Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300

Detalhes bibliográficos
Autor(a) principal: Figueiredo, Nathália Cândido
Data de Publicação: 2018
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/206095
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2018.
id UFSC_5c913cc9b178c1e756f8813d69071a7e
oai_identifier_str oai:repositorio.ufsc.br:123456789/206095
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300Ciência dos materiaisEngenharia de materiaisCompostos intermetálicosAustenitaForjamentoAço MaragingTese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2018.Aços maraging são aços martensíticos de baixo carbono, altamente ligados, nos quais o endurecimento é atingido por meio de um tratamento térmico de envelhecimento, durante o qual ocorre a precipitação de compostos intermetálicos. A pesquisa nestes materiais é estratégica, pois é um material utilizado nas indústrias aeronáutica, aeroespacial, militar e nuclear. Neste trabalho foi estudado o efeito do forjamento a morno no aço maraging 18Ni C300, utilizando duas temperaturas de conformação (250 e 350 °C), determinadas mediante ensaio de tração. Previamente foi realizada a solubilização dos corpos de prova em duas temperaturas. Já o tratamento térmico de envelhecimento foi feito em três temperaturas e em cinco tempos cada tratamento. As amostras foram analisadas através de microscopia óptica e eletrônica de varredura. Foi feita a quantificação de austenita reversa por meio de difração de raio-X. O efeito da conformação na textura cristalográfica foi analisado por meio de EBSD e por último, a dureza do material foi analisada através do ensaio de microdureza Vickers. Foi observado o efeito Portevin Le Chatelier no ensaio de tração a 350 °C. Nesta temperatura também foi observada a presença de trincas localizadas na região de deformação concentrada. Em ambas as deformações foi observado refino da microestrutura martensítica, sendo esta mais evidente na deformação a 250 °C. Também foi observado que a deformação promoveu a formação de maior quantidade de austenita reversa com o aumento da temperatura de forjamento. Com relação à textura, observou-se que as fibras {110} // DF e {111} // DF aumentaram de intensidade à medida em que se aproxima do centro do corpo de prova forjado, enquanto que a intensidade da orientação {001} // DF diminui. Além disso, os níveis mais baixos de deformação foram observados perto da superfície em contato com a matriz de forjamento, contendo a menor quantidade de emaranhado de discordâncias, que aumentou gradualmente em direção ao centro da amostra.Abstract : Maraging steels are low carbon martensitic steels, highly alloyed, in which hardening is achieved by aging, during this occurs the precipitation of intermetallic compounds. The research in these materials is strategic as it is a material used in the aeronautical, aerospace, military and nuclear industry. In this work was studied forging of 18Ni C300 steel, with two forging temperatures (250 and 350 °C), determined by a tensile test. Previously an annealing treatment was performed at two temperatures. The heat treatment has been done in three temperatures and in five times each. The samples were analyzed by optical and scanning electron microscopy. A quantification of reverted austenite was done by X-ray diffraction. The effect of forging in grain orientation changes was analyzed by back-scatter electron microscopy. A microhardness evaluation was performed by Vickers test. The Portevin Le Chatelier effect was observed in the tensile test at 350 ° C. On this condition, it was also observed the presence of cracks in the shear bands. In both deformations a refinning of the martensitic microstructure was observed, and it was more evident in the deformation at 250 ° C. It was also observed that at higher forging temperature, more reverted austenite was detected. With respect to the texture the {110} // FD and {111} // FD fibers increased with depth, whilst {001} decreases. In addition, the lower strain levels were observed on the surface in contact with the die, containing a smaller amount of tangles of dislocations, which increases towards the center of the sample.Oliveira, Carlos Augusto Silva deUniversidade Federal de Santa CatarinaFigueiredo, Nathália Cândido2020-03-31T14:45:43Z2020-03-31T14:45:43Z2018info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis130 p.| il., gráfs., tabs.application/pdf359953https://repositorio.ufsc.br/handle/123456789/206095porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2020-03-31T14:45:43Zoai:repositorio.ufsc.br:123456789/206095Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732020-03-31T14:45:43Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
title Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
spellingShingle Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
Figueiredo, Nathália Cândido
Ciência dos materiais
Engenharia de materiais
Compostos intermetálicos
Austenita
Forjamento
Aço Maraging
title_short Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
title_full Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
title_fullStr Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
title_full_unstemmed Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
title_sort Efeito do forjamento a morno na microestrutura e dureza de um aço maraging 18Ni C300
author Figueiredo, Nathália Cândido
author_facet Figueiredo, Nathália Cândido
author_role author
dc.contributor.none.fl_str_mv Oliveira, Carlos Augusto Silva de
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Figueiredo, Nathália Cândido
dc.subject.por.fl_str_mv Ciência dos materiais
Engenharia de materiais
Compostos intermetálicos
Austenita
Forjamento
Aço Maraging
topic Ciência dos materiais
Engenharia de materiais
Compostos intermetálicos
Austenita
Forjamento
Aço Maraging
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2018.
publishDate 2018
dc.date.none.fl_str_mv 2018
2020-03-31T14:45:43Z
2020-03-31T14:45:43Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 359953
https://repositorio.ufsc.br/handle/123456789/206095
identifier_str_mv 359953
url https://repositorio.ufsc.br/handle/123456789/206095
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 130 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808651898329235456