Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril

Detalhes bibliográficos
Autor(a) principal: Santos, Vinícius Oliveira dos
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/215843
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2020.
id UFSC_4c2909aa6ea95c1afd2b7d9c9ee2f980
oai_identifier_str oai:repositorio.ufsc.br:123456789/215843
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadrilEngenharia mecânicaArtroplastia total do quadrilParticulasIonsDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2020.Os íons e partículas metálicas, provenientes da degradação de próteses de quadril, induzem reações teciduais adversas, tornando necessária a realização da cirurgia de revisão da artroplastia total do quadril. A degradação ocorre principalmente pelo mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril. O objetivo do presente trabalho é investigar a degradação gerada pelo mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril por meio de análises in vitro e in silico, buscando identificar quais das superfícies de contato é a mais degradada e qual é a potencialmente mais nociva ao corpo humano. Para tanto, foram realizadas análises de dureza, de composição química, dimensional e de superfície na haste e na cabeça, ensaios in vitro da degradação da superfície de contato haste-cabeça e haste-cimento e análise in silico para mensuração da tensão de contato e micromovimentação. Os ensaios in vitro foram realizados com monitoramento eletroquímico, e, após o ensaio, foram analisados os íons, as partículas e os mecanismos de fretting-corrosion. Os resultados da análise eletroquímica demonstraram que a superfície de contato haste-cimento sofreu uma maior degradação por fretting-corrosion. A maior perda de massa do corpo da haste, identificada na análise eletroquímica, foi confirmada pela análise de íons totais. A maior degradação da superfície de contato haste-cimento provavelmente está relacionada a maior micromovimentação nessa superfície. Esta hipótese é corroborada pelos resultados in silico aqui obtidos, onde os resultados foram compatíveis também com outros resultados de ensaios in vitro da literatura. Os mecanismos associados à degradação por fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento avaliadas in vitro foram semelhantes aos identificados em análises de explantes. A similaridade dos mecanismos in vitro e in vivo possibilitam a correlação da degradação observada in vitro com a degradação que ocorreria in vivo. Desta forma, parece que a maior degradação da superfície de contato haste-cimento pode ser o principal motivador para as reações teciduais adversas identificadas in vivo, fato que contrasta com a maioria das pesquisas atuais.Abstract: Metal ions and debris generates from the degradation of hip prostheses, induce adverse tissue reactions, and the need for total hip arthroplasty revision. The degradation occurs mainly by the fretting-corrosion mechanism at the stem-head and stem-cement interface of hip prostheses. The present work aims to investigate the degradation generated by the fretting-corrosion mechanism at the stem-head and stem-cement interface of hip prostheses by in vitro and in silico analysis to identify which interface is the most degraded and is the most potentially harmful to the human body. For this purpose, analyzes of hardness, chemical, dimensional, and surface composition were carried out on the stem and head, in vitro tests of the degradation of the stem-head and stem-cement interface, and in silico analysis to measure contact pressure and micromotion. The in vitro tests were performed with electrochemical monitoring, and after the test was analyzed metal ions, debris, and the fretting-corrosion mechanisms. The results of the electrochemical analysis demonstrated that the stem-cement interface was the most degraded by fretting-corrosion. The greater mass loss of the stem body, identified in the electrochemical analysis, was confirmed by the analysis of total ions. The greater degradation of the stem-cement interface probably correlates with the greater micromotion at this interface. This hypothesis is corroborated by the in silico results obtained here, where the results were also similar to other in vitro results from the literature. The mechanisms associated with fretting-corrosion degradation on the stem-head and stem-cement interface evaluated by in vitro were similar to those identified in retrieval analysis. The similarity of the in vitro and in vivo mechanisms makes it possible to correlate the degradation observed in vitro with the degradation that would occur in vivo. Thus, it seems that the greater degradation of the stem-cement interface may be the main reason for the adverse tissue reactions identified in vivo, a fact that contrasts with most current research.Roesler, Carlos Rodrigo de MelloOrtega Cubillos, PatríciaUniversidade Federal de Santa CatarinaSantos, Vinícius Oliveira dos2020-10-21T21:22:36Z2020-10-21T21:22:36Z2020info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis187 p.| il., gráfs.application/pdf370478https://repositorio.ufsc.br/handle/123456789/215843porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2020-10-21T21:22:36Zoai:repositorio.ufsc.br:123456789/215843Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732020-10-21T21:22:36Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
title Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
spellingShingle Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
Santos, Vinícius Oliveira dos
Engenharia mecânica
Artroplastia total do quadril
Particulas
Ions
title_short Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
title_full Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
title_fullStr Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
title_full_unstemmed Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
title_sort Análise experimental e numérica do mecanismo de fretting-corrosion nas superfícies de contato haste-cabeça e haste-cimento de próteses de quadril
author Santos, Vinícius Oliveira dos
author_facet Santos, Vinícius Oliveira dos
author_role author
dc.contributor.none.fl_str_mv Roesler, Carlos Rodrigo de Mello
Ortega Cubillos, Patrícia
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Santos, Vinícius Oliveira dos
dc.subject.por.fl_str_mv Engenharia mecânica
Artroplastia total do quadril
Particulas
Ions
topic Engenharia mecânica
Artroplastia total do quadril
Particulas
Ions
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2020.
publishDate 2020
dc.date.none.fl_str_mv 2020-10-21T21:22:36Z
2020-10-21T21:22:36Z
2020
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 370478
https://repositorio.ufsc.br/handle/123456789/215843
identifier_str_mv 370478
url https://repositorio.ufsc.br/handle/123456789/215843
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 187 p.| il., gráfs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652230464634880

Registros relacionados