Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose

Detalhes bibliográficos
Autor(a) principal: Sornas, Jéssica Jenifer
Data de Publicação: 2018
Tipo de documento: Trabalho de conclusão de curso
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/191441
Resumo: TCC(graduação) - Universidade Federal de Santa Catarina. Campus Blumenau. Engenharia Têxtil
id UFSC_50c8da0c32f88fb4534fc00e00ffcdd7
oai_identifier_str oai:repositorio.ufsc.br:123456789/191441
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celuloseNanocristais de celuloseAlgodãoBeneficiamentoTCC(graduação) - Universidade Federal de Santa Catarina. Campus Blumenau. Engenharia TêxtilA nanotecnologia é um ramo de extrema importância, pois possibilita a obtenção de nanomateriais com propriedades únicas e diferenciadas. Assim, a obtenção e aplicação desses nanomateriais têm sido intensivamente estudadas em diversos segmentos. Um nanomaterial que possui excelentes características e grande potencial para aplicação em compósitos é o nanocristal de celulose, sendo biodegradável, de fácil obtenção, com alta resistência mecânica, cristalinidade, possibilidade de auto-montagem e modificação química da superfície, entre tantas outras propriedades. Para obter-se os nanocristais de celulose podem ser utilizadas variadas fontes celulósicas encontradas na natureza. Neste trabalho estudou-se cinco tipos de algodões como fonte, sendo a diferença entre eles o beneficiamento químico utilizado. Dessa forma, o objetivo geral deste trabalho é estudar a influência do beneficiamento químico do algodão na obtenção e caracterização dos nanocristais de celulose. Os beneficiamentos químicos realizados a partir de fita de algodão cru foram a purga, o alvejamento e a caustificação. Além destes, uma fita de carda alvejada industrialmente foi utilizada. Para a extração dos nanocristais de celulose utilizou-se hidrólise ácida com solução de ácido sulfúrico 64% m., temperatura de 45 ºC e tempo de 45 minutos. Foram realizadas também caracterizações das amostras de algodão beneficiadas e dos nanocristais formados. As amostrasalvejadas apresentaram coloração esbranquiçada e as demaiscontinuaramcom coloração amarelada semelhante a fita de carda de algodão cru. Notou-se alteração da seção longitudinal do algodão que foi caustificado em relação aos outros algodões, devido à mudança do alomorfismo da celulose. As nanoceluloses obtidas apresentaram alta cristalinidade (>80%), estrutura cristalina de celulose I e dimensões entre 100 e 360 nm, sendo os menores valores observados quando utilizou-se as fontes celulósicas alvejadas. A nanocelulose obtida do algodão cru foi a mais estável em suspensão e com maior cristalinidade, porém a com maior dimensão. Os nanocristais de celulose das amostras de algodão alvejado obtiveram o formato de agulhas que era esperado para a nanocelulose. De forma geral conclui-se que os tratamentos químicos dos algodões influenciam na nanocelulose formada, pois alteram aspecto, dimensão e estabilidade dos nanocristais. Devido ao menor tamanho e adequadas cristalinidade e estabilidade, o algodão alvejado apresenta maior potencial para estudos em compósitos.Nanotechnology is a branch of extreme importance because it makes it possible to obtain nanomaterials with unique and differentiated properties. Thus, the obtaining and application of these nanomaterials has been highly studied in several fields. A nanomaterial that has excellent properties and great potential for the application in composites is the cellulose nanocrystal, being biodegradable, easy to obtain, with high mechanical resistance, crystallinity, possibility of self-assembly and surface chemistry modification, among many other properties. In order to obtain cellulose nanocrystals, various cellulosic sources found in nature can be used. In this work, five types of cottons with different chemical beneficiation were studied as source. Thus, the general objective of this work is to study the influence of cotton chemical processing on the production and characterization of cellulose nanocrystals. The chemical treatments made from carded cotton were purging, bleaching and causticizing. In addition, industrially bleached card strip was used. For the extraction of the cellulose nanocrystals, acid hydrolysis with sulfuric acid solution (64% m.) was performed at temperature of 45 °C for 45 minutes. Characterization of the beneficiated cottons and the formed nanocrystals were also carried out. The cottons submitted to bleaching showed whitish coloring while samples with purge and causticizing remained with yellowish coloration, similar to raw cotton card ribbon. It was noticed a change in the longitudinal section of the cotton that was causticized in relation to the other cottons, due to a change in the alomorphism of the cellulose. The obtained nanocellulose had high crystallinity (> 80%), crystalline structure of cellulose I and dimensions between 100 and 360 nm, being the smaller values observed when the cellulosic sources bleached were used. The nanocellulose obtained from raw cotton was the most stable and with the highest crystallinity, but the largest one. The cellulose nanocrystals of the bleached cottons showed the format of needles that were expected for the nanocellulose. In general, it is concluded that the chemical treatments of the cottons influence the formed nanocellulose formed, because they alter the appearance, dimension and stability of the nanocrystals. Due to the smaller size and adequate crystallinity and stability, the bleached cotton presents greater potential for further studies on composites.Blumenau, SCBierhalz, Andrea Cristiane KrauseAguiar, Catia Rosana Lange deUniversidade Federal de Santa CatarinaSornas, Jéssica Jenifer2018-11-21T16:14:53Z2018-11-21T16:14:53Z2018-08-07info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesis61 fapplication/pdfhttps://repositorio.ufsc.br/handle/123456789/191441info:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSC2018-11-21T16:14:56Zoai:repositorio.ufsc.br:123456789/191441Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732018-11-21T16:14:56Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
title Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
spellingShingle Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
Sornas, Jéssica Jenifer
Nanocristais de celulose
Algodão
Beneficiamento
title_short Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
title_full Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
title_fullStr Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
title_full_unstemmed Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
title_sort Influência do beneficiamento químico do algodão na obtenção e caracterização de nanocristais de celulose
author Sornas, Jéssica Jenifer
author_facet Sornas, Jéssica Jenifer
author_role author
dc.contributor.none.fl_str_mv Bierhalz, Andrea Cristiane Krause
Aguiar, Catia Rosana Lange de
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Sornas, Jéssica Jenifer
dc.subject.por.fl_str_mv Nanocristais de celulose
Algodão
Beneficiamento
topic Nanocristais de celulose
Algodão
Beneficiamento
description TCC(graduação) - Universidade Federal de Santa Catarina. Campus Blumenau. Engenharia Têxtil
publishDate 2018
dc.date.none.fl_str_mv 2018-11-21T16:14:53Z
2018-11-21T16:14:53Z
2018-08-07
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/bachelorThesis
format bachelorThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/191441
url https://repositorio.ufsc.br/handle/123456789/191441
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 61 f
application/pdf
dc.publisher.none.fl_str_mv Blumenau, SC
publisher.none.fl_str_mv Blumenau, SC
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652364311166976

Registros relacionados