformation. The welded structure was also characterized through non-conventional mechanical tensile tests before and after the heat treatment process, obtaining a behavior of greater resistance to mechanical stresses. It is noteworthy that new geometries of specimens were proposed to carry out the mechanical tensile tests. The tensile strength limit of the \"as-received\" condition, in which the weld bead line is perpendicular to the longitudinal tensile direction, was validated, confirming the effectiveness of the proposed test. Finally, through these comparative analyses, it was understood that the heat treatment for stress relief can enable improvements in the mechanical behavior of the structure of corrugated and laser welded plates of AISI 316L steel.102 p.| il., gráfs.porEngenharia mecânicaAço inoxidávelSolda e soldagemPermutadores térmicosCaracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laserinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINALPPCM0087-D.pdfPPCM0087-D.pdfapplication/pdf41552915https://repositorio.ufsc.br/bitstream/123456789/229154/-1/PPCM0087-D.pdf20cfea46b10e64dabb4d698f78cf79dfMD5-1123456789/2291542021-10-14 16:29:19.717oai:repositorio.ufsc.br:123456789/229154Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732021-10-14T19:29:19Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
title Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
spellingShingle Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
Bandeira, Vítor Freire
Engenharia mecânica
Aço inoxidável
Solda e soldagem
Permutadores térmicos
title_short Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
title_full Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
title_fullStr Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
title_full_unstemmed Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
title_sort Caracterização de placas de aço inoxidável AISI 316L corrugadas e soldadas a laser
author Bandeira, Vítor Freire
author_facet Bandeira, Vítor Freire
author_role author
dc.contributor.none.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Bandeira, Vítor Freire
dc.contributor.advisor1.fl_str_mv Mikowski, Alexandre
contributor_str_mv Mikowski, Alexandre
dc.subject.classification.none.fl_str_mv Engenharia mecânica
Aço inoxidável
Solda e soldagem
Permutadores térmicos
topic Engenharia mecânica
Aço inoxidável
Solda e soldagem
Permutadores térmicos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2021.
publishDate 2021
dc.date.accessioned.fl_str_mv 2021-10-14T19:29:19Z
dc.date.available.fl_str_mv 2021-10-14T19:29:19Z
dc.date.issued.fl_str_mv 2021
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/229154
dc.identifier.other.none.fl_str_mv 373310
identifier_str_mv 373310
url https://repositorio.ufsc.br/handle/123456789/229154
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 102 p.| il., gráfs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/229154/-1/PPCM0087-D.pdf
bitstream.checksum.fl_str_mv 20cfea46b10e64dabb4d698f78cf79df
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766805366367059968

Registros relacionados