Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores

Detalhes bibliográficos
Autor(a) principal: Luciano, Rosita Manoel
Data de Publicação: 2023
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/251865
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2023.
id UFSC_5c0f403a8ed28a32578a44520658ba4a
oai_identifier_str oai:repositorio.ufsc.br:123456789/251865
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutoresCiência dos materiaisEngenharia de materiaisLátexPolímeros condutoresPolimerização em emulsãoTese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2023.Nesta tese de doutorado, dispersões aquosas de nanopartículas condutoras de poli (acrilato de butila-co-estireno) (PABS), com as mesmas proporções monoméricas e condições experimentais, mas variando as concentrações de polianilina (PANI), foram produzidas pela polimerização in situ da anilina (ANI) na presença da emulsão de PABS e pela mistura física da PANI no látex. Os polímeros foram produzidos pelo método de polimerização em emulsão semeada e alimentada a 80°C, sob atmosfera de nitrogênio e usando persulfato de sódio como iniciador. Foi investigado o método de preparação do látex mais adequado para estabilizar a PANI na dispersão aquosa. Os látices obtidos se apresentaram com uma estreita curva de distribuição de tamanho de partículas, com valores de potencial zeta (?) negativos e inferiores a -25 mV que indicam partículas estáveis na dispersão devido à repulsão entre partículas causadas pela elevada carga superficial, o que evita formação agregados ao longo do tempo. Os látices na forma de filmes ?livres? obtidos pela polimerização in situ da anilina na emulsão de PABS e mistura física da polianilina no látex apresentaram valores de condutividade elétrica de 5,9 x 10-3 S.cm-1 e 1,9 x 10-5 S.cm-1 para concentrações de 3% m de PANI, respectivamente. As dispersões aquosas na forma que se encontram foram aplicadas sobre aço carbono 1020 lixado para avaliação da aderência e desempenho anticorrosivo. Os látices apresentaram boa aderência a seco, por apresentar temperatura de transição vítrea que indica que o látex desenvolvido apresenta boas propriedades de formação de filme, mas com restrições no desempenho de aderência á úmido que comprometeram as propriedades anticorrosivas. As características de adesão, propriedades eletroquímicas e térmicas da mistura de PABS contendo PANI não foram impactadas pelo método de preparação do látex. Nas micrografias de AFM e MEV foi possível verificar que as dispersões aquosas, desenvolvidas através da polimerização in situ, apresentaram maior homogeneidade nos filmes. As medidas de impedância mostraram que as amostras com incorporação de 1% m de PANI apresentaram melhores propriedades anticorrosivas, provavelmente em função a falhas no efeito barreira produzido pelo revestimento com PANI 3% m, da baixa aderência à úmido e/ou a camada de óxidos férricos produzidos pela atuação eletroquímica da PANI contida no revestimento ou a carga de DBSA, que deve sensibilizar o filme. As dispersões aquosas desenvolvidas neste trabalho apresentam potencial de aplicação para uso em revestimentos contra a corrosão, evidenciados nos ensaios eletroquímicos, em que se recomenda a polimerização in situ como melhor método de obtenção, indicando maior estabilidade, condutividade elétrica e homogeneidade do filme de látex produzido.Abstract: In this doctoral thesis, aqueous dispersions of conductive poly m(butyl-co-styrene acrylate) nanoparticles (PABS), with the same monomeric proportions and experimental conditions, but varying concentrations of polyaniline (PANI), were produced by in situ polymerization of aniline (ANI) in the presence of the PABS emulsion and by the physical mixture of PANI in the latex. The polymers were produced by the seeded and fed emulsion polymerization method at 80°C, under nitrogen atmosphere and using sodium persulfate as initiator. Initially, the most suitable conductive latex preparation method to stabilize PANI in aqueous dispersion was investigated. The obtained latices showed a narrow particle size distribution curve, with negative zeta potential (?) values and less than -25 mV, which indicate stable particles in dispersion due to the repulsion between particles caused by the high surface charge, which prevents formation of aggregates over time. Latices in the form of ?free? films obtained by in situ polymerization of aniline in the PABS emulsion and physical mixing of polyaniline in the latex showed electrical conductivity values of 5,9 x 10-3 S.cm-1 and 1,9 x 10-5 S.cm-1 for concentrations of 3% m PANI, respectively. The aqueous dispersions as they are were applied on sanded 1020 carbon steel to evaluate adhesion and anti-corrosion performance. The latices showed good dry adhesion, due to the glass transition temperature, which indicates that the latex developed has good film-forming properties, but with restrictions on wet adhesion performance that compromised the anticorrosive properties. The adhesion characteristics, electrochemical and thermal properties of the PABS mixture containing PANI were not impacted by the latex preparation method. In the micrographs of AFM and SEM it was possible to verify that the aqueous dispersions, developed through in situ polymerization, presented greater homogeneity in the films. The impedance measurements showed that the samples incorporating 1% m PANI showed better anticorrosive properties, probably due to failures in the barrier effect produced by the coating with PANI 3% m, the low adherence to wet conditions and/or the layer of oxides ferric compounds produced by the electrochemical action of the PANI contained in the coating or the DBSA charge, which should sensitize the film. The aqueous dispersions developed in this work have potential application for use in coatings against corrosion, evidenced in electrochemical tests, in which in situ polymerization is recommended as the best method of obtaining, indicating greater stability, electrical conductivity and homogeneity of the latex film produced.Barra, Guilherme Mariz de OliveiraAraújo, Pedro Henrique Hermes deUniversidade Federal de Santa CatarinaLuciano, Rosita Manoel2023-11-09T23:26:36Z2023-11-09T23:26:36Z2023info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis146 p.| il., gráfs.application/pdf384665https://repositorio.ufsc.br/handle/123456789/251865porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2023-11-09T23:26:36Zoai:repositorio.ufsc.br:123456789/251865Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732023-11-09T23:26:36Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
title Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
spellingShingle Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
Luciano, Rosita Manoel
Ciência dos materiais
Engenharia de materiais
Látex
Polímeros condutores
Polimerização em emulsão
title_short Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
title_full Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
title_fullStr Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
title_full_unstemmed Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
title_sort Dispersões aquosas de poli (acrilato de butila-co estireno) a base de polianilina para obtenção de recobrimentos condutores
author Luciano, Rosita Manoel
author_facet Luciano, Rosita Manoel
author_role author
dc.contributor.none.fl_str_mv Barra, Guilherme Mariz de Oliveira
Araújo, Pedro Henrique Hermes de
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Luciano, Rosita Manoel
dc.subject.por.fl_str_mv Ciência dos materiais
Engenharia de materiais
Látex
Polímeros condutores
Polimerização em emulsão
topic Ciência dos materiais
Engenharia de materiais
Látex
Polímeros condutores
Polimerização em emulsão
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2023.
publishDate 2023
dc.date.none.fl_str_mv 2023-11-09T23:26:36Z
2023-11-09T23:26:36Z
2023
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 384665
https://repositorio.ufsc.br/handle/123456789/251865
identifier_str_mv 384665
url https://repositorio.ufsc.br/handle/123456789/251865
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 146 p.| il., gráfs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652393386082304

Registros relacionados